• Journal of the Korean Society for Heat Treatment
• /
• v.6 no.4
• /
• pp.185-193
• /
• 1993

The effect and Condition of heat treatment on the tensile strength of welded joint was investigated in 300 grade 18% Ni-Co-Mo-Ti maraging steel sheets welded with electron beam. A good tensile strength of welded joint was obtained by following heat treatment cycle ; At $1100^{\circ}C$ the specimen was high temperature solution treated for 1 hour and then it was repeated solution treated at $900^{\circ}C$, $820^{\circ}C$ for 1 hour respectively to recrystallize the coarsened ${\gamma}$ grain. These heat treatment cycle was completed by an final aging heat treatment at $480^{\circ}C$ for 4 hour. Moreover, dissolution of dendrite, a significant decrease in seregation of Mo, Ti in weld metal were observed and also the coarsened ${\gamma}$ grain formed at $1100^{\circ}C$, $1200^{\circ}C$ changed to fine grain due to the effect of recrystallization.

• Journal of Advanced Marine Engineering and Technology
• /
• v.21 no.2
• /
• pp.157-165
• /
• 1997

The strength level of welded joint in room temperature and elevated temperature up to $600^{\circ}C$ was investigated in 250 and 300 grade 18% Ni maraging steel sheet welded with electron beam. The results obtained in this study are as follows; 1. Optimum welding heat input was 600J/cm in 1.0mm thickness and the room temperature tensile strength, joint efficiency of welded joint treated with optimum aging condition were found to be about 166kg/$mm^2$, 95% in 250 grade, 189kg/$mm^2$, 92% in 300 grade maraging steel sheet, respectively. 2. Tensile strength of welded joint in room temperature increased slightly by aging after repeated solution heat treatment, but the fracture mode showed a shear. 3. Joint efficiency at a temperature between $540^{\circ}C$and $600^{\circ}C$ found to be about 72% to 55%, but the joint efficiency exceeded about 90% below $300^{\circ}C$. 4. The fracture occurred in most weld metal, and the fracture surface showed a shallow dimple.

• Journal of the Korean Wood Science and Technology
• /
• v.42 no.1
• /
• pp.13-19
• /
• 2014

Three heat-treatment schedules were applied to $90{\times}90mm$ dimension square lumber of Pinus koraiensis, one of major domestic species, and their colors and physical properties were investigated for obtaining an optimum schedule. Each square lumber was heat-treated three times. The temperatures of $170^{\circ}C$ and $190^{\circ}C$, and the time of 9 hours and 13 hours were used for the first heat-treatment. The schedule of $190^{\circ}C$ and 7 hours were used for the next two heat-treatments. The averages of brightness $L^*$ decreased linearly as the heat-treatment repeated and its standard deviations also decreased slightly. While the averages of color difference ${\Delta}E^*$ increased linearly as the heat-treatment repeated and its standard deviations also increased slightly. The average compressive strength of the heat-treated specimen was higher than that of the control by 9%, which deviates from previous reports. ASE and WPG of the heat-treated specimens were measured to confirm that heat-treatment improved dimensional stability significantly.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.213-213
• /
• 2012

It has been known that quantum confinement effect of CdSe nanocrystal was observed by increasing the number of deposition cycle using successive ionic layer adsorption and reaction (SILAR) method. Here, we report on thermally-induced quantum confinement effect of CdSe at the given cycle number using spin-coating technology. A cation precursor solution containing $0.3\;M\;Cd(NO_3)_2{\cdot}4H_2O$ is spun onto a $TiO_2$ nanoparticulate film, which is followed by spinning an anion precursor solution containing $0.3\;M\;Na_2\;SeSO_3$ to complete one cycle. The cycle is repeated up to 10 cycles, where the spin-coated $TiO_2$ film at each cycle is heated at temperature ranging from $100^{\circ}C$ to $250^{\circ}C$. The CdSe-sensitized $TiO_2$ nanostructured film is contacted with polysulfide redox electrolyte to construct photoelectrochemical solar cell. Photovoltaic performance is significantly dependent on the heat-treatment temperature. Incident photon-to-current conversion efficiency (IPCE) increases with increasing temperature, where the onset of the absorption increases from 600 nm for the $100^{\circ}C$- to 700 nm for the $150^{\circ}C$- and to 800 nm for the $200^{\circ}C$- and the $250^{\circ}C$-heat treatment. This is an indicative of quantum size effect. According to Tauc plot, the band gap energy decreases from 2.09 eV to 1.93 eV and to 1.76 eV as the temperature increases from $100^{\circ}C$ to $150^{\circ}C$ and to $200^{\circ}C$ (also $250^{\circ}C$), respectively. In addition, the size of CdSe increases gradually from 4.4 nm to 12.8 nm as the temperature increases from $100^{\circ}C$ to $250^{\circ}C$. From the differential thermogravimetric analysis, the increased size in CdSe by increasing the temperature at the same deposition condition is found to be attributed to the increase in energy for crystallization with $dH=240cal/^{\circ}C$. Due to the thermally induced quantum confinement effect, the conversion efficiency is substantially improved from 0.48% to 1.8% with increasing the heat-treatment temperature from $100^{\circ}C$ to $200^{\circ}C$.

• Journal of the Korean Chemical Society
• /
• v.65 no.2
• /
• pp.125-132
• /
• 2021

An electrochromic nickel oxide thin film was fabricated on a flexible PET/ITO substrate using a nanocrystallite- dispersed coating sol and bar coater. Nanocrystalline NiOx of 3-4 nm crystallite size was first synthesized by base precipitation and thermal conversion. This NiOx nanocrystallite powder was mechanically dispersed in an alcoholic solvent mixed with a silane binder to prepare a coating sol for thin film. This sol method is different from the normal sol-gel method in that it does not require the conversion of precursor by heat treatment. Therefore, this method provides a very facile method to prepare NiOx thin films on any kind of substrate and it can be easily applied to mass production. The electrochromic performance of this NiOx thin film on PET/ITO electrode with a thickness of about 400 nm was investigated in a nonaqueous LiClO4 electrolyte solution by cyclic voltammetric and repeated chronoamperometric measurements in conjunction with spectrophotometry. The visible light modulation of 44% and the colorization efficiency of 41 ㎠/C at 550 nm were obtained at the step potentials of -0.8/+1.2 V vs Ag and a duration of 30 s.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.17 no.2
• /
• pp.93-103
• /
• 1981

It is well-known that nowadays heat resisting and anti-corrosive materials have been widely used as the components materials of gas turbines, nuclear power plants and engines etc. In the fields of machine production industry. And materials for engine components, like as the exhaust valve of internal combustion engine, have been required to operate under the high temperature range of $700^{\circ}C$-$800^{\circ}C$ and high pressured gas with repeated mechanical load for the high performance of engines. For these components, friction welding for bonding of dissimilar steels can be applied for in order to obtain process shortening, production cost reduction and excellent bonding quality. And age hardening recently has been noticed to the heat resisting materials for further strengthening of high temperature strength, especially high temperature fatigue strength. However, it is difficult to find out any report concerning the effects of age hardening for strengthening high temperature fatigue strength to the Friction welded heat resisting and anti-corrosive materials. In this study the experiment was carried out as the high temperature rotary bending fatigue testing under the condition of $700^{\circ}C$ high temperature to the friction welded domestic heat resisting steels, SUH3-SUS303, which were 10hr., 100hr. aging heat treated at $700^{\circ}C$ after solution treatment 1hr. at $1, 060^{\circ}C$ for the purpose of observing the effects of the high temperature fatigue strength and fatigue fracture behaviors as well as with various mechanical properties of welded joints. The results obtained are summarized as follows: 1) Through mechanical tests and micro-structural examinations, the determined optimum welding conditions, rotating speed 2420 rpm, heating pressure 8kg/mm super(2), upsetting pressure 22kg/mm super(2), the amount of total upset 7mm (heating time 3 sec and upsetting time 2 sec) were satisfied. 2) The solution treated material SUH 3, SUS 303, have the highest inclination gradient on S-N curve due to the high temperature fatigue testing for long time at $700^{\circ}C$. 3) The optimum aging time of friction welded SUH3-SUS 303, has been recognized near the 10hr. at $700^{\circ}C$ after the solution treatment of 1hr. at $1, 060^{\circ}C$. 4) The high temperature fatigue limits of aging treated materials were compared with those of raw material according to the extender of aging time, on 10hr. aging, fatigue limits were increased by SUH 3 75.4%, SUS 303 28.5%, friction welded joints SUH 3-SUS 303 44.2% and 100hr. aging the rates were 64.9%, 30.4% and 36.6% respectively. 5) The fatigue fractures occurred at the side of the base matal SUS303 of the friction welded joints SUH 3-SUS 303 and it is difficult to find out fractures at the friction welding interfaces. 6) The cracking mode of SUS 303, SUH 3-303 is intergranular in any case, but SUH 3 is fractured by transgranular cracking.

• Journal of Sericultural and Entomological Science
• /
• v.51 no.2
• /
• pp.142-146
• /
• 2013

The fluorescent proteins are generally denatured by heat treatment and thus lose their color. The normal reeling method includes processing by drying and cooking the cocoons near $100^{\circ}C$ before reeling. Therefore, the usual processing method cannot be used for making colored fluorescent silks. To develop a method that is applicable to producing transgenic silk without color loss, we develop reeling methods adequate for a recombinant fluorescence cocoons. It was found that the fluorescence cocoons keep their native color when dried at temperatures lower than $60^{\circ}C$ for 15 h. Also, a new cooking method to soften the fluorescent cocoons was developed: the cocoons were soaked in a solution of 0.2% sodium carbonate ($Na_2CO_3$)/0.1% nonionic surfactant (Triton X100) at $60^{\circ}C$ and then placed under vacuum. The repeated vacuum treatments enabled complete penetration of the solution into the cocoons, and the cocoons were thus homogenously softened and ready for reeling. In this state, the cooked cocoons can be reeled by an automated reeling machine. Our results suggest that drying and cooking of the cocoons at low temperature enables the subsequent reeling of the colored fluorescent silks by an automatic reeling machine without color loss and can produce silks that can be used for making higher value-added silk materials.