Synthesis and electrochemical properties of layered $Li[Ni_xCo_{1-2x}Mn_x]O_2$ materials for lithium secondary batteries prepared by mechanical alloying (기계적 합금법을 이용한 리튬 2차 전지용 층상 양극물질 $Li[Ni_xCo_{1-2x}Mn_x]O_2$ 의 합성 및 전기화학적 특성에 관한 연구)

  • 박상호;신선식;선양국
    • Proceedings of the Korea Crystallographic Association Conference
    • /
    • 2002.11a
    • /
    • pp.16-16
    • /
    • 2002
  • The presently commercialized lithium-ion batteries use layer structured LiCoO₂ cathodes. Because of the high cost and toxicity of cobalt, an intensive search for new cathode materials has been underway in recent years. Recently, a concept of a one-to-one solid state mixture of LiNO₂ and LiMnO₂, i.e., Li[Ni/sub 0.5/Mn/sub 0.5/]O₂, was adopted by Ohzuku and Makimura to overcome the disadvantage of LiNiO₂ and LiMnO₂. Li[Ni/sub 0.5/Mn/sub 0.5/]O₂ has the -NaFeO₂ structure, which is characteristic of the layered LiCoO₂ and LiNiO₂ structures and shows excellent cycleability with no indication of spinel formation during electrochemical cycling. Layered Li[Ni/sub x/Co/sub 1-2x/Mn/sub x/]O₂ (x = 0.5 and 0.475) materials with high homogeneity and crystallinity were synthesized using a mechanical alloying method. The Li[Ni/sub 0.475/Co/sub 0.05/Mn/sub 0.475/]O₂ electrode delivers a high discharge capacity of 187 mAh/g between 2.8 and 4.6 V at a high current density of 0.3 mA/㎠(30 mA/g) with excellent cycleability. The charge/discharge and differential capacity vs. voltage studies of the Li[Ni/sub x/Co/sub 1-2x/Mn/sub x/]O₂ (x = 0.5 and 0.475) materials showed only one redox peak up to 50 cycles, which indicates that structural phase transitions are not occurred during electrochemical cycling. The magnitude of the diffusion coefficients of lithium ions for Li[Ni/sub x/Co/sub 1-2x/Mn/sub x/]O₂(x = 0.5 and 0.475) are around 10/sup -9/ ㎠/s measured by the galvanostatic intermittent titration technique (GITT).

  • PDF

Fabrication of intermediate-temperature solid oxide fuel cells with La0.6Sr0.4CoO3-𝛿 nanowires based on polycarbonate membrane filter (Polycarbonate 멤브레인 필터 기반 La0.6Sr0.4CoO3-𝛿 나노와이어가 적용된 중온형 고체산화물 연료전지 제작)

  • Kang Han;Young Gyun Goh;Gyu Jin Hwang;Hyun Ho Shin;Sung Soo Shin
    • Particle and aerosol research
    • /
    • v.20 no.3
    • /
    • pp.95-102
    • /
    • 2024
  • Enhancing the oxygen surface exchange reaction by increasing the specific surface area of the electrode is a promising structural approach to lowering the operating temperature of solid oxide fuel cells (SOFCs). Nanowire structures, due to their high specific surface area and lower tortuosity of ion and electron conduction pathways, play a vital role in enhancing SOFC electrode performance. In this study, we synthesized La0.6Sr0.4CoO3-𝛿 (LSC) nanowires using a polycarbonate membrane filter as a nanotemplate and applied them to the cathode for intermediate-temperature SOFC fabrication. The fabricated cell exhibited a 10% increase in peak power density at 650℃, achieving 0.506 W·cm-2, compared to cell using only commercial LSC powder. Furthermore, distribution of relaxation times analysis revealed a 15% reduction in area-specific polarization resistance in the mid-frequency range. These findings demonstrated that the electrode with LSC nanowires fabricated through electrospray deposition can significantly improve electrochemical performance of intermediate-temperature SOFC.

Improvement of lower hybrid current drive systems for high-power and long-pulse operation on EAST

  • M. Wang;L. Liu;L.M. Zhao;M.H. Li ;W.D. Ma;H.C. Hu ;Z.G. Wu;J.Q. Feng ;Y. Yang ;L. Zhu ;M. Chen ;T.A. Zhou;H. Jia;J. Zhang ;L. Cao ;L. Zhang ;R.R. Liang;B.J. Ding ;X.J. Zhang ;J.F. Shan;F.K. Liu ;A. Ekedahl ;M. Goniche ;J. Hillairet;L. Delpech
    • Nuclear Engineering and Technology
    • /
    • v.54 no.11
    • /
    • pp.4102-4110
    • /
    • 2022
  • Aiming at high-power and long-pulse operation up to 1000 s, some improvements have been made for both 2.45 GHz and 4.6 GHz lower hybrid (LH) systems during the recent 5 years. At first, the guard limiters of the LH antennas with graphite tiles were upgraded to tungsten, the most promising material for plasma facing components in nuclear fusion devices. These new guard limiters can operate at a peak power density of 12.9 MW/m2. Strong hot spots were usually observed on the old graphite limiters when 4.6 GHz system operated with power >2.0 MW [B. N. Wan et al., Nucl. Fusion 57 (2017) 102019], leading to a reduction of the maximum power capability. With the new limiters, 4.6 GHz LH system, the main current drive (CD) and electron heating tool for EAST, can be operated with power >2.5 MW routinely. Long-pulse operation up to 100 s with 4.6 GHz LH power of 2.4 MW was achieved in 2021 and the maximal temperature on the guard limiters measured by an infrared (IR) camera was about 540 ℃, much below the permissible value of tungsten material (~1200 ℃). A discharge with a duration of 1056 s was achieved and the 4.6 GHz LH energy injected into the plasma was up to 1.05 GJ. Secondly, the fully-active-multijunction (FAM) launcher of 2.45 GHz system was upgraded to a passive-active-multijunction (PAM), for which the density of optimum coupling was relatively low (below the cut-off value). Good coupling with reflection coefficient ~3% has been achieved with plasma-antenna distance up to 11 cm for the new PAM. Finally, in order to eliminate the effect of ion cyclotron range of frequencies (ICRF) wave on 4.6 GHz LH wave coupling, the location of the ICRF launcher was changed to a port that is located 157.5° toroidally from the 4.6 GHz LH system and is not magnetically connected.

Nanocrystalline Si formation inside SiNx nanostructures usingionized N2 gas bombardment (이온화 N2 가스 입사를 이용한 SiNx 나노구조 내부의 Si 나노결정 형성)

  • Jung, Min-Cherl;Park, Young-Ju;Shin, Hyun-Joon;Byun, Jun-Seok;Yoon, Jae-Jin;Park, Yong-Sup
    • Journal of the Korean Vacuum Society
    • /
    • v.16 no.6
    • /
    • pp.474-478
    • /
    • 2007
  • Nanostructures of $SiN_x$ were made by bombardment of ionized $N_2$ on Si surface and subsequent annealing. Atomic force micrograph showed the density of $SiN_x$ nanostructures was $3\times10^{10}/cm^2$. Their lateral size and height were 40$\sim$60 nm and 15 nm, respectively. The chemical state of the nanostructure was measured using X-ray photoelectron spectroscopy, which changed from $SiN_x$ to $Si_3N_4\;+\;SiN_x$ as the bombarding ionized gas current increases. Upon annealing, transmission electron micrograph showed a clear evidence for crystalline Si phase formation inside the $SiN_x$ nanostructures. Photoluminescence peak observed at around 400nm was thought to be originated from the interface states between the nanocrystalline Si and surrounding $SiN_x$ nanostructures.

Fabrication of the Plasma Focus Device for Advanced Lithography Light Source and Its Electro Optical Characteristics in Argon Arc Plasma (차세대 리소그래피 빛샘 발생을 위한 플라스마 집속 장치의 제작과 아르곤 아크 플라스마의 발생에 따른 회로 분석 및 전기 광학적 특성 연구)

  • Lee S.B.;Moon M.W.;Oh P.Y.;Song K.B.;Lim J.E.;Hong Y.J.;Yi W.J.;Choi E.H.
    • Journal of the Korean Vacuum Society
    • /
    • v.15 no.4
    • /
    • pp.380-386
    • /
    • 2006
  • In this study, we had designed and fabricated the plasma focus device which can generate the light source for EUV(Extreme Ultra Violet) lithography. And we also have investigated the basic electrical characteristics of currents, voltages, resistance and inductance of this system. Voltage and current signals were measured by C-dot and B-dot probe, respectively. We applied various voltages of 1.5, 2, 2.5 and 3 kV to the anode electrode and observed voltages and current signals in accordance with various Ar pressures of 1 mTorr to 100 Torr in diode chamber. It is observed that the peak values of voltage and current signals were measured at 300 mTorr, where the inductance and impedance were also estimated to be 73 nH and $35 m{\Omega}$ respectively. The electron temperature has been shown to be 13000 K at the diode voltage of 2.5 kV and this gas pressure of 300 mTorr. It is also found that the ion density Ni and ionization rate 0 have been shown to be $N_i = 8.25{\times}10^{15}/cc$ and ${\delta}$= 77.8%, respectively by optical emission spectroscopy from assumption of local thermodynamic equilibrium(LTE) plasma.

Growth and Characterization of AgGa$Se_2$ Single Crystal Thin Films by Hot Wall Epitaxy (Hot Wall Epitaxy (HWE)법에 의한 AgGa$Se_2$ 단결정 박막 성장과 특성)

  • Hong, Gwang-Jun;Lee, Gwan-Gyo;Park, Jin-Seong
    • Korean Journal of Materials Research
    • /
    • v.11 no.5
    • /
    • pp.419-426
    • /
    • 2001
  • The stochiometric $AgGaSe_2$ polycrystalline mixture of evaporating materials for the $AgGaSe_2$ single crystal thin film was prepared from horizontal furnace. To obtain the single crystal thin films, $AgGaSe_2$ mixed crystal and semi-insulating GaAs(100) wafer were used as source material and substrate for the Hot Wall Epitaxy (HWE) system, respectively. The source and substrate temperature were fixed at$ 630^{\circ}C$ and $420^{\circ}C$, respectively. The thickness of grown single crystal thin films is 2.1$\mu\textrm{m}$. The single crystal thin films were investigated by photoluminescence and double crystal X-ray diffraction(DCXD) measurement. The carrier density and mobility of AgGaSe$_2$ single crystal thin films measured from Hall effect by van der Pauw method are $4.89\Times10^{17}$ cm$^{-3}$ , 129cm2/V.s at 293K, respectively. From the Photocurrent spectrum by illumination of perpendicular light on the c-axis of the AgGaSe$_2$ single crystal thin film, we have found that the values of spin orbit splitting $$\Delta$S_{o}$ and the crystal field splitting $\Delta$C$_{r}$, were 0.1762eV and 0.2474eV at 10K, respectively. From the photoluminescence measurement of AgGaSe$_2$ single crystal thin film, we observed free excision (EX) observable only in high quality crystal and neutral bound exciton ($D^{o}$ , X) having very strong peak intensity. And, the full width at half maximum and binding energy of neutral donor bound excition were 8mev and 14.1meV, respectively. By Haynes rule, an activation energy of impurity was 141 meV.ion energy of impurity was 141 meV.

  • PDF