• Journal of the Korea Organic Resources Recycling Association
• /
• v.20 no.2
• /
• pp.15-19
• /
• 2012

Wood wastes could be renewable resources by recycling as particleboard manufacturing or energy production. Particle board is the most common item of wood waste recycling and energy production from wood wastes has highlighted for energy recovery to reduce greenhouse gas generation in recent years. The aim of this study was to evaluate the environmental benefits of the processes for particle board manufacturing and energy production. The functional unit was one ton of wood wastes and the environmental impact was analyzed by life cycle assessment methodology. The result was that 112kg of carbon dioxide equivalent was produced from particle board manufacturing process and 382kg of carbon dioxide equivalent was produced from combined heat and power generation process. The concept of temporary biomass carbon storage was to applied to this study.

• Journal of the Korean Wood Science and Technology
• /
• v.11 no.3
• /
• pp.39-48
• /
• 1983

This research was performed to investigate the manufacturing possibility of the particleboard treated with commercial fire retardant chemicals. Laboratory test boards at this investigation were made from particles treated by soaking into 5, 10, 15, and 20 percent concentration solutions of ammonium sulfate and Minalith before resin was applied. According to the results, MOR (modulus of repture) and MOE (modulus of elasticity) in flexure exceeded type 100 (100 kgf/$cm^2$, $1.5{\times}10^4\;kgf/cm^2$) of the Korean Industrial Standard (KS F 3104). Except for 15 and 20 percent chemicals concentrations of Minalith, every internal bond stress values met type 100 (1.5 kgf/$cm^2$) of KS F 3104. However thickness swelling values of fire retardant treated particleboards were not reached in the Standard (12%).

• Journal of the Korean Wood Science and Technology
• /
• v.44 no.4
• /
• pp.600-606
• /
• 2016

Wood-based composite panels such as plywood, particleboard (PB), or medium density fiberboard (MDF) are mostly used in the lamination on their surface for the manufacturing of furniture, or interior building products, the concern on the formaldehyde emission (FE) from the surface laminated wood panels is increasingly attracting attentions from the public. Thus, this study was conducted to understand influence of surface laminating materials to the FE from PB and MDF with or without edge sealing, using 24-hour desiccator method. Both PB samples that had been laminated on their surface with low-pressure laminate (LPL) or polypropylene (PP) film and MDF that had been treated with poly(vinyl chloride) (PVC) or coating were tested for the FE with or without edge sealing. As expected, the FE of PB with the sealed edges decreased to 37.4% and 80.7% with the LPL and PP lamination, respectively. The surface laminated MDF with the sealed edges also showed a decrease in the emission up to 57.8% and 54.3%, with the PVC lamination and coating, respectively. However, the coated MDF samples showed 5.3% increase in the emission when their edges were not sealed, indicating a FE form the solvent used for coating. These results showed that the type of surface lamination materials on wood-based composite panels has a great impact on their resultant FE, indicating that the influence of surface laminating materials should be taken into consideration for the formaldehyde mission measurement.

• Journal of the Korean Wood Science and Technology
• /
• v.38 no.1
• /
• pp.11-16
• /
• 2010

Unlike other composites boards such as fiberboard and particleboard, plywood is manufactured with sheets of veneers. When the plywood manufactured, the adhesive is spreaded through gluelines on each surface of veneers. For that reason, formaldehyde emission of plywood can be considered as different way. Therefore, this research was conducted to understand the formaldehyde emission pattern of plywood. To measure formaldehyde emission, four different specimen preparing methods were used. The test specimen taken by a total surface area, a given number and a total side area showed inconsistent results. On the other hand, the result of formaldehyde emission showed consistency when considered only the length of adhesive layers.

• Journal of the Korea Furniture Society
• /
• v.11 no.2
• /
• pp.73-78
• /
• 2000

This study was carried out to measure formaldehyde emission with the passing of two years from plywood, sliver-board and strand-board bonded with urea resins which were made of 6 f/U molar ratios. The urea resins were manufactured by six kinds of formaldehyde/urea molar ratio of 1.0, 1.2, 1.4, 1.6, 1.8 and 2.0. 1. The plywood with molar ratio of 1.0 satisfied the KS F3101 $F_2$ directly after manufacture. The plywood with molar ratio of 1.2 satisfied m 3 days. The plywood with molar ratio of 1.4 satisfied the $F_3$ in 3 days and the $F_2$ in 600 days. And the plywood with molar ratio of 1.8 and 2.0 satisfied the $F_3$ in 365 days, but didn't satisfy the $F_2$ in 730 days. 2. Sliver-board with molar ratio of 1.0 and 1.2 satisfied the KS F3104 $E_2$ right after manufacture. Sliver-board with molar ratio of 1.4 and 1.6 satisfied in 150 and 360 days, respectively. Sliver-board with molar ratio of 1.8 and 2.0 satisfied in 730 days. 3. Strand-board with molar ratio of 1.0 and 1.2 satisfied the KS F3104$ E_2$ directly after manufacture. Strand-board with molar ratio of 1.4 and 1.6 satisfied in 150 days. But Strand-board with molar ratio of 1.8 and 2.0 didn't satisfied in 730 days.

• Journal of Korean Society of Forest Science
• /
• v.104 no.2
• /
• pp.254-260
• /
• 2015

This paper assesses the tariff reduction on imported wood products that will have impact on the demand for domestic wood products in South Korea, by estimating the Armington substitution elasticities based on the assumption that they are imperfect substitutes. Results indicate that domestic and foreign wood products are far from perfect substitutes to each other. The substitution elasticities in plywood and fiberboard appeared to be high, implying that tariff reduction may have negative effects on those industries. On the contrary, imported and domestic particleboard showed a low substitution elasticity. The decline of fiberboard industry may lead to the decline in forestry since fiberboard is produced mainly by thinned woods supplied from domestic forests. Therefore, effective countermeasures to enhance the competitiveness of wood products industry are needed to cope with the market opening.

• Journal of the Korean Wood Science and Technology
• /
• v.50 no.2
• /
• pp.93-103
• /
• 2022

Currently, biofibers are used as a reinforcement in polymer composites for structural elements and construction materials instead of the synthetic fibers which cause environmental problems and are expensive. One of the chemicals with a pH close to neutral that can be potentially used as a modified fiber material is sodium chloride (NaCl). Therefore, this study aims to investigate the characteristics of a composite board made from NaCl-treated kenaf fiber. A completely randomized design method was used with consideration of two factors: the content of NaCl in the treatment solution (1 wt%, 3 wt%, and 5 wt%) and the duration of immersion of fibers in the solution (1 h, 2 h, and 3 h). The NaCl treatment was conducted by soaking the fibers in the solution for different durations. The fibers were then rinsed with water until the pH of the water reached 7 and subsequently dried inside an oven at 80℃ for 6 h. Kenaf fiber and epoxy were mixed manually with the total loading of 20 wt% based on the dry weight of the fiber. Physical and mechanical properties of the fibers were then evaluated based on JIS A 5908 particleboard standards. The results showed that increasing NaCl content in the fiber treatment solution can increase the physical and mechanical properties of the composite board. The properties of fibers treated with 5 wt% NaCl for 3 h were superior with a modulus of elasticity of 2.085 GPa, modulus of rupture of 19.77 MPa, internal bonding of 1.8 MPa, thickness swelling of 3%, and water absorption of 10.9%. The contact angle of untreated kenaf fibers was 104°, which increased to 80° and 73° on treatment with 1 wt% and 5 wt% NaCl for 3 h, respectively.

• Journal of Korean Society of Forest Science
• /
• v.98 no.4
• /
• pp.417-425
• /
• 2009

This study analyzed core issues addressed in the tentative agreement of WTO ministerial meetings held to finish WTO/DDA negotiations in Geneva in July 2008. The objectives of this study are to analyze changes in tariff reduction on timber products, and their influence on demand and supply of the items according to the modality of Non-Agricultural Market Access (NAMA) and to provide basic information for strategy formulation of our country for further WTO/DDA negotiations. The results indicate that there will not be significant changes in the tariff on sawnwood and on veneer sheets, however, the tariff on plywood need to be cut by around 50% from the applicable tariff rates of 2008 on condition that our country is in the position of developed countries. Therefore, the item of plywood is expected to be influenced greatly according to the change in tariff reduction. From the analysis of influence of tariff reduction on the demand and supply of timber products including sawnwood and wood based panels, such as plywood, particleboard, and fiberboard, the import quantities of the items are expected to be changed from 0.8% to 13.3% if our country is in the position of developed countries, however, they are expected to decline by 0.8%~44.3%, if our country is in the position of developing countries (22, coefficient for developing members).

• Journal of the Korean Wood Science and Technology
• /
• v.34 no.5
• /
• pp.42-51
• /
• 2006

The this study, the effect of rice husk flour (RHF) as scavenger on formaldehyde emission rate and formaldehyde content from urea-formaldehyde (UF) resin bonded RHF content wood particleboards (PB). Two type of particle size ($30{\mu}m$ and $300{\mu}m$) of RHF was premixed with the UF resin at 5% and 15% by weight. The performance of UF resins is greatly influenced by the curing characteristics in their curing processing. The curing behavior was monitored activation energy ($E_a$) by DSC and pH variation according to RHF contents. PB with dimensions of $27cm{\times}27cm{\times}0.7cm$ was prepared at a specific gravity of 0.75 using $E_1$ and $E_2$ class UF resins. Formaldehyde emission and formaldehyde content from RHF filled PB bonded with UF resin was measured by 24 h desiccator and perforator method, respectively. RHF causes an increased pH of UF resin. $E_a$ of the modified UF resin decreased independently of RHF particle size. As the pH and the $E_a$ variation of the UF resin containing RHF increased, the amount of formaldehyde content decreased. The formaldehyde emission and formaldehyde content levels of the PB bonded with 15 wt% of $30{\mu}m$ RHF and $E_2$ type UF resin were low and satisfied grade $E_1$, as measured by 24 h desiccator and perforator method. The result of a comparison between 24 h desiccator and perforator test using PB showed that the linear regression analyses show a good correlation between the results for the 24 h desiccator and the perforator tests. The linear regression of a correlation between the desiccator and the perforator was Y=4.842X-0.064 ($R^2=0.989$). RHF was effective at reducing formaldehyde emission and formaldehyde content in urea-formaldehyde adhesives when used as scavenger.

• Journal of the Korean Wood Science and Technology
• /
• v.11 no.1
• /
• pp.12-17
• /
• 1983

The shear strength of plywoods using Douglus-fir bark powder and particlebard sander dust(PSD), abandoned materials in plywood and particleboard industries, as extender to UF resin, was compared with that of plywoods using wheat flour. Extenders were mixed at the rate of 0%, 5%, 10%, 20%, and 30% of UF resin weight. In obtained results, the dry shear strength of all extended plywoods was highest at extending ratio 5% and the wet shear strength was highest at no extending and 5%. Douglas-fir bark powder-and PSD-extended plywoods had as high dry and wet shear strength as wheat flour-extended plywoods up to extending ratio 10% and 20% respectively. But at 300%, wheat flour-extended plywoods had higher shear strength. Douglas-fir bark powder and PSD size should have been reduced (enough to pass through 325 mesh screen) in order to develop the satisfactory mixing, spreading and plywood bond quality. But in this study the powders to pass through 100 mesh screen were used.