• Journal of Biomedical Engineering Research
• /
• v.25 no.5
• /
• pp.383-389
• /
• 2004

A commercially pure Ti(CP-Ti) and Ti-25wt％Pd alloy for dental applications were cast into a phosphate-bonded Al$_2$ $O_3$/ $SiO_2$ investment mold and the surface of the casting specimens were investigated by means of SEM/EDS, XRD and XPS. The addition of 25wt％Pd in CP-Ti showed a moderate mold reaction owing to the considerable lowering of melting point. XRD analysis of the investment after burn-out treatment revealed that it consisted essentially of $SiO_2$, Al$_2$ $O_3$, P$_2$O$\_$5/, Mg$_3$(P $O_4$)$_2$, AlP $O_4$, Mg$_2$ $SiO_4$, MgAl$_2$ $O_4$ The mold reaction products were Ti$\_$5/Si$_3$ and Ti $O_2$ in case of CP-Ti casting and Ti $O_2$ and SiO$\_$x/ in case of Ti-25wt％ Pd casting.

• Journal of the Korean Ceramic Society
• /
• v.37 no.3
• /
• pp.211-218
• /
• 2000

The attrition-milled powder mixtures of Al and Al2O3 were oxidized below 140$0^{\circ}C$ for 1 hr and post-sintered at 150$0^{\circ}C$ and 1$600^{\circ}C$ for 2 hr. During attrition milling, ZrO2 was added to the system by grinding effect of ZrO2 balls. The average particle size of the powder mixtures was decreased by the attrition milling as the aluminum content decrease. Above 120$0^{\circ}C$, sintering behaviro was observed on the fine Al2O3 particles resulted from the oxidation of Al. The specimens heat-treated at 140$0^{\circ}C$ for 1 hr showed the bending strength of 166 MPa and hardness of 220 MPa. The specimens post-sintered at 1$600^{\circ}C$ for 2hr had a linear shrinkage of 9~12% and a relative density of about 95%. After the post-sintering, the specimens having 55 vol% Al content revealed the bending strength of 513 MPa and hardness of 718 MPa. The Weibull modulus to the bending strength was about 16.

• Journal of the Korean Ceramic Society
• /
• v.34 no.8
• /
• pp.854-860
• /
• 1997

The tribological property of ceramics is very important for use in seal rings, pump parts, thread guides and mechanical seal, etc. In the present study, which RBSC/graphite composites were manufactured by adding graphite powders with different particle sizes to mixtures of SiC powder, metallic silicon, carbon black and alumina, effects on the tribological property of each RBSC/graphite composite was investigated in accordance with the particle size of the added graphite powder. The water absorption, the bending strength and the resistance for the friction and wear were measured, and the crystalline phase and the microstructure were respectively examined by using XRD and SEM. In case that the particle size of the graphite powder was fine(2${\mu}{\textrm}{m}$), the formation of $\beta$-SiC was accelerated, thereby making the increase of the bending strength and the decrease of the water absorption, but no improvement for the tribological properties. Furthermore, in case that the particle size of the graphite powder was some large(88~149${\mu}{\textrm}{m}$), the formation of $\beta$-SiC was not accelerated, to thereby make the decrease of the bending strength and the increase of the water absorption, but the improvement for the tribological property of only the composite having the graphite powder of 20 vol%. In addition, in case that the particle size distribution of the graphite powder was large (under 53 ${\mu}{\textrm}{m}$), there was no improvement for every properties. However, the composites, which the graphite powder with the particle size of 53~88 ${\mu}{\textrm}{m}$ was added in 10~15 vol%, had the most increased resistance for the friction and wear which show the worn out amount of 0.4~0.6$\times$10-3 $\textrm{cm}^2$, and the value of the bending strength is 380~520 kg/$\textrm{cm}^2$.