• Journal of Welding and Joining
• /
• v.3 no.2
• /
• pp.16-26
• /
• 1985

Post weld heat treatment(PWHT), at more than 600.deg. C, is essential to remove residual stress and hydrogen in weld HAZ and improve fatigue characteristics. However, residual stress during PWHT is responsible for PWHT embitterment and it promotes precipitation of impurities to grain boundary. In this paper, the effect of stress simulated residual stress on fatigue failure was evaluated by fatigue test, microhardness test and fractograph. The obtained results are summarized as follows; (1) The fatigue crack growth rate(da/dN) of parent and heat treated parent was affected by microstructure due to heat treatment and it depended on stress intensity factor (.DELTA.k). (2) The fatigue strength of weld HAZ was dependent on applied stress during PWHT and da/dN after PWHT was slower than as-weld. (3) Softening amount of weld HAZ was bigger than any other due to PWHT. Hardness value of weld HAZ was affected by heat treatment under the applied stress of 10 $kgf/mm^2$, but beyond 20 $kgf/mm^2$ it was increased by the applied stress rather than heat treatment. (4) Beyond the applied stress of 20 $kgf/mm^2$ during PWHT, intergranular fracture surface was observed and its amount was increased with applied stress during PWHT. (5) Effect of applied stress during PWHT on aspect of fracture surface was larger rather than that on fatigue crack growth behavior.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1181-1182
• /
• 2006

Y-type barium ferrite $(Ba_2Zn_2Fe_{12}O_{22})$ was prepared by the glass-ceramic method. Glasses with composition of $0.1ZnO{\cdot}0.9(0.3Fe_2O_3{\cdot}0.5BaO{\cdot}0.2B_2O_3)$ were prepared, and the precipitation behavior of Y-type ferrite from the glass matrix was investigated by heating glass specimens at various temperature. $\alpha-BaFe_2O_4$ which is a precursor of M-type ferrite $(BaFe_{12}O_{19})$ was precipitated at about 813 K and an unknown compound, phase X, was precipitated at about 850 K. M-type ferrite and Y-type ferrite started to form at about 923 K and 1103 K, respectively. The formation of Y-type ferrite was int erpreted as the result of the reaction of M-type ferrite with a melt of phase X.

• Journal of the Korean Ceramic Society
• /
• v.44 no.9
• /
• pp.517-523
• /
• 2007

For the preparation of tricalciumaluminate $(C_3A)$ clinker, in traditional clinkering method using oxides and carbonates as a raw material, uneconomical repetition of burning have been necessary to avoid the melting of clinker by eutectic reaction in the system $CaO-Al_2O_3$. In this study, special starting raw materials for the clinker burning were prepared from a mixture of oyster shell and aluminium hydroxide by heating to $1100^{\circ}C$ and hydrating at $30^{\circ}C$. The starting raw materials, hardened body with weak hydraulic strength, were mainly composed of $C_3AH_6$ formed by resolution-precipitation mechanism of the system $CaO-Al_2O_3-H_2O$. By heating them, relatively pure $C_3A$ clinker could be obtained by one-time burning at the fairly lower temperature than that of conventional method. The easier formation of $C_3A$ clinker seemed to be caused by higher compositional homogeneity and stoichiometry of the starting materials, high surface area and crystallographic instability of the thermally decomposed products, and the catalytic effect of decomposed moisture on the early-stage crystallization of calciumaluminates. The basic hydration behavior of the clinker was also confirmed.

• Korean Chemical Engineering Research
• /
• v.56 no.5
• /
• pp.694-704
• /
• 2018

Novel $SnO_2$ mixed biochar composite was prepared from banana peel developed as electrode material for supercapacitor using simple chemical co-precipitation method. The physiochemical and morphological properties of activated composite $SnO_2$ mixed biochar were investigated with XRD, FTIR, UV-vis, FESEM and HRTEM. The composite accounts for outstanding electrochemical behavior such as high specific capacitance, significant rate capability and leading to good cycle retention up to 3500 cycles when used as electrode material for supercapacitors. Highly permeable $SnO_2$ mixed biochar derived from banana peel exhibited maximum specific capacitance of $465F\;g^{-1}$ at a scan rate of $10mV\;s^{-1}$ by cyclic voltammetry (CV) and $476Fg^{-1}$ at current density of $0.15Ag^{-1}$ by charge discharge studies significantly higher about 47% than previously reported identical work on banana peel biochar.

• KSBB Journal
• /
• v.16 no.4
• /
• pp.370-375
• /
• 2001

For the production of new exo-biopolymers from microorganisms, an exe-biopolymer producing bacterial strain was isolated from the composter used in composting of organic wastes. Bacteriological properties of this strain and physicochemical properties of producing exo-biopolymer were investigated. The isolated strain was identified as Enterobacter sp. through its morphological, cultural and physiological characteristics. The results of color reactions, CPC (cetyl pyridinium chloride) precipitation and infra red absorption spectral analysis indicated that this exo-biopolymer was presumed as an acidic polysaccharide with uronic acid. This polysaccharide was identified as hetero-polysaccharide consisting of galactose, mannose and galacturonic acid by gas chromatography, and the molecular weight of exopolysaccharide purified by gel chromatography were about 370,000 daltons. The polysaccharide solutions(0.50-2.0%, w/v) exhibited non-Newtonian flow behavior with pseudoplastic property and showed the ability of gel formation at above 1.5% (w/v) of polysaccharide concentration.

• Korean Journal of Materials Research
• /
• v.21 no.6
• /
• pp.303-308
• /
• 2011

The effect of heat treatment on the micro-structures and the mechanical properties of 0.002% boron added low carbon steel was investigated. The tensile strength reached the peak at about $880-890^{\circ}C$ with the rising quenching temperature and then the hardness decreased sharply, but the tensile strength hardly decreased. The tensile and yield strength decreased and the total elongation increased with a rising tempering temperature, but the tensile and yield strength sharply fell and the total elongation prominently increased from above a $400-450^{\circ}C$ tempering temperature. Tempered martensite embrittlement (TME) was observed at tempering condition of $350-400^{\circ}C$. In the condition of quenching at $890^{\circ}C$ and tempering at $350^{\circ}C$, the boron precipitates were observed as Fe-C-B and BN together. The hardness decreased in proportion to the tempering temperature untill $350^{\circ}C$ and dropped sharply above $400^{\circ}C$ regardless of the quenching temperature.

• Macromolecular Research
• /
• v.12 no.3
• /
• pp.263-268
• /
• 2004

We have synthesized a water-soluble polyimide precursor, poly(amic acid) amine salt (PAD), from pyromellitic dianhydride (PMDA), 4,4'-oxydianiline, and N,N -dimethylethanolamine (DMEA) and have investigated in detail its properties with respect to the degree of salt formation (D$\_$sf/). The maximum value of D$\_$sf/ we obtained upon precipitation of the precursor solution into acetone was 79%. We synthesized a PAD having a D$\_$sf/ of 100% (PAD100) by the solid state drying of an organic solution. The precursors showed different solubility depending on the D$\_$sf/ to make up to 4 wt% solutions in water containing a small amount of DMEA. PAD100 is completely soluble in pure water. We investigated the imidization behavior of PAD in aqueous solution using various spectroscopic methods, which revealed that PAD 100 has faster imidization kinetics relative to that of the poly(amic acid)-type precursors. The resulting polyimide films prepared from an aqueous precursor solution possess almost similar physical and thermal properties as those prepared from N-methyl-2-pyrrolidone(NMP) solution. Therefore, we have demonstrated that PAD can be used as a water-based precursor of polyimide; this procedure avoids the use of toxic organic solvents, such as NMP.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1995.06a
• /
• pp.151-151
• /
• 1995

Nitrogen implantation process has been applied for improvement of wear resistance of Z Zircaloy-4 fuel cladding materials. Nitrogen was implanted at 120 ke V to a total do range of 1xHP ions/cm2 to 8xlO17 ions/cm2 at various temperatures of 298"C to 676"C. The m microstructure changes by nitrogen implantation were analyzed by using TEM, XRD 뻐d A AES, cmd then wear behavior was evaluated by ball-on-disc wear testings at various loads a and sliding velocity under unlubricated condition. Nitrogen implantation produced ZrNx nitride above 4.37x1017 ions!cm2 as well as heavy d dislocations, which enhanced microhardness of the implanted surface of up to 900 Hk from 2 200 Hk of unimplanted substrate. Hardness was also found to be increased with increasing i implantation temperature and enhanced up to OOOHk at 620 "C. the wear resistance was g greatly improved with increasing total ion do않 as well as implantation temperature. The effective enhancement of wear resistance at high dose and tem야ratures is believed d due to significant hardening associated with high degree of precipitation of Zr nitrides and g generation of prismatic dislocation I$\infty$ps.infty$ps.

• 연구논문집
• /
• s.24
• /
• pp.161-174
• /
• 1994

The Ni-Al intermetallic compound that has the greatest potential to be commercialized shows the high ductility at room temperature with the addition of boron, but has extremely low ductility at high temperature and oxidation environment. On this research work, the changes of microstructure and compressive fracture properties were studied in ($NiAl+Ni_3Al$) two-phase alloys. The precipitation behavior of $Ni_3Al$ after solution treatment at $1300^\circC$ for 14hrs and aging treatment at $800^{\circ}C$ for 14hrs was varied with Al content in ($NiAl+Ni_3Al$) two-phase alloys. These microstructure could be modified dramatically by suitable heat treatments. Martensite or martensite plus $Ni_3Al$ microstructure was obtained upon oil quenching from $1300^\circC$. Aging of Martensite at $800^\circC$ resulted in the $Ni_3Al$ plus NiAl phase. The compressive fracture strength and compressive fracture strain were improved by the $Ni_3Al$ plus NiAl phase mixtures at room temperature and $1100^\circC$. Microcracks are observed mostly in the region of NiAl and the interface of $NiAl-Ni_3Al$ phase after compressive test at room temperature. In the case of high temperature compressive test, microcracks are formed in the region of $Ni_3Al$ phase.

• Journal of Power System Engineering
• /
• v.6 no.1
• /
• pp.61-67
• /
• 2002

15Cr-5Ni 석출강화 스테인리스강 3종류의 피로균열 발생과 성장 특성 및 파괴인성에 대하여 노치함수로서 연구하였다. 3종류강의 열처리 조건은 $482\;^{\circ}C,\;579\;^{\circ}C$ 및 $621\;^{\circ}C$이다. $621\;^{\circ}C$에서 4시간동안 열처리한 시험편 C는 약 $280\;MPa\;\sqrt{m}$의 가장 높은 파괴인성을 보였으며, 3종류에서 피로균열 성장이 가장 늦었다. $482\;^{\circ}C$에서 1시간 열처리한 시험편 A에서, 피로균열발생한계, ${\Delta}k{\rho}$, 는 노치반경0.3 mm에서 약 $280\;MPa\;\sqrt{m}$의 가장 높은 값을 보였다. 시험편 A는 시험편 B와 C보다 피로균열 성장이 빨랐지만, 피로균열 발생이 늦었다. 예 하중에 의한 노치선단의 압축잔류응력은 노치 시험편의 피로강도 향상에 유용한 방법이었다.