• 한국전기전자재료학회논문지
• /
• 제14권3호
• /
• pp.197-201
• /
• 2001

The microwave dielectric properties of (1-x)Ba(Mg$_{1}$3/Ta$_{2}$3/)O$_3$-xBa(Co$_{1}$3/Nb$_{2}$3)O$_3$(x=0.25~0.5) ceramics depending on the Ba(Co$_{1}$3/Nb$_{2}$3/)O$_3$[BCN] contents and the possibility of application as a microwave dielectric resonator were investigated. The specimens were prepared by he conventional mixed oxide method using there sintering temperature of 1575$^{\circ}C$. It was found that Ba(Mg$_{1}$3/Ta$_{2}$3/)O$_3$[BMT] and BCN formed a solid solution with complex perovskite structure. As the mole fraction of BCN increased, dielectric constant increased while temperature coefficient of resonant frequency decreased. The highest value of quality factor, Qxf$_{0}$=138,205GHz, obtained in the sample of 0.9BMT-0.1BCN ceramics. In the range of x$\geq$0.4, the dielectric constant was about 30. The 0.55BMT-0.45BCN ceramics showed excellent microwave dielectric properties with $\varepsilon$$_{r}$=30.84, Qxf$_{0}$=75,325GHz and $\tau$$_{f}$=2.9015ppm/$^{\circ}C$.EX>.EX>.

• 한국전기전자재료학회논문지
• /
• 제11권4호
• /
• pp.281-287
• /
• 1998

$BiNbO_4$ ceramics doped with 0.07wt% $V_2O_5$ and 0.03wt% CuO (BNC3V7) were sucessfully sintered at $900^{\circ}C$ through the firing process with Ag electrode. The BNC3V7 shows typically Dielectric constant of 44.3, Thermal Coefficient of resonance Frequency(TCF) of 2 ppm/$^{\circ} and $Qxf_o$ value of 22,000 GHz. The laminated chip Low Pass Filter (LPF) is very sensitive to chip processing parameters, was confirmed by the computer simulation as a function of Q(Quality factors), filter size, capacitor layer thickness, inductor pattern widths. The multilayer type LPF was fabricated by screen-printing with Ag electrode after tape casting and then compared with the simulated characteristics. The results show that characterization of band pass width was similar to that of designed ones.

• 한국전자파학회논문지
• /
• 제14권6호
• /
• pp.558-566
• /
• 2003

Li$_2$CO$_3$가 첨가된 BiNbO$_4$ 세라믹스를 이용하여 후막 모노폴 안테나를 제작하였다. 그 결과 Li 이온이 Bi, Nb 이온과 결합하여 이온간의 거리를 증가시켰다. 이에 따라 이온 분극량이 증가하여 유전율은 증가하였지만 세라믹 내 격자구조의 왜곡이 심해져 유전손실이 증가하였다. 안테나 특성에 있어서는 유전율 보다는 품질계수(Q)의 영향을 직접적으로 받았다. 대역폭을 측정한 결과 Li$_2$CO$_3$ 첨가에 따른 급격한 품질계수의 저하와 함께 37 %에서 81.7 %까지 증가한 반면 안테나 이득은 -5.5 dBi 에서 -10.03 dBi까지 급격히 감소하였다. 이로 인해 방사패턴은 Li$_2$CO$_3$ 미(未)첨가 시 보다 낮은 dBi 값을 보여 주었다. 특히 무 지향성을 보여야될 x-y면 방사패턴의 경우 격자구조의 왜곡으로 인한 파장의 산란과 공기와 유전체의 경계면에서 높은 유전율 차이로 굴절이 일어나 심하게 왜곡되어 있었다. 그러나 낮은 품질계수(Q)로 인하여 모든 조성 범위에서 1 GHz 이상의 우수한 -10 dB 대역폭 특성을 보여주었다.