• 한국결정성장학회지
• /
• 제24권4호
• /
• pp.151-157
• /
• 2014

The degradation mechanisms of thermal barrier coatings (TBCs) were investigated in different thermal fatigue condition in terms of microstructural analyses. The isothermal and cyclic oxidation tests were conducted to atmospheric plasma sprayed-TBCs on NIMONIC 263 substrates. The delamination occurred by the oxide layer formation at the interface, the Ni/Cr-based oxide was formed after Al-based oxide layer grew up to ${\sim}10{\mu}m$ in the isothermal condition. In the cyclic oxidation with dwell time, the failure occurred earlier (500 hr) than in the isothermal oxidation (900 hr) at same temperature. The thickness of Al-based oxide layer of the delaminated specimen in the cyclic condition was ${\sim}4{\mu}m$ and the interfacial cracks were observed. The acoustic emission method revealed that the cracks generated during the cooling step. It was considered that the specimens were prevented from the formation of the Al-based oxide by cooling treatment, and the degradation mode in the cyclic test was dominantly interfacial cracking by the difference of thermal expansion coefficients of the coating layers.

• 폴리머
• /
• 제33권5호
• /
• pp.435-440
• /
• 2009

가황제/가황촉진제의 비율이 서로 다른 CR(chloroprene)로 개질된 NR(natural rubber)고무복합재료에 대한 비등온 TGA 열분해곡선으로부터 Kissinger 및 Flynn-Wall-Ozawa의 해석방법을 적용하여 분해활성화 에너지를 구하였다. 각 샘플에 대해 Kissinger의 해석방법을 적용한 결과 매우 양호한 직선성을 보였으며 기울기로부터 얻은 활성화 에너지 값은 모든 샘플에 대해 $147.0{\pm}2.0$ kJ/mol로 거의 일정하였다. Flynn-Wall-Ozawa의 해석방법을 적용하여 전화율 $0.05{\sim}0.40$ 범위에서 계산된 분해활성화 에너지 값은 전화율의 변화에 따라 계속 변화하였고 전화율이 증가함에 따라 그 값도 증가하는 현상을 보여 주었으며, 평균활성화 에너지 값은 $211.6{\pm}19.0$ kJ/mol 이었다. 두 가지 해석 방법의 비교 연구로부터, 샘플들의 전체 분해반응은 반응 메카니즘이 서로 다른 여러 단계의 다중 반응으로 이루어 있는 것으로 생각할 수 있었다.