• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.31 no.4
• /
• pp.425-431
• /
• 2007

[ $Al_2O_3/SiC$ ]composite ceramics were sintered to evaluate the bending strength and elastic wave characteristics. The three-point bending test was carried out under room temperature. The elastic wave was detected by fracture wave detector. The crack healing behavior was investigated from 1373 K to 1723 K. The bending strength of $Al_2O_3/SiC$ composite by nanocomposite is higher than that of $Al_2O_3$ monolithic. Crack-healing behavior depended on an amount of additive powder $Y_2O_3$. In $Al_2O_3/SiC$ composite ceramics with 3 wt. % $Y_2O_3$ for additive powder, the bending strength at 1573 K is about 100% increase than that of the smooth specimens. From the result of wavelet analysis of elastic wave signal, the smooth specimen and heat treated specimen of $Al_2O_3$ monolithic and $Al_2O_3/SiC$ composite ceramics showed characteristics of frequency about 58 kHz. The strength of $Al_2O_3/SiC$ composite ceramics was a little higher than those of $Al_2O_3$ monolithic. The dominant frequencies were high with increasing of $Y_2O_3$ for additive powder. The dominant frequencies had direct connection with the bending strength.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2006.11a
• /
• pp.166-168
• /
• 2006

$Si_3N_4/SiC$ composite ceramics was sintered in order to investigate their bending strength behavior after crack healing. $Y_2O_$ and $TiO_2$ power was added as sintering additives to enhance it's sintering property. A three-point bending specimen was cut out from sintered plates. About $100\;{\mu}m$ semi-circular surface cracks were made on the center of the tension surface of the three-point bending specimen using Vickers indenter. After the crack-healing processing from $500^{\circ}C$ to $1300^{\circ}C$, for 1 h, in air, the bending strength behavior of these crack-healed specimen coated with $SiO_2$ colloidal were determined systematically at room temperature. $Si_3N_4/SiC$ ceramics using additive powder ($Y_2O_3+TiO_2$) was superior to that of additive powder $Y_2O_3$. The additive powder $TiO_2$ exerted influence at growth of $Si_3N_4$. The optimum crack healing conditions coated $SiO_2$ colloidal were $1000^{\circ}C$ at $Si_3N_4/SiC$ using additive powder ($Y_2O_3+TiO_2$), and $1300^{\circ}C$ at $Si_3N_4/SiC$ using additive powder $Y_2O_3$.

• Journal of the Korean Society for Precision Engineering
• /
• v.29 no.3
• /
• pp.273-278
• /
• 2012

$ZrB_2$ has a melting temperature of $3245^{\circ}C$ and a low density of $6.1\;g/cm^3$, which makes this a candidate for application to ultra-high temperature over $2000^{\circ}C$. Beside these properties, $ZrB_2$ has excellent resistance to thermal shock and oxidation compared with other non-oxide engineering ceramics. This paper reviewed briefly 2 research examples, which are related to densification and properties of $ZrB_2$-based ceramics for ultra-high temperature applications. In the first section, the effect of $B_4C$ addition on the densification and properties of $ZrB_2$-based ceramics is shown. $ZrB_2$-20 vol.% SiC system was selected as a basic composition and $B_4C$ or C was added to this system in some extents. With sintered bodies, densification behavior and hightemperature (up to $1400^{\circ}C$) properties such as bending strength and hardness are examined. In the second section, the effect of the SiC size on the microstructures and physical properties is shown. $ZrB_2$-SiC ceramics are fabricated by using various SiC sources in order to investigate the grain-growth inhibition and the mechanical/thermal properties of $ZrB_2$-SiC.

• Journal of Powder Materials
• /
• v.19 no.5
• /
• pp.379-384
• /
• 2012

This paper reports the microstructures and thermal conductivities of $ZrB_2$-SiC composite ceramics with size and amount of SiC. We fabricated sintered bodies of $ZrB_2$-x vol.% SiC (x=10, 20, 30) with submicron and nanosized SiC densified by spark plasma sintering. Microstructure retained the initial powder size of especially SiC, except the agglomeration of nanosized SiC. For sintered bodies, thermal conductivities were examined. The observed thermal conductivity values are 40~60 W/mK, which is slightly lower than the reported values. The relation between microstructural parameter and thermal conductivity was also discussed.

• Journal of the Korean Ceramic Society
• /
• v.52 no.6
• /
• pp.455-461
• /
• 2015

Porous ceramics with tailored pore size and shape are promising materials for the realization of a number of functional and structural properties. A novel method has been reported for the investigation of the role of SiC in the formation of $SiO_2$ foams by colloidal wet processing. Within a suitable pH range of 9.9 ~ 10.5 $SiO_2$, particles were partially hydrophobized using hexylamine as an amphiphile. Different mole ratios of the SiC solution were added to the surface modified $SiO_2$ suspension. The contact angle was found to be around $73^{\circ}$, with an adsorption free energy $6.8{\times}10^{-12}J$. The Laplace pressure of about 1.25 ~ 1.6 mPa was found to correspond to a wet foam stability of about 80 ~ 85%. The mechanical and thermal properties were analyzed for the sintered ceramics, with the highest compressive load observed at the mole ratio of 1:1.75. Hertzian indentations are used to evaluate the damage behavior under constrained loading conditions of $SiO_2$-SiC porous ceramics.

• Journal of the Microelectronics and Packaging Society
• /
• v.3 no.2
• /
• pp.27-38
• /
• 1996

Lithium fluorhectorite 결정상을 함유한 glass ceramics 분말의 형성과 제조된 glass ceramics 분말을 이용한 저온 소결기판의 특성평가를 하였다. Li2O-MgO-MgF2-SiO2 계 유 리로 핵형성 및 결정 성장을 실시하여 lithium fluorhectorite 결정상을 지닌 glass ceramics 를 제조하였다. 유리시편의 핵형성 온도는 46$0^{\circ}C$였고 결정성장온도는 600, 640, 110$0^{\circ}C$에서 나타났다. $600^{\circ}C$에서의 결정상으 Li2.4LiSi4O10F2가 나타났다. Li2.4Mg8LiSi4와 Li2.8Mg0.6SiO4은 lithium fluorhectorite 결정상으로 되기 위한 중간상임을 확인할수 있었다. 64$0^{\circ}C$에서 열처리 후 110$0^{\circ}C$에서 재열처리하여 형성된 결정은 lithium fluorhectorite 와 tridymite가 최종 결정 상으로 나타났다. 이것은 수중에서 water swelling 현상에 의하여 분말화할 수 있었다, 기판 제조용 slurry를 제조하기 위해 glass ceramics 분말에 Al2O3분말을 0,25,50wt%로 혼합한것 과 glass ceramics 분말에 potashborosilica-te glass 분말을 15, 30, 45, 60 wt% 로 배합하 여 doctor blade 법으로 green sheet를 제조하였다. green sheet 는 950~150$0^{\circ}C$로소성하여 기판의 특성을 평가하였다. 겉보기 기공율은 3.06~19,14%이었고, 전기적 특성으로 유전상수 는 3~5(100KHz)를 나타내었다.

• Journal of the Korean Ceramic Society
• /
• v.47 no.6
• /
• pp.578-582
• /
• 2010

$ZrB_2$ has a melting point of $3245^{\circ}C$ and a relatively low density of $6.1\;g/cm^3$, which makes this a candidate for application to ultrahigh temperature environments over $2000^{\circ}C$. Beside these properties, $ZrB_2$ is known to have excellent resistance to thermal shock and oxidation compared with other non-oxide engineering ceramics. In order to enhance such oxidation resistance, SiC was frequently added to $ZrB_2$-based systems. Due to nonsinterability of $ZrB_2$-based ceramics, research on the sintering aids such as $B_4C$ or $MoSi_2$ becomes popular recently. In this study, densification and high-temperature properties of $ZrB_2$-SiC ceramics especially with $B_4C$ are investigated. $ZrB_2$-20 vol% SiC system was selected as a basic composition and $B_4C$ or C was added to this system in some extents. Mixed powders were sintered using hot pressing (HP). With sintered bodies, densification behavior and high-temperature (up to $1400^{\circ}C$) properties such as flexural strength, hardness, and so on were examined.

• Journal of the Korean Ceramic Society
• /
• v.32 no.6
• /
• pp.643-652
• /
• 1995

Si-SiC-graphite composites were developed by incorporating solid lubricant graphite into Si-SiC, in the light of improving tribological properties of Si-SiC ceramics. Si-SiC-graphite composites were fabricated by infilterating silicon melt into the mixture of α-SiC, carbon black and graphite powder at 1750℃ under 3 Torr. The particle size of graphite was in the range of 150 to 500㎛, and the loading content of graphite was 0, 20, 25, 30, 35 vol% in the mixture of α-SiC and carbon black. The mechanical and tribological properties of this composites were studied. The density, hardness, flexural strength, compressive strength and Young's modulus were decreased with increasing of graphite content. An additiion of solid-lubricant graphite up to 30 vol% has improved tribological properties of Si-SiC ceramics without considerable degradation of mechanical properties.

• Proceedings of the Korean Ceranic Society Conference
• /
• 1986.12a
• /
• pp.156-161
• /
• 1986

Sialon $Si_3N_4$ and SiC powders and ceramics were prepared from Korean natural resources. The properties of the powders and sintered ceramics obtained in this work are considered to be comparable to those of foreign articles.

• Journal of the Korean Ceramic Society
• /
• v.43 no.8 s.291
• /
• pp.509-514
• /
• 2006

In this study, chopped Hi-Nicalon SiC fiber Reinforced Porous Reaction Bonded SiC (RBSC) composites and it fabrication process were developed by using Si melt infiltration process. The porosity and average pore size in fabricated chopped SiC fiber reinforced porous RBSC composites were in the range of $30{\sim}40%$ and $40-90{\mu}m$, which mainly determined by the SiC powder size used as starting material and amount of residual Si in porous composites. The maximum flexural strength of chopped SiC fiber reinforced porous RBSC composite was as high as 80 MPa. The delayed fracture behavior was observed in chopped SiC fiber reinforced porous RBSC composites upon 3-point bending strength test.