• Restorative Dentistry and Endodontics
• /
• 제24권3호
• /
• pp.519-527
• /
• 1999

The purpose of this study was to estimate shear bond strength according to difference in luting cements and Targis surface treatment. 70 non-carious extracted human molars and Targis shade D210(Ivoclar, Liechtenstein) were used in the present study and they were randomly assigned into 7 experimental groups ; Group 1 : specimens were bonded with using vitremer(3M, U.S.A). Group 2, 4, 6 : specimens were not-treated with silane and bonded with Panavia 21(Kuraray Japan), Choice(Bisco, U.S.A.) and Variolink II(Vivadent, Liechtenstein) respectively Group 3, 5, 7 : specimens were treated with silane and bonded with Panavia 21, Choice and Variolink II respectively. After the surface treatment, the luting cement was mixed by manufacturer's recommendation and then applied between dentin and Targis and excess cement was removed by brush. All specimens were stored for 24 hrs in distiled water at $37^{\circ}C$. Shear bond strength for each group was then measured. To examine the failure patterns of targis to dentin, specimens were fabricated and observed under the SEM. The results were as follows ; 1. The mean shear bond strength of the groups using resin cements was significantly higher than that using resin-modified GI cements (P<0.05). 2. There is no significant difference in shear bond strength between Panavia 21 and Choice whether silane was used or not(P>0.05). However, bond strength for the groups using Variolink II was higher in the specimens not-treated with silane than the treated specimens (P<0.05). 3. There is no significant difference in bond strength among the groups using silane surface treatment and resin cement (group 3, 5, 7) (P<0.05). 4. The proportions of the specimens showing the mixed fracture failure were 20% in groups using Panavia 21 and Variolink II and 15% in group using Choice.

• 구강회복응용과학지
• /
• 제37권4호
• /
• pp.199-208
• /
• 2021

목적: 이 연구의 목적은 고투명도 3종류의 지르코니아의 두께 및 하부 배경에 따른 색조 차단 효과를 비교, 평가하는 것이다. 연구 재료 및 방법: 3 종류의 고투명도 지르코니아(Ceramill zolid fx white, Ceramill zolid ht+ white, Ceramill zolid ht+ preshade A2)를 각각 CAD/CAM 방식으로 직경 10 mm의 원판 형태의 4가지 두께(0.6 mm, 1.0 mm, 1.5 mm, 2.0 mm)로 10개씩 시편을 제작하였다. 하부 배경은 직경 10 mm, 두께 10 mm로 A1, A2, A3 레진 하부 배경, 청색의 코어 레진 하부 배경, Ni-Cr 합금 하부 배경을 제작하였으며, 추가로 분광 광도계 제조사에서 제공하는 검정색 및 흰색 하부 배경을 사용하였다. 지르코니아 시편과 기준 배경을 접착제없이 겹쳐 분광 광도계로 L, a^*, b^* 값을 측정하고 다른 하부 배경과의 ΔE 값을 계산하였다. 계산된 평균 ΔE 값을 인지 한계 1.0과 허용 한계 3.7 값을 기준으로 색조 차단 효과를 비교하였다. 통계적 유의성 검증을 위해 비모수 검정인 Kruskal-Wallis 검정을 시행하였다(α = 0.05). 결과: 지르코니아 종류, 하부 배경 및 두께 변화에 따른 평균 ΔE 값의 유의한 차이를 보였다(P = 0.000). 결론: 본 연구 결과에 의하면, 색조를 가지는 고투명도 지르코니아는 청색 레진 코어를 제외한 치아, 복합레진 및 지대주상에 수복될 때 원하는 지르코니아 색조를 얻을 수 있다.

• 대한소아치과학회지
• /
• 제30권3호
• /
• pp.431-438
• /
• 2003

수복 치료과정에서 발생하는 온도증가가 치수조직에 미칠 수 있는 위해효과는 치의학의 오랜 관심사였다. 일반적으로, $5.5^{\circ}C$를 초과하는 치수 내 온도변화는 치수조직 에 비가역적인 손상을 야기할 수 있다. 기존의 할로겐 램프 광중합기와 더불어 최근 시판되고 있는 플라즈마 아크 중합기, LED 중합기를 사용하여 복합레진 중합시 치수강 내 온도증가량을 조사하였다. 한 개의 우식이 없는 치아를 대상으로 V급 와동을 형성하였다. 와동 내에 복합레진(Z250, Shade A2)을 충전한 후, 광중합조건을 달리하여 5군(I군: VIP, 20초 (mode 3), II군: VIP, 20초 (mode 6), III군: Flipo, 3초, IV군: Flipo, 5초 (2-step), V군: Lux-O-Max, 40초)으로 분류하고, 각 조건에 맞게 복합레진을 중합시키면서 치수강 내의 온도측정 단자를 통하여 $37.0^{\circ}C$로부터 증가되는 치수강 내 최대 온도증가량을 측정한 결과 다음과 같은 결론을 얻게 되었다. 1. 모든 군에서 치수강 내 최대 온도 증가량은 치수의 변성을 일으키기 시작하는 경계온도인 $5.5^{\circ}C$ 보다 낮았으며, II군에서 치수강 내 최대 온도증가량이 통계적으로 유의하게 가장 높았다(p<0.05). 또한 Lux-O-Max를 조사한 V군은 다른 군보다 낮은 치수강 내 최대 온도증가량을 나타내었다(p<0.05). 2. VIP로 조사한 두 군을 비교할 경우, 조사강도가 높은 II군이 I군보다 치수강 내 최대 온도증가량이 더 높게 증가하였으며(p<0.05), Flipo로 조사한 III군과 IV군 사이에서는 2-step 조사모드로 5초간 조사한 IV군이 3초간 조사한 III군보다 치수강 내 최대 온도증가량이 더 높게 증가하였다(p<0.05). 3. VIP와 Flipo를 비교할 경우, II군이 III, IV군보다 더 높게 증가하였고, IV군이 I군보다 더 높게 증가하였으나(p<0.05), I군과 III군 사이에는 차이를 보이지 않았다.

• Restorative Dentistry and Endodontics
• /
• 제34권4호
• /
• pp.309-323
• /
• 2009

본 연구는 순면 잔존 치질의 두께와 후방 복합레진의 색상이 최종 수복된 치아표면의 색상에 미치는 영향을 알아보고자 시행하였다. 배경판으로 사용될 복합레진은 Filtek Supreme (3M ESPE, St. Paul, U.S,A.)의 A1, A2, A6D, B1, B2, B3, C1, C2, C6D를 선택하였다. 배경판으로 사용될 복합레진 시편은 직경 10 mm, 두께 4.5 mm로 각 shade당 한 개씩 제작하였다. 순면 잔존 치질은 상악 중절치 치관의 순면을 제외한 나머지 부위를 아크릴릭 레진을 이용하여 매몰 후 저속의 Diamond Wheel Saw (Isomet ; Buehler Ltd, Lake Bluff, U.S.A.)를 이용하여 주수 하에 순면으로부터 2.5 mm 두께로 절단하였다. 절단된 상아질측 표면을 2000번 사포로 연마하여 2.2 mm 두께의 시편을 얻었다. 분광광도계 $Spectrolino^{(R)}$(Serial No. 3257-18522, GretagMacbeth, Regensdorf, Switzerland)를 이용하여 치아 시편을 9개의 복합레진 시편위에 접촉면에 수분이 있는 상태로 위치시켜 치아 순면색상을 측정하였다. 그 후, 치아시편의 상아질 측면을 1.0 mm까지 0.3 mm 간격으로 연마하면서 복합레진 시편위에 위치시켜 동일한 방법으로 색상을 측정하였다. 모든 시편에서 $L^{\ast}$값과 $b^{\ast}$값은 배경색에 무관하게 치아시편의 두께가 두꺼워질수록 증가하는 양상을 보였으나(p < 0.05), $a^{\ast}$값은 배경색에 무관하게 두께에 따른 유의한 차이를 보이지 않았다.

• 대한소아치과학회지
• /
• 제31권3호
• /
• pp.391-399
• /
• 2004

현재 복합레진의 중합에 사용되는 광원으로 할로겐광 중합기, 플라즈마 아크 중합기, 레이저, LED 등이 사용되고 있으나 광조사에 따른 온도 증가와 중합 깊이 등이 수복치과학의 오랜 관심이었다. 본 연구의 목적은 광원에 따라 얼마나 온도 증가가 일어나는지, 그리고 중합 깊이에 따른 표면경도를 측정함으로써 전통적인 할로겐광 중합기에 대해 새로 개발된 중합기의 중합능력을 비교 평가하는 것이다. 기존의 할로겐광 중합기(Optilux 360)에 대해 최근 시판되는 플라즈마 아크 중합기(Flipo), 열 발생을 감소시킨 플라즈마 아크 중합기(Aurys), LED(Starlight), 그리고 중합시간을 감소시킨 고강도 LED(Freelight 2) 등을 광원으로 사용하였다. 우선 상온$(23^{\circ}C)$에서 각 중합기 표면의 온도를 측정한 후 각각 2, 3, 4mm의 테플론 mold에 레진(Z-100, $A_2\;Shade$)을 충전하고 하면에서 중합시 최고 온도를 측정하였으며 각 시편 상, 하면의 미세경도를 측정하여 다음과 같은 결론을 얻었다. 1. 중합기 표면의 온도를 측정한 결과 Flipo가 평균 $52.4^{\circ}C$로 가장 높았고 Freelight $2(37.86^{\circ}C),\;Optilux\;360(32.68^{\circ}C),\;Aurys(32.34^{\circ}C),\;Starlight(26.14^{\circ}C)$ 순으로 낮게 나타났다. 2. 복합레진을 2, 3, 4mm 테플론 mold에 채우고 중합시 온도 변화를 측정한 결과 Flipo와 Freelight 2가 유사하게 가장 높았고 Optilux 360과 Aurys가 유사하게 그 다음이었으며 Starlight가 가장 낮게 나타났다. 3. 복합레진 상면의 미세경도는 전반적으로 유사하였으나 Aurys로 중합한 군에서 약간 낮게 측정되었다. 4. 복합레진 하면의 미세경도는 2, 3, 4mm모두에서 Optilux 360과 Freelight 2로 중합한 군에서 유사하게 가장 높았고 그 다음이 Flipo, Starlight 순이었으며 Aurys로 중합한 군에서 가장 낮게 측정되었다. 연구 결과에서 볼 때 Flipo와 Freelight 2를 주의깊게 사용한다면 중합도와 시간면에서 임상적으로 유용하게 사용될 수 있으리라 사료된다.

• 대한소아치과학회지
• /
• 제24권1호
• /
• pp.325-336
• /
• 1997

The purpose of this study was to evaluate the compensation effect of exposure duration increase to decreased light intensity of visible-light curing unit. The specimen with 2mm thickness was made of Restorative $Z-100^{TM}$ (A2 shade, 3M Dental Products, U.S.A.) and cured with $Optilux^{TM}$ (Demetron Research Co. U.S.A.). The light intensity was controlled to 420 $mW/cm^2$, 540 $mW/cm^2$, 630 $mW/cm^2$ and curing time, also, controlled to 40, 60, 80 seconds. Cured specimen was stored in a light-proof container for 24 hours to post-irradation was completed. Microhardness of top and bottom surface of specimen were measured to evaluate the depth of cure. The obtained results were as follows: 1. The microhardness of top and bottom surface of the composite resin specimen was increased significantly as light intensity and exposure time was increased (P<0.01). 2. Light intensity was more correlated with bottom microhardness(${\gamma}{\geq}$0.438) than top microhardness(${\gamma}{\geq}$0.213), and exposure time was more correlated with top microhardness (${\gamma}{\geq}$0.424) than bottom microhardness(${\gamma}{\geq}$0.335). 3. The regressive equation was obtained in this study as follows : $H=0.07{\times}D+0.012{\times}I+76$ (H : Microhardness(KHN), D : Exposure time, I : Light intensity)

• 구강회복응용과학지
• /
• 제30권2호
• /
• pp.192-198
• /
• 2014

본 증례는 심미적인 개선을 위해 내원한 30대 여성에서 도재 라미네이트 비니어(porcelain laminate veneer: PLV)와 전 부도재관을 이용하여 치료를 시행한 증례로서, 환자는 앞니가 튀어나오고 고르지 않다는 주소로 내원하였고 최소의 치아 삭제를 원하였다. 환자는 골격성 II급 부정교합이었으며, 진단 납형 제작 시 이를 고려하기 위해 체크 바이트법을 이용하여 교합기에 마운팅 하였고, 진단 납형 제작한 상태의 mock-up을 이용하여 치아 삭제를 시행한 후 삭제량을 인덱스로 확인하였다. 보철물의 전체적인 색조의 조화를 위해 도재 라미네이트 비니어를 먼저 수복하였고, 전부도재관의 지대치 색상을 고려한 뒤 수복하여 만족스러운 심미성의 개선을 얻을 수 있었다.

• The Journal of Advanced Prosthodontics
• /
• 제16권4호
• /
• pp.231-243
• /
• 2024

PURPOSE. The objective of the study was to analyze the impact of cement, bonding pretreatment, and ceramic abutment material on the overall color results of CAD-CAM ceramic crowns bonded to titanium-based hybrid abutments. MATERIALS AND METHODS. For single implant restoration of a maxillary lateral incisor a total of 51 CAD-CAM-fabricated monolithic lithium disilicate crowns were fabricated and subsequently bonded onto 24 lithium disilicate Ti-base abutments, 24 zirconia Ti-base abutments and 3 resin abutment replicas as a control group. The 48 copings were cemented with three definitive and one provisional cement on both grit-blasted and non-blasted Ti-bases. The color of each restoration and surrounding artificial gingiva was measured spectrophotometrically at predefined measuring points and the CIELAB (ΔE_ab) color scale values were recorded. RESULTS. The color outcome of ceramic crowns bonded to hybrid abutments and soft tissues was affected differently by cements of different brands. Grit-blasting of Ti-bases prior to cementing CAD-CAM copings affected the color results of allceramic crowns. There was a significant difference (P = .038) for the median ΔE value between blasted and non-blasted reconstructions at the cervical aspect of the crown. Full-ceramic crowns on zirconia Ti-base abutments exhibited significantly lower ΔE values below the threshold of visibility (ΔE 1.8). In all subcategories tested, the use of a highly opaque temporary cement demonstrated the lowest median ΔE for both the crown and the artificial gingiva. CONCLUSION. Various cements, core ceramic materials and airborne particle abrasion prior to bonding can adversely affect the color of Ti-base supported ceramic crowns and peri-implant soft tissue. However, zirconia CAD-CAM copings and an opaque cement can effectively mask this darkening.

• Restorative Dentistry and Endodontics
• /
• 제32권6호
• /
• pp.542-549
• /
• 2007

본 연구의 목적은 네 종류의 복합레진의 연마 후의 표면 거칠기에 있어서의 차이와 염색액에 담근 후 색 안정성에 있어서의 차이를 평가하기 위한 것이다. 필러 크기와 함량이 다른(나노입자형, 혼합형, 미세입자형, 흐름성) 네 종류의 광중합 복합레진(색상 A2)을 사용하였다. 산화 알루미늄 마모 디스크(Super-Snap)로 연마하기 전과 후에 평균 표면 거칠기(Ra)를 표면 조도 측정기 (Surftest Formtracer)로 측정하였다. 2% 메틸렌 블루 용액으로 착색하기 전과 후 표본의 색은 SCI geometry를 이용해 spectrophotometer(CM-3700d)로 측정되었다. 표면 거칠기와 색 변화 값은 one-way ANOVA, Scheffe multiple comparison test와 Student t-test로 분석되었다. 연마 후, 표면 거칠기 값은 복합레진의 종류에 관계없이 감소하였다. 연마 후 표면 거칠기와 착색 후 색 안정성에 있어서, 나노입자형 복합레진이 흐름성 레진을 제외한 다른 복합레진들과 유사하였다.

• Restorative Dentistry and Endodontics
• /
• 제34권3호
• /
• pp.199-207
• /
• 2009

본 연구에서는 동일한 수광 방식을 사용하는 2종의 이동형과 고정형 spectrophotometer인 MiniScan XE plus (Model 4000S, Hunter Lab, USA)와 CM-3500d(Minolta, Japan), 그리고 다른 수광 방식을 사용하는 miniature VIS reflection spectrometer인 Specbos 2100(JETI Technische Instrumente GmbH, Germany)를 이용하여 직경 15 mm, 두께 4 mm의 디스크로 제작한 광중합 복합레진의 색상을 측정하였다. Spcebos 2100은 분광 특성을 측정하는 기기이지만 주문에 의해 제조사에서 측색이 가능한 형태로 제공하였다. 3종의 측색 기기를 사용한 측색 결과를 분석한 결과 동일한 수광 방식, 광원 및 관찰자 각도를 적용한 2종의 기기 간에도 동일 색상에서 2.4-7.8까지의 색차(${\Delta}E^*$)를 보였으나, $L^*$, $a^*$, $b^*$ 값은 기기 간에 높은 상관관계를 보였다. 서로 다른 수광 방식을 사용하는 기기 간에는 약 20 정도의 큰 색차(${\Delta}E^*$)를 보이며, 측정된 각 값 간에도 낮은 상관관계를 보였다. 이상의 결과는 반투명의 치과용 수복 재료나 치아의 측색 시 측색 기기간에도 색차가 나타날 수 있음을 시사하며, 이는 기기에 대해 측정된 색상을 절대적인 색상으로 적용하기보다는 상대적인 측정치로 이용하는 것이 바람직하리라 사료된다.