• Membrane Journal
• /
• v.15 no.2
• /
• pp.157-164
• /
• 2005

In this study, composite hollow fiber membranes were developed for the recovery of olefin monomers in polyolefin industry off-gases. Polyetherimide (PEI) hollow fiber support membranes were fabricated from spinning solutions containing PEI, NMP and polyethylene glycol (PEG). The influence of dope solution and inner coagulant composition on the permeation properties and structure of hollow fiber supports was examined. PDMS was used as a selective layer and coated on PEI hollow fiber support. The thickness of active layer was controlled by changing coating solution concentration. The permeation properties of hollow fiber supports and composite membranes were characterized with a pure gas permeation test. The optimized composite hollow fiber membrane has $10\;{\mu}m$ selective layer and shows excellent separation performance; the ideal selectivity of olefins over nitrogen is in the following order: 1-butylene (6.4) > propylene (17) > ethylene (97), which selectivity data are similar to the intrinsic olefin/nitrogen selectivities of PDMS. This confirms that the new composite hollow fiber membranes suitable for olefin off-gas recovery has developed successfully.

• Applied Chemistry for Engineering
• /
• v.31 no.6
• /
• pp.679-687
• /
• 2020

In this study, poly(ether-block-amide) (PEBAX)/zeolitic imidazolate framework-8 (ZIF-8)-polyetherimide (PEI), and PEBAX/amine-modified ZIF-8 (amineZIF-8)-PEI composite membranes were prepared by varying the contents of ZIF-8 and amineZIF-8. Also the gas permeability properties of N2 and CO2 were investigated for each composite membrane. The N2 and CO2 permeability of the PEBAX/ZIF-8-PEI composite membrane increased as the ZIF-8 content increased, while the CO2/N2 selectivity gradually decreased. In the case of the PEBAX/amineZIF-8-PEI composite membrane, the permeability of N2 decreased slightly, and CO2 increased till amineZIF-8 amount was 0.5 wt% and then decreased when the content increased further. The CO2/N2 selectivity was the highest with a value of 78.3 at 0.5 wt% of amineZIF-8. because the amine modification in the amineZIF-8 improves the compatibility between PEBAX and amineZIF-8, It seems that amineZIF-8 was evenly dispersed in PEBAX, which could be greatly influenced by the porousity of ZIF-8 and also the affinity of amine toward CO2.