• Journal of the Korea Institute of Building Construction
• /
• v.3 no.3
• /
• pp.73-81
• /
• 2003

In this paper, salt damage resistance of high durable concrete was tested. High durable concrete was made by using low water cement ratio, chemical admixture called super-durable admixture and mineral admixtures such as fly-ash, ground granulated blast-furnace slag, silica fume. Two kinds of salt damage resistance test were carried out. One method is chloride ion penetration test(ASTM C1202), and the other one is depth of chloride penetration test in saline solution. Test results were as followers: 1) The depth of chloride ion penetration increased exponentially as water cement ratio was increased and time passed. 2) Super-durable admixture had little effect on the improvement of salt damage resistance of concrete. 3) Silica fume and ground granulated blast-furnace slag were effective on salt damage resistance because of pozzolanic reaction, but fly-ash had a little effect.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.10a
• /
• pp.51-56
• /
• 2002

Protection against salt attack in seawater is obtained by using a dense, quality concrete with a low water-cement ratio, and a components appropriate for producing concrete having the needed salt resistance. The objective of this study is to evaluate the feature of corrosion with using the various concrete materials under marine exposure environment. According to the test results, slag powder and anti -corrosion inhibitor showed high chloride resistance effect. Also concre crack have an influence on corrosion of steel in spite of mixed design for salt resistance concrete. The requirement for low permeability is essential not only to delay the effect of salt attack, but also to afford adquate protection to reinforcement with admixtures.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2020.06a
• /
• pp.109-110
• /
• 2020

In the event of a fire, fire engines usually arrive within 15 minutes and become a fire suppressor. In this paper, an analytical model was established to evaluate the salt damage resistance of concrete according to fire suppression time, and the concentration of salt inside the concrete after fire was measured and the time to reach the critical concentration was assessed by how short.

• International Journal of Concrete Structures and Materials
• /
• v.11 no.2
• /
• pp.315-325
• /
• 2017

The purpose of the paper is to determine the influence of two widely used steel fibers and polypropylene fibers on the sulphate crystallization resistance, freeze-thaw resistance and surface wettability of ultra-high performance concrete (UHPC). Tests were carried out on cubes and cylinders of plain UHPC and fiber reinforced UHPC with varying contents ranging from 0.25 to 1% steel fibers and/or polypropylene fibers. Extensive data from the salt resistance test, frost resistance test, dynamic modulus of elasticity test before and after freezing-thawing, as well as the contact angle test were recorded and analyzed. Fiber hybridization relatively increased the resistance to salt crystallization and freeze-thaw resistance of UHPC in comparison with a single type of fiber in UHPC at the same fiber volume fraction. The experimental results indicate that hybrid fibers can significantly improve the adhesion properties and reduce the wettability of the UHPC surface.

• International Journal of Highway Engineering
• /
• v.17 no.2
• /
• pp.47-53
• /
• 2015

PURPOSES: The scaling of a concrete surface caused by the combined effects of frost and de-icing salts is one of the main reasons for the need to repair transportation infrastructures in cold-climate regions. This study describes the results of attempts to determine the scaling resistance of concrete incorporating mineral admixtures such as fly ash, GGBFS, and silica fume, and subjected to the actions of frost and salt. METHODS : Conventionally, to evaluate the fundamental properties of concrete, flexural and compressive strength measurements are regularly performed. Based on the ASTM C 672 standard, concrete is subjected to 2%, 4%, and 8% $CaCl_2$ salt solutions along with repeated sets of 50 freeze/thaw cycles, and the scaling resistance was evaluated based on the mass of the scale and a visual examination. RESULTS : It was observed that silica fume is very effective in enhancing the scaling resistance of concrete. Meanwhile, concrete incorporating GGBFS exhibited poor resistance to scaling, especially in the first ten freeze/thaw cycles. However, fly ash concrete generally exhibited the maximum amount of damage as a result of the frost-salt attack, regardless of the concentrations of the solutions. CONCLUSIONS: It can be concluded that the scaling resistance of concrete is highly dependent on the type of the mineral admixture used in the concrete. Therefore, to provide a durable concrete pavement for use in cold-climate regions, the selection of a suitable binder is essential.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.05a
• /
• pp.755-760
• /
• 2002

The concrete structures in marine environment has been used type V cement(sulfate-resisting Portland cement), but according to the study results reported recently, the question has been raised for effect of the resistance to salt attack of the concrete using type V cement. It is increased the demands on the use of mineral admixtures such as fly ash, ground granulated blast-furnace slag instead of type V cement in order to improve the durability of concrete structures. Therefore, this study focused on the durability evaluation of concrete containing fly ash under marine environment, and the tests such as salt attack, carbonation, sulfate attack, and freezing-thawing were performed. Test results showed t]hat the resistance to salt attack, sulfate attack and freezing-thawing was improved, and the carbonation was in some disadvantage compared with normal concrete. Nevertheless, the durability of fly ash concrete would be maintained during the service life of structures.

• Corrosion Science and Technology
• /
• v.6 no.4
• /
• pp.177-185
• /
• 2007

The purpose of this study is to evaluate freezing-thawing and surface scaling resistance in order to examine the frost durability of concrete in a chloride-inherent environment. The mixing design for this study is as follows: 3 water binder ratios of 0.37, 0.42, and 0.47; 2-ingredient type concrete (50% OPC concrete and 50% ground granulated blast-furnace slag), and 3-ingredient type concrete (50% OPC concrete, 15% fly ash, and 35% ground granulated blast-furnace slag). As found in this study, the decrease of durability was much more noticeable in combined deterioration through both salt damage and frost damage than in a single deterioration through either ofthese; when using blast-furnace slag in freezing-thawing seawater, the frost durability and surface deterioration resistance was evaluated as higher than when using OPC concrete. BF 50% concrete, especially, rather than BFS35%+FA15%, had a notable effect on resistance to chloride penetration and freezing/expansion. It has been confirmed that surface deterioration can be evaluated through a quantitative analysis of scaling, calculated from concrete's underwater weight and surface-dry weight as affected by the freezing-thawing of seawater.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.11a
• /
• pp.509-512
• /
• 2004

This research is targeting that estimate the effect on cement concrete pavement with type of chloride deicers. In order to this study objective, when chloride deicers were spread on road surface, thermal characteristics test was conducted. Also, skid resistance test according to types and concentration of chloride deicier, road surface conditions were investigated. As a test results, thermal characteristics with kind of chloride deicier could know that sodium chloride(NaCl) is exothermic reactive material, calcium chloride$(CaCl_2)$ is endothermic reactive material. And, in case of mixed salt of the calcium and sodium chloride, it could know that can change to the exothermic or endothermic reaction according to dosage ratios. Skid value by British Pendulum Tester(BPT) has shown that it is seldom difference between the types($CaCl_2$, NaCl, mixed salt) and solution concentrations(0.5, 0.8, 1.0, 4.0, $10\%$) of chloride deicier comparing with tap water except mixed salt($10\%$ solution concentration).

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.27 no.5
• /
• pp.16-22
• /
• 2023

In this study, a salt water immersion test was performed on concrete specimens simulating the concrete mix design of the nuclear power plant, and the correlation between the amount of chloride and the XRF component according to the depth of the concrete was analyzed. The amount of chloride on the surface of the nuclear power plant concrete increased slightly with increasing immersion time in salt water, but the amount of chloride in the depth of 5.5 mm or more showed a clear tendency to increase with increasing immersion time in salt water. As a result of analyzing the correlation between the amount of chloride in concrete and the XRF component, the concrete with 20% FA substitution compared with the OPC concrete showed a very high correlation between the composition ratio of Cl ions and the evaluation result of salt damage resistance by XRF component analysis. Accordingly, it was confirmed that chlorine ion analysis and salt damage resistance performance evaluation by XRF component analysis were possible through repeated data accumulation in the nuclear power plant concrete mix with 20% fly ash replacement.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2010.05a
• /
• pp.207-208
• /
• 2010

The building that supply tidal and splash zone was constructed near Seamangeum Gate Bridge. The specimens that will be tested for maintenance of gate bridge were exposed on the tidal and splash zone, totally about 650. The characteristics of strength, salt penetration profile, field application of surface repair material and section recover material will be acquired by periodical test. The program was developed to obtain optimal maintenance strategy of gate bridge as a marine concrete structure and to deposit experimental data, lab. test result, field test result, on its D/B. On this paper, the comparison of concrete and recover material in the salt penetration characteristics was expressed. The quantitative analysis of salt contents in concrete surface was most important so the improvement for the machine of gathering power of concrete and the apparatus of measuring chloride contents was proceeded at this time. The two conclusions were summarized like as - The resistance of chloride attack of concrete was appeared 2.5 times bigger than that of recover material - The resistance of chloride attack of polymer series was appeared more higher than that of others.