• 한국세라믹학회지
• /
• 제39권4호
• /
• pp.346-351
• /
• 2002

중저온 영역에서 작동 가능한 고체산화물연료전지(SOFC)의 전해질 재료를 탐색하기 위해 $Sc_2O_3$와 $CeO_2$를 동시에 첨가하여 안정화시킨 $CeO_2$의 상안전성과 전기적 물성을 분석하였다. 분석결과 $Sc_2O_3$와 $CeO_2$를 동시에 첨가하여 안정화시킨 $ZrO_2$는 $1350^{Circ}C∼1550^{Circ}C$까지의 열처리과정중 다른 상전이 없이 상온에서 안정한 입방정상을 유지하였으며 넓은 온도영역($300∼^{Circ}C$)에서 기존의 YSZ보다 훨씬 높은 전기전도도값을 나타냈다. 또한 $Sc_2O_3$와 $CeO_2$가 동시에 첨가된 $ZrO_2$는 기존의 Sc-$ZrO_2$계 전해질 물질보다 훨씬 향상된 장기안정성을 나타내 중저온형 고체산화물 연료전지의 전해질재료로 적합함을 알 수 있었다.

• 한국세라믹학회지
• /
• 제53권5호
• /
• pp.500-505
• /
• 2016

Scandia-stabilized zirconia co-doped with $CeO_2$ is a promising electrolyte for intermediate temperature SOFC, but still shows rapid degradation during a long-term operation. In this study, $CeO_2$ (1 mol%) as a stabilizer is partially substituted with lanthanum oxides ($M_2O_3$, M=Yb, Gd, Sm) to stabilize a cubic phase and thus durability in reducing atmosphere. 0.5M0.5Ce10ScSZ electrolytes were prepared by solid state reaction and sintered at $1450^{\circ}C$ for 10 h to produce dense ceramic specimens. With addition of the lanthanum oxide, 0.5M0.5Ce10ScSZ showed lower degradation rates than 1Ce10ScSZ. Since $Gd_2O_3$ showed the highest ionic conductivity among the co-dopants, an electrolyte-supported cell with 0.5Gd0.5Ce10ScSZ was prepared to compare its long-term performance with that of 1Ce10ScSZ-based cell. Maximum power density of 0.5Gd0.5Ce10ScSZ-based cell was degraded by about 2.3% after 250 h, which was much lower than 1Ce10ScSZ-based cell (4.2%).

• 한국세라믹학회지
• /
• 제42권12호
• /
• pp.787-792
• /
• 2005

A symmetrical LSCF $(La_{0.6}Sr_{0.4}Co_{0.2}Fe_{0.8}O_{3-\delta})\;ScSZ(89ZrO_2-10Sc_2O_3-1CeO_2)/LSCF$ electrochemical cell with a GDC (Gadolinium-Doped Ceria, $90CeO_2-10Gd_2O_3$) interlayer that was inserted between the LSCF cathode and ScSZ electrolyte was fabricated, and the electrochemical performance of these cells was evaluated. The GDC interlayer was deposited on a ScSZ electrolyte using a screen-printing technique. The GDC interlayer prevented the unfavorable solid-state reactions at the LSCF/ScSZ interfaces. The LSCF cathode on the GDC interlayer had excellent electrocatalytic performance even at $650^{\circ}C$. The Area Specific Resistance (ASR) was strongly dependent on the thickness and heat-treatment temperature of the GDC interlayer. The impedance spectra showed that the cell with a $15\~27{\mu}m$ thick GDC interlayer heat-treated at $1200^{\circ}C$ had the lowest ASR.

• 한국세라믹학회지
• /
• 제45권12호
• /
• pp.766-771
• /
• 2008

We fabricated single cells with a cathode consisting of a $LaNi_{0.6}Fe_{0.4}O_3-Ce_{0.8}Sm_{0.2}O_{1.9}$ composite (LNF-S20DC composite) active layer and an LNF current collecting layer on a ${0.89ZrO_2}-{0.10Sc_2}{O_3}-0.01{Al_2}{O_3}$ electrolyte sheet. The cathode layers were prepared by the screen-printing method. The cathode properties of these cells were measured by the AC impedance method at $800^{\circ}C$. The cathodes with the ceria-LNF composite active layer exhibited high power performance prior to current loading. We investigated the influence of the mixture ratio of LNF and S20DC on the cathodes properties. The Sm in the ceria particles of the composite cathode was substituted with other rare-earth elements. Cathodes with Pr and Gd co-doped ceria in the active layer provided the better performance than those with Sm- or Gd-doped ceria.

• 세라미스트
• /
• 제21권4호
• /
• pp.378-387
• /
• 2018

The optimal fabrication conditions for $Gd_{0.1}Ce_{0.9}O_{2-{\delta}}$(GDC) buffer layer and $La_{0.6}Sr_{0.4}Co_{0.2}Fe_{0.8}O_{3-{\delta}}$ (LSCF) cathode on 1mol% $CeO_2-10mol%\;Sc_2O_3$ stabilized $ZrO_2$ (CeScSZ) electrolyte were investigated for application of IT-SOFCs. GDC buffer layer was used in order to prevent undesired chemical reactions between LSCF and CeScSZ. These experiments were carried out with $5{\times}5cm^2$ anode supported unit cells to investigate the tendencies of electrochemical performance, Microstructure development and interface reaction between LSCF/GDC/CeScSZ along with the variations of GDC buffer layer thickness, sintering temperatures of GDC and LSCF were checked, respectively. Electrochemical performance was analyzed by DC current-voltage measurement and AC impedance spectroscopy. Microstructure and interface reaction were investigated by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). Although the interfacial reaction between these materials could not be perfectly inhibited, We found that the cell, in which $6{\mu}m$ GDC interlayer sintered at $1200^{\circ}C$ and LSCF sintered at $1000^{\circ}C$ were applied, showed good interfacial adhesions and effective suppression of Sr, thereby resulting in fairly good performance with power density of $0.71W/cm^2$ at $800^{\circ}C$ and 0.7V.