• Structural Engineering and Mechanics
• /
• 제16권6호
• /
• pp.749-769
• /
• 2003

The structural deterioration of concrete structures due to reinforcement corrosion is a major worldwide problem. Service life of the age-degraded concrete structures is governed by the protective action provided by the cover concrete against the susceptibility of the reinforcement to the corrosive environment. The corrosion of steel would result in the various corrosion products, which depending on the level of the oxidation may have much greater volume than the original iron that gets consumed by the process of corrosion. This volume expansion would be responsible for exerting the expansive radial pressure at the steel-concrete interface resulting in the development of hoop tensile stresses in the surrounding cover concrete. Once the maximum hoop tensile stress exceeds the tensile strength of the concrete, cracking of cover concrete would take place. The cracking begins at the steel-concrete interface and propagates outwards and eventually resulting in the through cracking of the cover concrete. The cover cracking would indicate the loss of the service life for the corrosion-affected structures. In the present paper, analytical models have been developed considering the residual strength of the cracked concrete and the stiffness provided by the combination of the reinforcement and expansive corrosion products. The problem is modeled as a boundary value problem and the governing equations are expressed in terms of the radial displacement. The analytical solutions are presented considering a simple 2-zone model for the cover concrete viz. cracked or uncracked. A sensitivity analysis has also been carried out to show the influence of the various parameters of the proposed models. The time to cover cracking is found to be function of initial material properties of the cover concrete and reinforcement plus corrosion products combine, type of rust products, rate of corrosion and the residual strength of the cover concrete. The calculated cracking times are correlated against the published experimental and analytical reference data.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2000년도 가을 학술발표회 논문집(II)
• /
• pp.885-890
• /
• 2000

12 RC deep beams with a/d = 1.17 are reported. This paper is to study the effect of vertical and horizontal web reinforcement and web reinforcement arrangement on inclined cracking shear, ultimate shear strength, midspan deflection, and inclined crack width. Test results indicated that web reinforcement produces and arrangement seems to moderately affect inclined cracking shear, ultimate shear strength and crack width. However, addition of horizontal web reinforcement(pv = 0.0085) little or no influence on inclined cracking shear, ultimate shear strength and crack width. The member which vertical and horizontal web reinforcement concentrate on the center web considerably increases in load-carrying capacity.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2003년도 봄 학술발표회 논문집
• /
• pp.693-698
• /
• 2003

Corrosion of reinforcement and deterioration of concrete short the lifetime of reinforced concrete structure and affect the safety of the structure. In particular, the corrosion of reinforcement causing the inner pressure of the interface between the concrete and reinforcement is known to significantly contribute to the premature deterioration of concrete structure. Several attempts have been made to predict the cracking time of the concrete structure. However, problems such as the lack of reproducibility of concrete tests and non-uniformity of materials have hampered thess kinds of studies. Thus, the mechanism of the concrete cracking due to reinforcement corrosion is in the way. This studymeasured the mechanical properties of corrosion products using the nano-indentation test method. Likewise, the critical thickness of corrosion products for the cracking of concrete cover was investigated using the finite element and experimental methods.

• Computers and Concrete
• /
• 제18권2호
• /
• pp.165-178
• /
• 2016

The present work is concerned with a numerical investigation of the behaviour of reinforced-concrete beams with non-bonded flexural tension reinforcement. The numerically-established behaviour of such beams with and without transverse reinforcement is compared with its counterpart of similar beams with bonded reinforcement. From the comparison, it is found that the development of bond anywhere within the shear span inevitably leads to inclined cracking which is the cause of 'shear' failure. On the other hand, the lack of bond within the shear span of the beams is found, not only to prevent cracking within the shear span, but, also, to lead to a flexural type of failure preceded by the formation of horizontal splitting of concrete in the compressive zone. It is also found that delaying the extension of horizontal splitting through the provision of transverse reinforcement in the beam mid span can lead to flexural failure after yielding of the tension reinforcement. Yielding of the tension reinforcement before the horizontal splitting of the compressive zone may also be achieved by reducing the amount of the latter reinforcement.

• 한국마린엔지니어링학회:학술대회논문집
• /
• 한국마린엔지니어링학회 2000년도 춘계학술대회 논문집(Proceeding of the KOSME 2000 Spring Annual Meeting)
• /
• pp.122-126
• /
• 2000

In particle or short-fiber reinforced composites cracking of the reinforcements is a significant damage mode because the broken reinformcements lose load carrying capacity . The average stress in the inhomogeneity represents its load carrying capacity and the difference between the average stresses of the intact and broken inhomogeneities indicates the loss of load carrying capacity due to cracking damage. The composite in damage process contains intact and broken reinforcements in a matrix, An incremental constitutive relation of particle or short-fiber reinforced composites including the progressive cracking damage of the reinforcements have been developed based on the Eshelby's equivalent inclusion method and Mori-Tanaka's mean field concept. influence of the cracking damage on the Eshelby's equivalent inclusion method and Mori-Tanaka's mean field concept. Influence of the cracking damage on the stress-strain response of the composites is demonstrated.

• Structural Engineering and Mechanics
• /
• 제53권6호
• /
• pp.1183-1200
• /
• 2015

Reinforcement corrosion can cause serious safety deterioration to aging concrete structures exposed in aggressive environments. This paper presents an approach for reliability analyses of deteriorating reinforced concrete structures affected by reinforcement corrosion on the basis of the representative symptoms identified during the deterioration process. The concrete cracking growth and rebar bond strength evolution due to reinforcement corrosion are chosen as key symptoms for the performance deterioration of concrete structures. The crack width at concrete cover surface largely depends on the corrosion penetration of rebar due to the expansive rust layer at the bond interface generated by reinforcement corrosion. The bond strength of rebar in the concrete correlates well with concrete crack width and decays steadily with crack width growth. The estimates of cracking development and bond strength deterioration are examined by experimental data available from various sources, and then matched with symptom-based lifetime Weibull model. The symptom reliability and remaining useful life are predicted from the predictive lifetime Weibull model for deteriorating concrete structures. Finally, a numerical example is provided to demonstrate the applicability of the proposed approach for forecasting the performance of concrete structures subject to reinforcement corrosion. The results show that the corrosion rate has significant impact on the reliability associated with serviceability and load bearing capacity of reinforced concrete structures during their service life.

• 한국도로학회논문집
• /
• 제19권3호
• /
• pp.31-43
• /
• 2017

PURPOSES : The objective of this study is to verify the effect of fiber grid reinforcement on the long-term performance of asphalt pavement overlaid on old concrete pavement by performing field investigation, laboratory test, and finite element analysis. METHODS : The reflection cracking, roughness, and rutting of fiber grid reinforced overlay sections and ordinary overlay sections were compared. Cores were obtained from both the fiber grid reinforced and ordinary sections to measure bonding shear strength between the asphalt intermediate and asphalt overlay layers. Fracture energy, displacement after yield, shear stiffnesses of the cores were also obtained by analyzing the test results. Finite element analysis was performed using the test results to validate the effect of the fiber grid reinforcement on long-term performance of asphalt pavement overlaid on the old concrete pavement. The fatigue cracking and reflection-cracking were predicted for three cases: 1) fiber grid was not used; 2) glass fiber grid was used; 3) carbon fiber grid was used. RESULTS : The reflection-cracking ratio of fiber grid reinforced sections was much smaller than that of ordinary sections. The fiber grid reinforcement also showed reduction effect on rutting while that on roughness was not clear. The reflection-cracking was not affected by traffic volume but by slab deformation and joint movement caused by temperature variation. The bonding shear strength of the fiber grid reinforced sections was larger than that of the ordinary sections. The fracture energy, displacement after yield, and shear stiffnesses of the cores of the fiber grid reinforced sections were also larger than those of the ordinary sections. Finite element analysis results showed that fatigue cracking of glass or carbon fiber grid reinforced pavement was much smaller than that of ordinary pavement. Carbon fiber grid reinforcement showed larger effect in elongating the fatigue life of the ordinary overlay pavement compared to glass fiber grid reinforcement. The binder type of the overlay layer also affected the fatigue life. The fiber grid reinforcement resisted reflection-cracking and the carbon fiber grid showed the greater effect. CONCLUSIONS :The results of field investigation, laboratory test, and finite element analysis showed that the fiber grid reinforcement had a better effect on improving long-term performance of asphalt pavement overlaid on the old concrete pavement.

• 한국공작기계학회논문집
• /
• 제13권4호
• /
• pp.106-112
• /
• 2004

In particle or short-fiber reinforced composites, cracking or debonding of the reinforcements cause a significant damage mode because the damaged reinforcements lose load carrying capacity. The average stress in the inhomogeneity represents its load carrying capacity, and the difference between the average stresses of the intact and broken inhomogeneities indicates the loss of load carrying capacity due to cracking damage. The composite in damage process contains intact and broken reinforcements in a matrix. An incremental constitutive relation of discontinuously-reinforced composites including the progressive cracking damage of the reinforcements have been developed based on the Eshelby's equivalent inclusion method and Mori-Tanaka's mean field concept. Influence of the cracking damage on the stress-strain response of the composites is demonstrated.

• Journal of Mechanical Science and Technology
• /
• 제16권2호
• /
• pp.192-202
• /
• 2002

In particle or short-fiber reinforced composites, cracking of the reinforcements is a significant damage mode because the cracked reinforcements lose load carrying capacity. This paper deals with an incremental damage theory of particle or short-fiber reinforced composites. The composite undergoing damage process contains intact and broken reinforcements in a matrix. To describe the load carrying capacity of cracked reinforcement, the average stress of cracked ellipsoidal inhomogeneity in an infinite body as proposed in the previous paper is introduced. An incremental constitutive relation on particle or short-fiber reinforced composites including progressive cracking of the reinforcements is developed based on Eshelby's (1957) equivalent inclusion method and Mori and Tanaka\`s (1973) mean field concept. Influence of the cracking damage on the stress-strain response of composites is demonstrated.

• Structural Engineering and Mechanics
• /
• 제17권1호
• /
• pp.15-27
• /
• 2004

A rational and simple analytical model to predict the time varying cracking moment of reinforced concrete sections under sustained loading is developed. The modeling procedure is based on equilibrium and compatibility requirements and takes into account the interdependent effects of creep and shrinkage as well as the presence of axial loading. A parametric study is conducted in which particular consideration is given to the effects of reinforcement ratio, level of loading, and creep and shrinkage characteristics of concrete. It is concluded that the reduction in cracking moment is mainly attributed to shrinkage. The effect of shrinkage is more pronounced at low levels of sustained loading and at high reinforcement ratios. This effect is lessened by the compression steel and creep particularly when the applied moment is near the cracking moment.