• Journal of the Microelectronics and Packaging Society
• /
• v.14 no.4
• /
• pp.15-20
• /
• 2007

Growth kinetics of intermetallic compound (IMC) at various interface in Cu pillar bump during aging have been studied by thermal aging at 120, 150 and $165^{\circ}C$ for 300h. In result, $Cu_6Sn_5\;and\;Cu_3Sn$ were observed in the Cu pillar/SnPb interface and IMC growth followed parabolic law with increasing aging temperatures and time. Also, growth kinetics of IMC layer was faster for higher aging temperature with time. Kirkendall void formed at interface between Cu pillar and $Cu_3Sn$ as well as within the $Cu_3Sn$ layer and propagated with increasing time. $(Cu,Ni)_6Sn_5$ formed at interface between SnPb and Ni(P) after reflow and thickness change of $(Cu,Ni)_6Sn_5$ didn't observe with aging time. The apparent activation energies for growth of total $(Cu_6Sn_5+Cu_3Sn),\;Cu_6Sn_5\;and\;Cu_3Sn$ intermetallics from measurement of the IMC thickness with thermal aging temperature and time were 1.53, 1.84 and 0.81 eV, respectively.

• Korean Journal of Fisheries and Aquatic Sciences
• /
• v.32 no.5
• /
• pp.618-623
• /
• 1999

A relationship between SST (Sea Surface Temperature) fronts and formation of fishing grounds was examined using the data on fishing conditions obtained from 41 Korean purse-seiners during the period of 1991 to 1996. Good fishing grounds observed in the southern sea of Korea and the nothern area of the East China Sea were yearly found around the frontal zone and around the marginal area of Tsushima Current which was the periphery of fronts, Also, there were several fishing grounds, which are not related to the fronts. They can be classified into the following four types : The first type was found in the warm water pocket located in the western area of Cheju Island in winter. The second type was made in a intensive bending of isobathytherm with a higher temperature in the main stream of Tsushima Current between Cheju Island and the Goto Islands in winter. The third type was formed by the topographical vortex motion near the Tsushima Island in winter and spring. The fourth type was found at the area of the reflow Sea Warm Current in southwest sea of Korea between the costal front zone and the Yellow Bottom Cold Waters in summer and autumn.

• Journal of the Microelectronics and Packaging Society
• /
• v.26 no.3
• /
• pp.43-49
• /
• 2019

In this study, a new approach using graphene oxide (GO) powder-composited Sn-3.0Ag-0.5Cu(in wt.%) solder paste for improving the bending reliability of solder joints between a flexible substrate and small outline package (SOP) was suggested. The GO addition slightly affected the melting temperature, however, the change in the melting temperature was not significant. Meanwhile, we observed the addition of GO could suppress IMC growth and IMC thickness of solder joint during the reflow process. Moreover, the cyclic bending test was also performed for evaluation of reliability in solder joint and we could improve the cyclic bending reliability of solder joint by adding GO powders. For 0.2 wt.% of GO added to the solder joint, the bending lifetime was increased to 20% greater than that without GO. Pull strength and ductility of the solder joint with GO were also higher than those of the joint without GO and it was assumed that this effect by adding GO could contribute to improve cyclic bending reliability of solder joint.

• Journal of the Microelectronics and Packaging Society
• /
• v.29 no.3
• /
• pp.25-29
• /
• 2022

Recently, the importance of electronic packaging technology has been attracting attention, and heterogeneous integration technology in which chips are stacked out-of-plane direction is being applied to the electronic packaging field. The 2.5D integration circuit is a technology for stacking chips using an interposer including TSV, and is widely used already. Therefore, it is necessary to make the interposer mechanically reliable in the packaging process that undergoes various thermal processes and mechanical loadings. Considering the structural characteristics of the interposer on which several thin films are deposited, thermal stress due to the difference in thermal expansion coefficients of materials can have a great effect on reliability. In this study, the mechanical reliability of the metal pad for wire bonding on the silicon interposer against thermal stress was evaluated. After heating the interposer to the solder reflow temperature, the delamination of the metal pad that occurred during cooling was observed and the mechanism was investigated. In addition, it was confirmed that the high cooling rate and the defect caused by handling promote delamination of the metal pads.