• Applied Chemistry for Engineering
• /
• v.28 no.6
• /
• pp.638-644
• /
• 2017

Pitch based activated carbon fibers for electric double layer capacitor (EDLC) electrodes were treated by oxyfluorination via varying the ratio of fluorine and oxygen gases to improve high power property. As the partial pressure of fluorine increased, the oxyfluorinated activated carbon fibers showed an increase of linear fluorine functional groups. While the oxygen functional groups increased, no changes was observed with respect to the partial gas pressure. The specific surface area and pore volume decreased due to the etching reaction on the activated carbon fiber surface through oxyfluorination, but the mesopore volume increased about 4.5 times. In the case of activated carbon fibers treated with 50% of the fluorine gas partial pressure, the specific capacitance increased to about 29% and 61% at scan rates of 5 and 50 mV/s, respectively. The improvement of the specific capacitance was believed to be due to the introduction of oxygen and fluorine functional groups on the activated carbon fiber surface and the increase of mesopores through oxyfluorination.

• Carbon letters
• /
• v.3 no.4
• /
• pp.198-204
• /
• 2002

In this paper, impregnated activated carbon fiber (IACF) was manufactured to pitch-based activated carbon fibers (ACF) with potassium hydroxide (KOH) by using wet impregnation method to raise nitrogen oxides ($NO_x$) adsorptivity. The properties of IACF were observed using EPMA, TGA and DSC and $NO_x$ adsorptivity was observed at high and low temperature. Before and after adsorption was analyzed using ToF-SIMS for examine surface characterization of adsorbed $NO_x$. The results showed that the better adsorptivity appeared for increasing KOH ratio. So, $NO_x$ adsorptivity showed result that is proportional between KOH and the adsorbed amount. On the other hand, adsorbent that manufactured without washing was better $NO_x$ adsorptivity than adsorbent that manufactured with washing. The behavior of adsorption show that crossing time of NO and $NO_2$ delayed for a rising adsorptivity. And NO ratio increased but $NO_2$ ratio decreased according as KOH ratio increases. $NO_x$ was confirmed through surface analysis that remain in $NO_2^-$ and $NO_3^-$ form on IACF surface.

• Korean Chemical Engineering Research
• /
• v.46 no.5
• /
• pp.863-867
• /
• 2008

Pitch based activated carbon fiber(ACF) was prepared from reformed naphtha cracking bottom oil(NCB oil) by melt spinning. The fibers obtained were stabilized, carbonized, and then steam activated. The ACF was sensitized with Pd-Sn catalytic nuclei via a single-step activation approach. This sensitized ACF was used as precursors for obtaining copper plated ACFs via electroless plating. ACFs uniformly decorated with metal particles were obtained with reduced copper plating in the reaction solution. Effects of the amount of copper on characteristics of ACF/Cu catalysts were investigated through BET surface area, X-ray diffraction, scanning emission microscopy, and ICP. The amount of copper increased with plating time, but the surface area as well as the pore volume decreased. NO conversion increased with reaction temperature. NO conversion decreased with increasing the amount of copper, which is seemed to be due to the reduction of surface area as well as the dispersion of copper.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.12 no.4
• /
• pp.165-171
• /
• 2002

The study on the adsorption, the surface properties and the antibacterial effects of the metal-treated pitch based activated carbon fibers was carried out. From the adsorption studies on the series of metal-treated activated carbon fiber, the specific surface areas of the metal treated activated carbon fiber obtained from BET equation were in the range of 113.2~1574 $m^2$/g for the Ag-ACFs. And that of Cu treated ACF are distributed to 688.2-887.8 $\m^2$/g. And, the specific surface areas of the Ni-treated pitch based ACFs were in the range of 692.6~895.2 $\m^2$/g. From the ${\alpha}_s$- method, 0.06~1.1 cm^3/g of the micropore volumes were obtained from Ag-ACFs. And, 0.1~0.2 cm^3/ and 0.2~0.6 cm^3/g of the micropore volumes were obtained from Cu and Ni-ACFs, respectively. And, from the SEM morphology results, it was observed that the surface of activated carbon fiber are partially blocked and coated by metal after the treatment. Finally, from the antibacterial effects of metal-treated activated carbon fiber against E. coli, the areas of antibacterial effect become larger with the increase in mole ratio of metal treated. And, from the antibacterial effects using Shake flask method against E. coli, the percentage of the effects was 92.5~100 % and the antibacterial effect was increased with the increase in mole concentration of metal treated.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.15 no.3
• /
• pp.207-218
• /
• 2017

In this study, pitch-based activated carbon fibers (ACFs) were modified with pyrolysis fuel oil (PFO). Carbonized ACF samples were activated at $850^{\circ}C$, $880^{\circ}C$ and $900^{\circ}C$. A scanning electron microscope (SEM) and a BET surface area apparatus were employed to evaluate the indoor radon removal of each sample. Among three samples, the BET surface area and micropore area of ACF880 recorded the highest value with $1,420m^2{\cdot}g^{-1}$ and $1,270m^2{\cdot}g^{-1}$. Moreover, ACF880 had the lowest external surface area and BJH adsorption cumulative surface area of pores with $151m^2{\cdot}g^{-1}$ and $35.5m^2{\cdot}g^{-1}$. This indicates that satisfactory surface area depends on the appropriate temperature. With the above scope, ACF880 also achieved the highest radon absorption rate and speed in comparison to other samples. Therefore, we suggest that the optimum activation temperature for PFO containing ACFs is $880^{\circ}C$ for effective indoor radon adsorption.

• Korean Chemical Engineering Research
• /
• v.43 no.6
• /
• pp.745-750
• /
• 2005

Naphtha cracking bottoms(NCB) oil was reformed by varying the heat treatment temperature, treatment time, and nitrogen flow rate in preparation of precursor pitch for isotropic pitch-based carbon fibers and activated carbon fibers. The reformed pitches were investigated in the yield, softening point, elementary analysis, and molecular weight distribution, and then the precursors reformed were melt spun to certify the optimum reforming conditions. The optimum precursor pitch was prepared when the NCB oil was reformed at $380^{\circ}C$, 3 h and 1.25 vvm $N_2$, and it's the softening point was around $240^{\circ}C$. The reforming resulted in product yield of 21 wt％. The C/H mole ratio of the precursor pitch increased from 1.07 to 1.34, the aromaticity increased from 0.85 to 0.88. The insolubles in benzene and quinoline were 30.0 wt％ and 1.5 wt％, respectively. The spinning temperature was about $50^{\circ}C$ higher than the softening point. The molecular weights of the precursor components were distributed from 250 to 1250, and 80％ of them were in the range of 250 to 700.

• Transactions of the Korean hydrogen and new energy society
• /
• v.27 no.3
• /
• pp.298-305
• /
• 2016

In this study, we treated pitch-based activated carbon fibers (ACFs) in hydrogen peroxide using electron beam (E-beam) irradiation to improve nitrogen monoxide (NO) sensing ability as an electrode material of gas sensor. The specific surface area of ACFs treated by E-beam irradiation with 400 kGy increased from $885m^2/g$ (pristine) to $1160m^2/g$ without any changes in structural property and functional group. The increase in specific surface area of the E-beam irradiated ACFs enhanced NO gas sensing properties such as response time and sensitivity. When the ACFs irradiated with 400 kGy, response time was remarkably reduced from 360 s to 210 s and sensitivity was increased by 4.5%, compared to the pristine ACFs. These results demonstrate convincingly that surface modification of ACFs using E-beam in hydrogen peroxide solution can enhance textural properties of ACFs and NO gas sensing ability of gas sensor at room temperature.

• Applied Chemistry for Engineering
• /
• v.26 no.5
• /
• pp.598-603
• /
• 2015

In this study, electrochemical properties of pitch-based activated carbon fibers (ACFs) were investigated by different heat-treatment temperature of the pitch-based ACFs in order to improve the specific capacitance of electric double-layer capacitor (EDLC). The ACFs were prepared by different heat-treatment temperatures of 1050 and $1450^{\circ}C$, after activation with 4 M KOH at $800^{\circ}C$ using stabilized pitch fiber. The specific surface area of prepared ACFs increased from $828m^2/g$ to $987m^2/g$, also the micropore and mesopore volumes of prepared ACFs were increased. These results because pore was produced by desorbing oxygen and hydrogen elements within the ACFs, and pore size was increased by contraction ACFs by heat-treatment process. Because of the porous properties, the specific capacitance was increased from 73 F/g to 119 F/g using cyclic voltammetry with 1 M $H_2SO_4$ at scan rates of 5 mV/s.

• Korean Chemical Engineering Research
• /
• v.45 no.3
• /
• pp.269-276
• /
• 2007

$TiO_2$-containing pitch fibers were prepared and various stabilization variables were investigated by characterizations of the fibers and behaviors of $TiO_2$ particles in the optimum stabilization conditions. When pitch fiber was stabilized by air at the optimum condition, the fiber weight increased as an increase of the stabilization temperature and a decrease of $TiO_2$ concentration. The carbonization yield was 71~82 wt.%, showing a decrease of the yield with the $TiO_2$ increase caused by the catalytic activity of $TiO_2$ to combustion. During the stabilization, newly developed carbonyl and carboxyl groups were introduced on the fiber surface and cross-linking reactions were progressed resulting the thermosetting property, which was verified by the replacement of hydrogen with oxygen. Pore size of the activated carbon fiber was increased by an increase in $TiO_2$ concentration. In the considerations of the aggregation behaviors of the $TiO_2$ particles, the optimum stabilization conditions of 0.5 wt.% $TiO_2$ containing petroleum-based pitch fiber were suggested as $280^{\circ}C$, 3 hr.

• Applied Chemistry for Engineering
• /
• v.32 no.1
• /
• pp.55-60
• /
• 2021

Fluorination was carried out to improve the adsorption performance of pitch-based activated carbon fibers (ACFs) onto acetic acid. Both plasma and direct gas fluorination were used for fluorination, and the acetic acid gas adsorption performance of fluorinated ACFs was investigated. X-ray photoelectron spectroscopy (XPS) is analyzed to determine the surface characteristics of ACFs, and the pore characteristics were analyzed by 77 K nitrogen adsorption. An adsorption performance was measured through gas chromatography, and it was confirmed that the breakthrough time of plasma fluorinated sample was 790 min and that the breakthrough time was delayed compared to that of using untreated one of 650 min. However, the breakthrough time of direct gas fluorinated sample was 390 min, indicating that the adsorption performance was inhibited. The plasma fluorinated ACFs showed an increase in the adsorption performance due to an electrostatic attraction between the acetic acid gas (CH3COOH) with the fluorine group introduced to the surface without changing its specific surface area. On the other hand, the specific surface area of the direct gas fluorinated ACFs decreased significantly up to 55%, and the physical adsorption effect on the acetic acid gas also reduced.