Gas foil thrust bearings (GFTBs) have attractive advantages over rolling element bearings and oil film thrust bearings, such as oil-free operation, high speed stability, and high-temperature operation. However, GFTBs have lower load carrying capacity than the other two types of bearings owing to the inherent low gas viscosity. The load carrying capacity of GFTBs depends mainly on the compliance of the foil structure and the formed hydrodynamic wedge, where the gas pressure field is generated between the top foil and the thrust runner. The load carrying capacity of the GFTBs is very important for the suitable design of oil-free turbomachinery with high performance. The aim of the present study is to identify the characteristics of the load carrying performance of GFTBs. A new test rig for the experimental measurements is designed to provide static loads up to 800 N using a pneumatic cylinder. The maximum operating speed of the driving motor is 30,000 rpm. A series of experimental tests—lift-off test, static load performance test, and maximum load capacity test—estimate the performance of a six-pad GFTB, in terms of the static load, driving torque, and temperature. The maximum load capacity is determined by increasing the static load until the driving torque rises suddenly with a sharp peak. The test results show that the torque and temperature increase linearly with the static load. The estimated maximum load capacity per unit area is approximately 80.5 kPa at a rotor speed of 25,000 rpm. The test results can be used as a design guideline for GFTBs for realizing oil-free turbomachinery.

• Korean Journal of Metals and Materials
• /
• v.47 no.12
• /
• pp.811-818
• /
• 2009

In order to meet increasingly complex and rigorous technical specifications, extensive effort has been devoted to fabricate clad materials with multi-layered metal plates. In this study, novel stainless steel/aluminum/copper (STS/Al/Cu) three-ply clad materials were fabricated by a hot rolling process for cookware applications. The effect of the testing temperature on the mechanical properties of the clad materials and on each component metal was investigated during the tensile tests. The interface properties of the clad materials were also examined by optical microscopy (OM) and an electron probe micro-analyzer (EPMA). The best mechanical and interfacial properties for a warm working process were found in a sample annealed at a temperature of $300^{\circ}C$. For the sample annealed at $400^{\circ}C$, the results of the tensile test indicated that interface delamination occurred only in the region of the Al/Cu interfaces. This was due to the formation of the thick and brittle intermetallic compound of $Al_2Cu$ in the Al/Cu interface. In contrast, no interface delamination was observed in the STS/Al interface, most likely due to its strong bond strength.

• Korean Journal of Metals and Materials
• /
• v.47 no.7
• /
• pp.406-415
• /
• 2009

A study was conducted on the effects of carbon, tungsten, and vanadium on the wear properties and surface roughness of four High Speed Steel (HSS) rolls manufactured by the centrifugal casting method. Hot-rolling simulation tests were carried out using a high-temperature wear tester capable of controlling speed, load, and temperature. HSS rolls contained a large amount (up to 25 vol.%) of carbides such as MC, $M_{2}C$, $M_{7}C_{3}$, and $M_{6}C$ carbides formed in the tempered martensite matrix. The matrix consisted mainly of lath tempered martensite when the carbon content in the matrix was small, and contained a considerable amount of plate tempered martensite when the carbon content increased. The high-temperature wear test results indicated that the wear properties and surface roughness of the rolls improved when the amount of hard MC carbides formed inside solidification cells increased. The rolls distribution was also homogeneous. The best wear properties and surface roughness were obtained from a roll where a large amount of MC carbides was homogeneously distributed in the lath tempered martensite matrix. The proper contents of carbon equivalent, tungsten equivalent, and vanadium were 2.0~2.3%, 9~10%, and 5~6%, respectively.

• Journal of Trauma and Injury
• /
• v.34 no.1
• /
• pp.21-30
• /
• 2021

Purpose: The purpose of this study was to determine the influence of seasons and weather on the volume of trauma patients in central Korea. Methods: The records of 4,665 patients treated at Chungbuk National Hospital Regional Trauma Center from January 2016 to December 2019 were retrospectively reviewed. Meteorological data including hourly temperature (℃), precipitation (mm), humidity (%), and wind speed (m/s) for each district were collected retrospectively. Statistical analysis was done using the independent t-test, one-way analysis of variance (ANOVA), and linear regression analysis. Results: Patients' average age was 53.66 years, with a significant difference between men (49.92 years) and women (60.48 years) (p<0.001). Rolling/slipping down was a prominent cause of injury in winter (28.4%, n=283), with statistical significance (p<0.001). Trauma occurred least frequently in winter (p=0.005). Linear regression analysis revealed an increasing number of patients as the temperature increased (p<0.05), the humidity increased (p<0.001), and the wind speed decreased (p<0.001). Precipitation did not affect patient volume (p=0.562). One-way ANOVA revealed a decreased incidence of trauma when the temperature exceeded 30℃ (p<0.001), and when the humidity was more than 75%, compared to 25-50% and 50-75%. Conclusions: At the regional trauma center of Chungbuk National University Hospital, in central Korea, the number of trauma patients was lowest in winter, and patient volume was affected by temperature, humidity, and wind speed.

• Korean Journal of Materials Research
• /
• v.22 no.11
• /
• pp.591-597
• /
• 2012

For heat exchanger applications, 2-ply clad materials were fabricated by rolling of aluminum (Al) and mild steel sheets. Effects of annealing temperature on interface properties, especially on inter-layer formation and softening of strain hardened mild-steel, for Al/mild steel clad materials, were investigated. To obtain optimum annealing conditions for the Al/mild steel clad materials, annealing temperature was varied from room temperature to $600^{\circ}C$. At the annealing temperature about $450^{\circ}C$, an inter-layer was formed in an island-shape at the interface of the Al/mild steel clad materials; this island expanded along the interface at higher temperature. By analyzing the X-ray diffraction (XRD) peaks and the energy dispersive X-ray spectroscopy (EDX) results, it was determined that the exact chemical stoichiometry for the inter-layer was that of $Fe_2Al_5$. In some samples, an X-layer was formed between the Al and the inter-layer of $Fe_2Al_5$ at high annealing temperature of around $550^{\circ}C$. The existence of an X-layer enhanced the growth of the inter-layer, which resulted in the delamination of the Al/mild-steel clad materials. Hardness tests were also performed to examine the influence of the annealing temperature on the cold deformability, which is a very important property for the deep drawing process of clad materials. The hardness value of mild steel gradually decreased with increasing annealing temperature. Especially, the value of hardness sharply decreased in the temperature range between $525^{\circ}C$ and $550^{\circ}C$. From these results, we can conclude that the optimum annealing temperature is around $550^{\circ}C$ under condition of there being no X-layer creation.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.15 no.3
• /
• pp.237-251
• /
• 2013

This study aimed to estimate the axial stress and torque on a shaft in a disc cutter. The corresponding inner temperature and the surface temperature of a cutter ring were also measured by using strain gauges and thermocouples during the linear cutting tests. The maximum values of the axial stress and torque were recorded to 11.3 MPa, $171kN{\cdot}m$ respectively. They have higher correlations with normal force rather than rolling force. The results of temperature measured by thermocouples during a linear cutting test showed that the rate of increase in temperature was below $0.2^{\circ}C$. When the cutter spacing is set to be 70 mm, the inner temperature and surface temperature of a disc cutter were $0.1^{\circ}C/m$, $0.15{\sim}0.17^{\circ}C/m$ respectively. Similarly, when the cutter spacing is 90 mm, the temperature values were $0.09^{\circ}C/m$, $0.13{\sim}0.23^{\circ}C/m$ respectively.

• Journal of computational fluids engineering
• /
• v.19 no.3
• /
• pp.24-28
• /
• 2014

With ever rising concerns about saving of fossil fuel resource, there have been an increasing demand for use of energy more efficiently. The electric motor driven inverters can be a great help to improve energy efficiency. They are also used to control the motor speed to the actual need. Therefore the use of them can lead to reduce energy consumption. In particular, the medium voltage(MV) drive systems used for pumps, fans, steel rolling mills and tractions have widespread applications in the industry. They cover power ratings from 0.4MW to 40MW at the MV level of 2.3kV to 13.8kV. The majority of the installed MV drive systems however, are in the 1MW to 4MW range with voltage rating from 3.3kV to 6.6kV. But they are required to reduce size and weight like other power electronic equipments. In this paper, we studied on the 3.3kV(105A) compact rack type inverter system for improving the cooling efficiency. At first, we confirmed the tendency of temperature with computational simulation using ANSYS ICEPAK and actual experimental tests. And then we researched thermal performance improvement designs in order to reduce temperature of the transformer for the safe operation. It can reduce temperature of transformer that using pipe type flow guide in the system. As a result, we found out more efficient solution by thermal-fluid analysis.

• Korean Journal of Materials Research
• /
• v.20 no.7
• /
• pp.385-391
• /
• 2010

Twinning-induced plasticity (TWIP) steels have attracted great attention due to their excellent mechanical properties of high tensile strength (over 800MPa) and high ductility (over 50%), which result from the high strain hardening due to the mechanical twin formation during plastic deformation. The purpose of this study is to investigate the effect of annealing temperature and alloying elements on the mechanical properties of Fe-18Mn-0.6C TWIP steel. In 1.5%Al TWIP steel with 0.123%Ti content, the average recrystallized grain size was reduced to 2.5 ${\mu}m$ by cold rolling and annealing at $800^{\circ}C$ for 5 min, because of the pinning effect of the fine TiC carbides on grain coarsening. The tensile strength was decreased and the ductility was improved with the increase of the annealing temperature. However, a reversion of hardness and yield strength happened between $750^{\circ}C$ and $800^{\circ}C$ due to TiC and $M_3C$ type precipitation. 0.56% Ni added TWIP steel exhibited relatively lower yield strength, because Ni precipitates were not formed during the annealing process. When this specimen was annealed at $800^{\circ}C$ for 5min, the tensile strength and elongation were revealed at 1096MPa and 61.8%, respectively.

• Journal of Welding and Joining
• /
• v.33 no.3
• /
• pp.19-24
• /
• 2015

Joint properties of electric control unit (ECU) module using Sn-Cu-(X)Al(Si) lead-free solder alloy were investigated for automotive electronics module. In this study, Sn-0.5Cu-0.01Al(Si) and Sn-0.5Cu-0.03Al(Si) (wt.%) lead-free alloys were fabricated as bar type by doped various weight percentages (0.01 and 0.03 wt.%) of Al(Si) alloy to Sn-0.5Cu. After fabrications of lead-free alloys, the ball-type solder alloys with a diameter of 450 um were made by rolling and punching. The melting temperatures of 0.01Al(Si) and 0.03Al(Si) were 230.2 and $230.8^{\circ}C$, respectively. To evaluation of properties of solder joint, test printed circuit board (PCB) finished with organic solderability perseveration (OSP) on Cu pad. The ball-type solders were attached to test PCB with flux and reflowed for formation of solder joint. The maximum temperature of reflow was $260^{\circ}C$ for 50s above melting temperature. And then, we measured spreadability and shear strength of two Al(Si) solder materials compared to Sn-0.7Cu solder material used in industry. And also, microstructures in solder and intermetallic compounds (IMCs) were observed. Moreover, thickness and grain size of $Cu_6Sn_5$ IMC were measured and then compared with Sn-0.7Cu. With increasing the amounts of Al(Si), the $Cu_6Sn_5$ thickness was decreased. These results show the addition of Al(Si) could suppress IMC growth and improve the reliability of solder joint.

• Journal of the Korean Society for Heat Treatment
• /
• v.3 no.1
• /
• pp.34-41
• /
• 1990

Effects of grain size and cold rolling degree on shape memory ability and transformation temperature were studied in Fe-35% Mn-6% Si shape memory alloy. Md point of the alloy was determined by variation of yield stress with test temperature. The Md point measured in this way was linearly increased with increasing grain size. Shape memory ability of the alloy was decreased with increasing grain size, showing a minimum value at around $63{\mu}m$, and then increased with increasing grain size. From this result, it was concluded that the shape memory ability in the grain size smaller than a critical value is controlled by amount of retained ${\gamma}$ and prior ${\varepsilon}$ phase, but that the shape memory ability in the grain size greater than the critical value is mainly dominated by grain boundary area in unit volume of parent phase. The shape memory ability was decreased with increasing deformation degree. This was because the ${\gamma}$ content being available for the formation of ${\varepsilon}$ martensite during bending was decreased with increasing deformation degree.