A physical model experiment with GPR and 3-D resisitivity survey were conducted to investigate the geoelectrical response of hydrocarbon-impacted zone, so called smeared zone, on the geophysical data. The results from the experiment show that GPR signals were enhanced when LNAPL was present as a residual saturation in the water saturated system (${\varepsilon}_r$ = 21) due to less attenuation of the electromagnetic energy through the medium, compared to when the medium was saturated with only water (${\varepsilon}_r$ = 21). 3-D resistivity data obtained from the former gas station site demonstrate that the highly contaminated zones could be imaged with low resistivities attributed to the biodegradation of petroleum hydrocarbons at the aged, hydrocarbon-impacted sites. The study results also show that the geophysical methods, as a non-invasive sounding technique, can be a very useful tool for mapping hydrocarbon-contaminated zones.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2004.12a
• /
• pp.125-126
• /
• 2004

• Proceedings of the Korean Society of Soil and Groundwater Environment Conference
• /
• 2003.09a
• /
• pp.258-262
• /
• 2003

연안지역에서 해수침투대의 평가를 위하여 다양한 물리검층을 수행하였다. 특히, 해수침투대의 정량적인 평가에 활용될 수 있는 지층의 공극측정은 매우 어려운 문제중의 하나이다. 연안지역의 경우, 미고결지층에 대한 불교란 시료 채취가 어렵고 대부분의 관측정은 시추공 붕락방지를 위하여 내경 50mm 의 PVC 케이싱을 설치하는 경우가 많기 때문에 공극의 측정은 현실적으로 많은 어려움이 따른다. 본 연구에서는 전남 영광지역에서 각종 조사목적으로 굴착한 시추공에서 다양한 물리검층을 수행하여 공내수의 높은 전기전도도가 기원하는 지층을 확인하고자 하였다. 전자유도검층과 공극검층을 수행한 시추공(YK-4호공)에 대한 해석결과, 공내수의 높은 전기전도도는 물리검층법으로 추정한 사질층 공극수와 비슷한 범위를 보였다. 물리검층법으로 추정한 공극이나 높은 염수를 보이는 구간에 대한 해석결과는 보완해야할 많은 부분이 있지만 제한된 현장 상황에서 조사결과의 불화실성을 줄이는데 많은 기여를 할 것으로 기대된다.

• 한국초전도학회:학술대회논문집
• /
• v.9
• /
• pp.229-232
• /
• 1999

We have measured the temperature dependence of thermoelectric power (TEP) and resistivity for the Sr$_{1-x}K_xBiO_3$ superconductor (x=0.45-0.6). At T=10.2K, the resisitivity starts to increase from zero and a rather broad superconducting phase transition (${\Delta}$T ${\sim}$ 2.3K) is observed. TEP at room temperature has a small negative value ( S =-1.96${\mu}$V/K), characteristic of metallic-like TEP. The temperature dependence of TEP shows two distinct features. With decreasing temperature from room temperature, the absolute value of TEP decreases and the sign of TEP changes from negative to positive around 200k. Also, the negative slope of TEP(dS/dT) decreases substantially and becomes rather flat at around 160k, which is a feature already noted in Ba$_{1-x}K_xBiO_3$[1].

• Proceedings of the Korean Society of Soil and Groundwater Environment Conference
• /
• 2001.09a
• /
• pp.92-96
• /
• 2001

Although the problem of seawater intrusion at the coastal aquifer was recognized before over one hundred years at the coastal aquifer, much groundwater keep on being salinitized by several reasons such as groundwater exhaustion, coastalline change, and human activities. The horizontal and vertical electrical soundings and geostatistical methods were used to define the local characteristics of saltwater intrusion and to estimate the saltwater interface in the southeastern area of the Pusan City. The 24 points of the Schlumberger vertical electrical soundings(VES) to loom depth and the 2 lines of dipole-dipole horizontal soundings are peformed. The resistivity data have lognormal distributions. The horizontal extents of saline water intrusion were estimated from the inversion of horizontal prospecting data. Lognormal ordinary kriging is used in A-A' resistivity profiles on May and July because the data have stationary models in semivariograms. Lognormal IRF-k kriging is used for the isopleth maps using vertical resistivity data. The 10 ohm-m resistivity line on the isopleth maps of 21m, 30m, 50m, and 70m depth using resisitivity data measured in July is sifted to the east, cpomparing that of the isopleth maps measured in May. The kriged vertical and horizontal resistivity isopleth maps suggested that the geostatistical methods can be used to define the variation of earth resistivity distribution at the saltwater interface.

• Analytical Science and Technology
• /
• v.5 no.2
• /
• pp.213-216
• /
• 1992

Semiinsulating GaAs crystals employing LPLEC technique should be grown from the Ga-rich melt due to a very low incorporation of unintentional impurities such as carbon (<$10^{15}cm^{-3}$). High resisitivity of this material can be derived from the balanced compensation among not only EL2 deep donors and carbon acceptors but also H1 double charge native acceptors(Ev + 77meV, Ev + 200 meV) and H2 native acceptors(Ev + 68 meV). Considering of the complicated compensation mechanism using statistical calculation of the electron occupancy of each level, SI GaAs crystal with low impurity contents(<$10^{15}cm^{-3}$) can be successfully obtained by maintaining the melt composition around 0.45 As mole fraction.

• Polymer(Korea)
• /
• v.25 no.2
• /
• pp.293-301
• /
• 2001

Electrically conductive carbon fiber/high density polyethylene (CF/HDPE) composite films were fabricated by new method, so called electron-ion technology (EIT) and the effects of CF epoxy sizing on the volumetric resistivity. tensile strength and interphase properties of the films were investigated. While epoxy sizing increased conductivity of composite films resulting from enhanced tunneling effect it reduced interphase adhesion between CF and HDPE because polar epoxy sizing and nonpolar HDPE are incompatible. Consequently epoxy sized CF(CF(S)) caused significant reduction in the volumetric resisitivity and tensile strength of composite films when compared with unsized CF(CF(U)). Epoxy sizing reduced nucleating efficiency of CF(S), therefore CF(S)/HDPE composite films showed nonuniform transcrystalline layer when compared with CF(U)/HDPE composite films.

• Journal of Magnetics
• /
• v.18 no.1
• /
• pp.39-42
• /
• 2013

We studied the structural and electrical properties of $SrRuO_3$ thin films grown on $SrTiO_3$ (110) substrate. High resolution X-ray diffraction measurement of the grown film showed 1) very sharp peaks for $SrRuO_3$ film with a very narrow rocking curve with FWHM = $0.045^{\circ}$ and 2) coherent growth behavior having the same in-plane lattice constants of the film as those of the substrate. The resisitivity data showed good metallic behavior; ${\rho}$ = 63(205) ${\mu}{\Omega}{\cdot}cm$ at 5 (300) K with a residual resistivity ratio of ~3. The observed kink at ${\rho}(T)$ showed that the ferromagnetic transition temperature was ~10 K higher than that of $SrRuO_3$ thin film grown on $SrTiO_3$ (001) substrate. The observed rather lower RRR value could be partially due to a very small amount of Ru vacancy generally observed in $SrRuO_3$ thin films grown by PLD method and is evident in the larger unit-cell volume compared to that of stoichiometric thin film.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.355-356
• /
• 2008

In this work, ZnO films doped with different contents of Indium (0.1at.%, 0.3at.%, 0.6at.%, respectively) were deposited on Si (111) substrate that has 1~20 $\Omega$cm by pulsed laser deposition (PLD) at $600^{\circ}C$ for 30min. The thickness of the films are about 250 nm. The structural, optical and electrical properties of the films were investigated using X-ray Diffraction (XRD), Atomic force microscope (AFM), Photoluminescence (PL) and Hall measurement. It has been found that RMS of the films is decreased and grain size is increased with increasing the contents of doped Indium. The results of the Photoluminescence properties were indicated that the films have UV emission about 380nm and shows a little red shitf with increasing contents of doped indium. The result of the Hall measurement shows that the concentration and resisitivity in doped ZnO are as changing as one order, respectively ${\sim}10^{18}/cm^2$, ${\sim}10^{-2}cm{\Omega}cm$.

• Applied Chemistry for Engineering
• /
• v.7 no.4
• /
• pp.639-644
• /
• 1996

The $YBa_2Cu_{3-y}Ag_yO_{7-x}$ high-temperature superconductors were prepared by pyrophoric synthetic method from $Y_2O_3$, $BaCO_3$, CuO, and $AgNO_3$ powders. When we were partially substituted Ag for Cu in $YBa_3Cu_3O_{7-x}$, the superconducting properties of $YBa_2Cu_{3-y}Ag_yO_{7-x}$ were investigated with X-ray diffractometer, resisitivity measuring equipment, SEM, and Vickers Hardness. The Tc,zero of $YBa_2Cu_3O_{7-x}$ was 91K, the density was $5.2g/cm^3$, and the hardness was $590kg/mm^2$. When Ag was substituted below y=0.15, electrical property of $YBa_2Cu_{3-y}Ag_yO_{7-x}$ did not change but microstructure, density, and hardness were enhanced.