• The Journal of the Korea institute of electronic communication sciences
• /
• v.16 no.6
• /
• pp.1095-1100
• /
• 2021

In this study, ITZO thin films were deposited on glass, sapphire, and PEN substrates by RF magnetron sputtering, and their electrical and optical properties were investigated. The resistivity of the ITZO thin film deposited on the glass and sapphire substrates was 3.08×10-4 and 3.21×10-4 Ω-cm, respectively, showing no significant difference, whereas the resistivity of the ITZO thin film deposited on the PEN substrate was 7.36×10-4 Ω-cm, which was a rather large value. Regardless of the type of substrate, there was no significant difference in the average transmittance of the ITZO thin film. Figure of Merits of the ITZO thin film deposited on the glass substrate obtained using the average transmittance in the absorption region of the amorphous silicon thin film solar cell and the absorption region of the P3HT : PCBM organic active layer were 10.52 and 9.28×10-3 Ω-1, respectively, which showed the best values. Through XRD and AFM measurements, it was confirmed that all ITZO thin films exhibited an amorphous structure and had no defects such as pinholes or cracks, regardless of the substrate type.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2000.02a
• /
• pp.174-174
• /
• 2000

A strong antiferromagnetic coupling in Fe/Si multilayered films (MLF) had been recently discovered and much consideration has been given to whether the coupling in the Fe/Si MLF system has the same origin as the metal/metal MLF. Nevertheless, the nature of the interfacial ron silicide is still controversial. On one hand, a metal/ semiconductor structure was suggested with a narrow band-gap semiconducting $\varepsilon$-FeSi spacer that mediates the coupling. However, some features show that the nature of coupling can be well understood in terms of the conventional metal/metal multilayered system. It is well known that both magneto-optical (MO) and optical properties of a metal depend strongly on their electronic structure that is also correlated with the atomic and chemical ordering. In this study, the nature of the interfacial regions is the Fe/Si multilayers has been investigated by the experimental and computer-simulated MO and optical spectroscopies. The Fe/Si MLF were prepared by rf-sputtering onto glass substrates at room temperature with the number of repetition N=50. The thickness of Fe sublayer was fixed at 3.0nm while the Si sublayer thickness was varied from 1.0 to 2.0 nm. The topmost layer of all the Fe/Si MLF is Fe. In order to carry out the computer simulations, the information on the MO and optical parameters of the materials that may constitute a real multilayered structure should be known in advance. For this purpose, we also prepared Fe, Si, FeSi2 and FeSi samples. The structural characterization of Fe/Si MLF was performed by low- and high -angle x-ray diffraction with a Cu-K$\alpha$ radiation and by transmission electron microscopy. A bulk $\varepsilon$-FeSi was also investigated. The MO and optical properties were measured at room temperature in the 1.0-4.7 eV energy range. The theoretical simulations of MO and optical properties for the Fe/Si MLF were performed by solving exactly a multireflection problem using the scattering matrix approach assuming various stoichiometries of a nonmagnetic spacer separating the antiferromagnetically coupled Fe layers. The simulated spectra of a model structure of FeSi2 or $\varepsilon$-FeSi as the spacer turned out to fail in explaining the experimental spectra of the Fe/Si MLF in both intensity and shape. Thus, the decisive disagreement between experimental and simulated MO and optical properties ruled out the hypothesis of FeSi2 and $\varepsilon$-FeSi as the nonmagnetic spacer. By supposing the spontaneous formation of a metallic ζ-FeSi, a reasonable agreement between experimental and simulated MO and optical spectra was obtained.

• Journal of the Korean institute of surface engineering
• /
• v.56 no.2
• /
• pp.147-151
• /
• 2023

Transparent ZnO (100 nm thick) and ZnO/Ti/ZnO (ZTZ) films were prepared with radio frequency (RF) and direct current (DC) magnetron sputtering on the glass substrate at room temperature. During the ZTZ film deposition, the thickness of the Ti interlayer was varied, such as 6, 9, 12, and 15 nm, while the thickness of ZnO films was kept at 50 nm to investigate the effect of the Ti interlayer on the crystallization and opto-electrical performance of the films. From the XRD pattern, it is concluded that the 9 nm thick Ti interlayer showed some characteristic peaks of Ti (200) and (220), and the grain size of the ZnO (002) enlarged from 13.32 to 15.28 nm as Ti interlayer thickness increased. In an opto-electrical performance observation, ZnO single-layer films show a figure of merit of 1.4×10^-11 Ω^-1, while ZTZ films with a 9 nm-thick Ti interlayer show a higher figure of merit of 2.0×10^-5 Ω^-1.

• Korean Journal of Materials Research
• /
• v.33 no.4
• /
• pp.142-150
• /
• 2023

AZO/Cu/AZO thin films were deposited on glass by RF magnetron sputtering. The specimens showed the preferred orientation of (0002) AZO and (111) Cu. The Cu crystal sizes increased from about 3.7 nm to about 8.5 nm with increasing Cu thickness, and from about 6.3 nm to about 9.5 nm with increasing heat treatment temperatures. The sizes of AZO crystals were almost independent of the Cu thickness, and increased slightly with heat treatment temperature. The residual stress of AZO after heat treatment also increased compressively from -4.6 GPa to -5.6 GPa with increasing heat treatment temperature. The increase in crystal size resulted from grain growth, and the increase in stress resulted from the decrease in defects that accompanied grain growth, and the thermal stress during cooling from heat treatment temperature to room temperature. From the PL spectra, the decrease in defects during heat treatment resulted in the increased intensity. The electrical resistivities of the 4 nm Cu film were 5.9×10^-4 Ω·cm and about 1.0×10^-4 Ω·cm for thicker Cu films. The resistivity decreased as the temperature of heat treatment increased. As the Cu thickness increased, an increase in carrier concentration resulted, as the fraction of AZO/Cu/AZO metal film increased. And the increase in carrier concentration with increasing heat treatment temperature might result from the diffusion of Cu ions into AZO. Transmittance decreased with increasing Cu thicknesses, and reached a maximum near the 500 nm wavelength after being heat treated at 200 ℃.

• Journal of the Korean Magnetics Society
• /
• v.7 no.5
• /
• pp.265-273
• /
• 1997

The MR ratios and the exchange biasing field and interlayer coupling field were investigated in $Ni_{91}Fe_{19}/Co_{90}Fe_{10}/Cu/Co_{90}Fe_{10}/NiO$ spin-valve sandwiches grown on antiferromagnetic NiO films as a function of the NiO thickness, the thickness of Cu and pinning layer $Co_{90}Fe_{10}$. The spin-valve sandwiches were deposited on the Corning glass 7059 by means of the 3-gun dc and 1-gun rf magnetron sputtering at a 5 mtorrpartial Ar pressure and room temperature. The deposition field was 50 Oe. The MR curve was measured by the four-terminal method with applied magnetic soft bilayer [NiFe/CoFe] (90$\AA$) decreased dramatically to less than 10 Oe when the NiFe/CoFe bilayer used an NiFe bilayer thicker that 20$\AA$. So NiFe layer improved the softmagnetic properties in the NiFe/CoFe bilayer. The GMR ratio and the magnetic field sensitivity of the spin-valve film $Ni_{91}Fe_{19}(40{\AA})/Co_{90}Fe_{10}(50{\AA}) /Cu(30{\AA})/Co_{90}Fe_{10}(35{\AA})/NiO(800{\AA})$ was 6.3% and about 0.5 (%/Oe), respectively. The MR ratio had 5.3% below an annealing temperature of 20$0^{\circ}C$ which slowly decreased to 3% above 30$0^{\circ}C$. The large blocking temperature of the spin-valve film was taken (as being) due to the good stability of the NiO films. Thus, the spin-valve films with a free NiFe/CoFe layer clearly had a high large GMR output and showed a effective magnetic field sensitivity for a suitable spin-valve head material.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.368-370
• /
• 2013

투명 전극은 전기전도도를 갖는 동시에 가시광선을 투과하는 소재를 말하며, 구체적으로는 빛의 파장이 400~700 nm 영역대의 가시광선을 80% 이상 투과하며 전기전도도가 비저항으로 $10^{-3}{\Omega}cm$이하이거나 면저항이 $10^3{\Omega}$/${\Box}$소재를 의미한다. 투명 전극은 전기전도도에 따라 사용되는 용도가 다양하다. LCD, PDP, OLED 와 같은 평판디스플레이 및 3D 디스플레이의 투명전극으로 사용되는 핵심재료일 뿐만 아니라 터치스크린, 투명필름, 대전방지막, 열반사막, EMI 방지막, 태양전지 분야에 광범위하게 이용되고 있다. 일반적으로, 투명전극 박막에 가장 많이 사용되고 있는 소재는 ITO (indium tin oxide)이나, 주성분인 In의 사용량 증가로 상용 ITO 타겟 가격이 급등하고 있음으며, 고가의 ITO 타겟을 대체하기 위한 저가의 투명전극 소재 개발이 절대적으로 요구되며, 신규 소재 개발을 통한 기술력 우위 선점이 필수적으로 요구되는 상황이다. 본 연구에서는 기존에 디스플레이 분야에서 널리 활용되는 고가의 ITO를 대체하기 위한 다성분 금속산화물 투명전극 스퍼터링 타겟 제조기술을 개발하기 위한 연구로서, Metal이 첨가된 In-Ga-Zn-O기반의 3성분계 투명도전성 소재를 조성설계, 고밀도 균질 타겟 제조 및 투명전극 박막을 형성하는 연구를 실시하였다. 고체산화물 산화인듐(In2O3)분말, 산화갈륨(Ga2O3) 분말그리고 산화아연(ZnO)분말과 Metal을 몰비로 칭량한 후 분말을 폴리에틸렌제 포트에 넣고 에탄올을 충분히 채운 후 지르코니아(ZrO2) 볼(ball)을 이용하여 24 h 동안 볼 밀링(ball milling) 방법으로 혼합한 뒤, $120^{\circ}C$의 플레이트위에서 마그네틱 바로 stirring하면서 건조하였다. 이 분말을 건조기에서 완전히 건조한 후 알루미나 유발을 이용해서 pulverizing한 후 sieving기를 이용하여 분말의 조립화를 하였다. 이 분말을 금형에 넣고 300 kg/$cm^2$의 압력으로 press하여 성형한 뒤 대기중에서 소결하였다 소결을 위한 승온 온도는 $10^{\circ}C$/min이었고 소결은 $1,450^{\circ}C$에서 6 h 동안 하였다. IGZO target의 조성 비율은 1:1:12 (mol%)를 사용하였으며, 첨가한 Metal은 Boron (B), Germanium (Ge), Barium (Ba)을 사용하여 타겟을 제작하였다. M-IGZO 박막은RF magnetron Sputter를 이용하여 증착하였으며, 앞선 실험에서 제작한 타겟을 사용하여 M-IGZO박막을 투명전극으로 사용하기 위한 각각의 특성을 파악하였다. 모든 박막은 상온에서 증착을 하였으며, 증착된 박막두께를 측정하기 위해 ${\alpha}$-step IQ를 사용하였고, 광학적 특성을 분석하기 위해 UV-Visible spectrophotometer 로 투과율을 측정하였다. 그리고 전기적 특성을 측정하기 위해 Hall effect measurement 및 4-probe를 사용하였으며, 결정성 분석을 위하여 XRD를 이용하여 분석하였다. 표1은 M-IGZO타겟을 사용하여 증착시간에 따른 면저항 특성을 나타내었다. Ge, B, Ba이 첨가된 IGZO 박막은 증착시간이 증가할수록 면저항이 낮아짐을 알 수 있었다. 또한, Ge이 첨가된 IGZO 박막이 다른 금속이 첨가된 IGZO 박막의 면저항보다 현저히 낮음을 알 수 있었다. Fig. 1(a), (b), (c)는 각 타겟을 동일한 조건으로 증착을 하여 광학적특성을 나타내는 그래프이다. GZO 박막의 광학적 특성을 보면 가시광 영역에서 평균 투과율은 모두 80% 이상으로 우수한 광투과 특성을 보여 투명전자소자로 사용가능하다. 특히, 자외선 영역을 모두 차단하는 UV cut 능력이 우수함을 알 수 있었다. 따라서, 금속이 첨가된 IGZO 박막을 태양전지용 투명전극으로 사용할 경우, 자외선에 의하여 수명이 단축되는 현상을 줄여줄 수 있음을 기대할 수 있으며 내구성 향상에 크게 기여할 것으로 보인다. Fig. 2는 Ge=0, 0.5, 5%인 IGZO 투명전극을 총 40회 반복하여 증착을 실시한 후 각각의 면저항을 측정한 결과이다. 실험결과에 따르면 Ge가 0%, 5%인 IGZO 투명전극은 증착을 거듭할수록 면저항이 증가하는 결과를 나타내었으며, 0.5%인 IGZO 투명전극은 점차 안정화되어가는 결과를 나타내었다. 따라서 안정화 되었을 때 평균 면저항은 26ohm/sq.로 나타났으며, 광투과율은 Fig. 3과 같이 가시광영역에서 평균 80%이상의 결과를 보였으며, 550 nm에서는 86.36%의 우수한 특성을 나타내었다. 본 연구에서는 Metal이 첨가된 In-Ga-Zn-O기반의 3성분계 투명도전성 소재 target을 제작하여 RF magnetron sputter로 박막을 형성한 후 특성을 비교하였다. M-IGZO target 중 Ge (0.5%)을 첨가한 IGZO 타겟을 사용한 투명전극이 가장 우수한 특성을 보였으며, 제작된 M-target의 In 비율이 30% 정도로 기존의 ITO (90%) 대비하여 투명전극 제작 단가를 절감할 수 있다.

• Applied Microscopy
• /
• v.38 no.4
• /
• pp.279-284
• /
• 2008

The phase change materials have been extensively used as an optical rewritable data storage media utilizing their phase change properties. Recently, the phase change materials have been spotlighted for the application of non-volatile memory device, such as the phase change random access memory. In this work, we have investigated the crystallization behavior and microstructure analysis of In-Sb-Te (IST) thin films deposited by RF magnetron sputtering. Transmission electron microscopy measurement was carried out after the annealing at $300^{\circ}C$, $350^{\circ}C$, $400^{\circ}C$ and $450^{\circ}C$ for 5 min. It was observed that InSb phases change into $In_3SbTe_2$ phases and InTe phases as the temperature increases. It was found that the thickness of thin films was decreased and the grain size was increased by the bright field transmission electron microscopy (BF TEM) images and the selected area electron diffraction (SAED) patterns. In a high resolution transmission electron microscopy (HRTEM) study, it shows that $350^{\circ}C$-annealed InSb phases have {111} facet because the surface energy of a {111} close-packed plane is the lowest in FCC crystals. When the film was heated up to $400^{\circ}C$, $In_3SbTe_2$ grains have coherent micro-twins with {111} mirror plane, and they are healed annealing at $450^{\circ}C$. From the HRTEM, InTe phase separation was occurred in this stage. It can be found that $In_3SbTe_2$ forms in the crystallization process as composition of the film near stoichiometric composition, while InTe phase separation may take place as the composition deviates from $In_3SbTe_2$.

• Journal of Sensor Science and Technology
• /
• v.2 no.1
• /
• pp.101-108
• /
• 1993

$TiO_{2}$/Se : Te heterojunction for color sensor has been fabricated by RF reactive sputtering and thermal evaporation methods onto glass substrate. The optimum deposition condition of $TiO_{2}$ films was such that RF power was 120 W, substrate temperature was $100^{\circ}C$, oxygen concentration was 50%, working pressure was 50 mTorr for the $TiO_{2}$ film thickness of $1000{\AA}$. In this case, the optical transmittance of $TiO_{2}$ film at 550 nm-wavelength was 85%, resistivity was $2{\times}10^9{\Omega}{\cdot}cm$, refractive index was 2.3, and optical bandgap was 3.58 eV. The composition ratio of 0 to Ti by AES analysis was 1.7. When $TiO_{2}$ films were annealed at $400^{\circ}C$ for 30 min. in $O_{2}$ ambient, the optical transmittance of $TiO_{2}$ films at the wavelength range of $300{\sim}580$ nm was improved from 0 to 25%. When Se : Te films were annealed at $190^{\circ}C$ for 1 min., photosensitivity under illumination of 1000 lux was 0.75. The optical bandgap of Se : Te films was 1.7 eV. The structures of Se : Te films were the hexagonal with (100) and (110) orientation. The spectral response of a-Se was improved by the addition of Te, especially in the long wavelength region. The $TiO_{2}$/Se : Te heterojunction showed wide spectral response, and more improved one than that of a-Si film in the blue light region.