• Corrosion Science and Technology
• /
• 제13권3호
• /
• pp.87-94
• /
• 2014

Recently, the application of bending products has been increased since the industries such as automobile, aerospace, ships, and plants greatly need the usage of pipes. For facility fabrication, bending process is one of key technologies for pipings. Induction heat bending process is composed of bending deformation by repeated local heat and cooling. Because of local heating and compressive strain, detrimental phases may be precipitated and microstructural change can be induced. This work focused on the effect of induction heat bending process on the properties of ASME SA312 TP316 stainless steel. Evaluation was done on the base metal and the bended areas before and after heat treatment. Microstructure analysis, intergranular corrosion test including Huey test, double loop electropotentiokinetic reactivation test, oxalic acid etch test, and anodic polarization test were performed. On the base of microstructural analysis, grain boundaries in bended extrados area were zagged by bending process, but there were no precipitates in grain and grain boundary and the intergranular corrosion rate was similar to that of base metal. However, pitting potentials of bended area were lower than that of the base metal and zagged boundaries was one of the pitting initiation sites. By re-annealing treatment, grain boundary was recovered and pitting potential was similar to that of the base metal.

• Nuclear Engineering and Technology
• /
• 제44권3호
• /
• pp.343-354
• /
• 2012

Primary water stress corrosion cracking (PWSCC) is a major safety concern in the nuclear power industry worldwide. PWSCC is known to initiate only in the condition in which sufficiently high tensile stress is applied to alloy 600 tube material or alloy 82/182 weld material in pressurized water reactor operating environments. However, it is still uncertain how much tensile stress is re-quired to generate PWSCC or what causes such high tensile stress. This study was performed to pre-dict the magnitude of weld residual stress and operating stress and compare it with previous experi-mental results for PWSCC initiation. For the study, a pressurizer safety nozzle was selected because it is reported to be vulnerable to PWSCC in overseas plants. The assessment was conducted by nu-merical analysis. Before performing stress analysis for plant conditions, a preliminary mock-up ana-lysis was done. The result of the preliminary analysis was validated by residual stress measurement in the mock-up. After verification of the analysis methodology, an analysis under plant conditions was conducted. The analysis results show that the stress level is not high enough to initiate PWSCC. If a plant is properly welded and operated, PWSCC is not likely to occur in the pressurizer safety nozzle.

• Structural Engineering and Mechanics
• /
• 제84권4호
• /
• pp.517-530
• /
• 2022

In re-assessing the Jacket-type fixed steel structures, the current standards often allow the simplicity of corrosion sections using local buckling or equivalent section approach to applying empirical formulae of frame stress and resistance analyses. However, those approaches can lead to significant errors for non-uniform corroded frames in a specific area, including force distribution, stress, and allowable strength of the tubular section, compared to the actual cases. This paper investigates a suitable approach to determine the actual stress on non-uniform corroded tubular frames under compression through the non-linear ABAQUS model by considering the effect of large deformation on the frame axis and the frame section. There are 3 scenarios of interest. In the 1st and 2nd scenarios with simple corrosion cases, the stress ratios using the numerical model and theoretical formulae correspond to the calculation of allowable strength reduction ratios in standards. However, scenario 3, which describes non-uniform corroded sections based on survey data, provides considerable differences in results. Therefore, it proves the reliable and effective results when using this method to analyze the resistance of the actual corroded section in the Jacket platforms.

• Corrosion Science and Technology
• /
• 제8권5호
• /
• pp.184-187
• /
• 2009

The trend of the microjoining technology by the laser-soldering process has been reviewed. Among the production technologies, joining technology plays an important role in the fabrication of electronic components. This has led to an increasing attention towards the use of modern microjoining technology such as micro-resistance spot joining, micro-soldering, micro-friction stir joining and laser-soldering, etc. This review covers the recent technical trends of laser-soldering collected from the COMPENDEX DB analysis of published papers, research subject and research institutes.

• Corrosion Science and Technology
• /
• 제11권4호
• /
• pp.129-134
• /
• 2012

UT(Ultrasonic Test), one of the non-destructive tests, is the most common thickness measurement method for evaluating the wear rate in NPPs(Nuclear Power Plants). UT is used widely because it is easy and safe for use. However some amount of error inevitably occurs in attempting to measure the thickness. The error, that could make the thickness data thicker or thinner, may affect estimation of wear rate in pipes. NPPs are composed of a lot of pipes and components. Some of them are tested to check the current status during RFO(Re-Fueling Outage). Reliability analysis of UT is essential for evaluating pipe wear rate and establishing the long-term management plan in NPPs. This paper reviewed the cause of error occurrence and presented the UT data reliability analysis method. Also, this paper shows the application result of reliability analysis to the UT data acquired in NPPs.

• 한국재료학회지
• /
• 제25권10호
• /
• pp.516-522
• /
• 2015

Aging aircraft structures are inevitably exposed to environment for a long time facing many potential problems, including corrosion and wide spread fatigue damage, which in turn cause the degradation of flight safety. In this study, the environmental surface damages on aging aircraft structures induced during service were quantitatively analyzed. Additionally, S-N fatigue tests were performed with center hole specimens extracted from aging aircraft structures. From the results of quantitative analyses of the surface damages and fatigue tests, it is concluded that corrosion pits initiated during service reduce the fatigue life significantly. Finally, using the fracture mechanics and the EIFS (equivalent initial flaw size) concepts, the remaining fatigue life was predicted based on actual fatigue test results.

• 오토저널
• /
• 제7권2호
• /
• pp.55-63
• /
• 1985

This study is focused on deposition process leading to inefficiency and hot corrosion in fossil fuel-fired furnaces and engines. An improved understanding of the coupled thermodynamics, kinetics, and transport processes governing the deposition rate of inorganic oxides and salts from hot gases containing these compounds can suggest more efficient test strategies and control measures. Accordingly, an optical re-evaporation method for accurately measuring the growth rate of deposits under laboratory burner conditions has been developed. To demonstrate the technique and provide data suitable for theoretical model development, a deliberately simple chemical system and target geometry are used. Potassium sulfate(K$_{2}$SO$_{4}$)is introduced into a premixed propane-air flat flame at atmospheric pressure. The growth rate of $K_{2}$SO$_{4}$ on an electrically heated Pt ribbon is measured by re-evaporation technique.

• 보존과학연구
• /
• 통권17호
• /
• pp.1-19
• /
• 1996

Desalting methods for chloride ions from the excavated iron objects were studied. These methods were compared with room temperature and heating condition of treating solution. During the Desalting treatments the $Cl^-$concentration of the solution were measured regularly and the plotted for $Cl^-$concentrations the square root of time, heating methods showed that the $Cl^-$ ions are more extracted. For the desalting treatments these plots were found to be flattening line, it was showed the changing second solution. Also, the changing solution in the room temperation detected less $Cl^-$ ions of heating treatment solution. As the examination for the relative humidity has compared for desalting objects during 8 days, it was showed a re-corroded appearance of R.H90%. As it did not detected a $Cl^-$ ions of re-corroded section, these phenomena were showed the naturally occuring corrosion of the objects in the high relative humidity.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2004년도 춘계학술발표대회 논문집
• /
• pp.13-17
• /
• 2004

In recent years, the deterioration of reinforced concrete structures has become a serious problem in civil engineering fields. This situation is mainly due to corrosion of steel reinforcing bars embedded in concrete. Recently, there has been a greatly increased demand for the use of FRP (fiber reinforced plastic) in civil engineering field due to their superior mechanical and physical properties. This paper presents an experimental study on the behavior of concrete bridge deck reinforced with FRP Box, FRP Plate, and FRP Re-bar. In tlIe study, mechanical properties of FRP Box, FRP Plate, GFRP Re-bar, and CFRP Grid have been investigated. Full scale one-way deck slab was tested under four point lateral load (equivalent to actual wheel load of DB-24 including impact). Load-deflection and load-strain data were collected through LVDT's and strain gages attached to the specimen.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2013년도 추계 학술논문 발표대회
• /
• pp.106-107
• /
• 2013

The purpose of this study is to characterize the bonding properties between reinforced bar and re-emulsion polymer cement mortar through the pull off test. The properties of polymer cement mortar before and after hardening were measured. Spiral reinforced steel bar was used to control the brittleness fracture of test specimens. In addition polymer content as experimental factors, the types of reinforced bar and corrosion were considered as well. Non linear FEM analysis was carried out to expect the behavior of bonding interface under the certain load.