• 한국표면공학회지
• /
• 제40권6호
• /
• pp.279-282
• /
• 2007

Cr-Mo-Si-C-N coatings were deposited on steel and Si wafer by a hybrid system of AIP and sputtering techniques using Cr, Mo and Si target in $Ar/N_2/CH_4$ gaseous mixture. Instrumental analyses of XRD and XPS revealed that the Cr-Mo-Si-C-N coatings must be a composite consisting of fine(Cr, Mo and Si)(C and N) crystallites and amorphous $Si_3N_4$ and SiC. The hardness value of Cr-Mo-Si-C-N coatings significantly increased from 41 GPa of Cr-Mo-C-N coatings to about 53 GPa with Si content of 9.3 at.% due to the refinement of (Cr, Mo and Si)(C and N) crystallites and the composite microstructure characteristics. A systematic investigation of the microstructures and mechanical properties of Cr-Mo-Si-C-N coatings prepared with various Si contents is reported in this paper.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제49권10호
• /
• pp.559-563
• /
• 2000

The $(Sr_{1-x}Ca_x)TiO_3(SCT)$ thin films are deposited on Pt-coated(Pt/TiN/$SiO_2$/Si) using RF sputtering method with substitutional contents of Ca. The maximum grain of thin films is obtained by substitution of Ca at 15[mol%]. Also the composition of SCT thin films were closed to stoichiometry(1.081∼1.117 in A/B/ ratio). The dielectric constant was increased with increasing the substitutional contents of Ca, while it was decreased if the substitutional contents of Ca exceeded over 15[mol%]. The dielectric constant changes almost linearly in temperature ranges of -80∼+90[^${\circ}C$]. The temperature properties of the dielectric loss have a stable value within 0.02 independent of the substitutional contents of Ca. All SCT thin films used in this study show the phenomena of dielectric relaxation with the increase of frequency, and the relaxation frequency is observed above 2000[kHz]. The current-voltage characteristics of SCT15 thin films showed the increasing leakage current as the measuring temperature increase.

• 한국재료학회지
• /
• 제22권4호
• /
• pp.169-173
• /
• 2012

Recently, various attempts to produce a heat sink made of Al 6xxx alloys have been carried out using die-casting. In order to apply die-casting, the Al alloys should be verified for die-soldering ability with die steel. It is generally well known that both Fe and Mn contents have effects on decreasing die soldering, especially with aluminum alloys containing substantial amounts of Si. However, die soldering has not been widely studied for the low Si aluminum (1.0~2.0wt%) alloys. Therefore, in this study, an investigation was performed to consider how the soldering phenomena were affected by Fe and Mn contents in low Si aluminum alloys. Each aluminum alloy was melted and held at $680^{\circ}C$. Then, STD61 substrate was dipped for 2 hr in the melt. The specimens, which were air cooled, were observed using a scanning electron microscope and were line analyzed by an electron probe micro analyzer. The SEM results of the dipping soldering test showed an Al-Fe inter-metallic layer in the microstructure. With increasing Fe content up to 0.35%, the Al-Fe inter-metallic layer became thicker. In Al-1.0%Si alloy, the additional content of Mn also increased the thickness of the inter-metallic layer compared to that in the alloy without Mn. In addition, EPMA analysis showed that Al-Fe inter-metallic compounds such as $Al_2Fe$, $Al_3Fe$, and $Al_5Fe_2$ formed in the die soldering layers.

• Journal of Microbiology and Biotechnology
• /
• 제17권9호
• /
• pp.1573-1578
• /
• 2007

An increasing number of applications is being developed for the use of nanoparticles in various fields. We investigated possible toxicities of nanoparticles in cell culture and in mice. Nanoparticles tested were Zn (300 nm), Fe (100 nm), and Si (10-20, 40-50, and 90-110 nm). The cell lines used were brain, liver, stomach, and lung from humans. In the presence of nanopaticles, mitochodrial activity decreased zero to 15%. DNA contents decreased zero to 20%, and glutathione production increased zero to 15%. None of them showed a dose dependency. Plasma membrane permeability was not altered by nanoparticles. In the case of Si, different sizes of the nanoparticles did not affect cytotoxicity. The cytotoxicity was also shown to be similar in the presence of micro-sized ($45\;{\mu}m$) Si particles. Organs from mice fed with nanoparticles showed nonspecific hemorrhage, lymphocytic infiltration, and medullary congestion. A treatment with the micro-sized particle showed similar results, suggesting that the acute in vivo toxicity was not altered by nano-sized particles.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2016년도 춘계 학술논문 발표대회
• /
• pp.51-52
• /
• 2016

This paper researches the Chloride Binding of Cement Paste according to the Ca/Si and Ca/Al Ratio. The mechanisms of chloride ion binding are not completely known, although it is believed that Alumina contents in cementitious system have an important role. For changing cement paste composition, Ordinary Portland Cement(OPC) paste is substituted by Granulated Ground Blast Slag(GGBS). With increasing the ratio of GGBS substitution(Thus alumina contents is increasing), The chloride binding capacity has a tendency to increase of binding chloride ion capacity.

• International Journal of Contents
• /
• 제5권3호
• /
• pp.57-64
• /
• 2009

Korea has relied on top down development method, in which companies, research and education institutions move into the industrial complexes established by the government. However, to improve local competitiveness, the paradigm is shifting from the government initiated industrial complex to the clusters based on the cooperative network of the region. Representative case is 'Samcheok-si Fire & Emergency industry cluster construction project' that begun in 2007. AHP technique analysis results on first-stage showed that priority was on policy and network elements, and the results of second-stage analysis show that priority was on Policy incentives to internationalize the cluster and strengthen link,. Cluster branding, Sharing of organizational culture to cope with changes in environment, Creation of group learning culture. The subject of this research is limited to Samcheok-si's the Fire and Emergency Industry cluster formation project. Therefore, the research area and standard should be expanded to increase generality in further researches.

• 열처리공학회지
• /
• 제29권5호
• /
• pp.209-215
• /
• 2016

In this study, the effect of Nb contents and processing parameters on dynamic recrystallization behaviour of 0.15C-0.2Si-0.5Mn low-carbon steels was investigated. Three kinds of steel specimens with different Nb contents were fabricated and then high-temperature compressive deformation test was conducted by varying reheating temperature (RT), deformation temperature (DT), and strain rate (SR). The Nb2 and Nb4 specimens containing Nb had smaller prior austenite grain size than the Nb0 specimens, presumably due to pinning effect by the formation of carbides and carbonitrides precipitates at austenite grain boundaries. The high-temperature compressive deformation test results showed that dynamic recrystallization behavior was suppressed in the specimens containing Nb as the strain rate increased and deformation temperature decreased because of pinning effect by precipitates, grain boundary dragging effects by solute atoms, although the compressive stress increased with increasing strain rate and decreasing deformation temperature.

• 한국공작기계학회:학술대회논문집
• /
• 한국공작기계학회 2003년도 추계학술대회
• /
• pp.89-94
• /
• 2003

Hard coatings are known to improve the performance of cutting tools in aggressive machining applications, such as high speed machining. New superhard Ti-Al-Si-W films, characterized by a nanocomposite nano-sized (Ti,Al,Si)N crystallites embedded in amorphous $Si_3 N_4$ matrix, could be successfully synthesized on WC-Co substrates by a hybrid coating system of arc ion plating(AIP) and sputtering method. The hardness of Ti-Al-Si-N film increased with incorporation of Si, and had the maximum value ~50 GPa at the Si content of 9 at.%, respectively. And the X-ray diffraction patterns of Ti-Al-Si-N films with various Si content is investigated. In this study, Ti-Al-Si-N coatings were applied to end-mill tools made of WC-Co material by a hybrid coating system. Cutting tests fir the high-hardened material (STD11,$H_R$)C62 and their performances in high speed cutting conditions were studied. Also, the tool wear and tool lift of Ti-Al-Si-N with various si(6, 9, 19) contents were measured.

• 한국광학회지
• /
• 제11권1호
• /
• pp.13-18
• /
• 2000

Si(100) 위에 RF 스퍼터링법으로 SiOxNy 박막을 제작하였다. 제작 조건은 반응 가스 비율에 따른 증착율과 RF 출력으로 하였다. XRD, XPS, n&k analyzer 그리고 FTIR로 SiOxNy 박막의 특성을 조사하였다. XRD 측정결과 ${SiO_x}{N_y}$ 박막은 비정질이었으며, XPS와 n&k analyzer 측정 결과 ${SiO_x}{N_y}$ 박막의 질소성분이 증가할수록 굴절률은 증가함을 알 수 있었다.

• 한국세라믹학회지
• /
• 제51권5호
• /
• pp.459-465
• /
• 2014

In this study, Si-SiC composites were fabricated using a Si melt infiltration method using ${\beta}$-SiC/C composite powders synthesized by the carbothermal reduction of $SiO_2-C$ precursors made from a TEOS and a phenol resin. The purity of the synthesized SiC-C composite powders was higher than 99.9993 wt% and the average particle size varied from 4 to $6{\mu}m$ with increasing carbon contents of the $SiO_2-C$ precursors. It was found that the Si-SiC composites fabricated in this study consist of ${\beta}$-SiC and residual Si, without any trace of ${\alpha}$-SiC. The 3-point bending strengths of the fabricated Si-SiC composites were measured and found to be higher than 550 MPa, although the density of the fabricated Si-SiC composite was less than $2.9g/cm^3$. The bending strengths and the densities of the fabricated Si-SiC composites were found to decrease with increasing C/Si mole ratios in the SiC-C composite powders. The specific resistivities of the Si-SiC composites fabricated using the SiC-C composite powders were less than $0.018{\Omega}cm$. With increasing C content in the SiC-C composite powders used for the fabrication of Si-SiC composites, the specific resistivity of the Si-SiC composites was found to slightly increase from 0.0157 to $0.018{\Omega}cm$.