We examined soil properties and provenance of loess-paleosol sequences at the Daebo Granite area of Buan, Jeonbuk Province, South Korea. The section consists of the surface layer, Layer 1(paleosol), Layer 2(loess), Layer 3(paleosol), Layer 4(loess), and Layer 5(paleosol), from top to bottom and thickness of the exposed section is approximately 280cm. The magnetic susceptibility values show the distinct variations between the loess- and the paleosol layer. Even though pH, ORP, water content, and soil hardness do not display the obvious differences in the section, the organic content indicates the variation similar to those of the magnetic susceptibility. In the respect of the soil colors measured under 3 conditions, although the variations of the wet soil color exceedingly reflect the difference of the layers, these variations are obscure in some points in the section due to the characteristics of the Munsell color system. Based on the geomorphological properties, sedimentary structure, the difference of the major element composition and the condrite-normalized rare earth element(REE) patterns showing the clear difference from the adjacent bedrocks and stream sediments and the similarity to those of the Chinese Loess Plateau, it is suggested that the section was formed by the material originated from the Chinese Loess Plateau and peripheral areas. However, because the material experienced the alteration after sedimentation under the environment of the sediment area, it has the properties different from the material in the provenance areas. This phenomenon may result in the climatic condition of Korea, especially in precipitation.

• Korean Journal of Materials Research
• /
• v.9 no.12
• /
• pp.1252-1262
• /
• 1999

The effect of microstructures on the strength-flangeability of Nb bearing hot-rolled high strength steel was investigated in order to improve the strength-flangeability of conventional TS 580MPa grades HSLA steel for the automotive wheel disc. The low temperature coiling method using 3-step controlled cooling pattern after hot rolling was effective to produce the Nb-bearing high strength steel with the polygonal ferrite and bainite duplex microstructures. It was suggested that the suppressed precipitation of grain boundary cementites and the decreased hardness difference between ferrite matrix and bainite cause the excellent stretch-flangeability of ferrite-bainite duplex microstructure steel. Therefore, the formation and propagation of microcracks were suppressed relative to the conventional HSLA steel with ferrite and pearlite microstructure. In addition, the elongation was improved as compared with that of hot-rolled steel sheets using conventional early cooling pattern because the volume fraction of polygonal ferrite was increased.

• Journal of Korea Foundry Society
• /
• v.41 no.5
• /
• pp.419-433
• /
• 2021

Al-Si-Cu alloys benefit from the addition of copper for better hardness and strength through precipitation hardening, which results in remarkably strong alloys. However, the addition of copper expands the solidification range of Al-Si-Cu alloys, and due to this, these alloys become more prone to hot tearing, which is one of the most common and serious fracture phenomena encountered during solidification. The conventional evaluation method of the hot tearing properties of an alloy is a relative and qualitative analysis approach that does not provide quantitative data about this phenomenon. In the present study, the mold itself part of a device developed in Instone et al. was partially modified to obtain more reliable quantitative data pertaining to the hot tearing properties of an Al-Si-Cu casting alloy. To assess the influence of Cu element, four levels of Cu contents were tested (0.5, 1.0, 3.0, and 5.0 wt.%) in the Al-Si-Cu system alloy and the hot tearing properties were evaluated in each case. As the Cu content was increased, the hot tearing strength decreased to 2.26, 1.53, 1.18, and 1.04 MPa, respectively. At the moment hot tearing occurred, the corresponding solid fraction and solidification rate decreased at the same temperature due to the increase in the solid-liquid coexistence range as the Cu content increased. The morphology of the fracture surfaces was changed from dendrites to dendrites covered with residual liquid, and CuAl₂ phases were observed in the vicinity of hot tearing.

• Journal of Technologic Dentistry
• /
• v.20 no.1
• /
• pp.37-49
• /
• 1998

The specimens used were Ag-25 Pd-15 Cu ternary alloy and Au addition alloy. These alloys were melted and casted by induction electric furnace and centrifugal casting machine in Ar atmosphere. These specimens were solution treated for 2hr at $800^{\circ}C$ and were then quenched into iced water, and aged at $350{\sim}550^{\circ}C$ Age- hardening characteristics of the small Au-containing Ag-Pd-Cu dental alloys were investigated by means of hardness testing. X-ray diffraction and electron microscope observations, electrical resistance, ergy dispersed spectra and electron probe microanalysis. Principal results are as follows : Hardening occured in two stages, i.e., stage I in low temperature and stage II in high temperature regions, during continuous aging. The case of hardening in stage I was due to the formation of the $L1_0$ type face-centered tetragonal PdCu-ordered phase in the grain interior and hardening in stage I was affected by the Cu concentration. In stage II, decomposition of the ${\alpha}$ solid solution to a PdCu ordered phase($L1_0$ type) and an Ag-rich ${\alpha}2$ phase occurred and a discontinuous precipitation occurred at the grain boundary. From the electron microscope study, it was conclued that the cause of age-hardening in this alloy is the precipitation of the PdCu ordered phase, which has AuCu I type face-centered tetragonal structure. Precipetation procedure was ${\alpha}{\to}{\alpha}+{\alpha}_2+PdCu {\to}{\alpha}_1+{\alpha}_2+PdCu$ at Pd/Cu = 1.7 Ag-Pd-Cu alloy is more effective dental alloy as ageing treatment and is suitable to isothermal ageing at $450^{\circ}C$.

• Korean Journal of Fisheries and Aquatic Sciences
• /
• v.18 no.6
• /
• pp.538-544
• /
• 1985

This study was carried cut to evaluate the water quality of spring waters in Pusan area(see Fig. 1). In this experiment, twenty-five water samples were collected from 5 stations from December 1983 to August 1984. Range and mean values of constituents of the samples are as follows: pH $5.80{\sim}7.25$, 6.60; water temperature $6.0{\sim}23.0^{\circ}C,\;12.9^{\circ}C$; total residue $33.0{\sim}325mg/l$, 121.2mg/l; alkalinity $4.75{\sim}51.6mg/l$, 24.1mg/l; hardness $9.47{\sim}85.0mg/l$, 30.3mg/l; electrical conductivity $0.495{\sim}2.750{\times}^2{mu}{\mho}/cm,\;1.239{\times}10^2{\mu}{\mho}/cm$;turbidity $0.54{\sim}7.80$NTU, 2.04NTU; $KMnO_4$ consumed $0.51{\sim}8.47mg/l$, 1.96mg/l; chloride ion $4.91{\sim}36.0mg/l$, 12.55mg/l; fluoride ion ND-0.30ppm, 0.08ppm; nitrate-nitrogen ND-8.94mg/l, 1.94m:g/l; nitrite-nirogen ND-0.10mg/l, 0.03mg/l; ammonia-nitrogen ND-0.16mg/l, 0.03mg/l: phosphate-phosphorus ND-0.09mg/l, 0.03mg/l; silicate-silicious $0.42{\sim}22.7ng/l$, 7.96mg/l; copper ND-10.5ppb, 2.46ppb; lead ND-22.7ppb, 3.54ppb; zinc ND-103ppb, 21.33ppb; iron $20.3{\sim}2,800ppb$, 801.72ppb, respectively. Arsenic, cyan, cadmium, manganese, mercury, chrome and phenol were not detected. Total residue, electrical conductivity, turbidity and chloride ion of station 1 (Milrakdong) were higher than others as 178.1mg/l, $2.127{\times}10^2{\mu}{\mho}/cm$, 3.16NTU and 16.32mg/l. The concentration of silicious had a great influence on precipitation. The concentration of fluoride ion of spring waters was lower as 0.08ppm than the criterion for drinking water as 1ppm, while iron was exceed 2.7 times as 801.72ppb.