• 한국세라믹학회지
• /
• 제36권6호
• /
• pp.655-661
• /
• 1999

${\beta}$-SiC formation mechanism in Si melt-C-SiC system with varying in size of carbon source was investigated. A continuous reaction sintering process using Si melt infiltration method was adopted to control the reaction sintering time effectively. It was found that ${\beta}$-SiC formation mechanism in Si melt-C-SiC system was directly affected by the size of carbon source. In the Si melt-C-SiC system with large carbon source ${\beta}$-SiC formation mechanism could be divided into two stages depending on the reaction sintering time: in early stage of reaction sintering carbon dissolution in Si melt and precipitation of ${\beta}$-SiC was occurred preferentially and then SIC nucleation and growth was controlled by diffusion of carbon throughy the ${\beta}$-SiC layer formed on graphite particle. Furthmore a dissolution rate of graphite particles in Si melt could be accelerated by the infiltration of Si melt through basal plane of graphite crystalline.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2001년도 추계학술대회논문집A
• /
• pp.27-31
• /
• 2001

Hi-Nicalon SiC fiber reinforced SiC composites (SiC/SiC) have been fabricated by the reaction sintering process. Braided Hi-Nicalon SiC fiber with double interphases of BN and SiC was used in this composite system. The microstructures and the mechanical properties of reaction sintered SiC/SiC composites were investigated through means of electron microscopies (SEM, TEM, EDS) and bending tests. The matrix morphology of reaction sintered SiC/SiC composites was composed of the SiC phases that the composition of the silicon and the carbon is different. The TEM analysis showed that the residual silicon and the unreacted carbon were finely distributed in the matrix region of reaction sintered SiC/SiC composites. Reaction sintered SiC/SiC composites also represented proper flexural strength and fracture energy, accompanying the noncatastrophic failure behavior.

• 한국세라믹학회지
• /
• 제32권9호
• /
• pp.1027-1032
• /
• 1995

SiC had been widely applied for mechanical sealing as a sealing material. SiC sintering is commonly made of reaction sintering, presureless sintering, and hot isostatic pressing (HIP) sintering. In this investigation, however, clay bonded sintering was used to avoide any complications of the special sintering methods as mentioned above. In order to prevent harmful SiC oxidation in the clay bonded sintering, clay and frit were used to form the SiC oxidation protecting layer and graphite was added to provide high solid lubricity. As a result, the material with 6% clay (clay 5.4% and frit 0.6%) and 2~4% graphite (45 mesh) sintered at 140$0^{\circ}C$ for 3 hours, showed the following physical properties; porosity 6%, static friction coefficient 0.15, kinematic coefficient 0.1,. and specific wear rate 4.8$\times$10-8 $\textrm{mm}^2$kgf-1. On the other hand, the flexural strength was 900kgf/$\textrm{cm}^2$. This tribological characteristic properties were similar to those of the reaction sintered SiC except the flexural strength.

• 한국세라믹학회지
• /
• 제45권4호
• /
• pp.204-207
• /
• 2008

This paper presents a new process for producing SiC fiber-SiC matrix(SiC/SiC) composites by reaction sintering. The processing strategy for the fabrication of the SiC/SiC composites involves the following: (1) infiltration of the SiC fiber fabric using a slurry consisting of Si and C precursors, (2) stacking the slurry-infiltrated SiC fiber fabric at room temperature, (3) cross-linking the stacked composites, (4) pyrolysis of the stacked composites, and (5) hot-pressing of the pyrolyzed composites. It was possible to obtain dense SiC/SiC composites with relative densities of >96% and a typical flexural strength of ${\sim}400$ MPa.

• 한국세라믹학회지
• /
• 제25권6호
• /
• pp.609-614
• /
• 1988

This study was carried out to investigate the effects of B4C or Y2O3 additives on the tendency of sintering, $\beta$-SiC synthesis and mineral phase changes by reaction bonding of SiC at 145$0^{\circ}C$. At the sintering temperature of 145$0^{\circ}C$, the additives such as B4C or Y2O3 did not improved porosity and bending strength. Added more than 1.5% of Y2O3, 0.5-0.3% of B4C, the formation of $\beta$-SiC was increased. At higher temperature above 145$0^{\circ}C$, it seems that the bodies added B4C, contained 3C form of SiC were denser than that of Y2O3 added. Because the transition of 3Clongrightarrow4Hlongrightarrow6H promoted sintering.

• 한국세라믹학회지
• /
• 제36권11호
• /
• pp.1261-1265
• /
• 1999

Effect of SiC particle size of the densification of Al2O3-SiC composite during pressureless sintering was investigated. Two types of SiC powders having average particle size of 0.15${\mu}{\textrm}{m}$ and 3${\mu}{\textrm}{m}$ were used. Densification rate of the specimen containing 0.15${\mu}{\textrm}{m}$ SiC particles was slower than that of the specimen containg 3${\mu}{\textrm}{m}$ SiC particles. Although the relative density of the specimen containing 0.15${\mu}{\textrm}{m}$ SiC particles was below 90% of theoretical density after sintering at 155$0^{\circ}C$ the complete closure of open pores occurred. Therefore full densification could be obtained by subsequent HIP. On the other hand in the specimen containing 3${\mu}{\textrm}{m}$ SiC particles the complete closed pore was observed at 95% of theoretical density. Such a fast pore closure in the specimen containing 0.15${\mu}{\textrm}{m}$ SiC particles is likely to occur as a result of dense reaction layer formation on the specimen surface which is attributed to the high reactivity of small size particles with sintering atmosphere.

• 한국산학기술학회논문지
• /
• 제20권3호
• /
• pp.29-34
• /
• 2019

SiC는 큰 에너지 밴드 갭을 갖고, 불순물 도핑에 의해 p형 및 n형 전도의 제어가 용이해서 고온용 전자부품 소재로 활용이 가능한 재료이다. 특히 $N_2$ 분위기, $2000^{\circ}C$에서 ${\beta}-SiC$ 분말로부터 제조한 다공질 n형 SiC 반도체의 경우, $800{\sim}1000^{\circ}C$에서의 도전율 값이 단결정 SiC와 비교해서 비슷하거나 오히려 높은 값을 나타내었으며, 반면에 열전도율은 치밀한 SiC 세라믹스와 비교시 1/10~1/30 정도로 낮은 값을 나타내었다. 본 연구에서는 소결온도를 낮추기 위해 n형 ${\beta}-SiC$에 함침 시킨 polycarbosilane (PCS)의 열분해에 의한 반응소결 공정 ($1400{\sim}1600^{\circ}C$)으로 다공질 소결체를 제작하였다. 함침 및 소결공정($N_2$ 분위기, $1600^{\circ}C$, 3시간)을 반복함에 따라 상대밀도는 크게 증가하지 않았지만 Seebeck 계수 및 도전율은 크게 증가하였다. 본 연구에서의 열전변환 효율을 반영하는 power factor는 고온에서 상압소결 공정으로 제작한 다공질 SiC 반도체에 비해 1/100~1/10 정도 작게 나타났지만, 미세구조 및 캐리어 밀도를 정밀하게 제어하면, 본 연구에서의 반응소결 공정으로 제작한 SiC 반도체의 열전물성은 크게 향상될 것으로 판단된다.

• 한국세라믹학회지
• /
• 제51권5호
• /
• pp.392-398
• /
• 2014

$Al_2O_3$-SiC composites reinforced with SiC whisker ($SiC_w$) were fabricated using three different methods. In the first, $Al_2O_3-SiC_w$ starting materials were used. In the second, $Al_2O_3-SiC_w$-SiC particles ($SiC_p$) were used, which was intended to enhance the mechanical properties by $SiC_p$ reinforcement. In the third method, reaction-sintering was used with mullite-Al-C-$SiC_w$ starting materials. After hot-pressing at $1750^{\circ}C$ and 30 MPa for 1 h, the composites fabricated using $Al_2O_3-SiC_w$ and $Al_2O_3-SiC_w-SiC_p$ showed strong mechanical properties, by which the effects of reinforcement by $SiC_w$ and $SiC_p$ were confirmed. On the other hand, the mechanical properties of the composite fabricated by reaction-sintering were found to be inferior to those of the other $Al_2O_3$-SiC composites owing to its relatively lower density and the presence of ${\gamma}-Al_2O_3$ and ${\gamma}-Al_{2.67}O_4$. The greatest hardness and $K_{1C}$ were 20.37 GPa for the composite fabricated using $Al_2O_3-SiC_w$, and $4.9MPa{\cdot}m^{1/2}$ using $Al_2O_3-SiC_w-SiC_p$, respectively, which were much improved over those from the monolithic $Al_2O_3$.

• 한국세라믹학회지
• /
• 제33권12호
• /
• pp.1414-1420
• /
• 1996

평균 입경 8${\mu}{\textrm}{m}$ Si 분말을 사용하여 무가압 분말 충전 성형볍에 의해 Si 성형체를 제조하였다. 이 Si 성형체를 1350,140$0^{\circ}C$의 온도에서 3~35시간동안 N2/H2 분위기에서 반응 소결한 후 미세구조를 관찰하였다. 반응 소결체는 90% 이상의 질화율과 88%의 상대밀도를 보였다. 반응 소결체의 가스압 소결을 위해 소결조제로서 MgO를 Mgnitrate 수용액 형태로 Si 성형체에 5wt% 첨가한 후140$0^{\circ}C$에서 15시간동안 반응 소결하였다. 이후 반응 소결체를 1800, 1900, 200$0^{\circ}C$에서 각각 150, 300분 동안 가스압 소결을 행하여 95%의 상대밀도와 598 MPa의 꺾임강도, 6 MPa.m1/2의 파괴인성을 나타내는 질화규소 소결체를 제조하였다.

• 한국세라믹학회지
• /
• 제31권5호
• /
• pp.561-571
• /
• 1994

For the preparation of SiC composite, the properties of reaction sintering in the SiC-C-Si-Ti system with the titanium contents variation were investigated. Either the case of titanium additions or the case of direct infiltration of titanium in SiC+C preform, the newly formed fine-grained $\beta$-SiC, which was reacted from the molten silicon with graphite, was intergranulated between the original $\alpha$-SiC particles. Also titanium disilicide (TiSi2) was discontinuously formed isolated pocket in silicon matrix. The amount of titanium disilicide was gradually increased as titanium content increase. With the results of hardness and fracture toughness measurement, SiC-titanium disilicide (TiSi2) composite represented high properties compared with the system of the infiltrated pure silicon.