• Restorative Dentistry and Endodontics
• /
• 제28권3호
• /
• pp.209-221
• /
• 2003

The objectiveness of this study was to evaluate whether low-viscosity composite can bond effectively to dentin surface without bonding resin. The low-viscosity composites being 50wt% filler content were made by the inclusion of bonding resin of two self-etching systems(Cleafil SE Bond, Unifil Bond) varied with contents as 0, 10, 20, 30, 40, 50wt%. Exposed dentin surfaces of extracted 3rd molars are used. Dentin bond strengths were measured. The tests were carried out with a micro-shear device placed testing machine at a CHS of 1mm/min after a low-viscosity composite was filled into an iris cut from micro tygon tubing with internal diameter approximately 0.8mm and height of 1.0mm. 1 Flexural strength and modulus was increased with the addition of bonding resin. 2. Micro-shear bond strength to dentin was improved according to content of bonding resin irrespective of applying or not bonding resin in bonding procedure, and that of Clearfil SE Bond groups was higher than Unifil Bond. 3. There were no significant difference whether use of each bonding resin in bonding procedure for S-40, S-50, U-50(p＞0.05). 4. In SEM examination, resin was well infiltrated into dentin after primed with self-etching primer only for S-50 and U-50 in spite of the formation of thinner hybrid layer. Low viscosity composite including some functional monomer may be used as dentin bonding resin without an intermediary bonding agent. It makes a simplified bonding procedure and foresees the possibility of self-adhesive restorative material.

• Restorative Dentistry and Endodontics
• /
• 제45권1호
• /
• pp.12.1-12.8
• /
• 2020

Objectives: The aim of this in vitro study was to evaluate the microhardness and surface roughness of composite resins before and after tooth bleaching procedures. Materials and Methods: Sixty specimens were prepared of each composite resin (Filtek Supreme XT and Opallis), and BisCover LV surface sealant was applied to half of the specimens. Thirty enamel samples were obtained from the buccal and lingual surfaces of human molars for use as the control group. The surface roughness and microhardness were measured before and after bleaching procedures with 35% hydrogen peroxide or 16% carbamide (n = 10). Data were analyzed using 1-way analysis of variance and the Fisher test (α = 0.05). Results: Neither hydrogen peroxide nor carbamide peroxide treatment significantly altered the hardness of the composite resins, regardless of surface sealant application; however, both treatments significantly decreased the hardness of the tooth samples (p < 0.05). The bleaching did not cause any change in surface roughness, with the exception of the unsealed Opallis composite resin and dental enamel, both of which displayed an increase in surface roughness after bleaching with carbamide peroxide (p < 0.05). Conclusions: The microhardness and surface roughness of enamel and Opallis composite resin were influenced by bleaching procedures.

• 대한치과보철학회지
• /
• 제51권1호
• /
• pp.27-32
• /
• 2013

연구 재료 및 방법: 본 연구에서는 간접 레진 수복시에 상아질 접착제와 저점도 레진을 이용한 상아질 레진코팅법을 자가 접착 레진 시멘트에 적용해 전단결합강도가 증가하는지 비교하고 기존의 레진 시멘트와의 전단결합강도 차이가 어떠한지 평가하고자 하였다. 연구 목적: 사람의 발거된 건전한 구치 36개의 치관부를 삭제하고 상아질을 노출시킨 후 3개의 군으로 분류하였다. 1군과 3군은 상아질에 아무런 처리 과정을 거치지 않고 2군만 Clearfil SE bond와 Metafil Flo를 사용해 상아질 레진코팅법을 시행하였다. 24시간의 임시수복 기간을 둔 후 Tescera를 이용하여 제작한 레진 인레이 블록을 1군과 2군에는 Unicem, 3군에는 Panavia F를 사용해 접착하였다. 그 후 증류수에 48시간 동안 보관한 후 전단결합강도를 측정하였다. 측정된 전단결합강도는 one-way ANOVA를 이용하여 비교 분석하였으며 유의한 차이가 있는 경우 Tukey method를 이용하여 multiple comparison를 시행하였다. 결과:상아질에 레진코팅법을 시행한 경우의 Unicem의 결합강도가 상아질에 아무런 처리를 하지 않은 대조군의 결합강도보다 높게 나타났고(P<.0001), 레진코팅을 하지 않고 Panavia F로 접착한 실험군의 결합강도보다 높게 나타났다(P<.0001). 결론: 상아질 레진코팅법은 자가 접착 레진 시멘트의 접착 강도를 증가시켰다.

• 대한소아치과학회지
• /
• 제49권4호
• /
• pp.428-441
• /
• 2022

이 연구의 목적은 알카자이트 수복재와 소아치과 영역에서 널리 사용되고 있는 수복재들의 색 안정성을 비교하고, 다양한 음료에서의 색상 변화를 비교하는 것이다. 글라스아이오노머, 레진강화형 글라스아이오노머, 알카자이트 수복재, 복합레진의 시편을 준비하였고, 열순환 후 색 안정성을 측정하였다. 침전 전과 7일, 14일, 21일, 28일 후 CIE L^*a^*b^*값의 색상 변화를 분석하기 위해 각 수복재료의 시편을 5개의 군으로 나누어 각각 PBS, 커피, 녹차, 콜라, 오렌지주스 용액에 침전시켰다. 열순환 후 복합레진에서 가장 높은 색 안정성을 보였고, 알카자이트 수복재, 글라스아이오노머, 레진강화형 글라스아이오노머 순으로 높은 안정성을 보였다. 7일간 다양한 용액에 침전시킨 결과 모든 시편에서 색상 변화가 나타났으며, 알카자이트 수복재는 글라스아이오노머 계열보다 낮은 색상 변화를 보였고, 복합레진보다는 높은 색상 변화를 나타냈다. 알카자이트 수복재는 커피에서 가장 많은 색상 변화가 나타났으며 그 다음은 녹차, 오렌지주스 순이었으나, 콜라와 PBS 용액에서는 침전 28일 이후에도 색상 변화를 거의 보이지 않았다.

• Restorative Dentistry and Endodontics
• /
• 제26권4호
• /
• pp.316-325
• /
• 2001

The purpose of this study was to evaluate the effect of adhesive curing timing on the direction of polymerization shrinkage of light-curing composite resin. In this study, the curing times of adhesive and composite resin were measured by differential scanning calorimeter(DSC). 28 extracted human molars were embedded in clear resin and box-type cavities were prepared. Based on DSC data, the experimental teeth were divided into 4 groups. Group 1: no bond; Group 2: late curing; Group 3: Intermediate curing; Group 4: Early curing. After treating with adhesive, the buccal cavities were filled with Z-100 hybrid composite resin and the lingual ones were filled with AEliteflo flowable composite resin. The depressions at the surface were measured by surface profilometer, then the specimens were embedded in clear resin and sectioned. Impressions were obtained and used to get epoxy resin replicas. The epoxy replicas were gold-coated and observed under SEM. Average Maximum Gap(AMG), Gap Proportion(GP), Average Marginal Index(AMI) were used to compare the shrinkage gap of each group. The results were statistically analyzed using the Kruskal-Wallis One Way ANOVA, Student-Newman-Keuls method. The results of this study were as follows. 1. Average Maximum Gap, Gap Proportion, Average Marginal Index and depression at the surface or Z-100 hybride composite resin were smaller than those of AEliteflo flowable composite resin(P<0.05). 2. When the bonding between composite resin and tooth structure was strong, the shrinkage gap was small, and depression at the surface was deep(P<0.05). 3. In the well-bonded group, light-curing composite resin shrank toward bonded cavity wall, not toward light source. The result suggested that the direction of polymerization shrinkage was affected by the quality of bonding in the dentin-resin interface. The strong was the bonding between composite resin and tooth structure, the smaller was the gap and the deeper was the depression at the surface. Then the flow to compensate the polymerization shrinkage proceeded from surface to bonded cavity wall.

• Restorative Dentistry and Endodontics
• /
• 제45권1호
• /
• pp.9.1-9.7
• /
• 2020

The restorative procedure in posterior teeth involves clinical steps related to professional skill, especially when using the incremental technique, which may fail in the long term. A recent alternative is bulk-fill resins, which can reduce polymerization shrinkage, decreasing clinical problems such as marginal leakage, secondary caries, and fracture. This scientific study aims to report a clinical case using bulk-fill resin with an occlusal matrix. As determined in the treatment plan, an acrylic resin matrix was produced to establish an improved oral and aesthetic rehabilitation of the right mandibular first molar, which presented a carious lesion with dentin involvement. The occlusal matrix is a simple technique that maintains the original dental anatomy, showing satisfactory results regarding function and aesthetic rehabilitation.

• Restorative Dentistry and Endodontics
• /
• 제42권1호
• /
• pp.1-8
• /
• 2017

Objectives: The purpose of this study was to evaluate the effect of adhesive luting on the fracture resistance of zirconia compared to that of a composite resin and a lithium disilicate glass ceramic. Materials and Methods: The specimens (dimension: $2mm{\times}2mm{\times}25mm$) of the composite resin, lithium disilicate glass ceramic, and yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) were prepared. These were then divided into nine groups: three non-luting groups, three non-adhesive luting groups, and three adhesive luting groups, for each restorative material. In the non-luting groups, specimens were placed on the bovine tooth without any luting agents. In the non-adhesive luting groups, only zinc phosphate cement was used for luting the specimen to the bovine tooth. In the adhesive luting groups, specimens were pretreated, and the adhesive luting procedure was performed using a self-adhesive resin cement. For all the groups, a flexural test was performed using universal testing machine, in which the fracture resistance was measured by recording the force at which the specimen was fractured. Results: The fracture resistance after adhesive luting increased by approximately 29% in the case of the composite resin, 26% in the case of the lithium disilicate glass ceramic, and only 2% in the case of Y-TZP as compared to non-adhesive luting. Conclusions: The fracture resistance of Y-TZP did not increased significantly after adhesive luting as compared to that of the composite resin and the lithium disilicate glass ceramic.

• Restorative Dentistry and Endodontics
• /
• 제21권1호
• /
• pp.360-365
• /
• 1996

The purpose of this study was to evaluate the changes in the degree of conversion on a composite resin surface following heat treatment and mylar strip finishing. The effects of the time interval between the light-curing and heat-curing process were also evaluated. The composite resin surface which had been covered with a coverglass showed a lower conversion rate than the surface from which a layer of $500{\mu}m$ was ground away. The composite resin surface was definitely affected by oxygen during the heat curing process when it had not been insulated. When the composite resins were heat cured after 3 days of storage following the light curing process, the increased in the degree of conversion through heatcuring was limited.

• Restorative Dentistry and Endodontics
• /
• 제38권2호
• /
• pp.103-104
• /
• 2013

• Restorative Dentistry and Endodontics
• /
• 제22권1호
• /
• pp.35-60
• /
• 1997

Physical properties of composite resins such as strength, resistance to wear, discoloration, etc, depend on the degree of conversion of the resin components. The clinical behavior of restorative resins varies brand to brand. Part of this variation is associated with the filler and differences in the polymer matrix. The polymer matrix of resins may differ because the involved monomers are dissimilar and because of variation in the catalyst system. The purpose of this study was to evaluate the degree of conversion of the composite resins according to the depth of cure and light curing time. 7mm diameter cylindrical aluminum molds were filled with each of five different hybrid light curing composite resins(Z-100, Charisma, Herculite XRV, Prisma TPH, Veridonfil) on the thin resin films. The molds were 1mm, 2mm, 3mm, 4mm, and 5mm in depth to produce resin films of various heights. Each sample was given 20sec, 40sec, and 60sec illumination with a light source. The degree of conversion of carbon double bonds to single bonds in the resin films was examined by means of Fourier Transform Infrared Spectrometer. The results were obtained as follows; 1. There was difference in the degree of conversion among five light curing composite resins according to the depth of cure for 20sec, 40sec, and 60sec illumination with light source with statistical significance(P<0.05). 2. Five light curing composite resins show lower degree of conversion at surface of the resin than depth of 1mm. 3. The degree of conversion of five light curing composite resins was siginificantly reduced from the maximum for the resin film when the light passed through as little as 1mm of each composite. 4. The degree of conversion of five light curing composite resins decrease significantly at the depth of 4mm, and polymerization was not occured at the depth of 5mm except for Prisma TPH. 5. The degree of conversion of five light curing composite resins was increased with increased light curing time, and there was no significant differences in the degree of conversion above 4mm in Z-100, 3mm in Charisma, and at depth of 5mm in Herculite XRV and Veridonfil(P>0.05).