• Proceedings of the KSME Conference
• /
• 2004.04a
• /
• pp.78-83
• /
• 2004

Environmental fatigue crack propagation of CF8M and CF8A steels used in the domestic PWR were investigated on the simulated PWR condition(Temperature: $316^{\circ}C$, Pressure: 15MPa). The test equipment for environmental fatigue(high temperature-high pressure loop, autoclave, load frame, measurement system) were designed. As-received and 60-year aged specimens were used in the test. To compare with environmental fatigue test, another test was performed in the air condition. The fracture surface of specimens were difficult to verify the fracture modes such as striation, intergranular crack and cleavage and so on. As the ferrite content of CF8M is increased, more particles covered fracture surface were peeled.

• Proceedings of the KSME Conference
• /
• 2003.11a
• /
• pp.1062-1067
• /
• 2003

In this study, corrosion fatigue characteristics of CF8M and CF8A steel were investigated on the simulated PWR condition(Temp.:$316^{\circ}C$, Pres.: 15:MPa). To make the simulated PWR condition. the special test machine consisted of INSTRON, Autoclave, LOOP and Measurement system was developed. As ${\Delta}K$ is ranged from 11 to $20MPa{\sqrt{m}}$, Crack growth rate of PWR condition is faster than air condition. Above $20MPa{\sqrt{m}}$, the crack growth rate of PWR and air condition is similar. Corrosion fatigue characteristics regardless of the ferrite contents($10{\sim}25wt.%$) is not different. After the test, the fracture surface of specimens was examined. It was difficult to verify the fracture modes such as striation, intergranular crack and cleavage and so on. As the ferrite content of CF8M is increased, the more particles covered fracture surface were peeled.