• Proceedings of the Korean Nuclear Society Conference
• /
• 1999.10a
• /
• pp.263.1-263
• /
• 1999

• Journal of the Korean Society for Heat Treatment
• /
• v.18 no.1
• /
• pp.18-23
• /
• 2005

Effect of cold rolling on microstructural changes has been investigated for a Zn-15%Al alloy to elucidate the reason for its work softening behavior. Fully annealed microstructure of the Zn-15%Al alloy is characterized by ${\eta}$ grains and (${\eta}+{\alpha}$) lamellar colonies, where ${\eta}$ and ${\alpha}$ are Zn-rich HCP and Al-rich FCC phases, respectively. The hardness decreases continuously with increasing cold rolling degree, exhibiting work softening behavior. It is revealed that during the cold rolling, (${\eta}+{\alpha}$) lamellar colonies gradually change into equiaxed ${\eta}$ and ${\alpha}$ grains due to dynamic recrystallization at room temperature, while pre-existing ${\eta}$ grains are only deformed without recrystallization. Furthermore, cold rolling causes the precipitation of dissolved Al solutes in ${\eta}$ grains. In view of these results, change of (${\eta}+{\alpha}$) phases from lamellar to equiaxed morphology, which results in structural softness and increase in equiaxed ${\eta}/{\alpha}$ grain boundaries with higher mobility, and deterioration of solution hardening by precipitation of Al solutes from ${\eta}$ grains, are thought to contribute to the work softening of Zn-15%Al alloy.

• Journal of the Korean Society for Heat Treatment
• /
• v.31 no.6
• /
• pp.269-274
• /
• 2018

Grain-oriented electrical steel sheets are mainly used as core materials for transformers and motors. They should have excellent magnetic properties such as low core loss, high magnetic flux density and high permeability. In order to improve the magnetic properties of the electrical steel sheet, it is important to form Goss oriented grains with a very strong {110}<001> orientation. Recently, efforts have been made to develop Goss grains by controlling processes such as hot rolling, cold rolling, and primary and secondary recrystallization. In this study, the sheets containing 3.2 and 3.4wt.% Si were used, which were rolled with 1 and 10 passes with total thickness reduction of 89%. Heating was carried out for primary recrystallization with different heating rates of $25^{\circ}C/s$ and $24^{\circ}C/min$ until $720^{\circ}C$. The behavior of Goss-, {411}<148>-, and {111}<112>-oriented grains were analyzed using X-ray diffraction(XRD) and electron back-scatter diffraction(EBSD) analysis. The area fraction of Goss-oriented grains increased with the number of rolling passes during cold rolling; however, after the primary recrystallization, the area fraction of the Goss grains was higher and exact Goss grains were found in the specimens subjected to rapid heating after one rolling pass.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2001.10a
• /
• pp.293-296
• /
• 2001

The dynamic softening mechanisms of AISI 316, AISI 304 and AISI 430 stainless steels were studied with torsion test in the temperature range of $900 - 1200^{\circ}C$ and the strain rate range of $5.0x10^{-2}-5.0x10^0/sec$. The austenitic stainless steels, such as AISI 316 and AISI 304 were softened by dynamic recrystallization (DRX) during hot deformation. Also, the evolutions of flow stress and microstructure of AISI 430 ferritic stainless steel show the characteristics of continuous dynamic recrystallization (CDRX). To establish the quantitative equations for DRX of AISI 316 stainless steel, the evolution of flow stress curve with strain was analyzed. The critical strain (${\varepsilon}_c$) and strain for maximum softening rate (${\varepsilon}^{*}$) could be confirmed by the analysis of work hardening rate ($d{\sigma}/d{\varepsilon}={\theta}$). The volume fraction of dynamic recrystallization ($X_{DRX}$) as a function of processing variables, such as strain rate ( $\varepsilon$ ), temperature (T), and strain ( $\varepsilon$ ) were established using the ${\epsilon}_c$ and ${\varepsilon}^{*}$. For the exact prediction the ${\varepsilon}_c,\;{\varepsilon}^{*}$ and Avrami' exponent (m') were quantitatively expressed by dimensionless parameter, Z/A, respectively. It was found that the calculated results were agreed with the experimental data for the steels at my deformation conditions. Also, we can reasonably conclude that the DRX, CDRX and grain refinement of stainless steels can be achieved by large strain deformation at high Z parameter condition.

• Korean Journal of Materials Research
• /
• v.11 no.2
• /
• pp.104-114
• /
• 2001

To investigate the effects of the addition of Nb and Sn on the recrystallization of Zr- Sn-Nb alloys, both Vickers micro-hardness test and TEP measurement were carried out on cold-worked specimens annealed at various temperatures from $300^{\circ}C$ to 75$0^{\circ}C$. The microstructures of heat treated specimens were analyzed by optical microscope, SEM, and TEM. The study of microhardness and microstructures showed that both recrystallization process and grain growth were retarded as the activation energy was increased by the addition of Nb and Sn. Especially, the addition of Sn was more effective on retarding recrystallization. Precipitates were formed more easily when Nb was added because the solubility of Nb into Zr is lower than that of Sn. However, the recrystallization process was affected more by Sn than Nb because the strain field formed by substitutional Sn repressed the dislocation movement. TEP was increased due to the decrease of electron scattering as recovery and recrystallization were proceeded and saturated when the recrystallization completed. However, when precipitates formed, TEP was increased because the decrease of solute concentration near the precipitates caused the decrease of electron scattering.

• Transactions of Materials Processing
• /
• v.7 no.5
• /
• pp.450-458
• /
• 1998

The high temperature deformation behavior of Al 5083 alloy has been studied in the temperature range of 350 to 520 ${\circ}C$ and strain rate range of 0.2 to 3.0/sec by torsion test. The strain rate sensitivity(m) of the material was evaluated and used for estabilishing power dissipation maps following the dynamic material model. These maps show the variation of efficiency of power dissipation(${\eta}$=2m/(2m+1)) with temperature and strain rate. Hot restoration of dynamic recrystallization (DRX) was analyzed from the flow curve, deformed microstructure, and processing maps during hot deformation. Also, the effect of deformation strain on the efficiency of power dissipation of the alloy was analysed using the processing maps. Moreover relationship between the hot-ductility and efficiency of power dissipation of the alloy depending on thmperature and strain rate was studied using the Zener-Hollomon parameter(Z=${\varepsilon}$exp(Q/RT) It is found that the maximum efficiency of power dissipation for DRX in Al 5083 alloy is about 74.6 pct at the strain of 0.2. The strain rate and temperature at which the efficiency peak occurred in the DRX domain is found to be ∼0.1/sec and ∼450${\circ}C$ respectively.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2002.05a
• /
• pp.69-72
• /
• 2002

The high temperature deformation behavior of SiCp/2124Al composite and 2124Al alloy was investigated by hot compression test in a temperature ranged $400~475^{\circ}C$ over a strain rate ranged $10^{-3}~1s^{-1}$. The billets of 2124Al alloy and SiCp/2124Al composite were fabricated by vacuum hot pressing process. The stress-strain curve during high temperature deformation exhibited a peak stress, and then the flow stress decreased gradually into a steady state stress with increasing the strain. It was found that the flow-softening behavior was attributed to the dynamic recovery, local dynamic recrystallization and dynamic precipitation during the deformation. The precipitation phases were identified as S' and S by TEM diffraction pattern. Base on the TEM inspection, the relationship between the Z-H parameter and subgrain size was found based on the experiment data. The dependence of flow stress on temperature and strain rate could be formulated well by a hyperbolic-sinusoidal relationship using the Zener-Hollomon parameter.

• Transactions of Materials Processing
• /
• v.11 no.6
• /
• pp.529-537
• /
• 2002

A series of load-relaxation tests and tensile tests were conducted to study the high temperature deformation mechanism of fine duplex gamma TiAl alloy at temperatures ranging from 800 to 105$0^{\circ}C$. Results of load relaxation test showed that deformation behavior at a small imposed strain ($\varepsilon$≒0.05) was dominated by dislocation glide and dislocation climb. To investigate the deformation behavior at a large amount of strain, the processing map was constructed using a dynamic materials model. Two domains were characterized in the processing map obtained at a strain level of 0.6. One domain was found at the region of 98$0^{\circ}C$ and $10^{-3}/sec$ with a peak efficiency of 48%, which was identified as a domain of dynamic recrystallization from the microstructural observation. The order was observed at the region of 125$0^{\circ}C$ and $10^{-4}/sec$ with a peak efficiency of 64%. The strain rate sensitivity measured indicates that the material was deformed by the superplasticity in the region.

• Advances in materials Research
• /
• v.3 no.4
• /
• pp.217-225
• /
• 2014

In this study, a forging steel alloyed with both Nb and V was used as experimental material and the hot deformation behavior has been studied for this steel by conducting the compressive deformation test at temperature of $900-1150^{\circ}C$ and strain rate of $0.01-0.01s^{-1}$ in a MMS-300 thermo-mechanical simulator. The microstructure evolution, particularly the dynamically recrystallized microstructure, of the experimental steel at elevated temperatures, strain rates and strain levels, was characterized by optical microstructural observation and the constitutive equation in association with the activation energy and Zener-Hollomon parameter. The curves of strain hardening rate versus stress were used to determine the critical strain and peak strain, and their relation was connected with Zener-Hollomon parameter. Under the conditions of processing temperature $900^{\circ}C$ and strain rate $0.01s^{-1}$, the dynamic recrystallization took place and the austenite grain size was refined from $164.5{\mu}m$ to $28.9{\mu}m$.

• Journal of the Korean Society for Precision Engineering
• /
• v.21 no.10
• /
• pp.162-169
• /
• 2004

High temperature uniaxial compression tests in the alpha single phase region were carried out on the Ti -43mo1%Al intermetallic compound, in order to obtain oriented lamellar microstructure. The compression deformation temperatures and strain rates are from 1573k to 1623k and 1.0x10$^{-4}$ s to 5.0x10$^{-3}$ s, respectively. Fully lamellar microstructure was observed after the uniaxial compression deformation in a single phase region followed by cooling to room temperature. Lamellar colony diameter depended on strain rates and test temperatures. The diameter varied between 8601m and 300fm. Stress-strain curve showed a work softening and the size of lamellar colony diameter varied depending on peak stresses. This shows the occurrence of dynamic recrystallization. Texture measurements after the uniaxial compression deformation, showed the development of fiber during dynamic recrystallization. It is seen that the area for the maximum pole density existed in 35 degrees away from the compression plane. The texture sharpens with a decrease in strain rate