• Journal of Electrochemical Science and Technology
• /
• v.10 no.4
• /
• pp.424-432
• /
• 2019

Planar BiVO₄ and 3 wt% Mo-doped BiVO₄ (abbreviated as Mo:BiVO₄) film were prepared by the facile spin-coating method on fluorine doped SnO₂(FTO) substrate in the same precursor solution including the Mo precursor in Mo:BiVO₄ film. After annealing at a high temperature of 450℃ for 30 min to improve crystallinity, the films exhibited the monoclinic crystalline phase and nanoporous architecture. Both films showed no remarkably discrepancy in crystalline or morphological properties. To investigate the effect of surface passivation exploring the Al₂O₃ layer, the ultra-thin Al₂O₃ layer with a thickness of approximately 2 nm was deposited on BiVO₄ film using the atomic layer deposition (ALD) method. No distinct morphological modification was observed for all prepared BiVO₄ and Mo:BiVO₄ films. Only slightly reduced nanopores were observed. Although both samples showed some reduction of light absorption in the visible wavelength after coating of Al₂O₃ layer, the Al₂O₃ coated BiVO₄ (Al₂O₃/BiVO₄) film exhibited enhanced photoelectrochemical performance in 0.5 M Na₂SO₄ solution (pH 6.5), having higher photocurrent density (0.91 mA/㎠ at 1.23 V vs. reversible hydrogen electrode (RHE), briefly abbreviated as V_RHE) than BiVO₄ film (0.12 mA/㎠ at 1.23 V_RHE). Moreover, Al₂O₃ coating on the Mo:BiVO₄ film exhibited more enhanced photocurrent density (1.5 mA/㎠ at 1.23 V_RHE) than the Mo:BiVO₄ film (0.86 mA/㎠ at 1.23 V_RHE). To examine the reasons, capacitance measurement and Mott-Schottky analysis were conducted, revealing that the significant degradation of capacitance value was observed in both BiVO₄ film and Al₂O₃/Mo:BiVO₄ film, probably due to degraded capacitance by surface passivation. Furthermore, the flat-band potential (V_FB) was negatively shifted to about 200 mV while the electronic conductivities were enhanced by Al₂O₃ coating in both samples, contributing to the advancement of PEC performance by ultra-thin Al₂O₃ layer.

• Journal of the Microelectronics and Packaging Society
• /
• v.27 no.2
• /
• pp.33-38
• /
• 2020

In the photoelectrochemical (PEC) water splitting, GaN is one of the most promising photoanode materials due to high stability in electrolytes and adjustable energy band position. However, the application of GaN is limited because of low efficiency. To improve solar to hydrogen conversion efficiency, we introduce a Cobalt Phosphate (Co-pi) catalyst by photo-electrodeposition. The Co-pi deposition GaN were characterized by SEM, EDS, and XPS, respectively, which illustrated that Co-pi was successfully decorated on the surface of GaN. PEC measurement showed that photocurrent density of GaN was 0.5 mA/㎠ and that of Co-pi deposited GaN was 0.75 mA/㎠. Impedance and Mott-Schottky measurements were performed, and as a result of the measurement, polarization resistance (R_p) and increased donor concentration (N_D) values decreased from 50.35 Ω to 34.16 Ω were confirmed. As a result of analyzing the surface components before and after the water decomposition, it was confirmed that the Co-pi catalyst is stable because Co-pi remains even after the water decomposition. Through this, it was confirmed that Co-pi is effective as a catalyst for improving GaN efficiency, and when applied as a catalyst to other photoelectrodes, it is considered that the efficiency of the PEC system can be improved.

• Journal of the Korean Ceramic Society
• /
• v.53 no.4
• /
• pp.400-405
• /
• 2016

Ferric oxide (${\alpha}-Fe_2O_3$, hematite) is an n-type semiconductor; due to its narrow band gap ($E_g=2.1eV$), it is a highly attractive and desirable material for use in solar hydrogenation by water oxidation. However, the actual conversion efficiency achieved with $Fe_2O_3$ is considerably lower than the theoretical values because the considerably short diffusion length (2-4 nm) of holes in $Fe_2O_3$ induces excessive charge recombination and low absorption. This is a significant hurdle that must be overcome in order to obtain high solar-to-hydrogen conversion efficiency. In consideration of this, it is thought that elemental doping, which may make it possible to enhance the charge transfer at the interface, will have a marked effect in terms of improving the photoactivities of ${\alpha}-Fe_2O_3$ photoanodes. Herein, we report on the synthesis by pulsed electrodeposition of ${\alpha}-Fe_2O_3$-based anodes; we also report on the resulting photoelectrochemical (PEC) properties. We attempted Ti-doping to enhance the PEC properties of ${\alpha}-Fe_2O_3$ anodes. It is revealed that the photocurrent density of a bare ${\alpha}-Fe_2O_3$ anode can be dramatically changed by controlling the condition of the electrodeposition and the concentration of $TiCl_3$. Under optimum conditions, a modified ${\alpha}-Fe_2O_3$ anode exhibits a maximum photocurrent density of $0.4mA/cm^2$ at 1.23 V vs. reversible hydrogen electrode (RHE) under 1.5 G simulated sunlight illumination; this photocurrent density value is about 3 times greater than that of unmodified ${\alpha}-Fe_2O_3$ anodes.

• Transactions of the Korean hydrogen and new energy society
• /
• v.18 no.3
• /
• pp.244-249
• /
• 2007

The present work considers the concept of enzymatic photoelectrochemical generation of hydrogen through water splitting using a Xe lamp as a source of light. A solar cell was applied to the system in order to shift the level of electrochemical energy of the system, resulting in the rate of hydrogen production at $43\;{\mu}mol/(cm^2{\times}hr)$ in cathodic compartment with an anodized tubular $TiO_2$ electrode(ATTE, $5^{\circ}C$/1hr in 0.5 wt% HF-$650^{\circ}C$/5hr). The trend of the rate of hydrogen production, for the ATTEs with different annealing temperature from $350^{\circ}C$ to $850^{\circ}C$, fairly well coincided with the photoelectrical properties measured by potentiostat. The actual chemical bias through imposition of two electrolytes of different pHs between anode(13.68) and cathode(7.5) was 0.24eV.

• Korean Journal of Materials Research
• /
• v.29 no.8
• /
• pp.491-496
• /
• 2019

In this study, we prepare pure $WO_3$ inverse opal(IO) film with a thickness of approximately $3{\mu}m$ by electrodeposition, and an ultra-thin $TiO_2$ layer having a thickness of 2 nm is deposited on $WO_3$ IO film by atomic layer deposition. Both sets of photoelectrochemical properties are evaluated after developing dye-sensitized solar cells(DSSCs). In addition, morphological, crystalline and optical properties of the developed films are evaluated through field-emission scanning electron microscopy(FE-SEM), High-resolution transmission electron microscopy(HR-TEM), X-ray diffraction(XRD) and UV/visible/infrared spectrophotometry. In particular, pure $WO_3$ IO based DSSCs show low $V_{OC}$, $J_{SC}$ and fill factor of 0.25 V, $0.89mA/cm^2$ and 18.9 %, achieving an efficiency of 0.04 %, whereas the $TiO_2/WO_3$ IO based DSSCs exhibit $V_{OC}$, $J_{SC}$ and fill factor of 0.57 V, $1.18mA/cm^2$ and 50.1 %, revealing an overall conversion efficiency of 0.34 %, probably attributable to the high dye adsorption and suppressed charge recombination reaction.

• Journal of the Korean Applied Science and Technology
• /
• v.30 no.1
• /
• pp.49-56
• /
• 2013

Excellent electron transport properties with enhanced light scattering ability for light harvesting have made well-ordered one dimensional $TiO_2$ nanotube(TNT) arrays an alternative candidate over $TiO_2$ nanoparticles in the area of solar energy conversion applications. The principal drawback of TNT arrays being activated only by UV light has been addressed by coupling the TNT with secondary materials which are visible light-triggered. As well as extending the absorption region of sunlight, the introduction of these foreign components is also found to influence the charge separation and electron lifetime of TNT. In this study, a novel method to fabricate the TNT-based composite photoelectrodes employing visible responsive $CuInS_2$ (CIS) nanoparticles is presented. The developed method is a square wave pulse-assisted electrochemical deposition approach to wrap the inner and outer walls of a TNT array with CIS nanoparticles. Instead of coating as a dense compact layer of CIS by a conventional non-pulsed-electrochemical deposition method, the nanoparticles pack relatively loosely to form a rough surface which increases the surface area of the composite and results in a higher degree of light scattering within the tubular channels and hence a greater chance of absorption. The excellence coverage of CIS on the tubular $TiO_2$ allows the construction of an effective heterojunction that exhibits enhanced photoelectrochemical performance.

• Journal of Powder Materials
• /
• v.17 no.3
• /
• pp.216-222
• /
• 2010

Self-standing $TiO_2$ nanotube arrays were fabricated by potentiostatic anodic oxidation method using pure Ti foil as a working electrode and ethylene glycol solution as electrolytes with small addition of $NH_4F$ and $H_2O$. The influences of anodization temperature and time on the morphology and formation of $TiO_2$ nanotube arrays were investigated. The fabricated $TiO_2$ nanotube arrays were applied as a photoelectrode to dye-sensitized solar cells. Regardless of anodizing temperature and time, the average diameter and wall thickness of $TiO_2$ nanotube show a similar value, whereas the thickness show a different trend with reaction temperature. The thickness of $TiO_2$ nanotube arrays anodized at $20^{\circ}C$ and $30^{\circ}C$ was time-dependent, but on the other hand its at $10^{\circ}C$ are independent of anodization time. The conversion efficiency is low, which is due to a morphology breaking of the $TiO_2$ nanotube arrays in manufacturing process of photoelectrode.

• Elastomers and Composites
• /
• v.47 no.1
• /
• pp.2-8
• /
• 2012

In this study, in order to develop renewable bio-based nanocomposites, multi-functional nanocomposites from soybean resins (AESO, MAESO) and nanoclay were prepared. Photoelectrodes for environmental friendly dye-sensitized solar cell using soybean resin were also prepared. Organo-modified nanoclay was directly dispersed in functionalized soybean resins after mixing with styrene as a comonomer and radical initiator was used to copolymerize the nanocomposites. The observed morphology was a mixture of intercalated/exfoliated structure and the physical properties were improved by adding nanoclay. A nanocomposite using MAESO, which added COOH functional group to the soybean resin, showed better dispersibility than AESO composites. Ultrasonic treatment of the nanocomposites also improved the physical properties. Nanoporous $TiO_2$ photoelectrode was also prepared using soybean resins as a binder, after acid-treatment of $TiO_2$ surface using nitric acid. Dye-sensitized solar cells were prepared after adsorbing dye molecules on it. The $TiO_2$ photoelectrode prepared using soybean binder had high current density because of increased surface area by improved dispersibility. The photoelectrochemical properties and conversion efficiency of the solar cell were significantly improved using the soybean binder.

• Transactions of the Korean hydrogen and new energy society
• /
• v.11 no.4
• /
• pp.161-169
• /
• 2000

In the case of photocatalytic hydrogen production from water, the performance-property relationships of CdS-TiO2 film type composite catalysts were investigated. To control the physical properties of the primary particles, the mixture of CdS and TiO2 nano-sols prepared by the sol-gel method at room temperature was hydrothermally treated at 240oC for 12hr. The film electrodes were prepared by the casting method. The photocurrents measured by a photoelectrochemical method and the hydrogen production rates measured by a photochemical method were closely dependent on the physical properties such as crystalline form, primary particle size and CdS/TiO2 mole ratio, and these varied in the range of 1.2~2.6 mA/cm2 and $1.0{\sim}1.6{\times}10-3mol/hr$, respectively.

• Korean Journal of Materials Research
• /
• v.27 no.11
• /
• pp.631-635
• /
• 2017

We report facile solution processing of mesoporous hematite (${\alpha}-Fe_2O_3$) thin films for high efficiency solar-driven water splitting. $Fe_2O_3$ thin films were prepared on fluorine doped tin oxide(FTO) conducting substrates by spin coating of a precursor solution followed by annealing at $550^{\circ}C$ for 30 min. in air ambient. Specifically, the precursor solution was prepared by dissolving non-toxic $FeCl_3$ as an Fe source in highly versatile dimethyl sulfoxide(DMSO) as a solvent. The as-deposited and annealed thin films were characterized for their morphological, structural and optical properties using field-emission scanning electron microscopy(FE-SEM), X-ray diffraction(XRD), X-ray photoelectron spectroscopy(XPS) and UV-Vis absorption spectroscopy. The photoelectrochemical performance of the precursor (${\alpha}-FeOOH$) and annealed (${\alpha}-Fe_2O_3$) films were characterized and it was found that the ${\alpha}-Fe_2O_3$ film exhibited an increased photocurrent density of ${\sim}0.78mA/cm^2$ at 1.23 V vs. RHE, which is about 3.4 times higher than that of the ${\alpha}-FeOOH$ films ($0.23mA/cm^2$ at 1.23 V vs. RHE). The improved performance can be attributed to the improved crystallinity and porosity of ${\alpha}-Fe_2O_3$ thin films after annealing treatment at higher temperatures. Detailed electrical characterization was further carried out to elucidate the enhanced PEC performance of ${\alpha}-Fe_2O_3$ thin films.