• Journal of Korea Foundry Society
• /
• 제12권5호
• /
• pp.397-402
• /
• 1992

The effect of the solution & aging treatment on the tensile strength, yield strength, elongation, reduction of area, hardness was studied in the 17-4 PH stainless steel. SEM pictures were also taken in order to examine the fracture surfaces and precipitated particles. X-ray diffraction patterns for the heat treated samples were also observed. Mechanical properties of the heat treated samples were superior to those of as cast samples. Tensile strength, yield strength, hardeness decreased with the increase of aging temperature. On the other hand, elongation and reduction of area increased as the aging temperature increased.

• Textile Coloration and Finishing
• /
• 제9권6호
• /
• pp.87-95
• /
• 1997

Wool samples were treated by potassium tert-Butoxide(t-BuOK) in anhydrous tert-butanol to remove the bound surface lipid-layer, and the weight loss behaviors in protease solution and dyeabilities of the samples were studies. The C/N ratio of the surface of the t-BuOK-treated wool was shown to be 4.3 from XPS analysis. From SEM pictures any remarkable change in the shape of surface curticle during the proteasw treatment was not observed regardless of prior t-BuOK treatment. Dyeing rate and equilibrium adsorption of Orange II, a typical levelling type acid dye, on wool were not changed by protease or t-BuOK treatment, but those of Milling Cyanine 5R, a typical milling type acid dye, on wool were greatly enhanced by t-BuOK treatment in spite that, from alkali and urea-bisulfite solubilities, no damage on the inner part of wool fiber was expected by t-BuOK treatment.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 한국정밀공학회 2005년도 추계학술대회 논문집
• /
• pp.149-153
• /
• 2005

The electron beam machining provides very high resolution up to nanometer scale, hence the E-beam writing technology is rapidly growing in MEMS and nano-engineering areas. In the optical column of the e-beam writer, there are several lenses condensing and focusing electron beams from electron gun with fringing magnetic fields. The polepieces of these lenses are usually made with high purity iron which is hard to fabricate and very expensive. In this paper, the possibility of using polepiece of object lens composed with pure iron and low carbon steel was examined to reduce cost. The magnetic field at object lens was calculated with finite element method, and practical focusing qualities of SEM pictures were observed comparing for the object lens polepieces with pure iron and two type of composed with low carbon steel.

• Restorative Dentistry and Endodontics
• /
• 제35권5호
• /
• pp.321-334
• /
• 2010

Objectives: The purpose of this study is to evaluate bonding efficacy by means of measuring the effect of remained solvent on Degree of conversion(DC) and ${\mu}TBS$ and FE-SEM examination. Materials and Methods: Two 2-step total etching adhesives and two single-step self etching adhesives were used in this study. First, volume weight loss of 4 dentin adhesives were measured using weighting machine in process of time in normal conditions and calculate degree of evaporation (DE). Reaction/reference intensity ratio were measured using micro-Raman spectroscopy and calculate DC according to DE. Then 2 experimental groups were prepared according to air-drying methods (under, over) and control group was prepared to manufacturer's instruction. Total 12 groups were evaluated by means of micro tensile bond strength and FE-SEM examination. Results: Degree of evaporation (DE) was increased as time elapsed but different features were observed according to the kind of solvents. Acetone based adhesive showed higher DE than ethanol and butanol based adhesive. Degree of conversion (DC) was increased according to DE except for $S^3$ bond. In ${\mu}TBS$ evaluation, bond strength was increased by additional air-drying. Large gaps and droplets were observed in acetone based adhesives by FE-SEM pictures. Conclusions: Additional air-drying is recommended for single-step self etching adhesive but careful consideration is required for 2-step total etching adhesive because of oxygen inhibition layer. Evaporation method is carefully chose and applied according to the solvent type.

• Membrane Journal
• /
• 제14권4호
• /
• pp.304-311
• /
• 2004

The poly(1-trimethylsilyl-1-propyne) (PTMSP) and silica-filled PTMSP membranes were prepared by casting from a toluene solution on porous polyetherimide (PEI). FT-IR spectrum, GPC and SEM pictures have been taken to characterize the membranes. The particle size of membrane decreases as silica content of the membrane increases from 23 to 60 wt%, and a uniform distribution of the silica is observed. The separation properties of the gas mixture (32 mol% $H_2$/ 68 mol% $N_2$) through the composite membranes were studies as a function of pressure and percentage of silica. Selectivity values of $H_2$/$N_2$ increased as the pressure of permeation cell and silica content of the membrane increased. The real separation factor($\alpha$), head separation factor($\beta$), and tail separation factor((equation omitted)) of PTMSP-PEI composite membrane were 2.28, 1.58, and 1.44 respectively at $\Delta$P 30 psi and $25^{\circ}C$. $\alpha$, $\beta$, and (equation omitted) of PTMSP-Silica-PEI composite membrane for 60 wt% silica were 3.34, 1.95, 1.72 at $\Delta$P 30 psi and $25^{\circ}C$.

• Journal of the Korean Home Economics Association
• /
• 제45권10호
• /
• pp.73-81
• /
• 2007

The purpose of this study was to increase the ultraviolet-light (UV)-cut ability of cellulose fabrics (cotton, ramie, and rayon) dyed with safflower yellow colorants. For this purpose, samples treated with UV-cut agent and tannic-acid were compared with the untreated samples after UV exposure in terms of K/S value, color changes(${\Delta}E$), SEM, and strength retention. The K/S value rapidly decreased after 28 days exposure, whereas the K/S value of the samples treated with both UV-cut agent and tannic-acid decreased to less than that of the untreated samples. In color changes, $L^*$ increased while $a^*$ and $b^*$ decreased, indicating less red and yellow character in color. This induced a change in the hue, value and chroma values. However the color change(${\Delta}E$) of the samples treated with both UV-cut agent and tannic-acid was less than that of the untreated samples. Scanning electron microscopy (SEM) pictures showed a severe degradation by exposure in all samples. Tensile strength rapidly decreased after 28 days for cotton and rayon, and after 21 days for ramie. However, the strength retention of the samples treated with UV-cut agent and tannic-acid was higher than that of the untreated samples.

• Applied Chemistry for Engineering
• /
• 제5권5호
• /
• pp.878-888
• /
• 1994

In order to investigate the fracture behavior of ABS terpolymer under the tension and impact load, varing the content of rubber, molecular weight of SAN, content and kinds of lubricant, tension speed, the mechanical properties were measured and SEM pictures of fracture area were taken. Under the tension, the tensile strength increased as rubber content and lubricant content decreased, while molecular weight and tension speed increased. The deformation of area near fracture site did not occur as rubber content, tension speed and molecular weight decreased and liquid lubricant was used. And in the shape of fracture seemed phase seperation. Under the impact load, the notched izod impact strength increased as rubber content, molecular weight, ambient temperature and lubricant content increased. In the SEM picture, the strength was high white the fracture surface was small.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• 제21권4호
• /
• pp.619-624
• /
• 2012

In this study, MMT/fiber/polymer composites were fabricated by impregnating chopped strand glass mat into a vinylester resin mixed with clay. Tensile tests has been performed by using a universal testing machine to determine the effect of MMT addition on the tensile properties of MMT/chopped strand glass fiber/vinylester composites. And some pictures which are magnified cross section of breaking parts are has been taken by using a FE-SEM to confirm the behavior at breaking. The contents ratio of MMT applied in the composites were 0.5, 1.0, 1.5, and 2.0 wt% respectively. It has been found that the tensile strength and elastic modulus of MMT/chopped strand glass fiber/vinylester composites were improved at a proper content of MMT. Tensile strength and elastic modulus were maximized at a content of 1.0 wt% due to most effective dispersion of MMT. On the contrary, the failure strain was increased as MMT content was increased.

• Korean Membrane Journal
• /
• 제8권1호
• /
• pp.67-73
• /
• 2006

Transparent materials are well known but preparation of transparent poly 2-hydroxyethyl methacrylate {poly (HEMA)} material by varying solvent is a new one and economically reliable. This material is prepared from hydroxyl based monomer HEMA by radical polymerization using benzoyl peroxide (BPO) as initiator and isobutanol, 2-butanol, 1-butanol, hexane and toluene as a solvent. The reaction temperature, time and stirring speed were set at $70^{\circ}C$, 4 hrs and 150 rpm, respectively. The polymer was characterized for functional group by IR spectroscopy. It was observed that the intensity of band at $1637 cm^{-1}$ a characteristic band of C=C stretching disappeared indicating that it was completely consumed after polymerization. It was observed that swelling percentage increases with increase as time passes but after a certain time a constant swelling percentage is achieved. SEM pictures reveals that poly (HEMA) prepared by different solvent shows pore with a distinguishable void up to several micrometers. The BET surface area, cumulative pore volume and average pore diameter is greater in poly (HEMA) prepared by hexane as a solvent compared to other solvents. Poly (HEMA) prepared by 1-butanol as a solvent shows higher glass transition temperature compared to other solvents. Poly (HEMA) prepared by different solvents shows $90{\sim}94%$ light transmission property from light transmission measurement and looks transparent.

• Proceedings of the KIEE Conference
• /
• 대한전기학회 1998년도 하계학술대회 논문집 E
• /
• pp.1761-1763
• /
• 1998

ITO(Iridium-Tin Oxide) thin film, as discharge electrodes in AC PDP, should have low resistivity and high transparency. Regarded as a high deposition rate method, the ITO thin film fabricated by the facing target sputtering system has been studied in this paper. The electrical property of the ITO film deposited below $150^{\circ}C$ is not satisfied. The SEM pictures show that the ITO films deposited below $150^{\circ}C$ are amorphous. After being annealed the amorphous ITO films become crystalline, and for this reason, the electrical property of amorphous ITO films can be effectively improved by annealing process. An ITO film with the resistivity as low as $1.99{\times}10^{-4}$ and transparency above 85% has be gotten after vacuum annealing at $300^{\circ}C$ for 2 hours while deposited at $75^{\circ}C$. The corresponding deposition rate is $220{\AA}/min$.