• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2018년도 춘계 학술논문 발표대회
• /
• pp.197-198
• /
• 2018

As part of the effort to shorten the construction period, this study examined the strength expression characteristics at the early age of concrete using high fineness cement and blast furnace slag. accordingly to provide a basic data on how to solve the problem that the initial strength is lowered.

• 대한치과기공학회지
• /
• 제42권2호
• /
• pp.73-79
• /
• 2020

Purpose: The aim of this study was to investigate the influence of short and long duration sintering on microstructure and flexural strength of zirconia. Methods: To conduct three-point bending test, Zirconia specimens are milled according to ISO 6872 guidelines(N=18, n=9 per group). Two specimens group(n=8) is sintered for 10 hours(Standard schedule) and 3 hours(Speed schedule) at the peak temperature of 1550℃ with silicon carbide sintering furnace. Flexural strength of specimens are measured by instron. After coating each specimen(n=1), microstructure of specimens is observed using Scanning Electron Microscope(SEM). T-test was utilized to statistically assess the data. Results: The mean and standard deviation value of the flexural strength for standard schedule group are 578.15±57.48Mpa, that of speed schedule are 465.9±62.34Mpa. T-test showed significant differences in flexural strength between two zirconia specimen group which applied standard schedule and speed schedule respectively(p<0.05). Conclusion: The result of this study showed that the increase in sintering time led to increased grain size, and also to a positive effect on the flexural strength.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2005년도 추계 학술논문 발표대회
• /
• pp.101-104
• /
• 2005

The world's cement demand is anticipated to increase about 2.558$\%$ every year until the first half of the 21st century. To be closed the increase of cenment damand and simultaneously comply with the Kyoto Protocal, cement that gives less carbon dioxide(Co2) discharge should be urgently developed. If cement can be manufactured with industrial byproducts such as granulated blast furnace slag(GBFS), phosphogypsum(PG), and waste lime(WL) instead of clinker as its counterproposal, there would be many advantages including maximum use of these industrial byproducts for high value-added resources, conservation of natural resources and energy by omitting the use of clinker, minimized environmental pollution problems caused by Co2 discharge and reduction of the cost. So this study aims to solve the problems by manufacturing non-sintered cement.