We prepared the AZO thin film with different $O_2$ gas flow rate. the AZO thin films were deposited on glass substrate at room temperature, working gas pressure of 1mTorr. the electrical, structural and optical properties of AZO thin films were investigated by using Hall Effect measurement system, X-ray Diffractometer (XRD) and UV-VIS spectrometer. From the results, we could obtain that AZO thin film with low resistivity of $8.5{\times}10^{-4}{\Omega}cm$ was exhibited in specific $O_2$ gas flow rate. Also, the transmittance of over 80% in visible range was observed in specific $O_2$ gas flow rate. In all of the AZO thin film with the transmittance of over 80%, diffraction peak of (002) direction was observed, while amorphous peak was observed in the AZO thin film with the low transmittance.

• Proceedings of the KIEE Conference
• /
• 2006.10a
• /
• pp.69-70
• /
• 2006

The ITO thin films were prepared by Facing Targets Sputtering(FTS) method on polyethersulfon(PES) substrate. The ITO thin films were deposited with the film thickness of 100nm at room temperature and working gas pressure of 1 mTorr. As a function of sputtering conditions, electrical and optical properties of prepared ITO thin films were evaluated by Hall Effect Measurement(EGK) and UV-VIS spectrometer(HP), respectively. From the results, the ITO thin films was deposited was with a resistivity $8.3{\times}10^{-4}[{\Omega}-cm]$ and transmittance over 80% in the visible range.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.05a
• /
• pp.95-95
• /
• 2015

IGZO (Indium Gallium Zinc Oxide) 물질은 기존에 사용되던 Amorphous Silicon에 비해 전자 이동도가 더욱 빠르기 때문에 차세대 디스플레이 재료로서 각광받고 있으며, 이러한 빠른 전자 이동도는 디스플레이 소자에 있어서 매우 중요한 요소 중 하나이다. 이를 향상시키기 위하여 본 연구에서는 ICP(inductively coupled plasma) antenna를 이용하여 rf power와 requency를 변화함으로써 박막 증착 시 발생되는 플라즈마의 특성을 조절하여, 박막의 특성을 조절하고자 했다. 이렇게 증착된 IGZO 박막은 Hall Effect Measurement를 이용하여 전기적 특성을 분석하였으며, XPS(x-ray photoelectron spectroscopy)를 이용하여 박막의 조성을 분석하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.385-386
• /
• 2007

We prepared the Al doped ZnO coating Ag multilayer thin films on glass without substrate heating using FTS system. The structure of multilayer thin films has Al doped ZnO/Ag/Al doped ZnO(AZO/Ag/AZO). The thickness of top and bottom AZO thin films were fixed to 50 nm, respectively and controlled the thickness of Ag thin films with deposition time. As-doped multilayer thin films were prepared at 1mTorr and input power (DC) of 100W at room temperature. To investigate the film properties, we employed four-point probe, UVNIS spectrometer, X-ray diffractometer (XRD), scanning electron microscopy (SEM), Hall Effect measurement system and Atomic Force Microscope (AFM).

• Journal of Astronomy and Space Sciences
• /
• v.19 no.2
• /
• pp.141-150
• /
• 2002

The ionosphere plays an important role in the electrodynamics of space environment. In particular, the information on the ionospheric conductivity distribution is indispensable in understanding the electrodynamics of the magnetosphere and ionosphere coupling study. To meet such a requirement, several attempts have been made to estimate the conductivity distribution over the polar ionosphere. As one of such attempts we compare the ionospheric plasma convection patterns obtained from the Super Dual Auroral Radar Network (SuperDARN), from which the electric field distribution is estimated, and the simultaneously measured ground magnetic disturbance. Specifically, the electric field measured from the Goose Bay and Stokkseyri radars and magnetic disturbance data obtained from the west coast chain of Greenland are compared. In order to estimate ionospheric conductivity distribution with these information, the overhead infinite sheet current approximation is employed. As expected, the Hall conductance, height-integrated conductivity, shows a wide enhancement along the center of the auroral electrojet. However, Pedersen conductance shows negative values over a wide portion of the auroral oval region, a physically unacceptable situation. To alleviate this problem, the effect of the field-aligned current is taken into account. As a result, the region with negative Pedersen conductance disappears significantly, suggesting that the effect of the field-aligned current should be taken into account, when one wants to estimate ionospheric conductance based on ground magnetic disturbance and electric field measurements by radars.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.1
• /
• pp.87-90
• /
• 2006

In case of preparation of ITO thin film for using top electrode of Top-emitting Organic Light Emitting Diodes(TOLEDs), the ITO thin film should be prepared at room temperature and low oxygen gas flow condition in order to reduced the damage of organic layer due to the bombardment of highly energetic particles such as negative oxygen ions which accrued from the plasma. In this study, the ITO thin film with high optical transmittance and low resistivity prepared as a function of oxygen gas (0 ${\~}$ 0.8 sccm) and Ar gas was fixed at 20 sccm by the Facing Targets Sputtering (FTS) method. The electrical and optical properties of ITO thin films were measured by Hall effect measurement, UV/VIS spectrometer, respectively In the results, we obtained the ITO thin film with lowest resistivity($3{\times}10^{-4} {\Omega}{\cdot} cm$) at oxygen gas flow 0.2 sccm and optical transmittance over $80\%$ at oxygen gas flow over 0.2 sccm.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.439-440
• /
• 2008

Indium Zinc Tin Oxide (IZTO) thin films for transparent thin film transistor (TTFT) were deposited on glass substrate at room temperature by facing targets sputtering (FTS). The FTS system was designed to array two targets facing each other and forms the high- density plasma between. Two different kinds of targets were installed on FTS system. One is ITO ($In_2O_3$ 90wt.%, $SnO_2$ 10wt.%), the other is IZO($In_2O_3$ 90wt%, ZnO 10wt%). The conductive and optical properties of IZTO thin film is determined depending on variation of DC power and working pressure. Therefore, IZTO thin films were prepared with different DC power and working pressure. As-deposited IZTO thin films were investigated by a UV/VIS spectrometer, an X-ray diffractometer (XRD), a scanning electron microscopy (SEM), a Hall Effect measurement system. As a result, all IZTO thin films deposited on glass substrate showed over 80% of transmittance in visible range (400~800 nm) at $O_2$ gas flow rate. We could obtain IZTO thin films with the lowest resistivity $5.67\times10^{-4}$ [$\Omega{\cdot}cm$] at $O_2$ gas flow rate 0.4 [sccm).

• Korean Journal of Materials Research
• /
• v.20 no.9
• /
• pp.494-499
• /
• 2010

Tin oxide thin films were prepared on borosilicate glass by rf reactive sputtering at different deposition powers, process pressures and substrate temperatures. The ratio of oxygen/argon gas flow was fixed as 10 sccm / 60 sccm in this study. The structural, electrical and optical properties were examined by the design of experiment to evaluate the optimized processing conditions. The Taguchi method was used in this study. The films were characterized by X-ray diffraction, UV-Vis spectrometer, Hall effect measurements and atomic force microscope. Tin oxide thin films exhibited three types of crystal structures, namely, amorphous, SnO and $SnO_2$. In the case of amorphous thin films the optical band gap was widely spread from 2.30 to 3.36 eV and showed n-type conductivity. While the SnO thin films had an optical band gap of 2.24-2.49 eV and revealed p-type conductivity, the $SnO_2$ thin films showed an optical band gap of 3.33-3.63 eV and n-type conductivity. Among the three process parameters, the plasma power had the most impact on changing the structural, electrical and optical properties of the tin oxide thin films. It was also found that the grain size of the tin oxide thin films was dependent on the substrate temperature. However, the substrate temperature has very little effect on electrical and optical properties.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.96-96
• /
• 1999

CdTe는 일반적으로 광전 소자나 Xtjs 및 λ선 감지 소자로서 많은 연구가 되어지고 있는 물질이다. 특히 적외선 감지 소자로 쓰이고 있는 HgCdTe 물질의 기판으로서도 많은 연구가 진행되고 있다. 이러한 여러 가지 목적으로 사용함에 있어서 CdTe 내에 가지고 있는 여러 가지 불순물에 의한 영향으로 각종 결함밴드들이 형성됨으로서 소자로서의 응용에 많은 지장을 주고 있다. 이러한 이유로 여러 가지 방법으로 불순물 및 결합에 의한 준위에 관한 연구들이 진행되고 있다. 본 실험에서는 MBE 법으로 성장된 In 도핑된 CdTe 박막의 광학적 성질을 관찰하기 위하여 수소화 및 열처리를 하여 PL 법을 이용하여 관찰하여 보앗다. 열처리는 Cd 분위기의 50$0^{\circ}C$에서 5시간 동안 수행하였으며 수소화는 rf plasma 장치를 이용하여 8$0^{\circ}C$에서 50mW/c2의 출력으로 1시간동안 수행하여 주었다. 열처리한 시료의 경우 PL 신호는 갓 성장한 시료와 비교하여 깊은 준위에 관련된 신호들만 변화가 있었을뿐 그리 큰 변화가 있지는 않았다. 그러나 수소화시킨 시료의 경우 전체적으로 피크의 크기가 5배정도 감소하는 것을 볼 수 있었는데 이것은 수소에 의하여 passivation된 효과로 볼 수 있다. 정량적인 passivation 효과를 보기 위하여 온도의존성 PL 측정을 하여 보았다. 측정에서 관측된 (D,h) emission lines의 FWHM을 비교하여 본 결과 FWHM 온도가 증가함에 따라 선형적으로 증가하는 것이 아니라 급격한 증가를 q이는 구간을 관착할 수 있었다. 이것은 CdTe내에 존재하는 전하를 띠고 있는 주게와 받게의 결합의 결과로 나타나는 현상으로 보여진다. 이러한 결과를 통하여 얕은 준위에 있는 주게 불순물의 농도를 계산해 보았고 Hall 측정을 얻은 결과와 비교하여 보았다.판단된다. 따라서 이 기술은 기존의 광소자 제작을 위한 IFVD 방법의 문제점을 해결할 뿐만 아니라 결정 재성장 없이 도일한 기판상에 국부적으로 상이한 bandgap 영역을 만들 수 있기 때문에 광소자 제작에 적극 이용될 수 있다.나지 않았으며 BST 박막에서는 약 1.2V의 C-V이력현상이 보였다.를 이용하였으며, 이온주입후 열처리 온도에 따른 활성화 정도의 관찰을 위하여 4-point probe와 Hall measurement를 이용하였다. 증착된 다결정 SiGe의 두게를 nanospec과 SEM으로 분석한 결과 Gem이 함량이 적을 때는 높은 온도에서의 증착이 더 빠른 증착속도를 나타내었지만, Ge의 함량이 30% 되었을 때는 온도에 관계없이 일정한 것으로 나타났다. XRD 분석을 한 결과 Peak의 위치가 순수한 Si과 순수한 Ge 사이에 존재하는 것으로 나타났으며, ge 함량이 많아짐에 따라 순수한 Ge쪽으로 옮겨가는 경향을 보였다. SEM, ASFM으로 증착한 다결정 SiGe의 morphology 관찰결과 Ge 함량이 높은 박막의 입계가 다결정 Si의 입계에 비해 훨씬 큰 것으로 나타났으며 근 값도 증가하는 것으로 나타났다. 포유동물 세포에 유전자 발현벡터로써 사용할 수 있음으로 post-genomics시대에 다양한 종류의 단백질 기능연구에 맡은 도움이 되리라 기대한다.다양한 기능을 가진 신소재 제조에 있다. 또한 경제적인 측면에서도 고부가 가치의 제품 개발에 따른 새로운 수요 창출과 수익률 향상, 기존의 기능성 안료를 나노(nano)화하여 나노 입자를 제조, 기존의 기능성 안료에 대한 비용 절감 효과등을 유도 할 수 있다. 역시 기술적인 측면에서도 특수소재 개발에 있어 최적의 나노 입자 제어기술 개발 및 나노입자를 기능성 소재로 사용하여 새로운 제품의 제조와 고압 기상 분사기술의 최적화에 의한 기능성 나노 입자 제조 기술을 확립하고 2차 오염 발생원인 유