• Journal of Magnetics
• /
• v.15 no.4
• /
• pp.169-172
• /
• 2010

The coercivity mechanism in permanent magnets was analyzed according to the effects of domain nucleation and domain wall pinning. The coercivity mechanism of a TbCo thin film with high perpendicular magnetic anisotropy was considered in terms of the local inhomogeneity in the thin film. The initial magnetization curves of the TbCo thin films demonstrated domain wall pinning to be the main contributor to the coercivity mechanism than domain nucleation. Based on the coercivity model proposed by Kronmuller et al., the inhomogeneity size acting as a domain wall pinning site was determined. Using the measured values of perpendicular anisotropy constant ($K_u$), saturation magnetization ($M_s$), and coercivity ($H_c$), the inhomogeneity size estimated in a TbCo thin film with high coercivity was approximately 9 nm.

• 한국초전도학회:학술대회논문집
• /
• v.10
• /
• pp.262-267
• /
• 2000

To tap the possibility of exploiting the precipitates as flux-pinning center in the Bi-2223 superconducting system, as-received Bi-2223/Ag tapes with the starting composition of Bi$_{1.8}$Pb$_{0.4}$Sr$_2$Ca$_{2.2}$Cu$_3$O$_8$ were post-annealed at various temperature, oxygen partial pressure, and annealing time. The 2$^{nd}$ phases in the annealed specimen were analysed with XRD, SEM, TEM, and EDS. The size and the distribution of the precipitates such as (Ca,Sr)$_2$(Pb,Bi)O$_4$ and Bi$_{0.5}$Pb$_3$Sr$_2$Ca$_2$CuO$_{12+{\delta}}$ (3221) in the Bi-2223 matrix was controllable by varying heat-treatment condition without breaking the connectivity of the 2223 grains. The nano-size precipitates within the 2223 grains are conjectured as working as flux-pinning sites, resulting in increased J$_c$ value.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2007.05a
• /
• pp.66.1-66.1
• /
• 2007

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1241-1242
• /
• 2006

Electromagnetic properties of $CeO_2$ doped and undoped YBaCuO superconductors were evaluated to investigate the effect of pinning center on the magnetization and magnetic shielding. The variation $\DeltaM$ with doping was maximum for 3% doping and decrease with further doping. The magnetic shielding was evaluated by measuring the induced voltage in secondary coil and the voltage initially set to 0.5V, decreased to 0.17V and 0.28V respectively for the undoped and 3% $CeO_2$ doped sample. The much less change in the induced voltage for the 3% doped sample is attributed to the increased flux shielding by shielding vortex current. The $CeO_2$ was converted to fine $BaCeO_3$ particles which were trapped in YBaCuO superconductor during the reaction sintering. The trapped fine particles, $BaCeO_3$ may be acted as a flux pinning center.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2007.05a
• /
• pp.79.2-79.2
• /
• 2007

• Composites Research
• /
• v.35 no.5
• /
• pp.322-327
• /
• 2022

Composite lap joints have been extensively used due to their excellent properties and the demand for light structures. However, due to the weak mechanical properties in the thickness direction, the lap joint is easily fractured. various reinforcement methods that delay fracture by dispersing stress concentration have been applied to overcome this problem, such as z-pinning and conventional stitching. The Z-pinning is reinforcement method by inserting metal or carbon pin in the thickness direction of prepreg, and the conventional stitching process is a method of reinforcing the mechanical properties in the thickness direction by intersecting the upper and lower fibers on the preform. I-fiber stitching method is a promising technology that combines the advantages of both z-pinning and the conventional stitching. In this paper, the static and fatigue strengths of the single-lap joints reinforced by the I-fiber stitching process were evaluated. The single-lap joints were fabricated by a co-curing method using an autoclave vacuum bag process and I-fiber reinforcing effects were evaluated according to adherend thickness and stitching angle. From the experiments, the thinner the composite joint specimen, the higher the I-fiber reinforcement effect, and Ifiber stitched single lap joints showed a 52% improvement in failure strength and 118% improvement in fatigue strength.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.34 no.6
• /
• pp.438-441
• /
• 2021

The electrical characteristics of single-crystal composite superconductors produced by a melting process were studied by neutron irradiation. In order to improve the current characteristics of the YBa₂Cu₃O_7-y superconductor, it is necessary to form an effective flux pinning center inside the superconductor. In this study, an increase in flux pinning was attempted through neutron irradiation onto YBa₂Cu₃O_7-y superconductors. The neutron irradiation was performed at 30 MeV for 500 sec, The electrical properties of the superconductors were measured in a magnetic field of 5 Tesla at 50 K using a magnetic properties measurement system (MPMS). After neutron irradiation, the critical current density of the YBa₂Cu₃O_7-y superconductor in a 1 Tesla magnetic field was 1×10⁵ A/cm². Once neutrons were irradiated at 30 MeV and 10 μA for 500 sec, the critical current density was observed to increase significantly. When neutrons are irradiated to a superconductor, micro-defects are created in the superconductor, and they act as flux pinning centers that hold the magnetic field generated when an electric current flows.

• 한국초전도학회:학술대회논문집
• /
• v.9
• /
• pp.300-304
• /
• 1999

To tap the feasibility of exploiting the 2$^{nd}$ phases as flux-pinning centers in the (Bi,Pb)$_2Sr_2Ca_2CuO_{10}$ superconductor, the size and the distribution of the precipitates have been controlled by changing reaction temperature and time, oxygen partial pressure Po$_2$ and annealing condition. Various annealing heat treatments were also conducted on the as-received 61 filament Bi-2223 tapes with Bi$_{1.8}Pb_{0.4}Sr_2Ca_{2.2}Cu_3O_8$ starting composition and annealed specimen were analyzed with XRD, SEM, EDS and TEM.. The grain size of (Ca,Sr)$_2$(BiPb)O$_4$ or Bi$_{0.5}Pb_3Sr_2Ca_2CuO_{\delta}$ was controllable by optimizing the heat treatment condition and critical current density (J$_c$) showed dependence on the size of the 2$^{nd}$ phases.

• 한국초전도학회:학술대회논문집
• /
• 2007.07a
• /
• pp.77-77
• /
• 2007

• 한국초전도학회:학술대회논문집
• /
• 2007.07a
• /
• pp.4-4
• /
• 2007