• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.10a
• /
• pp.211.1-211
• /
• 2003

• Korean Membrane Journal
• /
• v.9 no.1
• /
• pp.34-42
• /
• 2007

A perovskite-type ($La_{0.6}Sr_{0.4}Ti_{0.2}Fe_{0.8}O_{3-{\delta}}$) dense ceramic membrane was prepared by polymerized complex method, using citric acid as a chelating agent and ethylene glycol as an organic stabilizer. Effect of Ti addition on lanthanum-strontium ferrite mixed conductor was investigated by evaluating the thermal expansion coefficient, the oxygen flux, the electrical conductivity, and the phase stability. The thermal expansion coefficient in air was $21.19\;{\times}\;10^{-6}/K$ at 473 to 1,223 K. At the oxygen partial pressure of 0.21 atm ($20%\;O_2$), the electrical conductivity increased with temperature and then decreased after 973 K. The decrement in electrical conductivity at high temperatures was explained by a loss of the lattice oxygen. The oxygen flux increased with temperature and was $0.17\;mL/cm^2{\cdot}min$ at 1,223 K. From the temperature-dependent oxygen flux data, the activation energy of oxygen ion conduction was calculated and was 80.5 kJ/mol at 1,073 to 1,223 K. Also, the Ti-added lanthanum-strontium ferrite mixed conductor was structurally and chemically stable after 450 hours long-term test at 1,173 K.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1112-1113
• /
• 2006

The perovskite- type oxide $(ABO_3)$ containing transition metals on the B-site show mixed (electronic/ionic) conductivity. These mixed-conductivity oxides are promising materials for oxygen permeating membranes. The main objective of this research work is to synthesize and characterization ceramic powders of the Sr-Co-Fe-O system for methane conversion using membrane reactor. SCFO powders were synthesized from the route was based on the complex method of combination of acid EDTA and citrate and shown be available by control efficient of synthesis to performed $SrCo_{0.8}Fe_{0.2}O_{3-\delta$, moreover, it presented easy implementation, reproducibility and operation. Powder ceramic was characterized by XRD, microscopic optic, SEM and TG-DTA.

• Korean Chemical Engineering Research
• /
• v.47 no.3
• /
• pp.310-315
• /
• 2009

Perovskite-type ceramic powder, $La_{0.7}Sr_{0.3}Co_{0.3}Fe_{0.7}O_{3-{\delta}}$, have been synthesized successfully by the citrate method. As a result of TGA for precursor, metal-citrate complex in precursor was decomposed in the temperature range of $150{\sim}650^{\circ}C$. XRD analysis showed the single perovskite structure was observed over $1,000^{\circ}C$ without impurities. Typical dense membrane with 1.6 mm thickness has been prepared using as-prepared powder by pressing unilaterally and sintering at $1,300^{\circ}C$. The electrical conductivity of $La_{0.7}Sr_{0.3}Co_{0.3}Fe_{0.7}O_{3-{\delta}}$ membrane increased with increasing temperature at atmosphere of air and then decreased over $600^{\circ}C$ due to oxygen loss from the crystal lattice. The oxygen flux of $La_{0.7}Sr_{0.3}Co_{0.3}Fe_{0.7}O_{3-{\delta}}$ membrane in the range of 700 to $950^{\circ}C$ increased with the increasing temperature from 0.045 to $0.415ml/cm^2{\cdot}min$. The activation energy for oxygen permeation was calculated to be 89.17 kJ/mol.

• Journal of the Korean Ceramic Society
• /
• v.38 no.9
• /
• pp.787-793
• /
• 2001

$La_{0.6}Sr_{0.4}Co_{0.2}Fe_{0.8}O_{3-{\delta}}$ membranes were fabricated by solid-state reaction. We investigated sintering behavior and oxygen permeation flux as a function of time-on-stream, temperature and upstream oxygen partial pressure. The oxygen was permeated at temperatures form 750$^{\circ}$C to 950$^{\circ}$C by mixed conducting through oxygen vacancy diffusion in the dense membrane. The oxygen permeation flux through the membrane were about 0.1ml/$cm^3{\cdot}$min at 850$^{\circ}$C. A constant time was required for reaching stable oxygen flux, and oxygen partial pressure affected the oxygen permeation fluxes.

• Journal of Electrochemical Science and Technology
• /
• v.9 no.3
• /
• pp.212-219
• /
• 2018

Perovskite type ceramic membranes which exhibit dual ion conduction (proton and oxygen ion conduction) can permeate water and can aid solving operational problems such as temperature gradient and carbon deposition associated with a working solid oxide fuel cell. From this point of view, it is crucial to reveal water transport mechanism and especially the nature of the surface sites that is necessary for water incorporation and evolution. $BaCe_{0.8}Y_{0.2}O_{3-{\alpha}}$ (BCY20) was used as a model proton and oxygen ion conducting membrane in this work. Four different catalytically modified membrane configurations were used for the investigations and water flux was measured as a function of temperature. In addition, CO was introduced to the permeate side in order to test the stability of membrane against water and $CO/CO_2$ and post operation analysis of used membranes were carried out. The results revealed that water incorporation occurs on any exposed electrolyte surface. However, the magnitude of water permeation changes depending on which membrane surface is catalytically modified. The platinum increases the water flux on the feed side whilst it decreases the flux on the permeate side. Water flux measurements suggest that platinum can block water permeation on the permeate side by reducing the access to the lattice oxygen in the surface layer.

• Journal of the Korean Ceramic Society
• /
• v.39 no.10
• /
• pp.994-1000
• /
• 2002

Oxygen permeability and the mechanical properties of mixed ionic-electronic conductive $La_{0.6}Sr_{0.4}Co_{0.2}Fe_{0.8}O_{3-{\delta}}$ perovskite-type membrane, fabricated by solid state reaction, were investigated with regard to microstructure. The microstructure of the membrane was controlled by changing the sintering temperature and holding time. The average grain size and relative density were evaluated as a function of sintering conditions. As the fraction of grain boundary decreased, oxygen permeability showed a tendency to increase. Especially the maximum oxygen flux of 0.37 ml/$cm^2$${\cdot}$min was measured for the specimen sintered at 1300${\circ}C$ for 10 h, which has high density and relatively large grain size. Fracture strength was dependent on the relative density of sintered body, while fracture toughness increased with average grain size.

• Journal of the Korean Ceramic Society
• /
• v.38 no.10
• /
• pp.886-893
• /
• 2001

We synthesized $La_{0.6}Sr_{0.4}Co_{0.2}Fe_{0.8}O_{3-\delta}$ powders by coprecipitation, citration and solid-state reactions. The oxygen permeation membranes were fabricated by cold isostatic pressing of the synthesized powders, followed by sintering in air. All powders and membranes consist of perovskite phases. The coprecipitated powders showed the highest surface area ($7.5m^2/g$) but strontium deficiency was found during washing and filtering in the process. The membrane with lower relative density was fabricated by citration method. On the other hand, solid state reacted powders had high relative density (95%), and mechanical properties showed superior properties. Especially, the composition of the solid-state reacted powders was relatively well-controlled.

• Membrane Journal
• /
• v.11 no.4
• /
• pp.143-151
• /
• 2001

We have fabricated mixed-ionic conducting membranes, L $a_{0.6}$S $r_{0.4}$ $Co_{0.2}$F $e_{0.8}$ $O_{3-}$$\delta$/ and L $a_{0.7}$S $r_{0.3}$G $a_{0.6}$F $e_{0.4}$ $O_{3-}$$\delta$/ by the solid state method. Ceramic membranes consisted of perovskite-type structures and exhibited high relative density, >95%. Especially, dense L $a_{0.6}$S $r_{0.4}$Co $O_{3-}$$\delta$/ layer was coated on the L $a_{0.7}$S $r_{0.3}$G $a_{0.6}$F $e_{0.4}$ $O_{3-}$$\delta$/ membranes by using screen printing technique in order to improve oxygen ion flux. We measured oxygen ion flux on uncoated L $a_{0.6}$S $r_{0.4}$ $Co_{0.2}$F $e_{0.8}$ $O_{3-}$$\delta$/, uncoated L $a_{0.7}$S $r_{0.3}$G $a_{0.6}$F $e_{0.4}$ $O_{3-}$$\delta$/, and coated L $a_{0.7}$S $r_{0.3}$G $a_{0.6}$F $e_{0.4}$ $O_{3-}$$\delta$/ membranes. The L $a_{0.6}$S $r_{0.4}$ $Co_{0.2}$F $e_{0.8}$ $O_{3-}$$\delta$/ membranes showed the highest flux, 0.26 mL/min.$\textrm{cm}^2$ at 90$0^{\circ}C$, after steady state had been reached. The oxygen flux of coated L $a_{0.7}$S $r_{0.3}$G $a_{0.6}$F $e_{0.4}$ $O_{3-}$$\delta$/ membranes showed higher value, 0.19 mL/min.$\textrm{cm}^2$ at 95$0^{\circ}C$. This flux was as much as 2 or 3 times higher than those of uncoated L $a_{0.7}$S $r_{0.3}$G $a_{0.6}$F $e_{0.4}$ $O_{3-}$$\delta$/ membranes. 3-$\delta$/ membranes.X> 3-$\delta$/ membranes.membranes.

• Journal of the Korean Ceramic Society
• /
• v.40 no.6
• /
• pp.594-600
• /
• 2003

L $a_{0.7}$S $r_{0.3}$G $a_{0.6}$F $e_{0.4}$ $O_{3-}$$\delta$/ perovskite-type mixed conducting membranes, which could permeate oxygen selectively, have been fabricated and the microstructural features developed by varying the sintering conditions have been analyzed. The effects of surface modification and the membrane thickness on oxygen permeability have been evaluated under He/air environment. With increasing a grain boundary fraction, the overall oxygen permeability decreased. The syngas (CO+ $H_2$) has been produced by partial oxidation reaction of methane with the oxygen permeated through the membrane. Methane conversion and syngas yield have been evaluated as functions of the compositional ratio of feed gas and reaction temperature. In long-term duration test for 600 h, under C $H_4$+He/air environment, L $a_{0.7}$S $r_{0.3}$G $a_{0.6}$F $e_{0.4}$ $O_{3-}$$\delta$/ membrane showed a highly stable performance.