• Corrosion Science and Technology
• /
• v.21 no.5
• /
• pp.340-347
• /
• 2022

In this research, mixed metal oxide (TiO₂, RuO₂) coating was applied to grade 1 titanium as a bipolar plate for polymer electrolyte membrane fuel cell (PEMFC). Electrochemical experiments were carried out in an aqueous solution of pH 3 (H₂SO₄ + 0.1 ppm HF, 80 ℃) determined by DoE. The air was bubbled to simulate a cathode environment. Potentiodynamic polarization test revealed that corrosion current densities of the titanium substrate and MMO-coated specimen were 0.180 µA/cm² and 4.381 µA/cm², respectively. There was no active peak. After potentiostatic experiment, current densities of the titanium substrate and the MMO-coated specimen were 0.19 µA/cm² and 1.05 µA/cm², respectively. As a result of observing the surface before and after the potentiostatic experiment, cracked dried clay structures were observed without corrosion damage. Both the titanium substrate and the MMO-coated specimen could not satisfy the interfacial contact resistance suggested by the DoE. Thus, further research is needed before they could be applied as bipolar plates.

• Corrosion Science and Technology
• /
• v.20 no.6
• /
• pp.451-465
• /
• 2021

In this investigation, electrochemical characteristics and damage behavior of 316L stainless steel polymer electrolyte membrane fuel cell(PEMFC) were analyzed by potentiodynamic and potentiostatic tests in cathode operating condition of PEMFC. As the result of potentiodynamic polarization test, range of passive region was larger than range of active region. In the result of potentiostatic test, damage depth and width, pit volume, and surface roughness were increased 1.57, 1.27, 2.48, and 1.34 times, respectively, at 1.2 V compared to 0.6 V at 24 hours. Also, as a result of linear regression analysis of damage depth and width graph, trend lines of damage depth and width according to applied potentials were 16.6 and 14.3 times larger, respectively. This demonstrated that applied potential had a greater effect on pitting damage depth of 316L stainless steel. The damage tendency values were 0.329 at 6 hours and 0.633 at 24 hours with applied potentials, representing rapid growth in depth direction according to the test times and applied potentials. Scanning electron microscopy images revealed that surface of specimen exhibited clear pitting damage with test times and applied potentials, which was thought to be because a stable oxide film was formed by Cr and Mo.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.254-254
• /
• 2012

The purposed of this work was to determine surface charateristics of anodized Ti-30Nb-xTa alloys with Ta content. Samples were prepared by arc melting, followed by followed by homogenization for 12 hr at $1000^{\circ}C$ in argon atmosphere. The electrolyte for anodization treatment was prepared by mixing 465ml $H_2O$ with 35M $H_3PO_4$ and anodized at 180V to 220V. The microstructures of the alloys were examined by X-ray diffractometer (XRD) and optical microscopy (OM). Surface characteristics of anodized Ti-30Nb-xTa alloys was investigated by potentiodynamic test and potentiostatic in 0.9% Nacl solution at $36.5{\pm}1^{\circ}C$. It was observed that the changed ${\alpha}$ phase to ${\beta}$ phase with Ta content.

• Journal of Electrochemical Science and Technology
• /
• v.2 no.2
• /
• pp.76-84
• /
• 2011

Potentiostatic oxidation of Pb-1.7%Sb alloy used in the manufacture of grids of lead-acid batteries over the potential range from -1.0V to 2.3V in 5M $H_2SO_4$ in the absence and the presence of 0.4M $H_3PO_4$ and the self-discharge characteristics of the oxide layer formed is studied by electrochemical impedance spectroscopy (EIS). Depending on the potential value, sharp variations in resistance and capacitance of the alloy are recorded during the oxidation and they can be used for identification of the various substances involved in passive layer. Addition of $H_3PO_4$ is found to deteriorate the insulating properties of the passive layer by the retardation of the formation of $PbSO_4$. $H_3PO_4$ completely inhibits the current and impedance fluctuations recorded in $H_3PO_4$-free solutions in the potential range 0.5 V-1.7 V. These fluctuations are attributed to the occurrence of competitive redox processes that involve the formation of $PbSO_4$, $PbOSO_4$, PbO and $PbO_2$ and the repeated formation and breakdown of the passive layer. Self-discharge experiments indicate that the amount of $PbO_2$ formed in the presence of $H_3PO_4$ is lesser than in the $H_3PO_4$-free solutions. The start of transformation of $PbSO_4$ into $PbO_2$ is greatly shortened. $H_3PO_4$ facilitates the diffusion process of soluble species through the passive layer ($PbSO_4$ and basic $PbSO_4$) but impedes the diffusion process through $PbO_2$.

• Corrosion Science and Technology
• /
• v.20 no.6
• /
• pp.435-450
• /
• 2021

The interest in eco-friendly energy is increasing, and polymer electrolyte membrane fuel cell (PEMFC) is attracting attention as alternative power sources. Research on metallic bipolar plates, a fuel cell component, is being actively conducted. However, since the operating conditions of PEMFC, in which sulfuric acid (H₂SO₄) and hydrofluoric acid (HF) are mixed, are strong acidity, the durability of the metallic bipolar plate is very important. In this research, the electrochemical characteristics and corrosion damage behavior of 316L stainless steel, a material for metallic bipolar plates, were analyzed through potentiostatic corrosion tests with test times and chloride concentrations. As the test times and chloride concentrations increased, the current density and corrosion damage increased. As a result of observation with scanning electron microscope(SEM) and 3D microscope, both the depth and width of pitting corrosion increased with increases in test times and chloride concentrations. In particular, the pitting corrosion damage depth at test conditions of 6 hours and 1000 ppm chloride increased the most. The growth of the pitting corrosion damage was not directly proportional to time and increased significantly after a certain period.

• Journal of the Korean Electrochemical Society
• /
• v.9 no.4
• /
• pp.158-169
• /
• 2006

The present article is concerned with the overview of the chemically/surface modified cubic spinel $LiMn_2O_4$ as a cathode electrode far lithium ion secondary batteries. Firstly, this article presented a comprehensive survey of the cubic spinel structure and its correlated electrochemical behaviour of $LiMn_2O_4$. Subsequently, the various kinds of the chemically/surface modified $LiMn_2O_4$ and their electrochemical characteristics were discussed in detail. Finally, this article reviewed our recent research works published on the mechanism of lithium transport through the chemically/surface modified $Li_{1-\delta}Mn_2O_4$ electrode from the kinetic view point by the analyses of the experimental potentiostatic current transients and ac-impedance spectra.

• Journal of the Korean Electrochemical Society
• /
• v.6 no.3
• /
• pp.187-195
• /
• 2003

The present article is concerned with the overview of carbonaceous materials used as anode materials for lithium ion secondary batteries. This article first classified carbonaceous materials into graphite, soft carbon and hard carbon according to their crystal structures, and then summarised the previous works on the characteristics of lithium intercalation/deintercalation into/from the carbonaceous materials. Finally this article reviewed our recent research works on the mechanism of lithium transport through graphite, soft carbon and hard carbon electrodes from the kinetic view point by the analysis of the theoretical and experimental potentiostatic current transients.

• Nuclear Engineering and Technology
• /
• v.56 no.1
• /
• pp.42-47
• /
• 2024

The electrochemical extraction of uranium in ternary low melting LiCl-KCl-CsCl eutectic on inert and reactive electrodes via different electrochemical techniques was investigated. It was established that the electrochemical reduction process of U(III) ions on the inert W electrode was irreversible and proceeded in one stage. On reactive liquid Ga and liquid Cd electrodes the reduction of uranium ions took place with the considerable depolarization with the formation of UGa₂, UGa₃ and UCd₁₁ intermetallic compounds. Thermodynamic characteristics of uranium compounds and alloys were calculated. The conditions for the extraction of uranium from the electrolyte in the form of alloys on both liquid reactive electrodes via potentiostatic electrolysis were found.

• Journal of the Korean Society for Heat Treatment
• /
• v.9 no.2
• /
• pp.103-111
• /
• 1996

In this paper, we studied on both electrochemical polarization behaviors and pitting characteristics of ultra high strength Al-Cu-Li-Mg-Ag-Zr alloys(named C1 and C2) and 2090 alloy according to their treatments in the deaerated 3.5% NaCl, using by the potentiodynamic and the potentiostatic method, SEM micrograph and surface roughness including depth of pitting attack. With the cyclic polarization curves, the hysteresis of the C1 and C2 alloys appeared more remarkably than that of the 2090 alloy, because of precipitation microstructural difference between C1, C2 alloys and 2090 alloy. In the pitting experiments, the correlations between pitting growth and aging conditions were analyzed with the SEM micrograph and measurement of the pit depth.

• Journal of the Korean institute of surface engineering
• /
• v.44 no.6
• /
• pp.277-283
• /
• 2011

In this study, the cavitation test and electrochemical experiments were conducted for ALBC3(Cu-Al) alloy that has an excellent corrosion resistance and cavitation characteristic in sea water. Based on the ASTMG32 regulation, the cavitation test was performed with the cavitation and cavitation erosion tester using piezoelectric effect. The electrochemical characteristics are evaluated with potentiostatic experiments in activation polarization potential range. As a result, cavitation damage is increased proportionally to temperature and time at $30{\mu}m$ amplitude. It is appeared that acceleration period in weight loss presented over 6 hours under the cavitation environment in sea water. In addition, corrosion damages were observed at the potential range of -3.2~-1.4 V as the result of potensiostatic experiments during 12 hours in activation polarization potential range.