• 한국세라믹학회지
• /
• 제37권2호
• /
• pp.194-200
• /
• 2000

Sb-doped tin oxide films were deposited on Corning glass 1737 substrate by plasma enhanced chemical vapor deposition(PECVD) technique using a gas mixture of SnCl4/SbCl5/O2/Ar. The deposition behaviors of tin oxide films by PECVD were compared with those by thermal CVD, and effects of deposition temperature, r.f. power and Sb doping on the electrical properties of tin oxide films were investigated. PECVD technique largely increased the deposition rate and smoothed the surface of tin oxide films compared with thermal CVD. Electrical resistivity decreased with doping of Sb due to the increase of carrier concentration. However, large doping of Sb diminished carrier concentration and mobility due to the decrease of crystallinity, which resulted in the increase of electrical resistivity. As the deposition temperature and r.f. power increased, Cl content in the film decreased.

• Transactions on Electrical and Electronic Materials
• /
• 제13권5호
• /
• pp.241-244
• /
• 2012

Antimony doped tin oxide (ATO) thin films on glass substrate were prepared by the chemical solution deposition (CSD) method, using sol-gel solution synthesized by non-alkoxide precursors and the sol-gel route. The crystallinity and electrical properties of ATO thin films were investigated as a function of the annealing condition (both annealing environments and temperatures), and antimony (Sb) doping concentration. Electrical resistivity, carrier concentration, Hall mobility and optical transmittance of ATO thin films were improved by Sb doping up to 5~8 mol% and annealing in a low vacuum atmosphere, compared to the undoped tin oxide counterpart. 5 mol% Sb doped ATO film annealed at $550^{\circ}C$ in a low vacuum atmosphere showed the highest electrical properties, with electrical resistivity of about $8{\sim}10{\times}10^{-3}{\Omega}{\cdot}cm$, and optical transmittance of ~85% in the visible range. Our research demonstrates the feasibility of low-cost solution-processed transparent conductive oxide thin films, by controlling the appropriate doping concentration and annealing conditions.

• Transactions on Electrical and Electronic Materials
• /
• 제16권1호
• /
• pp.5-9
• /
• 2015

Optical and electrical properties were studied for Antimony doped tin oxide thin films from precursors containing 10, 30, 50, and 70 atom% of Sb deposited on bare sodalime silica, barrier layer coated sodalime silica, and pure silica glass substrates by sol-gel spinning technique. The direct band gaps were found to vary from 3.13~4.12 eV when measured in the hv range of 2.5~5.0 eV, and varied from 4.22~5.08 eV when measured in the range of 4.0~7.0 eV. Indirect band gap values were in the range of 2.35~3.11 eV. Blue shift of band gap with respect to bulk band gap and Moss-Burstein shift were observed. Physical thickness of the films decreased with the increase in % Sb. Resistivity of the films deposited on SLS substrate was in the order of $10^{-2}$ ohm cm. Sheet resistance of the films deposited on barrier layer coated soda lime silica glass substrate was found to be relatively less.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 하계학술대회 논문집 Vol.6
• /
• pp.361-362
• /
• 2005

Antimony doped tin oxide(ATO) nano powders have been synthesized by homogeneous precipitation method using $SnCl_4\cdot5H_2O$ for precursor, $SbCl_3$ as doped material and urea. The hydrolysis of urea and conductive mechanism and Heat treatment was performed at the temperature from $500^{\circ}C$ to $700^{\circ}C$ in air. The ATO nano powders are characterized by means of Thermogravimetry differential thermal analyzer (TG-DTA), X-ray diffraction (XRD), Brunauer, Emmett, and Teller adsorption (BET), Scanning electron microscopy (SEM) ATO nano powders with an average size of nm and the highest surface area 129 $m^2g^{-1}$ are obtained.

• 한국전기전자재료학회논문지
• /
• 제22권3호
• /
• pp.269-276
• /
• 2009

Antimony doped tin oxide ($SnO_2:Sb$) films, which are used as the front contact and back reflector of thin film solar cells, have been deposited by d,c, magnetron sputtering. The dependence of electrical and optical properties of the films on the preparation conditions, such as $O_2$ gas ratio, substrate temperature, annealing temperature was investigated. The sputter gas composition was found to affect the properties of the films. With incorporating $O_2$ gas, the electrical and optical properties of films significantly were improved. The minimum resistivity and optical transmittance over 80 % in visible region were obtained at the oxygen concentration of 30 %, When the substrate temperature was higher, the resistivity of $SnO_2:Sb$ films was decreased, while the absorption edge shifted to shorter wavelength, indicating higher optical band gap. Heat treatment over $600^{\circ}C$ resulted in poorer electrical and optical properties due to SnO phase (102) plane.

• 한국결정성장학회지
• /
• 제13권5호
• /
• pp.241-246
• /
• 2003

ATO(antimony-doped tin oxide) 투명전도막을 sol-gel dip coating 방법에 의해 $SiO_2$/glass 기판 위에 성공적으로 제조하였다 ATO막의 결정상은 $SnO_2$상임을 확인하였고, 막의 두께는 withdrawal speed를 50 mm/minute로 코팅시 약 100 nm/layer였다. $SiO_2$/glass 기판 위에 코팅한 400 nm두께의 ATO 박막을 질소분위기에서 annealing한 후, 측정한 광 투과율과 전기 저항치는 각각 84%와 $5.0\times 10^{-3}\Omega \textrm{cm}$였다. 이러한 특성은 $SiO_2$막이 Na 이온의 확산을 제어하여 $Na_2SnO_3$ 및 SnO와 같은 불순물의 형성을 억제하고, 막 내부의 Sb의 농도와 $Sb^{3+}$에 대한 $Sb^{5+}$의 비를 증가시키는데 기여했기 때문으로 확인되었다. 또한, $N_2$ annealing은 $Sb^{5+}$뿐만 아니라 $Sn^{4+}$를 환원시킴으로써 전기전도도를 향상시킴을 확인하였다.

• 한국재료학회지
• /
• 제10권8호
• /
• pp.525-531
• /
• 2000

플라즈마 화학증착법을 이용하여 Corning glass 1737 기판에 안티몬 도핑 산화주석 박막을 증착하였다. 플라즈만 화학증착시 반응변수에 따른 박막의 결정상 및 형성된 표면거칠기에 대하여 XRD와 AFM을 이용하여 검토하였다. 반응온도 $450^{\circ}C$, 유입가스비 R[$P_{SbCl}P_{{SnCl}_4}$]=1.12, r.f. power 30W에서 비교적 결정성이 뛰어난 박막을 얻을 수 있었다. 화학증착법(TCVD)에 비해 플라즈마 열화학증착법(PECVD)으로 얻은 박막의 표현형상이 보다 균일하였다. 안티몬 도핑농도가 증가할수록, 증착온고가 낮을수록, 증착두께가 작을수록 박막의 표면거칠기가 보다 감소하였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 하계학술대회 논문집
• /
• pp.361-364
• /
• 2000

Antimony doped tin oxide (ATO) thin films were deposited at room temperature by reactive ion-beam sputter deposition (IBSD) technique in oxidizing atmosphere utilizing Sb and Sn metal targets. Effect of Sb doping concentration, film thickness and heat treatment on electrical and optical properties was investigated. The thickness of as-deposited films was controlled approximately to 1500 $\AA$ or 2000$\AA$, and Sb concentration to 10.8 and 14.9 wt%, as determined by SEM and XPS analyses. Heat treatment was performed at the temperature from 40$0^{\circ}C$ to 80$0^{\circ}C$ in flowing $O_2$or forming gas. The resulting ATO films showed widely changing electrical resistivity and optical transmittance values in the visible spectrum depending on the composition, thickness and firing condition.

• 한국결정성장학회지
• /
• 제13권5호
• /
• pp.254-259
• /
• 2003

Sol-gel dip coating법으로 soda lime glass 기판 위에 ATO(antimony-doped tin oxide) 투명전도막을 제조할 때, 기판 위에 형성된 $SiO_2$ barrier 층 및 $N_2$ gas annealing 에 따른 광투과율 및 전기적 특성에 대한 효과를 정량적으로 측정하고, XPS(X-ray photoelectron spectroscopy) 분석을 통해 고찰하였다. $SiO_2$ barrier층을 갖는 glass 기판 위에 코팅된400 nm 두께의 ATO 박막을 질소분위기에서 annealing한 결과, 광 투과율은 84%그리고 전기저항은 약 $5.0\times 10^{-3}\Omega \textrm{cm}$로 측정되었다 XPS 분석결과 이러한 우수한 전기전도성은 $SiO_2$ buffer층이 glass 기판으로부터 Na 이온의 확산을 막아 ATO막 내에 $Na_2SnO_3$ 및 SnO와 같은 2차상 불순물의 형성을 억제하여 막 내부의 Sb의 농도 및 $Sb^{5+}/Sb^{3+}$ 비를 증가시키고, $N_2$ annealing은 $Sb^{5+}$ 도 환원시키지만 $Sn^{4+}$를 환원시키는 효과가 크게 작용하였기 때문으로 사료된다.

• 한국세라믹학회지
• /
• 제39권4호
• /
• pp.386-393
• /
• 2002

본 연구는 티탄산칼륨 섬유(K2O·$nTiO_2$)를 제조한 후, 도전율이 우수한 Sb-doped $SnO_2$(ATO: Antimony Tin Oxide)를 티탄산 칼륨 섬유에 코팅하는 기술을 개발하는데 목적이 있다. 티탄산칼륨 섬유는 서냉 소성법으로 제조하였으며 섬유의 평균 길이는 $15{\mu}m$, 평균 직경은 $0.5{\mu}m$이었다. ATO를 졸-겔법, 공침법, 균일침전법등 세가지 방법으로 티탄산칼륨 섬유에 코팅 하였으며 ATO 코팅된 티탄산칼륨 섬유는 ATO 함량(5∼70 wt%), Sb 함량(0∼20 wt%), 온도($450∼800^{\circ}C$), 수세 여부 및 회수(3∼4회) 등을 변화 시키며 비저항 변화를 관찰하였다. 공침법의 경우 ATO 함량이 30wt%에서 103${\Omega}$·cm 낮은 비저항을 나타내었으며, 그 이상의 함량에서는 거의 일정한 값($60{\Omega}{\cdot}cm∼90{\Omega}{\cdot}$cm)을 보였다.