• KOREAN JOURNAL OF PACKAGING SCIENCE & TECHNOLOGY
• /
• v.23 no.2
• /
• pp.61-66
• /
• 2017

Poly lactic acid(PLA) and poly butylene adipate-co-terephthalate(PBAT) film was prepared using a twin extruder. PLA (25%) and PBAT (75%) were mixed with various ratio of chain extenders, such as $Joncryl^{(R)}$ and hexamethylene diisocyanate(HDI) to improve the mechanical and thermal properties of produced bio composite films. Tensile strengths of films were steadily increased with increasing ratio of chain extender. The tensile strength of control films was about 25 MPa, and the tensile strength of films with combined chain extenders was above 40 MPa. The films with $Joncryl^{(R)}$ resulted in improved tensile strength, while the film with HDI alone showed improved percent elongation at break. By adding chain extenders into PLA/PBAT resin, the cold crystallization temperature (Tcc) and decomposition temperature (Td) of the produced bio composite films increased. It revealed that the addition of two types of chain extenders was efficient way to get PLA/PBAT film with improved strength and elongation.

• KOREAN JOURNAL OF PACKAGING SCIENCE & TECHNOLOGY
• /
• v.29 no.2
• /
• pp.79-86
• /
• 2023

In this study, poly(lactic acid) (PLA) and Poly(butylene-adipate-co-terephthalate) (PBAT) composite films containing calcined oyster shell powder (OSP) were evaluated for the applicability of antimicrobial packaging. PLA/PBAT-OSP composite films were prepared using twin-screw extruder. The OSP composite was incorporated into PLA/PBAT blend with different ratios (0, 1, 3, 5 and 10%) and the effect of OSP in the PLA/PBAT matrix was evaluated. The PLA/PBAT-OSP composite films were evaluated for properties using FT-IR, SEM, TGA, DSC, UTM, UV-vis, and Contact angle, as well as antimicrobial property was examined according to ISO 22196 - Antimicrobial Plastic Test. As OSP was added, it showed high antimicrobial activities for both Gram-positive (Staphylococcus aureus) and Gram-negative (Escherichia coli) bacteria. On the other hand, it was found that mechanical properties decreased as OSP was added. For the application of PLA/PBAT-OSP composite films as an antimicrobial packaging material, it is necessary to improve the dispersibility of OSP in the PLA/PBAT composite films and their physical properties at the same time.