• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 1998년도 제28회 추계학술대회
• /
• pp.258-264
• /
• 1998

Three kinds of reation-bonded SiC that reaction-bonded SiC(RBSC), RBSC reinforced by carbon fiber and RBSC reinforced by activated carbon fiber were prepared for investigating the change of erosion properties. The characteristics of microstructures and the phases have been investigated by using scanning electron microscope and XRD analysis. The hardness test, toughness test and erosion test were camed out. In the cases with no carbon fiber, those kind of specimens had the highest result of hardness test and the lowest result of toughness test. With the increase of carbon fiber content, The hardness and the weight loss were decreased but the toughness was increased in the cases with carbon fiber In the cases with activated carbon fiber those specimens had the highest result of toughness test and the lowest result of hardness test with 30% contents of activated carbon fiber.

• Tribology and Lubricants
• /
• 제15권1호
• /
• pp.59-67
• /
• 1999

Three kinds of reation-bonded SiC that reaction-bonded SiC(RBSC), RBSC reinforced by carbon fiber and RBSC reinforced by activated carbon fiber were prepared for investigating the change of erosion properties. The characteristics of microstructures and the phases have been investigated by using scanning electron microscope and XRD analysis. The hardness test toughness test and erosion test was carried out. In the cases with no carbon fiber, those kind of specimens had the highest value of hardness and the lowest value of toughness. With the increase of carbon fiber content the hardness and the weight loss were decreased, but the toughness was increased in the cases with carbon fiber. In the cases with activated carbon fiber specimens had the highest value of toughness and the lowest value of hardness with 30% contents of activated carbon fiber.

• 한국세라믹학회지
• /
• 제33권5호
• /
• pp.479-484
• /
• 1996

The tribological properties of ceramics are very important in the application to engineering ceramic parts such as mechanical seal slurry valve disc and so on. In this study the effect of graphite addition on the mechanical and tribological properties of RBSC/graphite composites were investigated. The composites were prepared by adding graphite powder to the mixture of SiC powder metallic siliconcarbon black and alumina. Bending strength water absorption friction coefficient the amount of worn out material at a certain time and maximum surface roughness(Rmax) of the prepared composites were measured and crystalline phases were examined with XRD. The composite containing 5 vol% graphite powder showed improved bending strength due to high green density and decreased friction coefficient and wear resistance. The friction coefficient and the wear resistance of the composite were increased by adding graphite powder up to 10 vol% They decreased however as increasing the amount of graphite powder more that 10vol% There was no linear relationship between the tribological properties and bending strength of the composites.

• 한국세라믹학회지
• /
• 제36권9호
• /
• pp.937-945
• /
• 1999

반응결합 탄화규소(RBSC) 반응관을 보호하기 위하여, 반응결합 탄화규소 기판 위에 탄화규소를 1~10 범위의 입력기체비(${\alpha}=P_{H2}/P_{MTS}=Q_{H2}/Q_{MTS}$)와 1050~1300$^{\circ}C$범위의 증착온도에서 methyltrichlorosilane(MTS)로부터 수소분위기에서 저압화학기상법으로 증착하였다. 1250$^{\circ}C$의 증착온도에서 입력기체비가 감소함에 따라 증착속도는 증가하다가 감소하였다 입력기체비가 높을 때에는 (111) 우선배향성을 나타내고 과립형의 미세구조를 보이며, 입력기체비가 작을 경우에는 (220) 우선배향성을 가지는 마면주상의 미세구조가 관찰되었다. 증착온도가 증가함에 따라 입력기체비와 비슷하게 미세구조의 변화하는결과를 얻었으며, 이러한 결과는 증착기구의 변화와 밀접한 관련이 있다. 일정한 증착온도에서 입력기체비의 조정를 통하여 얻었으며, 이러한 결과는 증착기구의 변화와 밀접한 관련이 있다. 일정한 증착온도에서 입력기체비의 조절을 통하여 과립형과 미면주상의 미세구조를 함께 가지는 복층구조를 연속공정을 통하여 성공적으로 제조하였다.

• 한국세라믹학회지
• /
• 제34권8호
• /
• pp.854-860
• /
• 1997

The tribological property of ceramics is very important for use in seal rings, pump parts, thread guides and mechanical seal, etc. In the present study, which RBSC/graphite composites were manufactured by adding graphite powders with different particle sizes to mixtures of SiC powder, metallic silicon, carbon black and alumina, effects on the tribological property of each RBSC/graphite composite was investigated in accordance with the particle size of the added graphite powder. The water absorption, the bending strength and the resistance for the friction and wear were measured, and the crystalline phase and the microstructure were respectively examined by using XRD and SEM. In case that the particle size of the graphite powder was fine(2${\mu}{\textrm}{m}$), the formation of $\beta$-SiC was accelerated, thereby making the increase of the bending strength and the decrease of the water absorption, but no improvement for the tribological properties. Furthermore, in case that the particle size of the graphite powder was some large(88~149${\mu}{\textrm}{m}$), the formation of $\beta$-SiC was not accelerated, to thereby make the decrease of the bending strength and the increase of the water absorption, but the improvement for the tribological property of only the composite having the graphite powder of 20 vol%. In addition, in case that the particle size distribution of the graphite powder was large (under 53 ${\mu}{\textrm}{m}$), there was no improvement for every properties. However, the composites, which the graphite powder with the particle size of 53~88 ${\mu}{\textrm}{m}$ was added in 10~15 vol%, had the most increased resistance for the friction and wear which show the worn out amount of 0.4~0.6$\times$10-3 $\textrm{cm}^2$, and the value of the bending strength is 380~520 kg/$\textrm{cm}^2$.

• 한국세라믹학회지
• /
• 제40권9호
• /
• pp.891-896
• /
• 2003

IGCC 발전 시스템에 사용되는 고온 가스 필터에 대하여 용융 Si 침윤공정 방법을 사용한 고강도 반응소결 탄화규소 고온 가스 필터 제조 공정이 개발되었다. 용융 Si 침윤 반응으로 제조된 반응소결 탄화규소의 상온 및 고온 파괴강도는 약 50-123, 60-66 MPa이었으며, 반응소결 탄화규소 다공체의 평균기공크기 및 기공율의 범위는 각각 60- 70 $\mu\textrm{m}$ 및 약 34 vol%이었다. 용융 Si 침윤 방법으로 제조된 반응 소결 탄화 규소 다공체에서는 SiC 입자 사이에 SiC/Si으로 이루어진 기지 상이 형성되어 고온 파괴 강도가 점토 결합 탄화 규소 다공체보다 우수하였다. 소결된 지지층 위에 Si 분말이 첨가되지 않은 slurry를 사용하여 여과층을 제조하였다. 여과층에 사용된 Sic 입자의 크기가 10$\mu\textrm{m}$에서 34 $\mu\textrm{m}$로 증가됨에 따라 SiC 입자 사이에 형성된 기지상의 두께가 증가하였다. 분진이 포함된 유체의 face velocity 변화에 따른 압손의 관계는 US filter사 Schumacher type 20 filter의 기체 유동 특성과 비슷하게 나타났으며, 분진여과 측정시 4분 내에 누출 분진의 크기가 1 $\mu\textrm{m}$ 크기 이하로 감소되었다.

• 한국재료학회지
• /
• 제31권5호
• /
• pp.301-311
• /
• 2021

The conversion of all carbon preforms to dense SiC by liquid infiltration can become a low-cost and reliable method to form SiC-Si composites of complex shape and high density. Reactive sintered silicon carbide (RBSC) is prepared by covering Si powder on top of 0.5-5.0 wt% Y₂O₃-added carbon preforms at 1,450 and 1,500℃ for 2 hours; samples are analyzed to determine densification. Reactive sintering from the Y₂O₃-free carbon preform causes Si to be pushed to one side and cracking defects occur. However, when prepared from the Y₂O₃-added carbon preform, an SiC-Si composite in which Si is homogeneously distributed in the SiC matrix without cracking can be produced. Using the Si + C = SiC reaction, 3C and 6H of SiC, crystalline Si, and Y₂O₃ phases are detected by XRD analysis without the appearance of graphite. As the content of Y₂O₃ in the carbon preform increases, the prepared RBSC accelerates the SiC conversion reaction, increasing the density and decreasing the pores, resulting in densification. The dense RBSC obtained by reaction sintering at 1,500 ℃ for 2 hours from a carbon preform with 2.0 wt% Y₂O₃ added has 0.20 % apparent porosity and 96.9 % relative density.

• 한국세라믹학회지
• /
• 제36권8호
• /
• pp.805-812
• /
• 1999

• 한국세라믹학회지
• /
• 제45권9호
• /
• pp.531-536
• /
• 2008

Reaction bonded silicon carbide (RBSC) composite for heat-exchanger was fabricated by molten Si infiltration method. For enforcing fracture toughness to reaction bonded silicon carbide composite, the surface of carbon fiber has coating layer by SiC or pyro-carbon. For SiC layer coating, CVD method was used. And for carbon layer coating, the phenol resin was used. In the case of carbon layer coating, fracture toughness and fracture strength were enhancing to 4.4 $MPa{\cdot}m^{1/2}$ and 279 MPa.

• 한국세라믹학회지
• /
• 제45권8호
• /
• pp.486-492
• /
• 2008

Reaction bonded silicon carbide(RBSC) composite for heat-exchanger was fabricated by molten Si infiltration method. The raw materials with variable particle sizes were used in this experience. The finer the particle size in sintered silicon carbide was the more increasing 3-point bending strength and fracture toughness. As the adaptable particle sizes had been occupied interstice arising from packing sample, the mechanical properties were increased. In the PCS1-1 sample, the 3-point bending strength and fracture toughness were 323MPa and $4.9\;MPa{\cdot}m^{1/2}$, respectively.