• 한국표면공학회지
• /
• 제36권4호
• /
• pp.307-316
• /
• 2003

Salt spray, CASS(copper accelerated acetic salt spray) and EC(electrolytic corrosion) tests were performed in order to evaluate the corrosion resistance of plated Ni and Ni-Cr layers on Fe substrate. Compared with the conventional methods such as salt spray and CASS, the electrochemical method such as EC test may be beneficial in terms of test time span and quantitative accuracy. Furthermore, EC test can also become the alternative method to evaluate the resistance to corrosion of coatings by measuring the corrosion potentials of the coated layers in the electrolyte during the off-time of EC cycles. Compared with the corrosion potentials of pure iron, nickel, chromium, those potentials of coated layers can be used to anticipate the extent of corrosion. Results showed that in terms of the test time span, EC test gave 14 times and 21 times faster results than the salt spray test in cases of $5\mu\textrm{m}$ Ni and $20\mu\textrm{m}$ Ni plated layers, respectively. In addition, EC test also offered the shorter test time span than CASS test in cases of $5 \mu\textrm{m}$ Ni + $0.5\mu\textrm{m}$ Cr, and $20\mu\textrm{m}$ Ni + $0.5\mu\textrm{m}$ Cr on Fe substrate by 78 times and 182 times, respectively. Therefore, EC test can be regarded as the better method to evaluate the resistance to corrosion of coated layers than the conventional methods such as salt spray and CASS.

• 콘크리트학회지
• /
• 제6권6호
• /
• pp.173-179
• /
• 1994

콘크리트내 철근의 부식을 방지하여 내구성을 증대시키기 위해 국내에서 시험 생산한 에폭시도막 철근의 내부식성능을 실험, 평가하였다. 본 연구에서는 국내 산업규격(KS)과 미국재료시험기준 시험결과로부터 에폭시도막 철근을 내약품성능, 염화물 투과성은 양호하였다. 그러나, 에폭시도막 철근표면의 결함부에서 부식이 발생되었으며 도막두계 $200{\mu}m$ 미만의 시험체에서 부식발생률이 높았다. 4mm 정도의 부분에폭시 도막손상은 전체적인 부식에 영향을 미치지는 않았다. 도막의 결함이 생기지 않도록 에폭시도막 과정에서 철근의 표면처리에 주의가 특별히 필요하다.

• 한국주조공학회지
• /
• 제34권2호
• /
• pp.60-66
• /
• 2014

A Zr-based amorphous alloy specimen was produced by vacuum die casting process. The salt spray test was carried out using the specimens in the as-cast, $Al_2O_3$ and $ZrO_2$ particle blasted state. Using these specimens, the SEM-EDX and XRD analyses, DSC measurement and bending strength test were conducted. After the salt spray test, the specimens were not experienced phase change and thermal characteristics of the alloys were remained unchanged. In the as-cast specimen, corrosion products were not observed. However, in the $Al_2O_3$ particle blasted specimen, pitting corrosion occurred and the detected corrosion products were $ZrCl_2$ and $NaZrO_3$. Due to the salt spray test, bending strength of the $Al_2O_3$ blasted specimens showed about 100 MPa lower strength than the other specimens. The bending fracture surface was vein pattern which was shown typically in the amorphous alloys.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2005년도 춘계학술대회 논문집
• /
• pp.391-396
• /
• 2005

Salt water spray test and salt water immersion test were experimentally conducted in order to investigate the durability of fiber reinforced composites under salt water environment. The specimens were made of glass fabric reinforcement and phenolic resin. Mechanical test was performed to obtain mechanical properties such as tensile properties, flexural properties, and shear properties by varying with exposure times. Also dynamic mechanical test and FTIR were conducted to investigate a change in chemical structure as well as thermal analysis properties such as storage shear modulus, loss shear moduls, and tan ${\delta}$. According to the results, salt water environment has effected on mechanical properties and thermal analysis properties and especially the durability of glass fabric/phenolic composites were severely affected on salt water immersion environment rather than salt water spray environment.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2007년도 추계학술대회 논문집
• /
• pp.852-858
• /
• 2007

The durability of carbon/epoxy composites under salt water environment was investigated through salt water spray tester. Salt water environment was obtained through salt spray and salt immersion. 5% NaCl solution was used for salt water as natural salt water. Mechanical test was performed to obtain tensile properties, flexural properties, and shear properties of carbon/epoxy composite over 12 months under salt water environment. Dynamic mechanical analyzer was used to investigate thermal analysis properties such storage modulus, loss modulus, and tan ${\delta}$. Also FT/IR test was conducted to investigate a change in chemical structure. According to the results, mechanical properties were found to be slowly degraded as a function of exposure times. Regarding to thermal analysis properties, storage modulus was insensitive to exposure times, but loss modulus was shown to be slightly decreased. Although the shape and location of peak in FT/IR were not much changed, the intensity of peak in FT/IR was affected on exposure times. We also found that salt water immersion was more severe to the durability of carbon/epoxy composite rather than salt water spray.

• 소성∙가공
• /
• 제21권5호
• /
• pp.330-335
• /
• 2012

Roll formed steel bolts are electrodeposited with Zn-Ni to protect themselves from corrosion. However, white storage stain or white rust(corrosion) is found on Zn-Ni electrodeposited surface of steel bolts when they are exposed to moisture. In this paper a new process is introduced to protect Zn-Ni electrodeposited steel bolt from white storage stain or white rust for a long time under the salt spray test and high humidity test conditions. The better corrosion resistance could be gotten by the additional process of Ni-P electroless deposition and heat treatment to conventional manufacturing method of Zn-Ni coated steel bolt. The corrosion resistance of Zn-Al powder slurry coated steel bolt showed better than that of Zn-Ni electrodeposited one.

• 한국표면공학회지
• /
• 제49권2호
• /
• pp.141-146
• /
• 2016

In this study, electrophoretic paint (E-paint) was deposited on the knife-abraded surface of AZ31 magnesium alloy (AZ31), and its adhesion and corrosion resistance were examined by tape peel-test and salt spray test, respectively. E-paint started to deposit on AZ31 Mg alloy after an inductance time and pores were found in the E-paint layer which is ascribed to hydrogen bubbles generated on the surface during the painting process. The pores disappeared after curing for 15 min at $160^{\circ}C$. The E-paint on AZ31 exhibited good adhesion after immersion in deionized water for 500 h at $40^{\circ}C$. The E-paint sample without scratch showed no corrosion after 1500 h of salt spray test. However, on the scratched sample, blisters were visible adjacent to the scratched sites after 500 h of salt spray test.

• Corrosion Science and Technology
• /
• 제12권1호
• /
• pp.56-64
• /
• 2013

An Eectrolytic Corrosion(EC) test method was evaluated by the comparison with Copper Accelerated Acetic Salt Spray(CASS) and Neutral Salt Spray(SS) tests. Those methods were applied in order to evaluate corrosion resistance of Ni-Cr plated and Zn-plated Fe substrates. The correlations between results obtained by different test methods were investigated. Results showed that the electrochemical method such as the EC test method was superior to the conventional methods such as CASS and SS, in terms of the quantitative accuracy and the test-time span. Furthermore, the EC test method provided the useful means to estimate the initiation of corrosion of each layer by monitoring the rest potentials of the coated layers such as Ni, Cr, and Zn on Fe substrate. With regard to test time spans, the EC test provided the 78 times and 182 times faster results than the CASS test in cases of $Fe+5{\mu}m$ $Ni+0.5{\mu}m$ Cr and $Fe+20{\mu}m$ $Ni+0.5{\mu}m$ Cr respectively, while the EC test was 85 times faster results than the Salt Spray test in the case of $Fe+20g/m^2$ Zn. Therefore, the EC test can be the better method to evaluate the resistance to corrosion of coated layers than the conventional methods such as the SS test and the CASS.

• Corrosion Science and Technology
• /
• 제12권5호
• /
• pp.209-214
• /
• 2013

In the industry, accelerated corrosion test is used for the life time prediction. When anti-corrosion test proceeds in real environments, it is difficult that we predict and evaluate the corrosion life time because of the long test time such as 10 years or more time. Accelerated corrosion test and Salt spray test are able to test corrosion life time of products in the laboratory instead of outdoor corrosion test. Experimental procedure is selected for the corrosion standard specimen, exposure of the specimens, measurements of the mass loss and evaluating the mass loss data. As a result, the acceleration factor of the accelerated corrosion test to the outdoor corrosion test is 414.8. Therefore we can predict the corrosion life time of carbon steel during a short time period.

• Journal of Welding and Joining
• /
• 제32권4호
• /
• pp.55-62
• /
• 2014

The use of light-weight Al alloys in the automotive industry is increasing to meet requirements for fuel efficiency and emission reduction. Joining Al alloy to the conventional steel sheet is also very important issue with the increased use of Al alloy, and several joining processes have been introduced to enhance joining strength between dissimilar metals. This paper deals with a galvanic corrosion in the dissimilar metal joining. Salt spray tests up to 2000 hours were conducted on a self-piercing rivet, spot welded, adhesive bonded and weld-bonded joints, and cross-sections and tensile shear strength according the salt spray duration were analyzed at every 500-hour. Self-piercing rivet joint had relative low initial strength but the joint strength did not change regardless of the salt spray duration. The strength of other joints (spot welded, adhesive bonded and weld-bonded joints) decreased with the increase of salt spray duration and the corrosion behaviour of each joint was discussed.