• Korean Journal of Metals and Materials
• /
• v.49 no.6
• /
• pp.448-453
• /
• 2011

Pre-aging heat treatment after solution heat treatment (SHT) of Al-0.4 wt%Mg-1.2 wt%Si-0.1 wt%Mn alloy sheets for auto-bodies was carried out to investigate the effect of pre-aging and its conditions on the bake-hardening response. Mechanical properties were evaluated by a tensile and Vickers hardness test. Microstructural observation was also performed using a transmission electron microscope (TEM). It was revealed that pre-aging treatments play a great role in the bake-hardening response. In addition, it was found that the sphere-shaped nanosized clusters that can directly transit to the needle-shaped ${\beta}$" phase during the paint-bake process, not being dissolved into the matrix, are formed at 343 K. The result, reveals that the dominant factor of the bake-hardening response is the pre-aging temperature rather than the pre-aging time.

• Proceedings of the SCSK Conference
• /
• 2003.09a
• /
• pp.73-84
• /
• 2003

Skin aging process on pre-menopausal women is a problem that needs to be prevented as early as possible. The decrease of oestrogen level which is one of the intrinsic factors of the skin aging process will affect the skin biological process, due to oestrogen receptors on the skin. A number of researches conducted on pre-menopausal women with the allocation of oestrogen hormone resulted in delaying the skin aging process. The administration of soy isoflavon, a phytoestrogen found in daily food, on pre-menopausal women is hoped to be able to prevent skin aging process, even clinically or molecular biologically. This research aims to explain the benefit of administering of soy isoflavon on skin aging process. The design of the research is randomised controlled trial (RCT). As many as 60 pre-menopausal women were collected with simple random sampling method. Soy isoflavon is an independent variable, while skin aging process is a dependent variable assessed from the hydration, sebum level, average roughness, depth of wrinkles, skin clarity, length of the telomere. Analysis was conducted using t and MANDVA tests and.the result showed a significance (F = 10,439; p = 0,001) over the allocation of soy isoflavon to the whole variable dependent, including the telomere length and the skin hydration, meant that allocation of soy isoflavon could delay skin aging process.

• Journal of the Korean Society for Heat Treatment
• /
• v.7 no.4
• /
• pp.270-276
• /
• 1994

The effects of thermomechanical and duplex aging treatment on precipitation behavior were investigated for the 8090 aluminium alloy by tensile test, hardness test, plane-strain fracture toughness test and electron microscope. Both pre-aging stretch and duplex aging with pre-aging stretch were effective to homogenize the distribution of S' phase in this alloys. The latter makes more homogeneous distribution of S' phase than that of the former, but the sizes of S' phase in both specimens are almost same. The size and distribution of 0' phase were not changed by thermomechanical or duplex aging treatment. The strength was increased by thermomechanical treatment, but the elongation was decreased. Duplex aging treatment couldn't change the strength and elongation. Pre-aging stretch and duplex aging with pre-aging stretch have same effect on the strength and elongation. The increase of strength by thermomechanical treatment in 8090 alumunium alloy was caused by homogeneously precipitated S' phase.

• KOREAN JOURNAL OF CROP SCIENCE
• /
• v.59 no.4
• /
• pp.406-412
• /
• 2014

The influence of rainfall during the ripening stage on pre-harvest sprouting, seed viability, and seed quality was investigated in two Korean rice cultivars, Shindongjin and Hopum. When the rainfall was artificially treated in a greenhouse, HP started to pre-harvest sprouting at three days of rainfall treatment (DRT), but Shindongjin did not show pre-harvest sprouting at 40 DAH treatment and just 0.3~0.8% at 50 DAH, which was much lower than 15.3~25.8% of Hopum in the same treatment. After harvest, the seed germination of Hopum decreased about 10~25% compared to non-treated seeds, but that of Shindongjin decreased much little rate than that of Hopum. The seed longevity tested by accelerated aging decreased with prolonged rainfall period in both cultivars, but the varietal difference was clear; Shindongjin could withstand longer accelerated aging than Hopum. Shindongjin maintained its germination (>50%) ability after 15 days of accelerated aging regardless of the rainfall treatment period and time, but Hopum dropped below 50% germination ability after only 5 days of accelerated aging. In conclusion, rainfall during the ripening stage induced not only pre-harvest sprouting, but also reduced seed quality and longevity during storage, which varied between two cultivars.

• Journal of the Korean Society for Heat Treatment
• /
• v.36 no.5
• /
• pp.285-297
• /
• 2023

The effects of aging treatment sequence, specifically pre-aging and post-aging, on the microstructure and mechanical properties of Al-Zn-Mg-Cu aluminum alloys has been studied in comparison to symmetrically rolled specimens. In symmetrically rolled specimens, a straight-band precipitation distribution was observed, whereas asymmetrically rolled specimens exhibited a curved-band microstructure of fine precipitates. Notably, the asymmetrically rolled specimens displayed higher strengths. In the case of post-aging, the aging process occurred after rolling, and the dislocations generated during rolling acted as nucleation sites for precipitates during aging. This resulted in the formation of fine precipitates, contributing to improved mechanical properties compared to symmetric rolling. To enhance strength of the Al-Zn-Mg-Cu aluminum alloys, asymmetric rolling proves to be more effective than symmetric rolling, with post-aging showing greater efficacy than pre-aging.

• Korean Journal of Materials Research
• /
• v.27 no.10
• /
• pp.524-529
• /
• 2017

The effect of strain aging on the tensile properties of API X70 linepipe steel was investigated in this study. The API X70 linepipe steel was fabricated by controlled rolling and accelerated cooling processes, and the microstructure was analyzed using optical and scanning electron microscopes and electron backscatter diffraction. Strain aging tests consisting of 1 % pre-strain and thermal aging at $200^{\circ}C$ and $250^{\circ}C$ were conducted to simulate U-forming, O-forming, Expansion(UOE) pipe forming and anti-corrosion coating processes. The API X70 linepipe steel was composed of polygonal ferrite, acicular ferrite, granular bainite, and bainitic ferrite whose volume fraction was dependent on the chemical composition and process conditions. As the thermal aging temperature increased, the steel specimens showed more clearly discontinuous type yielding behavior in the tensile stress-strain curve due to the formation of a Cottrell atmosphere. After pre-strain and thermal aging, the yield and tensile strengths increased and the yield-to-tensile strength ratio decreased because yielding and aging behaviors significantly affected work hardening. On the other hand, uniform and total elongations decreased after pre-strain and thermal aging since dislocation gliding was restricted by increased dislocation density after a 1 % pre-strain.

• Journal of the Korean Society of Mechanical Technology
• /
• v.20 no.6
• /
• pp.818-823
• /
• 2018

In this study, the effect of pre-aging treatment for inhibition of natural aging of Al-4.8Zn-1.3Mg alloy by extrusion process was investigated. Firstly, the as-cast microstructure of Al-4.8Zn-1.3Mg alloy billet and its evolution during homogenization($460^{\circ}C$, $4h+510^{\circ}C$, 5h) were investigated by means of optical microscopy (OM), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), hardness analysis. The as-cast microstructures of Al-4.8Zn-1.3Mg alloy reveal $Mg_2Zn$, $Al_5Cu$, $Al_{13}Cu$ formed between dendrities. After homogenization, MgZn, $Al_4Cu$, $Al_{13}Cu$ phases precipitated into the matrix. In addition, standard deviation of homogenized billet was improved than as-cast billet from 2.62 to 0.99. According to pre-aging($100^{\circ}C$, 1h) Al-4.8Zn-1.3Mg alloy by extrusion process, yield strength and tensile strength deviation improved more than condition by natural aging.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.19 no.2
• /
• pp.402-407
• /
• 1995

The effects of room temperature and strain aging treatment are discussed on the critical condition for the onset of growth of non-propagating cracks on 0.15% C low carbon steel, with special emphasis on the length of the critical non-propagating crack and on the crack opening displacement(COD) at the crack tip. It is found from the experimental analysis that room temperature and strain aging of a fatigue pre-cracked specimen introduced the closure of a crack tip of the pre-crack and the reduction of crack opening displacement at the wake of crack, together with an improvement in crack growth resistance of the microstructure. This may cause an increase in the endurance limit of the specimen, through the enhancement of effective stress for the onset of growth of the critical non-propagating crack.

• Food Science of Animal Resources
• /
• v.36 no.2
• /
• pp.159-169
• /
• 2016

Animal muscles are stored for specific period (aging) at refrigerated temperatures, during and after which the living muscles start to convert into meat and thus, attain certain superior properties in the final product. Proteolysis, lipolysis, and oxidation are the major biochemical processes involved during the postmortem aging of meat that affect the tenderness, juiciness, and flavor, as well as sometimes may introduce certain undesirable traits. This review analyzes the role of pre- and post-mortem factors that are important for aging and their effect on the chemical and physical changes in the “dry- and wet-aged meat.” Thus, if the meat processing manufacturers optimize the effects of aging for specific muscles, the palatability, color, and the shelf life of the aged meat products could be significantly enhanced.

• Korean Journal of Materials Research
• /
• v.28 no.12
• /
• pp.702-708
• /
• 2018

This study deals with the effect of microstructure factors on the strain aging properties of API X70 pipeline steels with different microstructure fractions and grain sizes. The grain size and microstructure fraction of the API pipeline steels are analyzed by optical and scanning electron microscopy and electron backscatter diffraction analysis. Tensile tests before and after 1 % pre-strain and thermal aging treatment are conducted to simulate pipe forming and coating processes. All the steels are composed mostly of polygonal ferrite, acicular ferrite, granular bainite, and bainitic ferrite. After 1 % pre-strain and thermal aging treatment, the tensile test results reveal that yield strength, tensile strength and yield ratio increase, while uniform elongation decreases with an increasing thermal aging temperature. The increment of yield and tensile strengths are affected by the fraction of bainitic ferrite with high dislocation density because the mobility of dislocations is inhibited by interaction between interstitial atoms and dislocations in bainitic ferrite. On the other hand, the variation of yield ratio and uniform elongation is the smallest in the steel with the largest grain size because of the decrease in the grain boundary area for dislocation pile-ups and the presence of many dislocations inside large grains after 1 % pre-strain.