• The Korean Journal of Ceramics
• /
• 제4권3호
• /
• pp.199-203
• /
• 1998

$Pb(Zr, Ti)O_3$ (Pb:Zr:Ti=1:0.52:0.48) thin films were prepared on single crystal MgO(100) substrates by dipping-pyrolysis process using a solution of constituent metal naphthenates as starting materials. The solution was spin-coated onto substrate and the precursor films were pyrolyzed at $200^{\circ}C$ in air or at $200^{\circ}C$ in argon for 1, 2, 5 and 24h, followed by final heat treatment at $750^{\circ}C$. For all the films, highly (h00)/(00l)-oriented Pb$Pb(Zr, Ti)O_3$ thin films with smooth surfaces and crack-free were obtained, whereas thin film pyrolyzed in air for 24 h exhibited polycrystalline character. According to the pole-figure analysis, epitaxy of the product films was found to depend on pyrolysis atmosphere.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1989년도 춘계학술대회 논문집
• /
• pp.70-73
• /
• 1989

(1-x-y)Pb($Zn_{1/3}Nb_{2/3})O_3-Ba(Zn_{1/3}Nb_{2/3})O_3-PbTiO_3(0.12{\leq}x{\leq}0.21, 0.24{\leq}y{\leq}0.33$) ternary compound ceramics were fabricated by the mixed oxide method. The sintering temperature and time were 1050 [$^{\circ}C$], 2[hr]. Morphotropic phase boundary region was chosen for the composition. 0.55 PZN-0.21 BZN-0.24 PT specimen had the highest value of relative dielectric constants, 5353. The curie temperature of specimens were increased linearly with PT content. Near the morphotropic phase boundary, electro-mechanical coupoling factor and mechanical quality factor of the specimens had the highest values.

• 한국세라믹학회지
• /
• 제35권9호
• /
• pp.969-973
• /
• 1998

Pb(Zr, Ti)O3 (PZT) (Zr:Ti= 52: 48) thin films were prepared on MgO(100) substrates by dipping-py-rolysis process using metal naphthenates as starting materials. Thin films were fabricated by spin coating technique and the precursor films were prefired at 20$0^{\circ}C$ in air for 0.5, 1, 2, 3, and 24 h followed by final heat treatment at 75$0^{\circ}C$ for 30min. Film prefired for 24 h lost orientational properties and pole figure analysis showed the lost of the epitaxial relationship between the films and substrate while highly a/c-axis oriented thin films were obtained for the samples prefired for 1, 2, and 3h.

• 한국세라믹학회지
• /
• 제24권4호
• /
• pp.397-403
• /
• 1987

Pb(Zr0.52Ti0.48)O3 powders were prepared by hydrothermal synthesis. Using soluble salts such as Pb(NO3)2, TiCl4 and ZrOCl2$.$8H2O and oxide such as PbO and TiO2 as starting materials, PZT powder was hydrothermally synthesized at the temperature range between 150$^{\circ}C$ and 200$^{\circ}C$. The result showed that reactivity by alkali was decreased in the sequence of Pb(NO3)2, TiCl4, ZrOCl2, PbO, TiO2 and ZrO2. Using the first three soluble salts, PZT powder was synthesiged at 150$^{\circ}C$ for 1hr. In PbO-TiCl4-ZrOCl2 system, PZT powder was synthesized at 150$^{\circ}C$ for 8rs. In Pb(NO3)2-TiO2-ZrOCl2 system, PZT powder was synthesized at 150$^{\circ}C$ for 16hrs, in PbO-TiO2-ZrOCl2 system, the powder was synthesized at 200$^{\circ}C$ for 8hrs.

• 한국세라믹학회지
• /
• 제24권3호
• /
• pp.263-269
• /
• 1987

It is investigated that the determination of the correlation between the change of microstructure and electrical properties. Yttria is added to the compositiojn of rhombohedral region in Pb(Mg1/3Nb2./3)O3-PbTiO3-PbZrO3 ternary system. Average grian size, lattice parameters and distribution of yttrium are characterized by XRD, SEM and EDS. Electrical properties are determined by measurement of Curie temperature, piezoelectric properties and hysteresis loops. The results are as follows; 1. Both lattice parameters, a and ${\alpha}$, are changed by addition of yttria to the composition of rhomboheadral region in Pb(Mg1/3Nb2./3)O3-PbTiO3-PbZrO3 ternary system and Curie temperature is proportional to the values at (90-${\alpha}$).

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1991년도 하계학술대회 논문집
• /
• pp.194-197
• /
• 1991

In this study, $(Pb_{0.99}La_{0.01})[(Sb_{1/2}Sn_{1/2})_{0.10}Ti_{0.25}Zr_{0.65}]O_3$, added $MnO_2$ (0-0.30[mol%]) ceramics were fabricated by the mixed oxide method. The sintering temperature and time were $1250[^{\circ}C]$, 2[hr], respectively. In the $(Pb_{0.99}La_{0.01})[(Sb_{1/2}Sn_{1/2})_{0.10}Ti_{0.25}Zr_{0.65}]O_3$ added $MnO_2$ (0.24[mol%]) specimens, relative dielectric constant and dielectric loss were minimum values 3.52, 0.003, respectively, and Curie temperature were highest values $256[^{\circ}C]$. Pyroelectric coefficient and voltage responsivity of the $(Pb_{0.99}La_{0.01})[(Sb_{1/2}Sn_{1/2})_{0.10}Ti_{0.25}Zr_{0.65}]O_3$, and added $MnO_2$ (0.24[mol%]) specimen were good values, $6.73{\times}10^{-8}[C/cm^2K],\;125[v/W]$, respectively. Figure of merit of pyroelectric current, voltage and detectivity of the specimen, $(Pb_{0.99}La_{0.01})[(Sb_{1/2}Sn_{1/2})_{0.10}Ti_{0.25}Zr_{0.65}]O_3$ added $MnO_2$ (0.24[mol%]) were good values $2.714{\times}10^{-8}[Ccm/J],\;7.706{\times}10^{-11}[Ccm/J],\;2.640{\times}10^{-8}[Ccm/J]$, respectively. Voltage responsivity of the $(Pb_{0.99}La_{0.01})[(Sb_{1/2}Sn_{1/2})_{0.10}Ti_{0.25}Zr_{0.65}]O_3$ added $MnO_2$ (0.24[mol%]) specimens were decreased with increasing the chopper frequency.

• 한국세라믹학회지
• /
• 제22권2호
• /
• pp.17-24
• /
• 1985

In the composition of $Pb(Mg_{0.15} W_{0.15})Ti_{0.35}-Zr_{0.35}O_3$ the effect of particle size on PbO vaporization were measured, . The initial step of discontinuous vaporization of unreated PbO during the calcining process was depended on the particle size. All additives $La_2O_3Nb_2O_5$ and $Al_2O_3$ inhibited the grain growth of the composition $Pb(Mg_{0.15} W_{0.15})Ti_{0.35}-Zr_{0.35}O_3$ +2wt% excess PbO. The dielectric and piezoelectric properties of the composition $Pb(Mg_{0.15} W_{0.15})Ti_{0.35}-Zr_{0.35}O_3$ were improved by the addition of 2wt% excess PbO and proper additive. The electromechanical planar coupling factor of 0.65 and mechnical quality factor of 390 could be obtained by adding 5wt% $Nb_2O_5$ to the composition 2wt% excess PbO+$Pb(Mg_{0.15} W_{0.15})Ti_{0.35}-Zr_{0.35}O_3$.

• 한국결정성장학회지
• /
• 제13권2호
• /
• pp.63-67
• /
• 2003

Synthesis of $PbLaTiO_{3}$ : Mn powders containing La and Mn was carried out using $PbO,\;TiO_{2},\;La_{2}O_{3}\;and\;MnO_{2}$ as starting materials by hydrothermal method. In the synthesis of single phase $PbLaTiO_{3}$ : Mn powder containing La and Mn, the optimal x value corresponding to La substitution was 0.01 which corresponds to $0.99(Pb_{1-x}La_{2x/3}TiO_{3})+0.01MnO_{2}$. The optimal conditions for the preparation of the powder synthesis were 8 M-KOH solvent of hydrothermal solvent, $270^{\circ}C$ of reaction temperature and 24 hrs of run time. It was found that the synthesized powders had spherical morphology with average particle size of 70 nm and specific surface area of $5.5\;m^{2}/g$.

• 한국전기전자재료학회논문지
• /
• 제19권3호
• /
• pp.228-232
• /
• 2006

In this paper, in order to develop low temperature sintering $PbTiO_3$-system piezoelectric ceramics for thickness-vibration-mode piezoelectric transformer, $Pb_{0.76}Ca_{0.24}[(Mn_{1/3}Sb_{2/3})_{0.04}Ti_{0.96}]O_3$ ceramics using $0.25\;wt\%\;CaCO_3$ and $0.2\;wt\%\;Li_{2}CO_3$ as sintering aids were manufactured according to the variation of poling field. The specimens could be sintered at $930\;^{\circ}C$. The piezoelectric properties were investigated according to the poling field. The maximum properties showed at the field of 6.5 kV/mm, which had kt of 0.49, Qmt of 1816, and $d_{33}$ of 81.4 pC/N.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 추계학술대회 논문집 Vol.18
• /
• pp.176-177
• /
• 2005

In this paper, in order to develop low temperature sintering $PbTiO_3$-system piezoelectric ceramics for thickness-vibration-mode piezoelectric transformer, $Pb_{0.76}Ca_{0.24}[(Mn_{1/3}Sb_{2/3})_{0.04}Ti_{0.96}]O_3$ ceramics using $0.25wt%CaCO_3$ and 0.2wt%$Li_2CO_3$ as sintering aids were manufactured according to the variation of poling field. Specimens could be sintered at the sintering temperature of $930^{\circ}C$. The piezoelectric properties increased according to the increase of poling field and showed the maximum values (kt=0.49, Qmt=1816, and $d_{33}$=81.4pC/N) under 6.5kV/mm.