• Journal of Sensor Science and Technology
• /
• v.12 no.2
• /
• pp.66-71
• /
• 2003

Pt/AlGaN Schottky-type UV photodetectors were designed and fabricated. A low-temperature AlGaN interlayer buffer was grown between the AlGaN and GaN film in the diode structure epitaxy to obtain crack-free AlGaN active layers. A comparison was then made of the structural, electrical, and optical characteristics of two different diodes: one with an AlGaN($0.5\;{\mu}m$)/n+-GaN(2 nm) structure (type 1) and the other with an AlGaN($0.5\;{\mu}m$)/AlGaN interlayer($150\;{\AA}$)/n+-GaN($3\;{\mu}m$) structure(type 2). A crack-free AlGaN film was obtained by the insertion of a low-temperature AlGaN interlayer with an aluminum mole fraction of 26% into the $Al_xGa_{1-x}N$ layer. The fabricated Pt/$Al_{0.33}Ga_{0.67}N$ photodetector had a leakage current of 1 nA for the type 1 diode and $0.1\;{\mu}A$ for the type 2 diode at a reverse bias of -5 V. For the photoresponse measurement, the type 2 diode exhibited a cut-off wavelength of 300 nm, prominent responsivity of 0.15 A/W at 280 nm, and UV-visible extinction ratio of $1.5{\times}10^4$. Accordingly, the Pt/$Al_{0.33}Ga_{0.67}N$ Schottky-type ultraviolet photodetector with an AlGaN interlayer exhibited superior electrical and optical characteristics and improved UV detecting properties.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.40 no.7
• /
• pp.486-493
• /
• 2003

Schottky type A $l_{0.33}$G $a_{0.67}$N ultraviolet photodetectors were fabricated on the MOCVD grown AlGaN/ $n^{＋}$-GaN and AlGaN/AlGaN interlayer/ $n^{＋}$-GaN structures. The grown layers have the carrier concentrations of -$10^{18}$, and the mobilities were 236 and 269 $\textrm{cm}^2$/V.s, respectively. After mesa etching by ICP etching system, the Si3N4 layer was deposited for passivation between the contacts and Ti/AL/Ni/Au and Pt were deposited for ohmic and Schottky contact, respectively. The fabricated Pt/A $l_{0.33}$G $a_{0.67}$N Schottky diode revealed a leakage current of 1 nA for samples with interlayer and 0.1$\mu\textrm{A}$ for samples without interlayer at a reverse bias of -5 V. In optical measurement, the Pt/A $l_{0.33}$G $a_{0.67}$N diode with interlayer showed a cut-off wavelength of 300 nm, a prominent responsivity of 0.15 A/W at 280 nm and a UV-visible extinction ratio of 1.5x$10^4./TEX>.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.33A no.2
• /
• pp.96-113
• /
• 1996

It has been found that the misfit dislocations in heavily boron-doped layers originate from wafer edges. Moreover, the propagation of the misfit dislocation into a heavily boron-doped region can be suppressed by placing a surrounding undoped region. Using a surrounding undoped region the disloction-free heavily boron-deoped silicon membranes have been fabricated. The measured surface roughness, fracture strength, and residual tensile stress of the membrane are 20.angs. peak-to-peak, 1.39${\times}$10$^{10}$ and 2.7${\times}$10$^{9}$dyn/cm$^{2}$, while those of the conventional heavily boron-doped silicon membrane with high density of misfit dislocations are 500 peak-to-peak, 8.27${\times}$10$^{9}$ and 9.3${\times}$10$^{8}$dyn/cm$^{2}$ respectively. The differences between these two membranes are due to the misfit dislocations. Young's modulus has been extracted as 1.45${\times}$10$^{12}$dyn/cm$^{2}$ for both membranes. Also, the effective lattice constant of heavily boron-doped silicon, the in-plane lattice constant of the conventional membrane, and the density of misfit dislocation contained in the conventional membrane have been extracted as density of misfit dislocation contained in the conventional membrane have been extracted as density of misfit dislocation contained in the conventional membrane have been extracted as 5.424.angs. 5.426.angs. and 2.3${\times}$10$^{4}$/cm for the average boron concentration of 1.3${\times}$10$^{20}$/cm$^{-23}$ cm$^{3}$/atom. Without any buffer layers, a disloction-free lightly boron-doped epitaxial layer with good crsytalline quality has been directly grown on the dislocation-free heavily boron-doped silicon layer. X-ray diffraction analysis revealed that the epitaxial silicon has good crystallinity, similar to that grown on lightly doped silicon substrate. The leakage current of the n+/p gated diode fabricated in the epitaxial silicon has been measured to be 0.6nA/cm$^{2}$ at the reverse bias of 5V.