• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.32 no.9
• /
• pp.788-795
• /
• 2008

To understand the tensile behaviors of GFRP at low temperature, three types of specimen have been used in this study. Tensile properties and fracture mechanisms for three orthogonal orientations of plain weave glass fabric reinforced epoxy resin laminate were investigated at temperature range of about -30 to $15^{\circ}C$. The tensile properties of axial and edge type specimen decrease slightly with decreasing temperature to $-20^{\circ}C$. However, at $-30^{\circ}C$ the decreases in the tensile properties increased considerably. Below $-20^{\circ}C$, thickness type specimen showed a marked decreases in the tensile properties. It was obvious that the fracture manner of thickness type specimen was adhesive failure at above $-10^{\circ}C$ and a mixed adhesive and cohesive failure at below $-20^{\circ}C$.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.17 no.3
• /
• pp.15-21
• /
• 2009

The anisotropic mechanical properties were measured for the three orthogonal orientations of plain weave glass fabric reinforced epoxy resin laminate. In tensile and flexural tests, axial and edge type specimens failed by pull-out of warp and fill yarns, respectively. In contrast, the thickness type specimens failed by adhesive failure process. Longitudinal cracking occurred in several of the edge type specimens during tensile test. That cracking caused pop-in in the stress-strain curve. Defects induced by improper coupon machining caused that cracking.

• Composites Research
• /
• v.17 no.6
• /
• pp.28-36
• /
• 2004

Micro-tow deformation during forming of PVC foam-fabric composite sandwich structure is investigated to find out the correlation between forming condition and material deformation. The foams used in this research are PVC foams which have 4 different densities and the fabric composite is Carbon/epoxy prepreg which is plain weave (3k) as a skin material. Tow parameters such as crimp angle and tow amplitude are measured using microscope and a proper image tool and are compared with each other. In order to find out the effect of foam deformation during forming on tow deformation the compressive tests of foams are performed in three different environmental temperatures ($25^{\circ}C$, $80{\circ}C$, $125^{\circ}C$). The microscopic observation results show that the micro tow deformations are quite different from each other with respect to the foam density and forming pressure.

• Composites Research
• /
• v.35 no.4
• /
• pp.269-276
• /
• 2022

In this paper, a composite stiffened panel was fabricated using a three-dimensional weaving method that can reduce the risk of delamination, and mechanical properties such as buckling load and natural frequency were investigated. The preform of the stringer and skin of the stiffened panel were fabricated in one piece using T800 grade carbon fiber and then, resin (EP2400) was injected into the preform. The compression test and natural frequency measurement were performed for the stiffened panel, and the results were compared with the finite element analyses. In order to compare the performance of 3D weaving structures, the stiffened panels with the same configuration were fabricated using UD and 2D plain weave (fabric) prepregs. Compared to the tested buckling load of the 3D woven panel, the buckling loads of the stiffened panels of UD prepreg and 2D plain weave exhibited +20% and -3% differences, respectively. From this study, it was confirmed that the buckling load of the stiffened panel manufactured by 3D weaving method was lower than that of the UD prepreg panel, but showed a slightly higher value than that of the 2D plain weave panel.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2005.04a
• /
• pp.154-157
• /
• 2005

This paper aims to investigate the tow deformation pattern with respect to shear angle and mold property during draping of plain weave carbon/epoxy prepreg. Aluminum and PVC foams with different foam density are used for the draping hemisphere molds with 250 mm diameters. Microscopic observation reveals that tow parameters like crimp angle and Y-directional tow intervals are influenced by shear angle and mold density at the same time. The correlation between crimp angle and Y-directional tow interval is also found out.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.30 no.12 s.255
• /
• pp.1603-1610
• /
• 2006

In this paper compressive characteristics of composite egg-box panels were investigated and energy absorption was calculated from the nominal stress-strain relations obtained by the compressive tests. Several different stacking sequences and number of plies were introduced for investigation of static compression characteristics and the energy absorption rates of composite egg-box panels. The compressive stress-strain relation and energy absorption of various composite egg-box panels were compared with those of aluminium egg-box panels. From the test results it was found that the fracture behavior of composite egg-box panel was affected by stacking angle causing different local deformation, during lay-up and draping processes and types of prepreg; that is, plain weave carbon/epoxy and 4-harness satin glass/epoxy. The energy absorption capacity of composite egg-box panels were proved to be higher than that of aluminium egg-box panels with low mass.