• International Journal of Korean Welding Society
• /
• 제3권1호
• /
• pp.39-44
• /
• 2003

The welded specimens were made by butt welding of the 2 wires of 50mm length using the pulsed YAG laser. The laser welded wires were tested for investigating the shape memory effect and the ability of super elasticity. The fatigue properties of the welded wires were investigated using the rotary bending fatigue tester specially designed for wires. Moreover, the effect of defocusing distance during laser welding on the static and fatigue properties was Investigated. The shape memory effect and super elasticity of the laser welded wires were approximately identical with that of base metal at the test temperature below 353K. However, the welded wires were broken within elastic limit at the test temperature above 353k. Under the cyclic bending loading conditions, the welded wires could be useful only below the elastic limit, while the base metal had sufficient fatigue life even the stress induced M-phase region. The fatigue strength of the welded wires was about half of that of the base metal. The deterioration of the static and fatigue properties in the welded wires was proven to be from the large difference of the transformation behavior between the base metal and welded part that is caused by vaporization of Ni-content at the welded part during the welding process. The defocusing distance below 3mm acted more largely on lowering the strength of the welded wires than that of 6mm or 8mm.

• Journal of Photoscience
• /
• 제5권1호
• /
• pp.39-43
• /
• 1998

Pulsed Er: YAG and CO$_2$ lasers induced temperature rise of tissue is studied using axisymmetric, two-dimensional, and transient Pennes bio-heat equation for elucidating the implications of skin resurfacing. Modeling indicates that Er:YAG laser induced temperature has much higher but more shallow distribution in tissue than that of the CO$_2$ laser because of much higher absorption coefficient. The increase of repetition rate does not much affect on temperature rise because these laser modalities have much shorter heat diffusion time than the temporal length of each off-pulse. This model works as a tool to understand the photothermal effect in the laser-tissue interaction.

• Journal of Oral Medicine and Pain
• /
• 제21권1호
• /
• pp.183-196
• /
• 1996

The author examined the clinical and histological changes on the dorsal tongue mucosa of adult Sprague-Dawley rats after lasing by pulsed Nd:YAG laser. The dorsal tongue was lased for 3 seconds by 1.5, 2.0, 2.5, 3.0, 3.5, 4.0W and 10, 15, 20, 20pps. After tissue changes were observed clinically, the excised samples were observed histologically and the width of tissue destruction was analyzed quantitatively under the Confocal laser microscope respectively. The following results were obtained : 1. Whitening of peripheral tissue was observed more as increasing pulsed per second (Hz) below power 2.5W and observed at all parameters above power 3.0W. 2. Charring of mucosal surface was observed at all parameters but mild at parameters below power 2.0W. 3. The destruction of epithelium was observed at all parameters and tissue destruction was extended to lamina propria at higher pulses per second. 4. The width of tissue destruction was more widening as increasing energies per pulse (p<0.001) and the narrowest at 20Hz than 10Hz, 15Hz and 30Hz(p<0.05). As the above results, author suggests power below-3.5W and 20Hz as the lasing parameters for oral soft tissue therapy.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.595-599
• /
• 2002

Edge welding of thin sheets is very difficult because of the fit-up problem and small weld area In laser welding, joint fit-up and penetration are critical for sound weld quality, which can be monitored by appropriate methods. Among the various monitoring systems, visual monitoring method is attractive because various kinds of weld pool information can be extracted directly. In this study, a vision sensor was adopted for the weld pool monitoring in pulsed Nd:YAG laser edge welding to monitor whether the penetration is enough and the joint fit-up is within the requirement. Pulsed Nd:YAG laser provides a series of periodic laser pulses, while the shape and brightness of the weld pool change temporally even in one pulse duration. The shutter-triggered and non-interlaced CCD camera was used to acquire a temporally changed weld pool image at the moment representing the weld status well. The information for quality monitoring can be extracted from the monitored weld pool image by an image processing algorithm. Weld pool image contains not only the information about the joint fit-up, but the penetration. The information about the joint fit-up can be extracted from the weld pool shape, and that about a penetration from the brightness. Weld pool parameters that represent the characteristics of the weld pool were selected based on the geometrical appearance and brightness profile. In order to achieve accurate prediction of the weld penetration, which is nonlinear model, neural network with the selected weld pool parameters was applied.

• Journal of Advanced Marine Engineering and Technology
• /
• 제28권8호
• /
• pp.1270-1278
• /
• 2004

This paper describes the effectiveness of laser pulse shaping in eliminating weld defects such as porosity, cracks and undercuts in pulsed Nd:YAG laser welding. A large porosity was formed in a keyhole mode of deeply penetrated weld metal of any stainless steel. Solidification cracks were present in STS 310S with above 0.017%P and undercuts were formed in STS 303 with about 0.3%S. The conditions for the formation of porosity were determined in further detail in STS 316. With the objectives of obtaining a fundamental knowledge of formation and prevention of weld defects, the fusion and solidification behavior of a molten puddle was observed during laser spot welding of STS 310S through a high speed video photographing technique. It was deduced that cellular dendrite tips grew rapidly from the bottom to the surface, and consequently residual liquid remained at the grain boundaries in wide regions and enhanced the solidification cracking susceptibility. Several laser pulse shapes were investigated and optimum pulse shapes were proposed for the reduction and prevention of porosity and solidification cracking.

• 한국컴퓨터산업학회논문지
• /
• 제2권3호
• /
• pp.369-376
• /
• 2001

펄스형 YAG 레이저 시스템의 효율개선을 위해서는 공진기 및 레이저 전원장치의 최적화가 필수적이다. 따라서, 본 연구에서는 공진기 출력거울의 반사율 최적화 및 기존의 전원보다 훨씬 컴팩하고, 경제적이며 가공목적에 따라 출력을 정밀하게 제어할 수 있는 새로운 방식의 레이저시스템을 설계 및 제작하였다. 그 결과 50[W]급의 펄스형 Nd:YAG 레이저 시스템에서는 출력거울의 반사율이 85%일 때 최대 출력을 나타내었다. 그리고 3단 병렬 충ㆍ방전 방식의 전원시스템은 3개의 콘덴서가 순차적으로 충ㆍ방전함으로서 1개의 콘덴가 충ㆍ방전하는 방식보다 더 많은 에너지를 플래쉬램프에 전달할 수 있어 더 높은 출력을 얻을 수가 있었다. 실험을 통해 제시한 방법의 타당성을 검증하였다.

• Journal of Photoscience
• /
• 제5권1호
• /
• pp.33-37
• /
• 1998

One macroscopic effect in the free-running Er:YAG laser is an accumulation of microscopic effects. Understanding of the exogenous water induced mechanical effect on the dental hard tissue by the Qswitched Er:YAG laser has an important impact on the further understanding of the free-running Er:YAG laser ablation on the dental hard tissue. The Q-switched Er:YAG laser (1-$\mu$s-long pulse width) was used in the recoil pressure measurement with an aid of water-jet system and a pressure transducer. The amplitude of the recoil pressure depends on the tooth surface conditions (dry and wet) and the volume of the water upon it. Wet surfaces yielded higher recoil pressure than that of dry, surface, and as the volume of the exogenous water drop increased, the amplitude of the recoil pressure increased also.

• Journal of Periodontal and Implant Science
• /
• 제26권2호
• /
• pp.522-530
• /
• 1996

Most dentists are very interested in laser therapy on the intraoral soft tissue lesions because they want to accomplish the analgesic and aseptic surgery with little or no bleeding. In order to determine the difference of pain threshold according to different gingival tissues with or without inflammation, 25 patients with inflammatory periodontal disease and 10 volunteers with good general and oral health were selected as the inflamed group and the normal group, respectively. Interdental papilla, marginal gingiva, attached gingiva, and alveolar mucosa were irradiated by the contact delivery($300{\mu]m$ fiber optic, for 5 seconds) of a pulsed Nd:YAG laser(EN.EL.EN06O, Italy). And the laser power was gradually increased from 0.5W by the increment of 0.1W. The highest laser power was recorded as the first painful power when the painful gesture was recognized at first. The difference of the first painful power of laser according to different gingival tissues with or without inflammation was statistically analyzed by paired t-test in MICROSTAT program. Following results were obtained: 1. In the comparison related with the inflammation, the first painful power was significantly lower in the inflamed group than in the normal group, regardless of interdental papilla and marginal gingiva(p<0.05). 2. In the comparison related with the tissue structure, the first painful. power was significantly lower in alveolar mucosa than in attached gingiva(p<0.05). The results suggest that, for the painless therapy by a pulsed-Nd:YAG laser irradiation, the laser surgery over 2.0W of power should be necessarily accomplished under the local anethesia, and the local anesthesia should be considered according to the degree of inflammation, the tissue structure, and the purpose of laser therapy.

• 한국광학회지
• /
• 제11권4호
• /
• pp.279-288
• /
• 2000

다양한 종류의 펄스형 Nd:YAG 레이저 공진기를 구성하여 출력경의 각도변화에 따른 레이저 출력에너지의 변화를 최대 출력에너지가 반으로 줄어드는 점의 각도변위인 반치폭 (FWHM)을 측정하여 비교하였다. 출력경의 기울어짐에 대하여 높은 반치폭을 갖고 반사경의 각도변화에 대해서도 덜 민감하게 반응하는 안정적인 펄스형 고체 레이저의 새로운 공지기를 구성하였다. ABCD 광선 전파 행렬식을 이용하여 이러한 공지기의 전파행렬식이 단위행렬이 됨을 해석함으로서 높은 정렬 안정성을 가지고 있음을 증명하였다.

• 한국레이저가공학회지
• /
• 제7권1호
• /
• pp.37-47
• /
• 2004

Laser-assisted selective infiltration is a new method of building metal layers to make metal parts layer by layer, in which superheated microscopic metal droplets are infiltrated into a laser-preheated layer of microscopic metal powders. In this work, the selective infiltration of a low melting-point metal, Sn-37Pb wt%, was conducted to investigate the effects of such dominant parameters as superheating temperature, Nd:YAG laser power for preheating, substrate temperature, etc. The optimal conditions for successful selective infiltration of a single layer of microscopic metal powder were experimentally obtained