• Journal of the Mineralogical Society of Korea
• /
• v.7 no.1
• /
• pp.62-79
• /
• 1994

The quanttative and structural analysis of the binary standard mixtures of albite and quartz, and microcline and albite were carried out using the Rietveld refinement method in order to investigate the accuracy and precision of the method. The quantitative analysis using the Rietveld method results in a standard deviation of 4 wt % for the albite-quartz standard mixtures and 1 wt % for the microcline-albite standard mixtures, suggesting that its accuracy is far better than that of the conventional XRD method in which only a few selected peaks are utilized. Furthermore, the unit-cell parameters of component minerals in mixtures were also estimated accurately during the analysis. It was observed that the refined weight fractions deviate systematically from their measured values when the method is applied to the mixtures that contain minerals with different degrees of preferred orientation, such as albite-quartz mixtures. The preferred orientation parameters and R-values suggest that the systematic deviation is caused as a result of the preferred orientation effect of feldspar crystallites. It is evident that the preferred orientation corrections are of help for the accurate determination of unit-cell parameters, although they may not improve the result of quantitative analysis significantly. The refined weight fraction of the mineral with higher degree of preferred orientation in mixture is greater than the measured one. This is apparently caused by the effect of geometry of feldspar crystallites in the surface of the mounted sample. The Rietveld refinement method minimizes the problems inherent in the traditional XRD methods, such as the line overlap, primary extinction, and preferred orientation effect, by fitting every data point in a whole pattern explicitly. Furthermore, accurate unit-cell parameters as well as scale factors that can be obtained from the Rietveld refinement are used for the quqantification. The present stdudy demonstrates that the Rietveld method yields far more accurate analytical result than the conventional XRD quantitative analysis method does.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.31 no.3
• /
• pp.116-126
• /
• 2021

Diesel particulate filter (DPF) is a typical application field of cordierite (Mg₂Al₄Si₅O₁₈) honeycomb. Green body for DPF honeycomb was extruded using slurry paste and sintered at the temperature range of 980~1450℃. Quantitative crystal phase analysis was carried out by using Rietveld refinement method for powder XRD data. In conjunction with the quantitative Rietveld analysis, SEM-EDS analysis was carried for the crystal phases (indialite, cordierite, cristobalite, alumina, spinel, mullite, pro-enstatite). After removing amorphous phase on the sintered surfaces by chemical etching method, the shape and composition of the crystal phases can be clearly identified by SEM-EDS method. By combining the Rietveld refinement method and SEM-EDS analysis, crystal phase evolution process in DPF cordierite ceramics could be clarified. In addition, the coefficient of thermal expansion (CTE) of the DPF honeycombs were measured and compared with the calculated CTEs based on the quantitative crystal phase analysis results.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.33 no.5
• /
• pp.174-180
• /
• 2023

Porcelain (white ware, celadon ware) coated with a ferrous sulfate and ferrous/cobalt sulfate was sintered at 1250℃. The specimens were investigated by HR-XRD, FE-SEM, HR-EDS, and UV-vis spectrophotometer. Through X-ray rietveld quantitative analysis, quartz and mullite were found to be the main phases for white ware, and mullite and plagioclase were found to be the main phases for celadon ware. When the pigment of ferrous/cobalt sulfate was applied, were identified as an andradite phase for celadon ware and a spinel phase for the white ware, and the amorphous phase, respectively. The L^* value, which was the brightness of the specimen, was 72.01, 60.92 for white ware and celadon ware, respectively. The ferrous and ferrous/cobalt pigment coated porcelain had L^* values of 44.89, 52.27 for white ware and celadon ware, respectively; with a^* values of 2.12, 1.40, an d at b^* values of 1.45 and 13.79. As for the color of the specimens, it was found that the L^* value was greatly affected by the white ware, and the b^* value differed greatly depending on the clay. It was thought to be closely related to the production of the secondary phase such as Fe₂O₃ and andradite phase produced in the surface layer.