• Journal of Welding and Joining
• /
• v.30 no.6
• /
• pp.62-67
• /
• 2012

In this study, the bonding strengths of adhesively bonded joints are experimentally investigated. A series of lap-shear tests are conducted using single lap type adhesive joints. In order to analyse the joint fabrication factors that affected the bonding strength, the parametric tests are conducted with various thickness of adhesive, surface roughness and fillet of adhesive. In addition, for the comparative study with the welded joint, lap-shear tests using specimens with 2 welded sides and 4 welded sides are also carried out. The quantitative results of the strength analysis are summarized, and some proposals are made on setting up testing standards for adhesively bonded joints.

• Journal of Welding and Joining
• /
• v.24 no.3
• /
• pp.55-59
• /
• 2006

This paper is concerned with a study on cyclic bending load of bus folding door pillar including adhesive bonding and spot welding. Three specimen types were used such as spot welding, I-type adhesive bonding and M-type adhesive bonding in this study. The tensile-shear tests were carried out to evaluate the tensile-shear strength of these three specimen types. Also four-point bending tests were carried out to evaluate the static and dynamic bending load. From the results, using adhesive bonding has a better effect on the static and dynamic bending load than using spot welding. Therefore, manufacturing better structural products can be expected by applying hybrid welding using adhesive and spot welding to those.

• Transactions of Materials Processing
• /
• v.20 no.1
• /
• pp.64-72
• /
• 2011

In this study, we have investigated bonding of metal and plastic parts with single planar interface. This is facilitated by surface processing of aluminum sheet, which consists of slitting and punching, followed by insert-molding of polybuthylelne terephthalate(PBT). An injection mold has been built to fabricate specimen. After processing of the specimen, tensile and bending shear adhesion tests have been fulfilled according to KS M3734 and KS M3723, respectively. We also have conducted simulation of tensile and bending shear adhesion tests. Based on the tests results, the proposed bonding method outperforms existing methods based on adhesion.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.5 no.2
• /
• pp.87-93
• /
• 1997

The bonding strength evaluation of light weight materials for electrical vehicle applications has been performed through single lap joint tests in which the design parameters such as fillet, joint style, adherend, bonding overlap length,bonding thickness, and environmental condition(soaking time in $25^{\circ}C$ water) are considered. It is experimentally oberved that lap shear strength of joint increases for higher fillet height, longer overlap length, and thinner bonding layer thickness. Al-Al adherend combination shows much higher lap shear strength than AL-FRP and FRP-FRP adherend combinations. Riveting at adhesive bonded joint of AL-AL adherend combination makes lap shear strength decrease. Effect of soaking time on lap shear strength is negligible.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.10 no.3
• /
• pp.130-135
• /
• 2002

This study investigates the effect of curing method on the bonding strength of aluminum/CFRP composites. The surface of aluminum panel was treated by DC plasma. Lap shear tests and T-peel tests were performed based on the procedure of ASTM 906-94a and ASTMD1876-95, respectively. Test samples were fabricated by using the co-curing method and the secondary curing method. The results showed that the shear strength of test samples made by the co-curing method was 2.5 times greater than that of test samples made by the secondary curing method. The T-peel strength of the co-curing method case was almost 2 times greater than that of the secondary curing method case.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2016.10a
• /
• pp.81-82
• /
• 2016

The present study aims to derive optimal interface treatment conditions for emulating a monolithic construction. The joints in this construction are formed through the bonding shear evaluation method during the placement of ultra-high-performance concrete (UHPC) and normal strength concrete (NSC). The evaluation items include push-off tests for homogeneous UHPC + UHPC and heterogeneous NSC + UHPC. The experimental samples comprised a monolithic placement as the baseline, two levels for the separated placement according to the compression strength of concrete, and five levels for the interface treatment. The increase in the number of grooves and their cross-sectional areas only slightly influenced the bonding shear performance. The optimal interface treatment method for the homogeneous UHPC + UHPC construction grooves was at least 30mm. The heterogeneous NSC + UHPC construction should utilize waterjet roughening to expose the aggregate for the increased roughness.

• International Journal of Highway Engineering
• /
• v.15 no.4
• /
• pp.85-94
• /
• 2013

PURPOSES: The performance of tack coat, commonly used for layer interface bonding, is affected by application rate and curing time. In this study, bonding strength tests were performed according to the application rate and curing time of asphalt emulsion. Based on finding from this study, optimum application rates and curing times are proposed. METHODS: In order to investigate bonding characteristic of asphalt emulsion, tests were performed on both asphalt concrete pavement and portland concrete pavement. Also, asphalt emulsions were tested at the application rate of 0, 0.2, 0.4, 0.6, and $0.8{\ell}/m^2$ and at the curing time of 0, 0.5, 1, 2, and 24 hours. Pull-off test and shear bonding strength test, which commonly used for bonding strength measurement of asphalt emulsion, were adopted for this study. To assess field performance under different testing condition, asphalt emulsions were applied to in-service pavement. Throughout coefficient of determination analysis between material index properties from asphalt emulsion and mechanical response from bonding strength tests, performance correlativity was analyzed. RESULTS: Test results show that optimum application rate for asphalt overlay on asphalt concrete pavement (AOA) and asphalt overlay on concrete pavement (AOC) was $0.4{\sim}0.5{\ell}/m^2$ and $0.3{\sim}0.5{\ell}/m^2$, respectively. According to the curing time increment, tensile strength and shear strength of AOC were increased to 22~44% and 20~39%, respectively. AOA case also show strength increment in tensile strength (42%) and shear strength (9%). We tested the applicability of tack coat materials at the field sites, and our findings demonstrated that the bonding (for D and E) and rapid curing (for B, C, and D, E) performances were superior than others. Among material index properties, there was a high correlation between penetration ratio and bonding strength test result. CONCLUSIONS : Result show that interlayer bonding strength was affected by asphalt emulsion type, application rate and curing time. AOC required slightly higher application ($0.1{\ell}/m^2$) than AOA. Both AOA and AOC cases show higher strength at longer curing time. Up to 2hours of curing, rapid strength increments were observed, but strength increment ratio was decreased after 2hours of curing. From the observed correlation between penetration ratio and bonding strength, it is expected that penetration ratio can be used as one of important factors affecting bonding strength analysis.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.10a
• /
• pp.513-518
• /
• 2002

In vertical construction joint, adhesives such as epoxy, acrylic, latex, etc. have been usually used for bonding fresh concrete to hardened concrete. In this study, performance of adhesives under various application conditions was investigated through tests for slant shear and flexural strength. From the results of the tests, it is found that superior bonding performance can be obtained under good surface preparation without adhesive when high strength concrete is used.

• Journal of Technologic Dentistry
• /
• v.35 no.2
• /
• pp.105-112
• /
• 2013

Purpose: This study was to analyze the castability, surface oxide characteristic of Co-Cr alloy for porcelain fused to metal crown and the bonding strength of porcelain fused to metal crown. Co-Cr and Ni-Cr alloy for porcelain fused to metal crown was used for tests of the castability and surface oxide state and shear bonding strength by various porcelain. The aim of this study was to suggest the differences of result according to Co-Cr and Ni-Cr alloy. Methods: The kinds of alloy as test specimen was Co-Cr and Ni-Cr alloy. The castability index on the alloy specimens. The surfaces of two alloys were analyzed by SEM and EDX in order to observe oxide characteristic. And the shear test was performed by MTS. Results: The castability index of Co-Cr alloy was 96.8% and Ni-Cr alloy was 94.4%. The strongest bonding strength of Co-Cr alloy was shown 67.37 MPa. Conclusion: The shear bonding strength between Co-Cr alloy and EX3 porcelain was the strongest comparing with others. And all of each alloy was indicated as same level about the castability.

• Journal of the Korean Wood Science and Technology
• /
• v.47 no.5
• /
• pp.655-662
• /
• 2019

This study evaluated the multi-bonding performances of timbers as well as those of reinforcement and timber to obtain data for preparing guidelines regarding the use of timbers as large structural members. For the multi-bonding performances of timbers, four types of bonding surfaces were prepared according to the pith position. For the bonding performances of FRP (fiber-reinforced plastic)/steel plate and timber, a total of 11 types of specimens were produced for the selection of the appropriate adhesive. The bonding performances of the produced specimens were evaluated through a water soaking delamination test, a water boiling delamination test, and a block shear strength test. The test results showed that the bonding strength of the bonding surface according to the pith position was highest in the specimen for which the two sections with the pith at the center of the cross-section on timber and between the bonding surfaces (the tangential and radial sections were mixed) were bonded. Furthermore, the specimens for which the section (radial section) with the pith on the bonding surface of the timber was bonded showed a high delamination percentage. The results of the block shear strength test showed that the bonding section did not have a significant effect on the shear strength, and that the measured wood failure percentage was higher than the KS standard value. The PVAc adhesive showed the highest bonding strength between larix timber and GFRP (glass FRP). Furthermore, the epoxy and polyurethane adhesives showed good bonding strength for CFRP (carbon FRP) and structure steel, respectively.