• 한국표면공학회지
• /
• 제29권5호
• /
• pp.430-436
• /
• 1996

We have grown superconducting thin films on various substrates using a pulsed laser deposition (PLD) method. $YBa_2Cu_3O_7-\delta$ (YBCO) superconducting thin films with the superconducting transition temperature ($T_{c. offset}$) of 87K were grown on Si substrates using yittria-stabilized zirconia (YSZ) and $CeO_2$ double buffer layers. We have developed a large area pulsed laser deposition system. The system was designed to deposit up to 6 different materials on a large area substrate up to 7.5cm in diameter without breaking a vacuum. The preliminary runs of the deposition of YBCO superconducting thin films on $SrTiO_3$ substrate using this system showed a very uniform thickness profile over the entire substrate holder area. $T_{c}$ of the deposited YBCO thin film, however, was scattered depending on the position and the highest value was 85K.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2003년도 추계학술발표회초록집
• /
• pp.54-54
• /
• 2003

DLC films were deposited on Si(100) substrates by inductively coupled plasma (ICP) assisted chemical vapor deposition (CVD). A mixture of acetylene (C$_2$H$_2$) and argon (Ar) gases was used as the precursor and plasma source, respectively. The structure of the films was characterized by the Raman spectroscopy. Results from the Raman spectroscopy analysis indicated that the property change of the DLC films is due to the sp$^3$ and sp$^2$ ratio in the films under various conditions such as ICP power, working pressure and RF substrate bias. The hydrogen content in the DLC films was determined by an electron recoil detector (ERB). The roughness of the films was measured by atomic force microscope (Am). A microhardness tester was used for the hardness and elastic modulus measurement. The DLC film showed a maximum hardness of 37㎬. In this work, the relationship between deposition parameters and mechanical properties were discussed.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2016년도 제50회 동계 정기학술대회 초록집
• /
• pp.264-264
• /
• 2016

최근에 charge trap flash (CTF) 기술은 절연막에 전하를 트랩과 디트랩 시킬 때 인접한 셀 간의 간섭현상을 최소화하여 오동작을 줄일 수 있으며 낸드 플래시 메모리 소자에 적용되고 있다. 낸드 플래시 메모리는 고집적화, 대용량화와 비휘발성 등의 장점으로 인해 핸드폰, USB, MP3와 컴퓨터 등에 이용되고 있다. 기존의 실리콘 기반의 플래시 메모리 소자는 좁은 밴드갭으로 인해 투명하지 않고 고온에서의 공정이 요구되는 문제점이 있다. 따라서, 이러한 문제점을 개선하기 위해 실리콘의 대체 물질로 산화물 반도체 기반의 플래시 메모리 소자들이 연구되고 있다. 산화물 반도체 기반의 플래시 메모리 소자는 넓은 밴드갭으로 인한 투명성을 가지고 있으며 저온에서 공정이 가능하여 투명하고 유연한 기판에 적용이 가능하다. 다양한 산화물 반도체 중에서 비정질 In-Ga-Zn-O (a-IGZO)는 비정질임에도 불구하고 우수한 전기적인 특성과 화학적 안정성을 갖기 때문에 많은 관심을 받고 있다. 플래시 메모리의 고집적화가 요구되면서 절연막에 high-k 물질을 atomic layer deposition (ALD) 방법으로 적용하고 있다. ALD 방법을 이용하면 우수한 계면 흡착력과 균일도를 가지는 박막을 정확한 두께로 형성할 수 있는 장점이 있다. 또한, high-k 물질을 절연막에 적용하면 높은 유전율로 인해 equivalent oxide thickness (EOT)를 줄일 수 있다. 특히, HfOx와 AlOx가 각각 trap layer와 blocking layer로 적용되면 program/erase 동작 속도를 증가시킬 수 있으며 넓은 밴드갭으로 인해 전하손실을 크게 줄일 수 있다. 따라서 본 연구에서는 ALD 방법으로 AlOx와 HfOx를 게이트 절연막으로 적용한 a-IGZO 기반의 thin-film transistor (TFT) 플래시 메모리 소자를 제작하여 메모리 특성을 평가하였다. 제작 방법으로는, p-Si 기판 위에 열성장을 통한 100 nm 두께의 SiO2를 형성한 뒤, 채널 형성을 위해 RF sputter를 이용하여 70 nm 두께의 a-IGZO를 증착하였다. 이후에 소스와 드레인 전극에는 150 nm 두께의 In-Sn-O (ITO)를 RF sputter를 이용하여 증착하였고, ALD 방법을 이용하여 tunnel layer에 AlOx 5 nm, trap layer에 HfOx 20 nm, blocking layer에 AlOx 30 nm를 증착하였다. 최종적으로, 상부 게이트 전극을 형성하기 위해 electron beam evaporator를 이용하여 platinum (Pt) 150 nm를 증착하였고, 계면 결함을 최소화하기 위해 퍼니스에서 질소 가스 분위기, $400^{\circ}C$, 30 분의 조건으로 열처리를 했다. 측정 결과, 103 번의 program/erase를 반복한 endurance와 104 초 동안의 retention 측정으로부터 큰 열화 없이 메모리 특성이 유지되는 것을 확인하였다. 결과적으로, high-k 물질과 산화물 반도체는 고성능과 고집적화가 요구되는 향후 플래시 메모리의 핵심적인 물질이 될 것으로 기대된다.

• 한국재료학회지
• /
• 제6권7호
• /
• pp.723-732
• /
• 1996

ICB 공정으로 선행 증착한 Cu Seeding 층이 이후의 CVD 공정으로 증착하는 최종의 Cu 박막의 기계적 전기적 특성에 미치는 영향을 고찰하였고, seening을 하지 않은 CVD-Cu 박막과의 특성을 비교하였다. seeding 층을 형성한 경우의 CVD-Cu 박막에 있어서 증착 속도가 증가하였으며, grain 크기의 균일성도 향상되는 경향을 보였다. 증착된 Cu 박막은 seening에 무관하게 모두 FCC 우선배향인 (111)의 결정배향을 나타냈으며, seeding 우에 성정된 박막의 경우 $I_{111}/I_{200}$비가 향상되었다.$ 180^{\circ}C$의 동일 조건하에서 증착하는 경우 $40\AA$ seeding층 위에 성장한 박막의 전기비저항이 $2.42\mu$$\Omega$.cm로 낮은 값을 나타내었으며, 130$\AA$ seeding 경우는 오히려 전기비저항이 증가하는 경향을 나타내었다. Cu 박막의 접착력은 seeding층의 두께가 $0\AA$에서 $130\AA$으 증가함에 따라 21N에서 27N 으로 향상되었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2010년도 하계학술대회 논문집
• /
• pp.11-11
• /
• 2010

Thin-film-transistors (TFTs) that can be deposited at low temperature have recently attracted lots of applications such as sensors, solar cell and displays, because of the great flexible electronics and transparent. Transparent and flexible transistors are being required that high mobility and large-area uniformity at low temperature [1]. But, unfortunately most of TFT structures are used to be $SiO_2$ as gate dielectric layer. The $SiO_2$ has disadvantaged that it is required to high driving voltage to achieve the same operating efficiency compared with other high-k materials and its thickness is thicker than high-k materials [2]. To solve this problem, we find lots of high-k materials as $HfO_2$, $ZrO_2$, $SiN_x$, $TiO_2$, $Al_2O_3$. Among the High-k materials, $Al_2O_3$ is one of the outstanding materials due to its properties are high dielectric constant ( ~9 ), relatively low leakage current, wide bandgap ( 8.7 eV ) and good device stability. For the realization of flexible displays, all processes should be performed at very low temperatures, but low temperature $Al_2O_3$ grown by sputtering showed deteriorated electrical performance. Further decrease in growth temperature induces a high density of charge traps in the gate oxide/channel. This study investigated the effect of growth temperatures of ALD grown $Al_2O_3$ layers on the TFT device performance. The ALD deposition showed high conformal and defect-free dielectric layers at low temperature compared with other deposition equipments [2]. After ITO was wet-chemically etched with HCl : $HNO_3$ = 3:1, $Al_2O_3$ layer was deposited by ALD at various growth temperatures or lift-off process. Amorphous InGaZnO channel layers were deposited by rf magnetron sputtering at a working pressure of 3 mTorr and $O_2$/Ar (1/29 sccm). The electrodes were formed with electron-beam evaporated Ti (30 nm) and Au (70 nm) bilayer. The TFT devices were heat-treated in a furnace at $300^{\circ}C$ and nitrogen atmosphere for 1 hour by rapid thermal treatment. The electrical properties of the oxide TFTs were measured using semiconductor parameter analyzer (4145B), and LCR meter.

• 센서학회지
• /
• 제2권1호
• /
• pp.101-108
• /
• 1993

컬러센서를 위한 $TiO_{2}$/Se : Te 이종접합을 고주파 반응성 스퍼터링법과 진공증착법을 이용하여 제작하였다. 제조된 $TiO_{2}$ 막형성의 최적조건은 $1000{\AA}$의 $TiO_{2}$ 두께에서 고주파전력 120 W, 기판온도 $100^{\circ}C$, 산소농도 50% 및 분위기압 50 mTorr였다. 이 때 광투과율은 파장 550 nm에서 85%, 저항률은 $2{\times}10^9{\Omega}{\cdot}cm$, 굴절률은 2.3이었다. 제조된 $TiO_{2}$막은 직접천이형 에너지 밴드구조를 가지며 광학적 밴드갭은 3.58 eV였다. 제조된$TiO_{2}$막을 $400^{\circ}C$에서 30분간 열처리함으로써 광투과율이 파장 $300{\sim}580$ nm범위에서 $0{\sim}25%$까지 개선되었다. 또한 화학양론적 조성비를 조사하기 위하여 AES 분석을 한 결과 Ti 및 0의 조성비는 1 : 1.7로 나타났다. 한편 Se : Te 막형성의 최적조건은 $190^{\circ}C$에서 1분간 열처리했을 때였다. 이러한 조건으로 제조된 Se : Te막의 광학적 밴드갭은 1.7 eV였으며 육방정계구조의 (100) 방향 및 (110) 방향으로 Se : Te 막이 결정화됨을 알 수 있었다. 1000 lux의 조도에서 Se : Te막의 광전변환률은 0.75였다. 또한 Se에 Te를 첨가함으로써 장파장영역의 분광감도가 향상되었다. $TiO_{2}$/Se : Te 이종접합의 분광감도는 가시광 전영역에서 비교적 넓은 분광감도를 나타내었으며, 특히 청색영역에서 a-Si박막보다 우수한 분광감도를 나타내었다.

• 전기화학회지
• /
• 제8권1호
• /
• pp.32-36
• /
• 2005

본 연구는 $WO_3$ 박막과 $NiO-WO_3$ 박막을 고진공 저항가열식 thermal evaporation 법으로 (100) n형의 실리콘 단결정 기판 위에 증착시켰고, 막의 결정성 증진을 위하여 공기 중 $500^{\circ}C$에서 30분 동안 열처리하였다. 박막의 결정성 및 결정구조를 분석하기 위해서 X선 회절분석기를 사용하였고, 표면 및 단면 관찰을 위해서는 주사전자현미경을 이용하였다. 그리고 화학 조성 결합에너지는 XPS를 이용하였다. 순수 $WO_3$ 박막의 결정 크기는 $500^{\circ}C$에서 30분 동안 공기중 열처리에 의해서 $0.6{\mu}m$로 성장하였고 $WO_3$ 박막의 두께가 증가할수록 거의 변화 없이 일정하였다. 반면, NiO가 첨가된 $WO_3$ 박막 두께별 결정크기는 각각 $0.12{\mu}m,\;0.28{\mu}m,\;0.32{\mu}m$및 $0.43{\mu}m$로 순수 $WO_3$ 박막에 비해 치밀한 표면을 형성하였고, 최대 5배정도 성장이 억제되었다. 가스감도 측정은 대기 중에서의 센서 저항 값을 기준으로 측정가스 저항 값의 비율 $(R_{NOx}/R_{air})$로 가스감도를 나타내었다. 전기적 성질은 MFC로 NOx가스 5ppm을 일정히 유지시켰고, Multimeter로 계측하여 컴퓨터에 자동 계측되는 시스템을 사용하였다. 순수 $WO_3$박막보다는 $NiO-WO_3$ 박막이 우수한 NOx 감도특성을 보였고 센서의 작동온도는 $250^{\circ}C$에서 우수한 감도를 나타내었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 하계학술대회 논문집 Vol.9
• /
• pp.66-66
• /
• 2008

Most of the properties of ITO films depend on their substrate nature, deposition techniques and ITO film composition. For the display panel application, it is normally deposited on the glass substrate which has high strain point (>575 degree) and must be deposited at a temperature higher than $250^{\circ}C$ and then annealed at a temperature higher than $300^{\circ}C$ in order to high optical transmittance in the visible region, low reactivity and chemical duration. But the high strain point glass (HSPG) used as FPDs is blocking popularization of large sizes FPDs because it is more expensive than a soda lime glass (SLG). If the SLG could be used as substrate for FPDs, then diffusion of Na ion from the substrate occurs into the ITO films during annealing or heat treatment on manufacturing process and it affects the properties. Therefore proper care should be followed to minimize Na ion diffusion. In this study, we investigate the electrical, optical and structural properties of ITO films deposited on the SLG and the Asahi glass(PD200) substrate by rf magnetron sputtering using a ceramic target ($In_2O_3:SnO_2$, 90:10wt.%). These films were annealed in $N_2$ and air atmosphere at $400^{\circ}C$ for 20min, 1hr, and 2hrs. ITO films deposited on the SLG show a high electrical resistivity and structural defect as compared with those deposited on the PD200 due to the Na ion from the SLG on diffuse to the ITO film by annealing. However these properties can be improved by introducing a barrier layer of $SiO_2$ or $Al_2O_3$ between ITO film and the SLG substrate. The characteristics of films were examined by the 4-point probe, FE-SEM, UV-VIS spectrometer, and X-ray diffraction. SIMS analysis confirmed that barrier layer inhibited Na ion diffusion from the SLG.

• 한국자기학회지
• /
• 제19권3호
• /
• pp.85-88
• /
• 2009

다결정 $Ge_{1-x}Mn_x$ 박막의 자기적 상들에 관한 연구가 이루어졌다. Molecular beam epitaxy(MBE) 장비를 이용해 $400^{\circ}C$ 에서 $Ge_{1-x}Mn_x$ 박막을 성장시켰다. $Ge_{1-x}Mn_x$ 박막의 캐리어 유형은 P타입 이였고, 전기 비저항 값은 $4.0{\times}10^{-2}{\sim}1.5{\times}10^{-4}ohm-cm$이었다. 자기적인 특성과 미세구조의 분석에 기초하여 $Ge_{1-x}Mn_x/SiO_2$/Si(100) 박막에 310 K 이내의 큐리에온도를 지닌 강자성의 $Ge_3Mn_5$ 상이 형성되었음을 알 수 있었다. 게다가, $Ge_3Mn_5$ 상이 형성된 $Ge_{1-x}Mn_x$ 박막은 20 K, 9 T의 자기장에서 약 9%의 음의 자기저항을 보였다.

• 한국정보통신학회:학술대회논문집
• /
• 한국해양정보통신학회 2005년도 춘계종합학술대회
• /
• pp.1026-1029
• /
• 2005

Grating 이 형성된 SiO$_2$ 기판상에 ZnO 박막을 graphoepitaxy 법으로 형성시킬 것을 제안하고 그 가능성을 고찰하였다. Si(100) 기판상에 노광작업(photolithograpy)을 이용하여 요철구조를 형성시킨 다음 자연산화를 시켜서 SiO$_2$ 기판을 제작하였고, 제작된 요철구조 위에 열증착 법으로 Zn 를 증착 시킨 후 이를 산화 시켜서 ZnO 박막을 형성 시켰다. 또한 열처리에 의한 결정성의 변화를 관찰하기 위하여 700 ${\sim}$ 900 $^{\circ}C$에서 열처리를 하였다. 제작된 시료는 Atomic Force Microscopy (AFM)로 표면을 관찰하였으며, Photoluminescence (PL) 을 이용하여 결정성의 변화를 관찰하였다.