• 한국표면공학회지
• /
• 제54권5호
• /
• pp.248-259
• /
• 2021

This study examined the influence of post weld heat treatment (PWHT) conditions on corrosion behaviors of laser-welded super duplex stainless steel tube. Due to the high cooling rate of laser welding, the phase fraction of ferrite and austenite in the weld metal became unbalanced significantly. In addition, the Cr₂N particles were precipitated adjacent to the fusion line, which can be susceptible to the localized corrosion. On the other hand, the phase fraction in the weld metal was restored at a ratio of 5:5 when exposed to temperatures above 1060 ℃ during the post weld heat treatment. Nevertheless, the high beltline speed during the PWHT, leading to the insufficient cooling rate, caused a precipitation of σ phase at the interface between ferrite/austenite in both weld metal and base metal. This resulted in the severe corrosion damages and significant decrease in critical pitting temperature (CPT), which was even lower than that measured in as-welded condition. Moreover, the fraction of σ phase in the center region of post weld heat treated steel tube was obtained to be higher than in the surface region. These results suggest that the PWHT conditions for the steel tube should be optimized to ensure the high corrosion resistance by excluding the precipitation of σ phase even in center region.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2007년도 추계학술대회 논문집
• /
• pp.65-70
• /
• 2007

Welding is the most commonly used method to produce bogie and carbody of Electrical Multiple Units(EMU), because it increases the strength and lowers the weight of EMU. Since bogies are constantly exposed to repeated reacting load during acceleration and deceleration, it is also true that crack normally occurs at welding parts. In this study, we have investigated the fatigue strength of SS400 on welded parts in order to find efficiency of treatment after welding by shot peening and Post-Weld heat treatment(PWHT) with butt welded specimens. The results of fatigue test indicate that the measurement of base material specimen is 236MPa, welded specimen is 132MPa and the specimen of PWHT is 107MPa approximately. We concluded that the measurement of welded specimen and PWHT is approximately 44 and 54 percents lower than the base material specimen, respectively. Another finding is that the peened specimen is approximately 23 and 61 percents higher than the base material specimen in terms of the fatigue in strength of specimens.

• 한국정밀공학회지
• /
• 제33권7호
• /
• pp.551-558
• /
• 2016

Reduction of welding residual stress is very important in the railway industry, but calculating its distribution in structures is difficult because welding residual stress formation is influenced by various parameters. In this study, we developed a finite element model for simulating the repair welding process to recover a surface damaged rail, and conducted a series of parametric studies while varying the cooling rate and the duration of post weld heat treatment (PWHT) to find the best conditions for reducing welding residual stress level. This paper presents a three-dimensional model of the repair welding process considering the phase transformation effect implemented by the ABAQUS user subroutine, and the results of parametric studies with various cooling rates and PWHT durations. We found that heat treatment significantly reduced the residual stress on the upper rail by about 170 MPa.

• Journal of Welding and Joining
• /
• 제34권3호
• /
• pp.52-60
• /
• 2016

Recently nickel based superalloys are extensively being regarded as the materials for the steam turbine parts for hyper super critical (HSC) power plants working at the temperature over $700^{\circ}C$, since the materials have excellent strength and corrosion resistance in high temperature. In this paper, alloy 617 of solution strengthened material and alloy 263 of ${\gamma}^{\prime}$-precipitation strengthened material were prepared as the testing materials for HSC plants each other. Post weld heat treatment (PWHT) was conducted with the gas tungsten arc (GTA) welded specimens. The microstructure of the base metals and weld metals were investigated with Electron Probe Micro-Analysis (EPMA) and Scanning Transmission Electron Microscope (STEM). The experimental results revealed that Ti-Mo carbides were formed in both of the base metals and segregation of Co and Mo in both of the weld metals before PWHT and PWHT leaded to precipitation of various carbides such as Mo carbides in the specimens. Furthermore, fine ${\gamma}^{\prime}$ particles, that were not precipitated in the specimens before PWHT, were observed in base metal as well as in the weld metal of alloy 263 after PWHT.

• Journal of Welding and Joining
• /
• 제28권5호
• /
• pp.51-57
• /
• 2010

Brittle microstructure created in a heat affected zone (HAZ) during the welding of low alloy steel can be eliminated by post-weld heat treatment (PWHT). If the PWHT is not possible during a repair welding, the controlled bead depositions of multi-pass welding should be applied to obtain tempering effect on the HAZ without PWHT. In order to anticipate and control the tempering effect during the temper bead welding, the definition of temperature curve obtained from the analytical solution was suggested in this research. Because the analytical solution for heat flow is expressed as a mathematical equation of weld parameters, it may be effective in anticipating the effect of each weld parameter on the tempering in HAZ during the successive bead depositions. The reheating effect by the successive bead layer on the brittle coarse grained HAZ formed by earlier bead deposition was estimated by comparing the overlapped distance between the temperature curves in the HAZ. Three layered weld specimens of SA508 base metal with A52 filler were prepared by controlling heat input ratio between layers. The tempering effect anticipated by using the overlapped distance between the temperature curves was verified by measuring the micro-hardness distribution in the HAZ of prepared specimens. The temperature curve obtained from analytical solution was expected as a good tool to find optimal temper bead welding conditions.

• 한국재료학회지
• /
• 제1권1호
• /
• pp.29-36
• /
• 1991

Pressurized Water Reactor (PWR) pressure vessels are made of forged low alloy steel plates internally clad with an austenitic stainless steel by welding to improve anti-corrosion properties. They display a characteristic behavior of dissimilar metal weld interface during post weld heat treatment (PWHT) and service at high temperature and pressure. In this Study, Metallugical structure of weld interface of SA 508 Class 3 forged steel clad with 309L, Austenitic stainless steel after PWHT was investigated. To estimate the width of the carburized/decarburized bands quantitatively, a model for carbon diffusion was proposed and a theoretical equation was derived.

• 동력기계공학회지
• /
• 제16권4호
• /
• pp.66-73
• /
• 2012

본 연구는 횡방향 TIG 용접된 Al6013-T4 알루미늄 합금 용접부의 피로균열전파거동에 미치는 용접후열처리(PWHT)의 영향을 조사하는 것이 주목적이다. 기초적으로 인장시험, 경도 및 미세조직이 조사되었으며, 피로균열전파거동을 고찰하기 위한 피로 시험은 모두 중앙균열인장(CCT) 시험편에 대하여 수행되었다. T82열처리에 있어서 시효시간은 피로균열전파율, 인장강도 및 경도에 대단히 민감함을 나타내었으며, 모재와 열영향부재의 경우가 용접재보다 기계적 성질이 우수하였다. 횡방향 TIG 용접한 Al6013-T4 시험재의 용접후열처리 조건에 따라서 피로균열전파 저항에는 차이가 나타났으며, 본 실험의 조건하에서 24시간 인공시효 PWHT-82 시험편이 피로균열전파 저항이 가장 우수한 결과를 나타내었다.

• Corrosion Science and Technology
• /
• 제20권6호
• /
• pp.426-434
• /
• 2021

The effect of two different annealing temperatures on the level of the second phase precipitated in the microstructure and the corrosion behaviors of super austenitic stainless steel were examined. The sample annealed at a higher temperature had a significantly lower fraction of the sigma phase enriched with Cr and Mo elements, showing more stable passivity behavior during the potentiodynamic polarization measurement. However, after the welding process with Inconel-type welding material, severe corrosion damage along the interface between the base metal and the weld metal was observed regardless of the annealing temperature. This was closely associated with the precipitation of the fine sigma phase with a high Mo concentration in the unmixed zone (UMZ) during the welding process, leading to the local depletion of Mo concentrations around the sigma phase. On the other hand, the fraction of the newly precipitated fine sigma phase in the UMZ was greatly reduced by post-weld heat treatment (PWHT), and the corrosion resistance was greatly improved. Based on the results, it is proposed that the alloy composition of welding materials and PWHT conditions should be further optimized to ensure the superior corrosion resistance of welded super austenitic stainless steel.

• Journal of Welding and Joining
• /
• 제6권2호
• /
• pp.30-39
• /
• 1988

Generally, as the welded region of weld structures has the incomplete bead and welded deposit which are able to behave like the surface cracks occasinally, there is a high possibility that the fatigue fracture of the weld structures is due to the surface cracks on the wlded region. This study was done to investigate the effects of post weld heat treatment (PWHT) on the fatigue behaviors of the surface crack of the heat affected zone (HAZ) for the multi-pass welds under the repetitive pure bending moment. The obtained results are summarized as follows : 1. The crack grows to the depth direction initially as the number of cylces increase, the amount of crack length is increased for the surface dir3ction and cive versa for the depth direction. 2. The fatigue life is increased in a order of as weld, PWHT specimens and parent. 3. As the number of cycles increase, the crack length is increased to th surface direction. The increase of the depth length is blunted at the center of specimen thickness. 4. The fatigue crack growth of PWHT specimens to the surface direction is dependent upon the holding time and applied stress during PWHT. In order words, the crack growth rate decreases with the holding time and increases with the applied stress during PWHT. 5. As the crack grows, the aspect formed in the course of crack propagation approaches to semicircle for parent and ellipse with the largest semidiameter for PWHT ($1/4hr, 15kgf/mm^2$) 6. At depth direction, it is difficult to apply to the paris' equation because of the scattered data between the crack growth rate and the stress intensity factor range.

• 한국산학기술학회논문지
• /
• 제12권12호
• /
• pp.5405-5411
• /
• 2011

본 연구에서는 교량용 구조용 강재인 HSB600 강의 용접부에서 입열량 (1.5~3.6 kJ/mm)과 용접후 열처리(PWHT, $600^{\circ}C$, 40hr.)가 미세조직과 기계적 특성에 미치는 영향에 관해 연구하였다. HSB600 강재를 GMA용접을 실시하였다. 용접된 상태에서는 인장강도와 경도는 입열량이 증가할수록 저하되었으며 충격 흡수 에너지는 큰 차이를 보이지 않았다. 낮은 입열량인 1.5 kJ/mm에서 침상형 페라이트가 가장 많이 생성되었다. 용접후 열처리를 통해 경도와 인장강도가 저하되었고, 용착금속의 충격흡수에너지가 증가되었다.