• Journal of Adhesion and Interface
• /
• v.21 no.3
• /
• pp.101-106
• /
• 2020

In this study, epoxy-modified acrylate was synthesized. The synthesized acrylate was added to the composition for sheet molding compound (SMC) in the range of 5 phr to 15 phr. The prepared SMC prepreg was molded at high temperature and pressure to produce a glass fiber reinforced composite. Physical properties such as tensile and impact strength of the composite were measured, respectively. Experimental data show that the composite with 5 phr of synthesized acrylate has 20% improved tensile strength and 12% improved impact strength than that of the reference sample.

• Journal of the Korean Applied Science and Technology
• /
• v.30 no.2
• /
• pp.305-311
• /
• 2013

PLA(polylactic acid), one of biodegradable polymers was blended with various amounts of wood pulp powder through solution blending technic to verify the effect of reinforcing pulp amount on the mechanical properties of blend films. Also these blend films were further modified with TDI(toluene diisocyanate) as crosslinking agent to introduce urethane functions by reaction of pulp hydroxyl groups and isocyanate. As a result, the tensile strength of blend film with 0.25 wt% pulp was increased from $565.25kg_f/cm^2$ for PLA film itself to $624.20kg_f/cm^2$. However, elongation of this film was decreased by 50% of that of PLA film itself. Only PLA/pulp blend film further modified with 500% of TDI/0.25 wt% pulp showed the slightly increased tensile strength but decreased elongation. Melting point and glass transition temperature of PLA/pulp blend films were confirmed by using Differential Scanning Calorimeter(DSC). Thermal stability of these blend films measured by TGA showed only a slight increase at temperature lower than $300^{\circ}C$.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.7
• /
• pp.4081-4086
• /
• 2014

Cellulose acetate butyrate (CAB) is a biodegradable resin with excellent optical properties, but it is difficult to apply film process. In this study, an attempt was made to improve the processability of CAB using polyactic acid and the mechanical properties using an impact modifier. Polylacitc acid (PLA)/Cellulose acetate butyrate (CAB) blends with an impact modifier were prepared using a twin screw extruder. The temperature range was $140^{\circ}C$ to $200^{\circ}C$, and the screw speed was fixed to 200 rpm. To evaluate the miscibility of impact modified CAB/PLA, the glass transition behavior and morphology were observed by DSC and FE-SEM. The mechanical properties were investigated by dynamic mechanical analysis (DMA) and a Universal Testing Machine (UTM). In addition, the effect of an impact modifier in the polymer matrix was determined using a notched Izod impact strength tester. Finally, the PLA/CAB/impact modifier 75/25/10 ratio was found to be a compatible system. In the 10wt.% impact modifier, the sample had a 4 times higher izod impact strength than the non-toughening composition.

• Applied Chemistry for Engineering
• /
• v.4 no.3
• /
• pp.616-626
• /
• 1993

Polyurethane(PU) have an excellent flexibility and toughness so that it has been widely used as an elastomer. PMMA was blended with PU to improve the impact property. Five types of PU, having different molecular weight and different polyol types, were prepared and blended with PMMA in order to investigate the effect of molecular weight and polyol type of PU on property of PU-PMMA blend. Tensile strength of PU-PMMA blend was determined by Inston. Differential Scanning Calorymetry(DSC) and Scanning. Elctron Microscopy(SEM) were used to observe morphology change and glass transition temperature changes of PU-PMMA blends. Transparency of PU-PMMA blends was determined by haze meter. But, owing to intrinsic incompatability of PU-PMMA, Low impact strength of PMMA wasn't improved through PU-PMMA blend. therefore, polyurethane dimethacrylate(PUD), having similiar chemical structure to PU and two vinyl group at both ends, was prepared and reacted with methyl methacrylate(MMA) to form crosslinked copolymer Mechanical property of this crosslinked polymer, such as impact strength and transparency, was investigated by Instron, Izod type (Cantilever beam) impact tester and haze meter. Results of these measurements showed that crosslinked copolymer of PUD-MMA was better impact resistance than PMMA and maintained similar transparency to PMMA.

• Membrane Journal
• /
• v.19 no.4
• /
• pp.341-347
• /
• 2009

Nanohybrid based on environmentally friendly and biodegradable polymer, poly propylene carbonate (PPC) and cloisite 20B (PPC/C-20B) have been synthesized by solution blending method and their morphology, thermal and water absorption properties have been evaluated. The structure of PPC/C-20B nanohybrid was confirmed by X-ray diffraction (XRD). The thermal property of PPC and PPC/C-20B nanohybrid were investigated by thermal gravimetric analysis (TGA) and differential scanning calorimetric (DSC). The experimental results demonstrated that nanohybrid showed the highest thermal stability in TGA and DSC. TGA tests revealed that the thermal decomposition temperature ($T_{d50%}$) of the nanohybrid increased significantly, being $23^{\circ}C$ higher than that of pure PPC while DSC measurements indicated that the introduction of 5 mass% of clay increased the glass transition temperature from 21 to $30^{\circ}C$. Further the water absorption capacity of the PPC was significantly decreased by the incorporation of clay. Water absorption cause degradation of the coating by the moistures and affect the physical and mechanical performance. This result indicates that organic modifiers have effect on thermal and water absorption capacity of PPC and are of importance for the practical process and application of PPC.