• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2003.04a
• /
• pp.46-49
• /
• 2003

Aluminum based metal matrix composites(MMCs) are well known for their high specific strength, stiffness and hardness. They are gaining further importance because of their high wear resistance. In this study, Al/Saffil-20%, Al/Saffil-5%/Al2O3(particle type)-15% and Al/Saffil-5%/SiC(particle type)-15% hybird MMCs' wear behavior were characterized by the pin-on-disk test under various normal load The superior wear resistance was exhibited at Al/Saffil-5%/SiC(particle type)-15% MMCs. And this MMCs' predominant wear mechanism is subsurface cracking in the low load wear regime. Others(Al/Saffil-20%, Al/Saffil-5%/Al2O3(particle type)-15%) showed the similar wear resistance with each other at the same test condition. In the low load & room temperature condition, the wear resistance was improved due to the high hardness of the ceramic reinforcements. As the test load increased, the wear properties were governed by the wear properties of matrix.

• Journal of Korea Foundry Society
• /
• v.14 no.3
• /
• pp.258-266
• /
• 1994

AC4A $Al/Al_2O_3+SiC_p$ hybrid composites were fabricated by the squeeze infiltration technique. Effect of applied pressure, volume fraction of reinforcement($Al_2O_3$ and SiC) and SiC particle size($4.5{\mu}m$, $6.5{\mu}m$ and $9.3{\mu}m$) on the solidification microstructure of the hybrid composites were examined. Mechanical properties were estimated preliminarly by fractographic observation, hardness measurement and wear test. Results show that the microstructure of the hybrid composites were quite satisfactory, namely revealing relatively uniform distribution of reinforcements and refined matrix. Some aggregation of SiC particle caused by particle pushing was observed especially in the hybrid composites containg in fine particle($4.5{\mu}m$). Refined matrix was attributed to applied pressure and increased nucleation sites with addition of reinforcements. Fractured facet also revealed finer for the hybrid composites possibly due to refined matrix. Hardness and wear resistance increased with volume fraction of reinforcements. For hybrid composites with $9.3{\mu}m$ SiC, hardness was somewhat lower and wear resistance higher than other composites.

• Journal of the Korean Ceramic Society
• /
• v.25 no.5
• /
• pp.473-478
• /
• 1988

In order to obtain the high purity $\beta$-SiC powder that possesses the excellent sinterability and is close to the spherical shape, the carbon black was mixed into the composition of Si(OC2H5)4-H2O-NH3-C2H5OH which the monodispersed spherical fine particles is formed the hydrolysis of Ethylsilicate and the mixture was carbonized under an argon atmosphere. Particle shpae, size and the yield of $\beta$-SiC powder were investigated according to the molar ratio of carbon/alkoxide and variations of reaction temperature and reaction time. The results of this study are as follow ; 1) The yield of $\beta$-SiC gained from the reaction for one hour at 150$0^{\circ}C$ almost got near 100% and the particle size of $\beta$-SiC from the reaction for 15 hrs at 150$0^{\circ}C$ was 0.2${\mu}{\textrm}{m}$ on the average and close to the spherical shape agglomerate state. 2) When the molar ratio carbon/alkoxide is over 3.1 and the reaction occurs at 145$0^{\circ}C$ for 5hrs, the carbon content has not an effect on the kind of crystal of product.

• Journal of the Korean Ceramic Society
• /
• v.37 no.2
• /
• pp.152-157
• /
• 2000

Si3N4/SiC nanocomposite ceramics containing 5 wt%dispersed SiC particles were prepared by gas-pressure-sintering at 200$0^{\circ}C$ under nitrogen atmosphere. SiC particles with average sizes of 0.2 and 0.5${\mu}{\textrm}{m}$ were used, and the effect of the SiC particle size on the microstructure was investigated. The addition of SiC particles effectively suppressed the growth of the Si3N4 matrix grains. The effect of grain growth inhibition was higher in the nanocomposites dispersed with fine SiC. SiC particles were dispersed uniformly inside Si3N4 matrix grains and on grain boundaries. When the fine SiC particles were added, large fraction of the SiC particles was trapped inside the grains. On the other hand, when the large SiC particles were added, most of the SiC particles were located on grain boundaries. Typically, the fraction of SiC particles located at grain boundaries was higher in the specimen prepared from $\beta$-Si3N4 than in the specimen prepared from $\alpha$-Si3N4.

• Korean Journal of Materials Research
• /
• v.7 no.2
• /
• pp.145-151
• /
• 1997

Remelting of $A-Si/SiC_{p}$ composites followed by isothermal holding and solidification, leads ro the settling of Sic particles to the bottom of the mold. With the isothermal holding time for molten $A-Si/SiC_{p}$ composites. the particle free zone increases rapidly up to approximately first 30 minutes of the holding time. Experimental resulls of the particle settling confirm that the larger SIC particles sink faster tlun the sniiller particles. An increase in volume fraction of Sic particles decreases the setrling velocity of the particles.

• Bulletin of the Korean Chemical Society
• /
• v.32 no.1
• /
• pp.145-148
• /
• 2011

The thermal behavior of lithiated Si anodes has been investigated using differential scanning calorimetry (DSC). In particular, the effect of Si particle size on the thermal stability of a fully lithiated Si electrode was investigated. For DSC measurements, a lithiated Si anode was heated in a hermetically sealed high-pressure pan with a polyvinylidene fluoride (PVDF) binder and a 1 M $LiPF_6$ solution in an ethylene carbonate (EC)-diethyl carbonate (DEC) mixture. The thermal evolution around $140^{\circ}C$ increases with lithiation and with decreasing particle size; this phenomenon is attributed to the thermal decomposition of the solid electrolyte interface (SEI) film. Exothermic peaks, following a broad peak at around $140^{\circ}C$, shift to a lower temperature with a decrease in particle size, indicating that the thermal stability of the lithiated Si electrode strongly depends on the Si particle size.

• Journal of the Korean institute of surface engineering
• /
• v.30 no.5
• /
• pp.347-354
• /
• 1997

Composite plating is a method of co-depositing fine particles of metallic, non-metallic compound or polymers in the plated layer to improve material properties such as were-resistance, lubrication, or corrosion resistance. Graded Ni-Sic composite coating were produced in this research. Prior to produce Graded Ni-SiC composite coatings, effects of particle size, particle content, pH of electrolyte, temperature, current density, stirring rate on the amount of SiC deposited in the Ni layer were investigated. By manipulating current density and plating time properties of these coating were evaluated by micro-indentation hardness test.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.4
• /
• pp.1301-1308
• /
• 1996

In order to save the energy and protect the environment, it were studied about ecomaterials with the developed countries as central figure. In the Metal Matrix Composites(MMCs), this trends appeared the development of the MMCs which had excellent mechanical properties in spite of the low volume fraction of reinforcement. Therefore, in this study, fatigue crack growth test, tensile and hardness test were conducted in order to investigate the mechanical and fatigue properties of 5 %, and 10 % $SiC_{p}$/Al composites. As the results, in the tensile and hardness test, tensile strength and hardness increased but fatigue crack growth rate decreased with $SiC_{p}$/Al volume fraction. And in the view of fatigue failured surface through the SEM, fatigue crack initiated around the SiC particle and in low $\Delta{K}$ regions, fatigue creck detoured the SiC particle but crack propagated through the SiC particle in the high $\DeltaK$ regions.

• Composites Research
• /
• v.25 no.6
• /
• pp.172-177
• /
• 2012

For the manufacture of low resistance Si-SiC composite, the properties of reaction sintering in the green body of various mixed ${\alpha}$-SiC powder size with the various carbon contents from 0wt% to 20wt% were investigated. The samples preparation was green body by CIP method under this condition, molten silicon infiltration process was conducted to reaction bonded silicon carbide. the results of sintered density, 3-point bending strength and resistance of analysis showed that varied carbon and silicon melt reacted to convert to fine ${\beta}$-SiC particle and the structure was changed to dense material. The amount of fine ${\beta}$-SiC particle was gradually increased as carbon content increase. According to mixed composite, it's mechanical and specific resistivity properties was strongly influenced by carbon content within 10wt% more then carbon content 10wt% was strongly influenced by phase transition.

• Journal of the Korean Ceramic Society
• /
• v.34 no.8
• /
• pp.854-860
• /
• 1997

The tribological property of ceramics is very important for use in seal rings, pump parts, thread guides and mechanical seal, etc. In the present study, which RBSC/graphite composites were manufactured by adding graphite powders with different particle sizes to mixtures of SiC powder, metallic silicon, carbon black and alumina, effects on the tribological property of each RBSC/graphite composite was investigated in accordance with the particle size of the added graphite powder. The water absorption, the bending strength and the resistance for the friction and wear were measured, and the crystalline phase and the microstructure were respectively examined by using XRD and SEM. In case that the particle size of the graphite powder was fine(2${\mu}{\textrm}{m}$), the formation of $\beta$-SiC was accelerated, thereby making the increase of the bending strength and the decrease of the water absorption, but no improvement for the tribological properties. Furthermore, in case that the particle size of the graphite powder was some large(88~149${\mu}{\textrm}{m}$), the formation of $\beta$-SiC was not accelerated, to thereby make the decrease of the bending strength and the increase of the water absorption, but the improvement for the tribological property of only the composite having the graphite powder of 20 vol%. In addition, in case that the particle size distribution of the graphite powder was large (under 53 ${\mu}{\textrm}{m}$), there was no improvement for every properties. However, the composites, which the graphite powder with the particle size of 53~88 ${\mu}{\textrm}{m}$ was added in 10~15 vol%, had the most increased resistance for the friction and wear which show the worn out amount of 0.4~0.6$\times$10-3 $\textrm{cm}^2$, and the value of the bending strength is 380~520 kg/$\textrm{cm}^2$.