• 한국세라믹학회지
• /
• 제45권8호
• /
• pp.477-481
• /
• 2008

$Eu^{2+}$ and $Dy^{3+}$ co-doped strontium aluminate, $SrAl_2O_4$ long phosphorescent phoshor was fabricated and its photoluminescence was characterized. The phosphor, $SrAl_2O_4:Eu^{2+},Dy^{3+}$ was synthesized by a coprecipitation in which metal salts of $Sr(NO_3)_2$, $Al(NO_3)_3{\cdot}9H_2O$, were dissolved in $(NH_4)_2CO_3$ solution with adding $Eu(NO_3)_3{\cdot}5H_2O$ and $Dy(NO_3)_3{\cdot}5H_2O$ as a activator and co-activator, respectively. The coprecipitated products were separated from solution, washed, and dried in a vacuum dry oven. The dried powders were then mixed with 3 wt% $B_2O_3$ as a flux and heated at $800{\sim}1400^{\circ}C$ for 3 h under the reducing ambient atmosphere of 95%Ar+$5%H_2$ gases. For the synthesized $SrAl_2O_4:Eu^{2+},Dy^{3+}$, properties of photoluminescence such as emission, excitation and decay time were examined. The emission intensity increased as the annealing temperature increased and showed a maximum peak intensity at 510 nm with a broad band from $400{\sim}650\;nm$. Monitored at 520 nm, the excitation spectrum showed a maximum peak intensity at $315{\sim}320\;nm$ wavelength with a broad band from $200{\sim}500\;nm$ wavelength. The decay time of $SrAl_2O_4:Eu^{2+},Dy^{3+}$ increased as the annealing temperature increased.

• 한국결정성장학회지
• /
• 제11권2호
• /
• pp.71-77
• /
• 2001

고상반응법에 의해 제조된 $SrAl_2$$O_4$ : $Eu^{2+}$,$Dy^{3+}$ 계 형광체에 $Dy_2$$O_3$의 농도를 0.0~9.5mol%까지 변화시켜, $Dy_2$$O_3$의 첨가량에 따른 결정특성과 장잔광 축광재료로서 가장 중요한 발광 및 장잔광 특성을 조사하였다. $SrAl_2$$O_4$ : $Eu^{2+}$,$Dy^{3+}$ 계 형광체는 $Dy_2$$O_3$의 농도에 관계없이 녹색의 520nm파장을 최대 발광파장으로 하는 발광스펙트럼을 나타내었고, 발광특성을 크게 저해하지 않는 $SrAl_2$$O_4$의 단일상을 얻기 위한 농도는 1.0mol%이하가 적절하였다. 또한 $SrAl_2$$O_4$ : $Eu^{2+}$,$Dy^{3+}$ 형광체의 잔광 강도는 $Dy_2$$O_3$의 농도에 무관하게 시간에 따라 모든 시료에서 지수 함수적으로 감소하나, $Dy_2$$O_3$의 농도가 1.0mol% 이하인 경우에 발광의 감쇠속도가 작은 뛰어난 장잔광특성을 나타내었다.

• 한국결정성장학회지
• /
• 제27권1호
• /
• pp.42-46
• /
• 2017

스컬용융법으로 $SrAl_2O_4$ : $Eu^{2+}$,$Dy^{3+}$ 형광체 합성을 하였으며, 합성한 형광체의 산화물 몰비는 $SrCO_3$ : $Al(OH)_3$ : $Eu_2O_3$ : $Dy_2O_3$= 1 : 2 : 0.015 : 0.02였다. 결정구조 및 표면 형상은 X-선 회절분석과 주사전자현미경으로 규명하였다. 합성한 $SrAl_2O_4$ : $Eu^{2+}$,$Dy^{3+}$의 광학적 특성인 여기, 발광 및 장잔광 특성의 심도 있는 연구를 위해 PL(photoluminescence) 분광계로 측정하였다. PL 측정을 통해 360 nm 영역에서 여기(excitation)되고, 300~420 nm의 파장까지 여기가 일어남을 확인하였다. 발광(emission)스펙트럼은 450~600 nm의 파장에서 폭넓은 스펙트럼을 보였으며, 530 nm에서 최대 발광파장을 나타내었다. $SrAl_2O_4$ : $Eu^{2+}$,$Dy^{3+}$ 형광체는 오랜 시간 동안 발광하는 장잔광 특성을 나타내었다.

• Bulletin of the Korean Chemical Society
• /
• 제34권9호
• /
• pp.2609-2615
• /
• 2013

A series of fluorene-carbazole copolymers containing the pendant phosphor chromophore $Ir(absn)_2(acac)$ (absn: 2-(1-naphthyl)benzothiazole; acac: acetylacetone) were designed and synthesized via Yamamoto coupling. In the film state, these copolymers exhibited absorption and emission peaks at approximately 389 and 426 nm, respectively, which originated from the fluorene backbone. However, in electroluminescent (EL) devices, a significantly red-shifted emission at approximately 611 nm was observed, which was attributed to the pendant iridium(III) complex. Using these copolymers as a single emission layer, polymer light-emitting devices with ITO/PEDOT:PSS/polymer:DNTPD/TmPyPb/LiF/Al configurations exhibited a saturated red emission at 611 nm. The attached iridium(III) complex had a significant effect on the EL performance. A maximum luminous efficiency of 0.85 cd/A, maximum external quantum efficiency of 0.77, maximum power efficiency of 0.48 lm/W, and maximum luminance of 883 $cd/m^2$ were achieved from a device fabricated with the copolymer containing the iridium(III) complex in a 2% molar ratio.

• 한국결정성장학회지
• /
• 제8권3호
• /
• pp.493-497
• /
• 1998

부활제인 $Eu_2O_3$의 농도를 변화시킨 $Sr_{1-x}Eu_xAl_2O_4$(x=0.005~0.2mol%)계 장잔광 형광체를 98%Ar+2% H2의 환원분위기에서 고상반응시켜 합성한 후 X-선 회절실험과 장잔광 축광재료로서 가장 중요한 발광특성과 장잔광 특성을 조사하였다. $SrAl_2O_4:Eu^{2+}$계 형광체는 $Eu_2O_3$의 농도에 관계없이 녹황색의 520nm파장을 최대 발광파장으로 하는 발광스펙트럼을 나타내었으나, 발광특성을 크게 저해하지 않는 SrAl2O4의 단일상을 얻기 위한 농도는 0.05mol% 이하가 적절하였다. 또한 $SrAl_2O_4:Eu^{2+}$ 형광체의 잔광강도는 $Eu_2O_3$의 농도에 무관하게 시간에 따라 모든 시료에서 지수 함수적으로 감소하나, Eu2O3의 농도가 0.05mol% 이하인 경우에 발광의 감쇠속도가 작은 뛰어난 장잔광특성을 나타내었다.

• 한국재료학회지
• /
• 제8권11호
• /
• pp.999-1004
• /
• 1998

$SrAl_2O_4$:$Eu^{2+}, Dy^{3+}$ 축광성 형광체의 합성에 있어서 $B_2O_3$는 일반적으로 고상반응의 촉진을 위한 플럭스로서 첨가된다. 본 연구에서는 플럭스로 첨가되는 $B_2O_3$가 $SrAl_2O_4$:$Eu^{2+}, Dy^{3+}$ 형광체의 결정구조 및 잔광 특성에 미치는 영향을 조사하였다. 합성된 $SrAl_2O_4$:$Eu^{2+}, Dy^{3+}$ 형광체는 520nm에서 최대 피크를 갖는 폭넓은 발광 스펙트럼을 나타내었고, $B_2O_3$ 첨가량의 5wt%일 때 최대값을 나타내었다. $B_2O_3$의 첨가에 의해 $SrAl_2O_4$:$Eu^{2+}, Dy^{3+}$ 결정 내부에는 균일 변형(uniform strain)이 발생하였고 이 결과로 결정격자의 a축과 c축의 길이 및 $\beta$각이 감소하여다. 그리고 $SrAl_2O_4$ 결정내부의 균일 변형은 $Eu^{2+}$이온의 여기과정에서 발생하는 정공(hole)의 포획 사이트인 음이온 결함(negative defect)을 다량 발생시키는 원인이 되고, 결과적으로 $SrAl_2O_4$:$Eu^{2+}, Dy^{3+}$ 결정의 잔광 특성을 향상시키는 것으로 생각되었다.