• 펄프종이기술
• /
• 제48권3호
• /
• pp.30-36
• /
• 2016

This study was conducted to investigate the influence of the changes in handsheet structure by beating, wet pressing and the addition of wood flour spacer on the water absorption and the moisture absorption properties. The higher beating treatment of BKP resulted in the denser structure of handsheet samples, which leaded to the lower water and moisture absorption. The wet pressing showed the similar effects by reducing the bulk of handsheets. In case of the handsheet samples with similar bulk structure made of different beaten pulps, the severer beating treatment increased the water absorption and the moisture absorption. The addition of the wood flour spacer resulted in the higher bulk following the higher water and moisture adsorption. Since the water and the moisture absorption properties of paper products could greatly affect on not only the product quality but also the process runnability, the control of the water response of paper product has been considered as very important technology. The results of this study might be useful for control of water and moisture absorption properties of paper products.

• International Journal of Ocean System Engineering
• /
• 제1권3호
• /
• pp.148-154
• /
• 2011

Generally, strength degradation is caused by the absorption of moisture in composites. For this reason, a fracture is generated in the composites and traces of glass fiber degrade human health and physical damage is generated. Therefore, in this research, we studied the mechanical properties change of composites by moistureabsorption. The composites were manufactured with and without the Gel-coating process and were immersed in a moisture absorption device at $80^{\circ}C$ for more than 100 days. The mechanical properties of the moistureabsorption composites and the composites which dry after moisture-absorption were compared. The mechanical properties degradation of basalt fiber composites according to the result of the measurement of moistureabsorption was smaller than that of glass fiber composites by about 20%. In addition, the coefficient of moisture absorption was lower for the case of Gel-coating processing than the composites without the Gel-coating process by about 2% and it was deduced that Gel-coating did not have a significant effect on the mechanical properties.

• Journal of the Korean Wood Science and Technology
• /
• 제42권5호
• /
• pp.615-623
• /
• 2014

Increases of public attention on healthy environment lead to the regulation of indoor air quality such as Clean Healthy House Construction Standard. This standard covers emission of total volatile organic compounds (TVOCs) (e.g., formaldehyde, benzene, and toluene), ventilation, and use of environmentally-friendly products or functional products. Moisture absorption and desorption abilities are a recommended functionality for improving indoor air quality. In this study, moisture absorption and desorption capacities of carbonized board from wood-based panels and other materials were determined by using UNT-HEAT-01 according to ISO 24358:2008. Pine had higher moisture absorption and desorption capacities ($49.0g/m^2$ and $35.3g/m^2$, respectively) than hinoki cypress, cement board, gypsum board, oriented strand board, and medium density fiberboard (MDF). The moisture absorption and desorption capacities differed considerably according to the wood species. After carbonization process at $400^{\circ}C$, the absorption and desorption ability of MDF increased to 38% and 60%, respectively. However, moisture absorption and desorption capacities decreased with increasing carbonization temperature, but they were still higher than original MDF. Therefore, it is suggested that carbonization below $600^{\circ}C$ can improve moisture absorption/desorption capacities.

• Journal of the Korean Wood Science and Technology
• /
• 제10권3호
• /
• pp.133-134
• /
• 1982

This experiment has been made to investigate the absorption of watersoluble zinc chloride by Pinus densiflora S. et Z. at different moisture content, under soaking process, to decide the optimum content condition for the maximum absorption of zinc chloride by the wood tested and to investigate the concentration of zinc chloride affecting each moisture content of wood. Material was cut in the Dept. of Forest, College of Agr. S.N.U. Suwon, Korea. Sample was divided into sap and heartwood group and cut $2{\times}2{\times}2\;cm$ in size, having exact three dimensions, using the part of D.B.H. The numbers of sample were 20 pieces for each moisture content condition for both sap and heartwood. Especially, the samples were protected from exposure to keep moisture content in green condition. The ranges of moisture content tested were as the table 3 and 4. The conclusions were as follows: 1. With 3% zinc chloride solution, the rate of absorption decreased with the time increased, if the air seasoned Korean red pine (Pinus densiflora S. et Z.) was treated in steeping process. Initial absorption for 30 minutes was more than 50% of total absorpon for 24 hours. 2. Rate of absorption was same under the green condition, while rate of absorption under the moisture content 7 to 30% varied. 3. Although it was not quite proportional change in the absorption with the difference of moisture content, the great change in the absorption occured by seasoning. With exception sap green condition, sapwood twice more permeable than the heartwood in the oven dried condition and it has been observed the nearly same amount of absorption at the moisture content of 7%, 10% and 15% respectively in heartwood. 4. It was better from water in wood from view-point of absorption of zinc chloride solution, but it was difficult practically to obtain the smallest moisture content, and then it was decided that values of allowable moisture content, on the basis of mean absorption, were 15% to 20% in the sapwood, and in the heartwood, 10% to 15%. The mean absorption for each moisture content in the sap and the heartwood were as following. 5. In general, the concentration of zinc chloride after steeping was nearly same between moisture content and sap and heartwood respectively.

• Composites Research
• /
• 제21권2호
• /
• pp.1-7
• /
• 2008

복합재료는 현재 항공-우주산업, 스포츠와 레저 산업에서 널리 사용되고 있으나, 흡습에 의해 기계적 성질이 저하하는 문제점을 가지고 있다. 본 연구에서는 이러한 문제점에 대한 규명을 위해 $80^{\circ}C$의 수 환경(담수/해수)에서 $100{\sim}200일$ 동안 침지/침지 - 건조한 시편으로 전단강도를 평가하였다. 그 결과, 전단강도의 하락은 초기에는 수지부의 흡습과 실란부의 흡습에 의한 물성저하 그리고 나중에는 실란부와 섬유와의 기계적 결합의 파괴가 주요원인으로 판단되었다. 결론적으로, 복합재료 내의 수분으로 인해 비가역구간을 넘어서게 되면 수분으로 인한 계면 파괴가 일어나 전단강도 회복이 어려워지는 것으로 판단된다.

• Journal of Electrical Engineering and Technology
• /
• 제13권2호
• /
• pp.892-901
• /
• 2018

Because of excellent electrical properties, epoxy resin is widely used in packaging and casting power equipment. Moisture and temperature in the environment are inclined to seriously affect the insulation tolerance of epoxy resin. This work focuses on the aging characteristics of epoxy resin in hygrothermal environment. Scanning electron microscopy images show that there are micro-crack, micro-slit and holes inside aged samples. The moisture absorption process undergoes three equilibrium stages and it does not follow the Fick's second law. Observing the change of hydrogen bonds in the infrared spectra of the dried samples, it is found that chemically moisture absorption immerges when the physical moisture absorption entered the third equilibrium stage. By Debye equation to fit the imaginary part of the dielectric constant, it is concluded that the uniformity of water molecule has a great influence on the electrical conductivity loss. Furthermore, the polarization loss can be more easily affected by water molecules than small free molecules. After the aged samples being dried, their real and imaginary part of the dielectric constant descend, but their original electrical properties cannot completely restored. After chemical moisture absorption appears inside the material, the residual space charges increase significantly and the charge dissipation rate slow down obviously.

• Journal of the Korean Wood Science and Technology
• /
• 제24권1호
• /
• pp.75-80
• /
• 1996

The purpose of this study is to clarify the mechanism of moisture transfer depend on the thickness of the spruce(Picea sitchensis Carr.). Therefore, as the basic research of moisture transmission, the amount of moisture transmission and the moisture distribution in specimens and temperature of it's surfaces in vapor transmission process were investigated. The experiment was conducted in a steady state. and the moisture distribution was measured by knife cutting and weighing the specimens. The following conclusions were obtained ; 1. It can be found that distribution of moisture in the specimen can be approximated by two different straight lines intersecting at nine or ten percent moisture content. The amount of moisture movement defends on the gradient of moisture in the wood. 2. It is investigated that the wood surface moisture contents(MCs) are less for thinner specimens than for thick ones on the absorption side. On the other hand, the wood surface MCs are greater for thinner specimens than for thick ones on the desorption side. The main factor that affects the EMC of wood would be temperature when the relative humidity of atmosphere is constant. The specimen generate heat with the absorption and desorption process. In addition, the velocities of moisture transmission varied with the thicknesses of specimens. If the temperature of wood becomes greater, its MC decreases. Then the difference between surface MC and EMC of adsorption and desorption side becomes greater for thinner specimens. Therefore it is considered that the coefficients of moisture transfer decreases with the increases of the specimens' thicknesses.

• Advances in aircraft and spacecraft science
• /
• 제6권4호
• /
• pp.315-331
• /
• 2019

The stiffness degradation of the cross-ply composite laminates containing a transverse cracking and delamination in $90^{\circ}$ layer is predicted by using a modified shear-lag model by introducing the stress perturbation function. The prediction shows better agreement with the experimental results published by Ogihara and Takeda 1995, especially for laminates with thicker $90^{\circ}$ plies in which extensive delamination occurs. A homogenised analytic model for average transient moisture uptake in composite laminates containing periodically distributed matrix cracks and delamination is presented. It is shown that the model well describes the moisture absorption in a cross-ply composite laminate containing periodically distributed transverse matrix cracks in the $90^{\circ}$ plies. The obtained results represent well the dependence of the stiffness degradation on the crack density, thickness ratio and moisture absorption. The present study has proved to be important to the understanding of the degradation of the material propertiesin the failure process when the laminates in which the delamination grows extensively.

• 한국농촌건축학회논문집
• /
• 제21권1호
• /
• pp.37-44
• /
• 2019

Recently, various tourist products using hanok have increased rapidly. In the meantime, there is a steady demand for Hanok architecture. However, there are many negative perceptions about wood deformation and biodeterioration. Wood deformation and biodeterioration are related to moisture content. And the cracks occur in the process of removing water from the wood. Therefore, this study investigates the moisture content and cracks of dried hanok made of wood according to the drying method of wood. Drying methods include natural seasoning and artificial seasoning. There was a difference in moisture removal depending on drying period and method of natural seasoning. Drying time should be about 3 years for natural seasoning, so the moisture content of the wood is stable. In addition, the moisture absorption rate was low even in a humid environment where the voids were removed. However, natural seasoning is time consuming. Artificial seasoning, on the other hand, can quickly remove moisture from the wood and reduce porosity, but it is costly. Cracks that occur during the drying of wood may become problematic in appearance and stability due to wider spacing over time. As a result, the difference in the moisture content of the timber depending on the drying method and drying period of the wood was maintained even after the formation. These gaps appeared to be differences in moisture absorption in a wet environment.

• 한국태양에너지학회 논문집
• /
• 제24권1호
• /
• pp.53-61
• /
• 2004

Absorption potential of desiccant solution significantly decreases after absorbing moisture from humid air, and a regeneration process requires a great amount of energy to recover absorption potential of desiccant solution. In an effort to develop an efficient solar water heater, this study examines a regeneration process using hot water obtained from solar water heater to recover absorption potential by evaporating moisture in the liquid desiccant. In this paper, a solar absorption dehumidifying system with solar water heater is suggested to save the electricity for operating an air conditioner. LiGl(lithium chloride) solution was adopted as a liquid desiccant in the proposed system, and hot water obtained from the solar water heater was used for regenerating the liquid desiccant. As a result, it was clear that the dilute LiCl solution could be regenerated by hot water, and the regeneration rate depends mostly on temperature level of liquid desiccant. The regeneration rates were about 2.4kg/h with $40^{\circ}C$, 4.0kg/h with $50^{\circ}C$, and 6.2kg/h with $60^{\circ}C$ of hot water respectively.