• Journal of the Korean Society for Railway
• /
• v.9 no.4 s.35
• /
• pp.349-356
• /
• 2006

At present, the selecting system and analytic estimation criterion on repair materials and methods of the deteriorated RC structures have not yet been set up in domestic. Under these circumstances, deterioration such as shrinkage crack, corrosion of rebar has been often occurred after repair, and this finally results in too frequent repairs. In this study, three types of repair methods were experimentally investigated by the accelerating test in a combined deterioration chamber and long-term field exposure test. Three types of repair methods applied in this study belong to a group of polymer cement mortar, which is commonly used in repair works. According to the results of this study, durability of repair mortar layers and corrosion properties of recovered rebar could be investigated in short period by the accelerating test in a combined deterioration chamber, which can simulate the condition of repeated high-and-low temperature and repeated dry-and-wet environment, spraying chloride solution and emitting $CO_2$ gas. After 36 month long-term filed exposure test in the coastal area, harmful macro-cracks are observed in the polymer cement mortar layer of some repair methods. These crack are considered to result from drying shrinkage of polymer cement mortar. Also, after 36 month exposure, amount of corrosion area and weight loss of rebar are found to be different according to the types of repair methods.

• Korean Journal of Materials Research
• /
• v.16 no.4
• /
• pp.235-240
• /
• 2006

We investigated the effect of ZnO filler on the microstructure of $BaO-B_2O_3-ZnO-P_2O_5$ glass system to find an etching mechanism of barrier ribs. The sintering behavior of composites heated in the temperature range $560-600^{\circ}C$ was studied by volumetric shrinkage rate and microstructure. The etching test was carried out in $HNO_3$ solution at $50^{\circ}C$ for 10 min. The volumetric shrinkage of sintered sample decreased with the increased firing temperature because of the formation of two crystals. Glass and ZnO filler react forming the $BaZn_2(PO_4)_2$ crystal phases during the sintering process. Etching phenomenon of sintered samples by $HNO_3$ showed that the $BaZn_2(PO_4)_2$ crystal phase was strongly leached compared to glass matrix, crystal phases and fillers. Therefore, the control of interface by condition of sintering is so important to achieve etching effect in barrier ribs.

• Advances in materials Research
• /
• v.13 no.2
• /
• pp.115-128
• /
• 2024

Concrete is the most significant material in the construction industry which is required to construct several facilities like roads, buildings, and bridges etc. which leads to the economic development of a country. But now days, in view of sustainable development and environmental problems, plastic waste management is one of the major environmental issues due to its non-biodegradable nature which allows it to stay in the landfills until they are cleaned up. To overcome all these concerns, plastic waste may be used as a substitute of natural fine and coarse aggregate in concrete and a valuable solution to utilize the plastic items which causes several problems. In order to, present study is focused on the affecting properties of concrete as workability, compressive strength, and tensile strength of concrete with using plastic waste and without using plastic waste. Based on the detailed literature, it was observed that the plastic waste is not affecting the quality and consistency of concrete. However, as the number of PVC particles in the mixture increased, the drying shrinkage values decreased and the inclusion of plastic flakes can mitigate drying shrinkage cracking which leads the higher durability of concrete. Based on the comprehensive literature, it was also observed that the plastic aggregate found to be suitable for low and medium strength concrete. However, the investigation on the application of plastic aggregate in the high strength concrete is found limited. It was concluded that the optimum percentage of the plastic aggregate was found about 20%.

• Journal of Conservation Science
• /
• v.30 no.1
• /
• pp.103-109
• /
• 2014

This study aimed to develop materials to compensate for problems of restoration for lost parts and material problems in the conservation treatment. First, there are several problems with existing materials as follows: secondary damage due to the high shrinkage rate and low adhesive strength, sense of difference due to the severe yellowing, remelting due to irreversibility of materials, processability due to the high strength, sag due to the prolonged setting time in the work process and surface contamination of artifacts due to tools or gloves. In order to solve these problems, this study set developmental goals after understanding the types and physical properties based on epoxy resin among the currently used restoration materials of pottery and earthenware. The developed epoxy resin is epoxy putty, which is cured within 5 minutes, for earthenware restoration. In the earthenware restoration method, the epoxy putty enhanced the workability by quickly curing in paste form and compensated disadvantages such as surface contamination. In addition, the use of white micro-balloon for the epoxy stock solution made coloring easier and weight lighter, and a restoration material with low shrinkage and superior processability was developed.

• Resources Recycling
• /
• v.21 no.6
• /
• pp.12-22
• /
• 2012

This study investigated a utilization technology of light burned dolomite. light burned dolomite ($CaMg(CO_3)_2$) generated in furnace (steel manufacturer) is an alternative to quick lime. Using light burned dolomite has an effect on reducing the consumption of fluorite slag MgO concentration in supersaturated solution by prolonging the life of softening effect. Armophous MgO, not containing periclase is formed by firing dolomite under $800^{\circ}C$. It has larger surface area and higher reactivity than periclase, and also shows better expansion effect than quicklime. Due to those effects, therefore, armophous MgO produced from light burned dolomite is used as an alternative expansion agent in mortar. In the experiment, characteristics of light burned dolomite were compared to those of existing expansion agents such as anhydrite and quicklime. Then, each expansion and shrinkage rates were measured over a period of about 3 months in both of 1m Jis mold at labscale and apartment mortar flooring at field scale. In the result, it was observed that light burned dolomite in mortar flooring more compensates for the expansion and shrinkage rates than the existing expansion agents, showing low expansion rate of below 0.05% and also decreases the crack.

• Journal of Conservation Science
• /
• v.16 s.16
• /
• pp.110-118
• /
• 2004

In order to evaluate two-step treatment of PEG-freeze drying for highly-degraded waterlogged ash woods (Fraxinus PP.; ca. 5,700 BP), which were excavated from peat lands in western Korea, dimension stability was examined during 45 months after complete treatment. The samples pre-treated with PEG in water solution showed better dimensional stabilities than the ones with PEG in t-butanol(TBA) solution. It suggests that TBA reduced the flexibility of wood cells and overflying by TBA induced micro-checks during freeze drying. Micro-checks results in fragile wood structures and consequently, large shrinkage by moisture absorbances of high PEG contents during exposure in humid condition. The results suggest that PEG in water-solution treatment is better than PEG in t-butanol as pretreament for freeze drying of highly-degraded waterlogged ash woods.

• Journal of Conservation Science
• /
• v.21
• /
• pp.49-58
• /
• 2007

Among the treatment results of test samples of the antique lacquer-ware, the treatment with PEG#3,350 40% solution displayed excellent effect with low shrinkage ratio; in weight gain the treatment with Sucrose 19%+Glycerin 1%(t-butanol 5% in water) solution showed consistent increase. However during the impregnation process of Sucrose, the weight of the testing samples decreased by dehydration because the inner part of the test samples and the treatment solution showed concentration gradient. Therefore, we concluded longer impregnation period should be necessary to prevent dehydration. Since both higher and lower molecular weight treatment chemicals could penetrate into the wood of the lacquer-ware, air drying and conditioning after impregnation treatment with high concentration chemicals would be possible, as well as vacuum freeze-drying.

• Journal of the Korean Wood Science and Technology
• /
• v.10 no.3
• /
• pp.13-44
• /
• 1982

1. Since long time ago, it has been talked about that soaking wood into water for a long time would be profitable for the decreasing of defects such as checking, cupping and bow due to the undue-shrinking and swelling. There are, however, no any actual data providing this fact definitly, although there are some guesses that water soluble extractives might effect on this problem. On the other hand, this is a few work which has been done about the effect of water soluble extractives upon the some physical properties of wood and that it might be related to the above mentioned problem. If man does account for that whether soaking wood into water for a long time would be profitable for the decreasing of defects due to the undue-shrinking and swelling in comparison with unsoaking wood or not, it may bring a great contribution on the reasonable uses of wood. To account for the effect of water soluble extractives upon physical properties of wood, this study has been made at the wood technology laboratory, School of Forestry, Yale university, under competent guidance of Dr. F. F. Wangaard, with the following three different species which had been provided at the same laboratory. 1. Pinus strobus 2. Quercus borealis 3. Hymenaea courbaril 2. The physical properties investigated in this study are as follows. a. Equilibrium moisture content at different relative humidity conditions. b. Shrinkage value from gre condition to different relative humidity conditions and oven dry condition. c. Swelling value from oven dry condition to different relative humidity conditions. d. Specific gravity 3. In order to investigate the effect of water soluble extractives upon physical properties of wood, the experiment has been carried out with two differently treated specimens, that is, one has been treated into water and the other into sugar solution, and with controlled specimens. 4. The quantity of water soluble extractives of each species and the group of chemical compounds in the extracted liquid from each species have shown in Table 36. Between species, there is some difference in quantity of extractives and group of chemical compounds. 5. In the case of equilibrium moisture contents at different relative humidity condition, (a) Except the desorption case at 80% R. H. C. (Relative Humidity Condition), there is a definite line between untreated specimens and treated specimens that is, untreated specimens hold water more than treated specimens at the same R.H.C. (b) The specimens treated into sugar solution have shown almost the same tendency in results compared with the untreated specimens. (c) Between species, there is no any definite relation in equilibrium moisture content each other, however E. M. C. in heartwood of pine is lesser than in sapwood. This might cause from the difference of wood anatomical structure. 6. In the case of shrinkage, (a) The shrinkage value of the treated specimen into water is more than that of the untreated specimens, except anyone case of heartwood of pine at 80% R. H. C. (b) The shrinkage value of treated specimens in the sugar solution is less than that of the others and has almost the same tendency to the untreated specimens. It would mean that the penetration of some sugar into the wood can decrease the shrinkage value of wood. (c) Between species, the shrinkage value of heartwood of pine is less than sapwood of the same, shrinkage value of oak is the largest, Hymenaea is lesser than oak and more than pine. (d) Directional difference of shrinkage value through all species can also see as other all kind of species previously tested. (e) There is a definite relation in between the difference of shrinkage value of treated and untreated specimens and amount of extractives, that is, increasing extractives gives increasing the difference of shrinkage value between treated and untreated specimens. 7. In the case of swelling, (a) The swelling value of treated specimens is greater than that of the untreated specimens through all cases. (b) In comparison with the tangential direction and radial direction, the swelling value of tangential direction is larger than that of radial direction in the same species. (c) Between species, the largest one in swelling values is oak and the smallest pine heartwood, there are also a tendency that species which shrink more swell also more and, on the contrary, species which shrink lesser swell also lesser than the others. 8. In the case of specific gravity, (a) The specific gravity of the treated specimens is larger than that of untreated specimens. This reversed value between treated and untreated specimens has been resulted from the volume of specimen of oven dry condition. (b) Between species, there are differences, that is, the specific gravity of Hymenaea is the largest one and the sapwood of pine is the smallest. 9. Through this investigation, it has been concluded that soaking wood into plain water before use without any special consideration may bring more hastful results than unsoaking for use of wood. However soaking wood into the some specially provided solutions such as salt water or inorganic matter may be dissolved in it, can be profitable for the decreasing shrinkage and swelling, checking, shaking and bow etc. if soaking wood into plain water might bring the decreasing defects, it might come from even shrinking and swelling through all dimension.

• Korean Journal of Food Science and Technology
• /
• v.40 no.1
• /
• pp.36-41
• /
• 2008

This study was conducted to investigate the effects of combined osmotic dehydration and hot-air drying on the quality of dried apple products. Apple cylinders were steeped in 30% and 50% sucrose solutions at different steeping times. During the osmotic dehydration, as the concentration of the sucrose solution and steeping time increased, weight reduction and water loss increased, and the solid gain showed similar results. Osmotic dehydration in the sucrose solutions was followed by hot-air drying at 50 and $70^{\circ}C$. The experimental data were fitted successfully using the modified Page model. At the drying temperature of $50^{\circ}C$, the drying time increased from 4.15 hr for the control to 5.78 hr and 6.42 hr for the 30 and 50% sucrose solution treatments, respectively. Similar results were shown at the $70^{\circ}C$ drying temperature. The k and n values of the apple cylinders decreased by osmotic dehydration, and the k and n of the apple cylinders steeped in the 50% sucrose solution were lower than those of the samples steeped in the 30% sucrose solution. The qualities of the dried apple products were compared to samples that did not undergo osmotic dehydration. The shrinkage and rehydration capacity of the apple products decreased via osmotic dehydration, and decreased as the concentration of the sucrose solution increased. The compressibility ratios of the apple products to raw apple cylinders increased by osmotic dehydration, and increased as the concentration of sucrose solution increased. The sensory evaluation results for the apple products rehydrated in yoghurt indicate that osmotic dehydration greatly enhances the palatability of apple products in terms of appearance, taste, and texture.

• Journal of Conservation Science
• /
• v.21
• /
• pp.21-32
• /
• 2007

Low-viscosity alkoxysilanes that polymerize into the porous network of decayed stone by a sol-gel process are widely used as stone consolidants. During drying, the gel network contracts due to capillary pressure generated by solvent evaporation. We have prepared tetraethoxysilane mixed solution containing methyltrisilane, ethyl trisilane and (3-glycidyloxypropyl)trimethoxysilane having epoxy ring in order to reduce the shrinkage happened inside the stone porous structure during the gel formation. Mixed solutions were applied into sandstone and granites and characterized by FT-IR, SEM. The gelation time, water uptake, contact angles were measured and compared with those of the commercial stone conservation materials.